Tanaka et al., 2006 - Google Patents
Fatigue crack propagation from a hole in tubular specimens under axial and torsional loadingTanaka et al., 2006
- Document ID
- 3284172907545502530
- Author
- Tanaka K
- Takahash H
- Akiniwa Y
- Publication year
- Publication venue
- International journal of fatigue
External Links
Snippet
Fatigue tests of crack propagation from a circular notch in thin-walled tubular specimens made of low-carbon steel were performed under cyclic uniaxial tension-compression, and combined loading of cyclic torsion with and without superposed static and cyclic axial …
- 125000004122 cyclic group 0 abstract description 28
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0014—Type of force applied
- G01N2203/0016—Tensile or compressive
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/025—Geometry of the test
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/0202—Control of the test
- G01N2203/0212—Theories, calculations
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/022—Environment of the test
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/06—Indicating or recording means; Sensing means
- G01N2203/0617—Electrical or magnetic indicating, recording or sensing means
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Shamsaei et al. | Effect of hardness on multiaxial fatigue behaviour and some simple approximations for steels | |
| Yang et al. | Rate-dependent constitutive models of S690 high-strength structural steel | |
| Gao et al. | Fatigue life of 7075-T651 aluminium alloy treated with vibratory stress relief | |
| Sun et al. | Proportional and non-proportional hardening behavior of dual-phase steels | |
| Lee et al. | Fatigue analysis under variable amplitude loading using an energy parameter | |
| Tanaka et al. | Fatigue crack propagation from a hole in tubular specimens under axial and torsional loading | |
| Hu et al. | Strain rate dependent constitutive behavior investigation of AerMet 100 steel | |
| Huang et al. | Cumulative fatigue damage in low cycle fatigue and gigacycle fatigue for low carbon–manganese steel | |
| Yin et al. | Study on ultra-low cycle fatigue behavior of austenitic stainless steel | |
| Zheng et al. | Low cycle fatigue and ratcheting behavior of 35CrMo structural steel at elevated temperature | |
| Nam et al. | Simulation of ductile fracture toughness test under monotonic and reverse cyclic loading | |
| Mariappan et al. | Influence of prior fatigue damage on tensile properties of 316L (N) stainless steel and modified 9Cr-1Mo steel | |
| Scott-Emuakpor et al. | A new distortion energy-based equivalent stress for multiaxial fatigue life prediction | |
| Alvarez-Armas et al. | Microstructure associated with crack initiation during low-cycle fatigue in a low nitrogen duplex stainless steel | |
| Perez et al. | Linear-elastic fracture mechanics | |
| Rozumek et al. | Surface cracks growth in aluminum alloy AW-2017A-T4 under combined loadings | |
| Guo et al. | Fatigue failure mechanism and life prediction of a cast duplex stainless steel after thermal aging | |
| Zhang et al. | Mechanisms and fatigue performance of two steels in cyclic torsion with axial static tension/compression | |
| Gao et al. | Experimental study of fatigue behaviour of Q690qENH bridge weathering high-strength steel welded joints | |
| Yonezu et al. | Evaluation of threshold stress intensity factor of hydrogen embrittlement cracking by indentation testing | |
| Morishita et al. | Multiaxial fatigue property of Ti–6Al–4V using hollow cylinder specimen under push-pull and cyclic inner pressure loading | |
| Seok et al. | A study on the decrease of fracture resistance curve under reversed cyclic loading | |
| Liu et al. | Fatigue life prediction based on the hysteretic loop evolution of carbon steel under tensile cyclic loading | |
| Abbasnia et al. | Experimental and numerical investigation of ratcheting behavior in seamless carbon steel 90° elbow pipe with small dimensions under constant internal pressure and in-plane cyclic bending | |
| Ohkawa et al. | Notch effect on torsional fatigue of austenitic stainless steel: Comparison with low carbon steel |