AU738836B2

AU738836B2 - Method and apparatus for the measurement of film formation temperature of a latex

Info

Publication number: AU738836B2
Application number: AU52909/98A
Authority: AU
Inventors: Marilyn Emily Karaman; Barry William Ninham; Richard Mark Pashley
Original assignee: Australian National University
Current assignee: Australian National University
Priority date: 1997-02-17
Filing date: 1998-02-03
Publication date: 2001-09-27
Anticipated expiration: 2018-02-03
Also published as: AU5290998A; GB2322453B; GB2322453A; GB9803148D0

Description

AUSTRALIA

PATENTS ACT 1990 COMPLETE SPECIFICATION NAME OF APPLICANT(S):

I'

T

tKiI.nmLt anan ana nt .pany AN- The Australian National University I.o ADDRESS FOR SERVICE: DAVIES COLLISON CAVE Patent Attorneys 1 Little Collins Street, Melbourne, 3000.

INVENTION TITLE: Method and apparatus for the measurement of film formation temperature of a latex The following statement is a full description of this invention, including the best method of performing it known to me/us:- 2 The critical temperature required for a latex coating to form a strong, continuous film is important in the design and use of these coatings. This temperature is known as the minimum film formulation temperature

(MFFT).

Presently, an optical method is employed to measure the MFFT. The method involves the observation of the clarity of a cast film on a large metal table. A temperature gradient is applied to the table and the position on the table where the film is judged to be clear is noted. The temperature at that point on the table is determined to be the MFFT value. This technique may provide variable, operator dependent results. Another difficulty with this method is that only optically dear latexes can be tested. Pigments and other additives which are known to alter the MFFT cannot be used using this method. Accordingly a method to objectively measure the film formation temperature of a latex is desirable, especially a method which can also be used with pigmented latices.

One aspect of the present invention is a method for measurine the minimum film formation temperature of latex comprising: providing the latex; measuring the initial conductivity of the latex; measuring the temperature of the latex heating the latex; measuring the conductivity of the latex while it is being heated; determining the point in which the conductivity slope of the latex changes sharply; and determining the minimum film formnation temperature by calculating the maximum point in the curve described by versus temperature.

Another aspect of the present invention provides apparatus for the film formation temperature a latex, comprising: a container for holding a latex in solution; means for measuring the conductivity of the latex; means for measuring the temperature of the latex means for modifying the temperature of the latex provided in the container; and 3 means for determining the minimum film formation temperature by calculating the maximum point in the curve described by d2K/dT 2 temperature.

The film formation properties of latex materials, such as paints and other coatings, can be dried in a controlled manner using osmotic suction to the point where latex becomes critically dependent on temperature. At the MFFT value the latex particles soften and deform, which in turn changes the solid drying curve.

Surprisingly, the conductivity of the latex is also sensitive to this same transition point and is an ideal parameter for monitoring this change.

As used throughout the specification, conductivity of the latex will be used to determine the MFFT.

ions in the latex between the particles while under osmotic suction. At the *o *o O oo ft fo plotting the conductivity of a latex solution at various temperatures it is possible to calculate the rate of change of the conductivity of the latex versus the rate of change of the temperature (dK/dT) versus temperature. This is the first also done by calculating the first derivative of the conductivity versus temperature curve.

By calculating the second derivative of the conductivity versus temperature versus temperature, the MFFT can be calculated.

The maximum in this curve is at the minimum film formation temperature.

This result is provided by fundamental principles of calculus. The ability to calculate the rate of change of the conductivity per the rate of change of temperature by taking a derivative is known by those with skill in the art.

The direction of the transition may be altered by the frequency at which the conductivity is measured. The present invention and the accompanying examples were conducted at 1000 HZ, although those with skill in the art could easily vary the frequency employed. The transition may be altered or enhanced by variation of the frequency without departing from the scope of the present invention.

