Yan et al., 2021 - Google Patents
Failure analysis of Erosion-Corrosion of the bend pipe at sewage stripping unitsYan et al., 2021
- Document ID
- 3293840645400637456
- Author
- Yan Z
- Wang L
- Zhang P
- Sun W
- Yang Z
- Liu B
- Tian J
- Shu X
- He Y
- Liu G
- Publication year
- Publication venue
- Engineering Failure Analysis
External Links
Snippet
Stainless-steel bend pipe is used to transport the media that contains H 2 S and NH 3 in sewage stripping unit. An obvious leakage occurs at the lateral wall and inner ridge of the elbow during service. Failure analysis is carried out by using traditional characterization …
- 238000005260 corrosion 0 title abstract description 70
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Yan et al. | Failure analysis of Erosion-Corrosion of the bend pipe at sewage stripping units | |
| Faes et al. | Corrosion and corrosion prevention in heat exchangers | |
| Zhu et al. | Erosion corrosion failure analysis of the elbow in sour water stripper overhead condensing reflux system | |
| Ilman | Analysis of internal corrosion in subsea oil pipeline | |
| Hu et al. | Case study on erosion–corrosion degradation of pipework located on an offshore oil and gas facility | |
| Sun et al. | Corrosion investigation of the inlet section of REAC pipes in the refinery | |
| Jin et al. | Failure analysis of multiphase flow corrosion–erosion with three-way injecting water pipe | |
| Elayaperumal et al. | Corrosion failures: theory, case studies, and solutions | |
| Ou et al. | Failure analysis of a reactor effluent air cooler | |
| Li et al. | Failure analysis of CO2 corrosion of natural gas pipeline under flowing conditions | |
| Bahadori | Corrosion and materials selection: a guide for the chemical and petroleum industries | |
| Zhang et al. | Corrosion behavior of X65 steel at different depths of pitting defects under local flow conditions | |
| Chen et al. | Erosion-corrosion coupling analysis of shale gas production pipe | |
| Liu et al. | Analysis on the corrosion failure of U-tube heat exchanger in hydrogenation unit | |
| Li et al. | Experimental testing and numerical simulation to analyze the corrosion failures of single well pipelines in Tahe oilfield | |
| Tang et al. | Failure analysis and prediction of pipes due to the interaction between multiphase flow and structure | |
| Liu et al. | Investigation of corrosion sequence in the overhead pipeline of H2S stripper column through CFD models | |
| Chen et al. | Comprehensive analysis of corrosion failure of blast furnace gas pipeline in a steel plant | |
| Yang et al. | Failure analysis on abnormal bursting of heat transfer tubes in spiral-wound heat exchanger for nuclear power plant | |
| Ali et al. | Corrosion-related failures in heat exchangers | |
| Chen et al. | Failure analysis on abnormal leakage of TP321 stainless steel pipe of medium temperature shifting gas in hydrogen production system | |
| Su et al. | Study of the mechanism of corrosion initiation and development in the elbow of a desulfurization unit | |
| Zheng et al. | Investigation on the deposition failure of a reactor effluent air cooler in hydrocracking unit | |
| Valeh-e-Sheyda et al. | Structural improvement of a control valve to prevent corrosion in acid gas treating plant pipeline: an experimental and computational analysis | |
| Liu et al. | Failure analysis and prediction based on corrosion thinning behaviour of atmospheric tower top and volatilization line connection area |