Effect of cathodic pretreatment on the passivation of iron in neutral solution

Rauscher et al., 1977

Document ID
366011788917583601
Author
Rauscher A
Konno H
Nagayama M
Publication year
Publication venue
Electrochimica Acta

External Links

Snippet

Pure iron specimens anodically oxidized at+ 600 mV (vs sce) for one minute were partially reduced with a cathodic current of 10 μA/cm 2 and then reoxidized at the same potential for one hour. The experiment was performed in a boric acid/borate buffer solution at pH= 8.43 at …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/04—Anodisation of aluminium or alloys based thereon
    • C25D11/18—After-treatment, e.g. pore-sealing
    • C25D11/24—Chemical after-treatment
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/04—Anodisation of aluminium or alloys based thereon
    • C25D11/045—Anodisation of aluminium or alloys based thereon for forming AAO templates
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/26—Anodisation of refractory metals or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
    • C25D11/02—Anodisation
    • C25D11/30—Anodisation of magnesium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25F—PROCESSES FOR THE ELECTROLYTIC REMOVAL OF MATERIALS FROM OBJECTS; APPARATUS THEREFOR
    • C25F3/00—Electrolytic etching or polishing
    • C25F3/16—Polishing
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of work-pieces
    • C25D5/34—Pretreatment of metallic surfaces to be electroplated

Similar Documents

Publication Publication Date Title
Szklarska‐Smialowska et al. Electrochemical and Ellipsometric Investigations of Passive Films Formed on Iron in Borate Solutions: I. The Kinetics of Film Growth on Iron at Constant Anodic Potentials
McCafferty Sequence of steps in the pitting of aluminum by chloride ions
Nguyen et al. On the mechanism of pitting of aluminum
Brummer The use of large anodic galvanostatic transients to evaluate the maximum adsorption on platinum from formic acid solutions
Qafsaoui et al. Quantitative characterization of protective films grown on copper in the presence of different triazole derivative inhibitors
Pyun et al. The permeation of hydrogen through the passivating films on iron and nickel
Bardwell et al. Use of 18O/SIMS and electrochemical techniques to study the reduction and breakdown of passive oxide films on iron
Sobolev et al. Kinetics and mechanism of corrosion of oxide coating fabricated on aluminum alloy by the plasma electrolytic oxidation in molten salt
MacDougall et al. Mechanism of the anodic oxidation of nickel
EP2867390B1 (en) Method for producing tinplate and product produced therewith
Teramoto et al. The composition of passive films on ferritic 30Cr stainless steels in H2SO4
CN101260521A (en) Aluminum alloy surface rare earth chemical conversion treatment method
Markovac et al. The anodic deposition of iron oxide films on iron
Gardner et al. The hydrophilic nature of gold and platinum
US1946151A (en) Protecting aluminum from corrosion
CN112981415A (en) Preparation method and application of layered double-metal hydroxide-based composite film
US20210262107A1 (en) Process for treating the surface of a part made of aluminium or aluminium alloy or of magnesium or magnesium alloy
Rauscher et al. Effect of cathodic pretreatment on the passivation of iron in neutral solution
Brookes et al. Nucleation and growth of anodic films on stainless steel alloys I. Influence of minor alloying elements and applied potential on passive film growth
Mao et al. Anodic Film Studies on Steel in Nitrate‐Based Electrolytes for Electrochemical Machining
Wallinder et al. Influence of hydrogen in iron and in two stainless steels on aqueous and gaseous corrosion
Datta et al. Mass transport effects during electropolishing of iron in phosphoric-sulfuric acid
Mayne et al. Inhibition of the corrosion of iron by benzoate and acetate ions
US1946153A (en) Protecting aluminum from corrosion
Burstein et al. The first stages of dezincification of freshly generated brass surfaces in sulfuric acid solution