Three representative curves are presented in Figure i. Figure IA depicts a typical conductivity versus temperature curve. Figure 1B depicts the first derivative calculated from the conductivity versus temperature curve. The curve describes the conductivity rate of change divided by the rate of change of the temperature plotted versus temperature. Figure 1C depicts the second derivative calculated from the conductivity versus temperature S curve. The negative of the second derivative is provided to have positive number. As depicted in the figure, the maximum point of the curve is the minimum film formation temperature.

o Figures 2A, 2B and 2C are provided to demonstrate the reverse transition of the curves found in Figure 1. These curves may be generated depending on the latex sample provided. If the sample provides these curves it will be necessary to calculate the d2K/dT in order to determine the minimum film formation temperature.

Figure 3A is a cross sectional view 6f the cell body (10) used to dry and maintain the latex. The cell body is constructed of a suitable material such as metals, plastics or ceramics. Suitable metals include aluminum, copper and iron, and alloys such as steel, stainless steel, brass and bronze.

Preferably the cell is constructed of a non-corrosive material, such as stainless steel. The cell has an osmotic membrane The cell can be used with a wide range of membrane materials. The membrane materials affects the rate of drying and whether any additives are leached out with water. For example, use of a reverse osmosis membrane cellulose acetate) will allow drying to occur at a low rate and will only allow water to pass through the membrane. Low molar mass solutes such as salts and additives such as ethylene glycol will not be withdrawn form the latex solution.

Use of dialysis membrane with a molar mass cut-off of 1000 gram mole 1) enables much faster drying and has been used successfully.

However, some loss of low molar mass solutes may occur. The loss of the solutes does not appear to alter the observed MFFT value.

Referring to Figure 3A, in the upper portion of the cell body a cavity is provided (15) in which the latex is provided. In the lower portion of the cell body on the side opposite of the latex solution a cavity (50) is provided to hold a solution of PVP. PVP is employed because accurate osmotic pressure values are available in the literature, such as the PVP osmotic pressure data given in: H. Link, European Polymer Journal, 1971, vol. 7, 1411-1419.

PVP

is also desirable because it is very water soluble and is available with a wide S: range of average molar mass values. The polymer solution generates an osmotic suction pressure acting on the water in the latex through the semi- S: permeable membrane.

Rapid, convenient drying was obtained using 10,000 gram-mole-' PVP with a dialysis membrane with a molar mass cut off of 1,000 gram-mole-'.

That is the membrane will only allow passage of low molar mass solutes less than 1,000 gram-mole'.

An alternative method would be to use sugar or salt solution to generate an osmotic suction across a reverse osmosis membrane. A reverse "i osmosis membrane will allow only water to pass. These membranes are, however, significantly slower at water transfer, although this can be compensated to some extent by the use of rnuch higher osmotic pressures.

S* Apertures for a conductivity electrdde (30) and thermistor (20) are also provided. The cell body is preferably threaded on both the top and bottom of the cell body (70) in order to facilitate the filling, emptying and cleaning of the cell body. Gasketing material (80) such as rubber o-rings are provided to minimize leakage of the fluids from the cell body. Ports (95) with a central cavity (96) are provided to facilitate free transfer of water across the membrane. Fastens such as screws, (75) are preferably provided in order to facilitate the easy assembly and disassembly of the cell body.

In an alternative embodiment of the invention, the cell body is replaced with a piece of dialysis tubing. Figure 3B illustrates an arrangement which employs a piece of tubing in order to contain a latex.

Suitable tubing, such as tubing used in dialysis treatments (25) is employed. The latex solution (15) is added to the tubing. PVP or other suitable solutions (50) is provided to the chamber (65) in which the dialysis tubing is immersed. Means for measuring the temperature, such as a thermistor and a conductivity measuring device, conductivity electrode are provided within the tubing.

The tubing and the PVP solution are contained in a jacketed cell The jacketed cell contains an annular space in which a heat transfer fluid, such as water is provided. For simplicity the means for modifying the temperature of the heat transfer fluid, pumps, associated equipment for the collection of the conductivity and temperature measurements and other apparatus are omitted.

Figure 4 is a simplified diagram of the equipment employed in the Smeasurement of the minimum film formation temperature. The chamber (100) containing the latex is placed in the heat transfer fluid, a water bath.

