Katsamas et al., 2004 - Google Patents
Stress-corrosion cracking of a Monel 400 tubeKatsamas et al., 2004
- Document ID
- 2262062670225970222
- Author
- Katsamas A
- Haidemenopoulos G
- Zervaki A
- Melas I
- Publication year
- Publication venue
- Journal of Failure Analysis and Prevention
External Links
Snippet
Abstract A bent Ni-Cu Monel 400 alloy tube, which operated as part of a pipeline in a petrochemical distillery installation, failed by through-thickness cracking. The pipeline was used to carry a stream of gaseous hydrocarbons containing hydrochloric acid (HCl) into a …
- 238000005260 corrosion 0 title abstract description 31
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Chen et al. | Stress corrosion cracking of type 321 stainless steels in simulated petrochemical process environments containing hydrogen sulfide and chloride | |
| Yang et al. | Failure analysis of a 304 stainless steel heat exchanger in liquid sulfur recovery units | |
| Crook | Corrosion of Nickel and Nickel-Base Alloys | |
| Holmes et al. | Sour service limits of dual-certified 316/316L austenitic stainless steel and weldments | |
| Katsamas et al. | Stress-corrosion cracking of a Monel 400 tube | |
| Takabe et al. | Application limits for 110ksi strength grade super 13Cr steel in CO2 environments containing small amounts of H2S | |
| Farmer et al. | Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers | |
| Leinonen et al. | Effect of selective dissolution on stress corrosion cracking susceptibility of austenitic and duplex stainless steels in alkaline solutions | |
| Gosh | Wet H2S cracking problem in oil refinery processes-Material selection and operation control issues | |
| Lu et al. | Effect of iron content on localised corrosion resistance of Ni-Cr-Mo alloy weld overlays in chloride ion-containing environments | |
| Fischer et al. | Investigation of the Sulfide Stress Cracking and Stress Corrosion Cracking Behaviors of Duplex and Lean Duplex Stainless Steel Parent and Welded Materials in Sour Service | |
| Rajole et al. | Failure analysis of industrial discharge hopper pipe | |
| Esteban et al. | Stress Corrosion Cracking of Superduplex Stainless Steels for Use in H2S Containing Environments in Oil and Gas Production | |
| Mitelea et al. | Susceptibility to Stress Corrosion Cracking in Hydrogen Sulfide Environment of MAG Welded Joints of API 5L x 65M Thermomechanical Treated Steel | |
| Bakkar et al. | Failure analysis of heat exchanger tubes of Ni-200 alloy in a titanium tetrachloride vaporizer | |
| Li et al. | Failure analysis of some petrochemical plant components | |
| Chen et al. | Stress corrosion cracking of type 321 stainless steels under simulated petrochemical conditions containing thiosulfate and chloride | |
| Jung et al. | Failure analysis of an operator shaft in a marine flow control valve | |
| Zheng et al. | Failure analysis of duplex stainless steel in an atmospheric tower | |
| Le Manchet et al. | Corrosion resistance of the lean duplex material UNS S32202 for oil & gas applications | |
| Crum et al. | Corrosion resistance of nickel alloys in caustic solutions | |
| Hinds et al. | Testing of supermartensitic stainless steel welds under cathodic protection at very low strain rates | |
| Hoffman et al. | Metallurgical evaluation of alloy 800HT pigtails | |
| Haase et al. | Influence of plastic strain on the resistance of heavy-wall SAWL large-diameter pipes to hydrogen induced cracking and sulfide stress cracking | |
| Esteban et al. | Evaluation of the Stress Corrosion Cracking of Different CRAs in Sour Well Environments |