The chamber has apertures suitable for connecting a thermistor (120) and conductivity measurement device (130). The thermistor is preferably connected to a temperature display (140) which in turn is connected to a digital analog interface (150). The digital analog interface is also connected to a conductivity meter (170). The digital analog interface is also connected to an electronic device (160) capable of measuring and modifying the temperature of the water bath. Means for both heating and cooling the water bath is preferably provided. A computer dvice (175) is preferably provided to both collect the conductivity and temperature data, as well as controlling and modifying the temperature of the water bath. In a preferred embodiment the computer is programmed to provide a print out of the information depicted in Figures 1 and 2, thereby providing the minimum film formation temperature. A computer with a 486 processor and the necessary associated software suitable for the task of collecting the required data and modifying the temperature of the water bath. The software employed was Labview, written by National Instruments, Austin, Texas.

The method of the present invention is performed as follows. The initial conductivity value of the latex sample is obtained and the data is recorded, preferably the data is transferred to a computer. The water bath remains at the specified temperature, typically about 2°C until the measured conductivity, with drying occurring, reaches a predetermined value.

The use of conductivity as a convenient and monitor of latex solids has been examined using Bruggeman equations Ann. Phys., 24, 636, 1935 and 'Surfactants in Solution', ed. Mittal and Lindeman, vol. 3 1982) on a range of latex samples. The standard form of the Bruggeman equation is: k k m(l- where k and k m are the conductivities of the latex solution and the continuous permeate) phase, respectively, and o is the volume fraction of the dispersed phase. The equation is most suitable for a monodisperse solution of non-conducting spheres. Preferably the predetermined value corresponds to the estimated conductivity value of approximately 75% solids in the latex.

Once this estimated conductivity is obtained the computer program e begins to ramp the temperature of the water bath at a continuous rate which "i is specified in the computer program. Typically the temperature of the water bath is increased at a rate of from about 1 0 C /hour and more preferably at a rate of 3 0 C /hour. Typically, the temperature of the water bath is raised to approximately 35 0 C while continuously monitoring the temperature and conductivity of the latex.

When the temperature of the bath reaches 35 0 C it is then maintained at this temperature until the temperature of the latex reaches approximately 0 C. At this latex temperature the test is concluded and the water bath is cooled and the sample removed.

The initial conductivity of the latex'solution is measured by the computer. The computer will then determine the conductivity of the latex solution achieved during osmotic drying at constant temperature. In addition, measurement of the initial latex conductivity, where percent solids is known, allow the calculation of both the permeate (continuous phase conductivity) and the conductivity expected at 75% by weight solids where it is desirable to begin the MFFT run for each latex sample. The Bruggeman equation should be valid up to about 75% solids, at which stage the latex particles will begin to come into physical contact with each other. When the conductivity at 75% solids value is reached the temperature ramp for the latex is started via the temperature bath. The temperature is then increased until it reaches the final desired temperature. The MFFT is then calculated from the curve by determining the rate of change of conductivity per rate of change of temperature versus temperature.

The present invention may be used to measure the minimum film formation temperature of a latex capable of forming a film. Such latices are suitable for use in a paints, lacquers, shellacs, stains and the like. As noted above, one advantage of the present invention is that the film forming substance may be pigmented as well as non-pigmented.

The following example are illustrative of the present invention. The following equipment was employed in the examples.

CDM 80 conductivity meter, platinum electrode; temperature meter and thermistor; Julabo F10 refrigerated water bath; 9** Jacketed glass cell; dialysis tubing (benzoylated cellulose) 1,000 molecular weight cutoff, tubing; Sigma Chemical Co.

40% by weight polyvinyl pyrrolidone solution of approximately 10,000 molecular weight, Aldrich Chemical Co.; 486 IBM personal computer; Software written for this application which stores conductivity and data temperature at a rate of approximately 3 data points per seconds, Labview, National Instruments, Austin, Texas.

*o Example 1 Apparatus and Method For Performing the Invention Using Tubing A 40% weight polyvinyl pyrrolidone (PVP) solution (approximately 10,000 molecular weight) was prepared arid transferred to a jacketed cell which is placed in a refrigerated water bath at 2 0 C. Plastic tubing suitable for use in dialysis, was softened by placing in water, wiped dry and one end was sealed. The tubing was filled with a precooled (about 2 0 C) latex sample and a conductivity electrode and thermistor were placed in the dialysis tubing and then the tubing was sealed. The tubing containing the sample was then placed into the cooled PVP solution.

A sample of Primal@ AC-261 acrylic latex Rohm and Haas Company) was tested in the apparatus described hereinabove. After an initial conductivity measurement the temperature of the water bath was ramped at a rate of 3°C per hour to a final temperature of 30°C. At the start of the temperature ramp the response between conductivity and temperature is linear. However as the latex solution approaches the MFFT temperature the response to the slope decrease rapidly. This is believed to be caused by the flattening of the latex particles and the reduction of pore size. For the AC-261 sample the MFFT occurred at a temperature of 10.5°C.

The conductivity versus temperature curve in Figure 3 was obtained from manual observation of the conductivity changes of latex sample AC-261, whereas Figure 6 was obtained and automatically using the instrument described. The MFFT values of Figures and 6 are substantially the same. The MFFT value was confirmed using the standard film casting method.

Example 2 Comparison of Bruggeman Equation Results to Observed Results Various latices were used to test the results provided by the Bruggeman equation and the results obtained by measuring the latex. The conductivity of the continuous phase was obtained via high pressure filtration of each latex sample through 6-8,000 molar mass cut-off dialysis membrane.

Latex Sample conductivity in mS/cm* o (meas)** e(calc)*** latex permeate 1 1.32 3.06 0.46 0.43 .2 1.87 5.40 0.47 0.51 3 3.00 8.05 0.50 0.48 4 2.55 7.35 0.50 0.51 mS/per centimeter refers to milli Slemen per cm. (A Siemen is an ohm measured calculated The results demonstrate that the standard Bruggeman equation is applicable to these samples and suggests that conductivity can be used quantitatively as a monitor of latex solids.

Document34-27WA)I 9A Throughout this specification and the claims which follow, unless the context requires otherwise, the word "comprise", and variations such as "comprises" and "comprising", will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of integers or steps.

The reference to any prior art in this specification is not, and should not be taken as, an acknowledgement or any form of suggestion that that prior art forms part of the common general knowledge in Australia.

oo *o*

Claims

1. A method for determining the minimum film formation temperature of a latex comprising: providing the latex; measuring the initial conductivity of the latex; measuring the temperature of the latex heating the latex; measuring the conductivity of the latex while it is being heated; determining the point in which the conductivity slope of the latex changes sharply; and determining the minimum film formation temperature by calculating the maximum point in the curve described by (+/-)d2K/dT2 versus temperature.

2. The method of claim 1 wherein the latex additionally contains a pigment.

3. The method of claim 1 wherein the latex is uniformly heated at the .o rate of 3°C per hour.

4. The method of claim 1 wherein the latex contains a pigment.

5. The method of claim 1 wherein the conductivity of the latex is measured when the latex solution contains from 65 to 80 percent by weight solids.

6. Apparatus for measuring the film formation temperature of a latex, said apparatus comprising: a container for holding a latex in solution; means for measuring the conductivity of the latex; means for measuring the temperature of the latex; means for modifying the temperature of the latex provided in the container; and means for determining the minimum film formation temperature by calculating the maximum point in the curve described by temperature.

7. The apparatus of claim 6 wherein the container is a piece of tubing. 11

8. The apparatus of claim 6 wherein the means for measuring the temperature of the latex is a thermistor.

9. The apparatus of claim 6 wherein the means for measuring the conductivity of the latex is a conductivity electrode. 4 o P:\OPER\Ar\1994397 pgl2.doc-13/07A1

12- A method for measuring film formation temperature substantially as hereinbefore described with reference to the drawings and/or Examples. 11. An apparatus for measuring film formation temperature substantially as hereinbefore described with reference to the drawings and/or Examples. DATED this 13th day of July, 2001. The Australian National University by DAVIES COLLISON CAVE 10 Patent Attorneys for the Applicant *o