Slovikovskii, 2008 - Google Patents

Rotary kiln corrosion-erosion-resistant linings

Slovikovskii, 2008

Document ID
16401510751045400109
Author
Slovikovskii V
Publication year
Publication venue
Refractories and Industrial ceramics

External Links

Snippet

The properties of magnesia refractories are studied with the aim of determining the possibility of their use for lining rotary kilns. Periclase-chromite refractory PKhPP has been developed with an increased Cr 2 O 3 content, whose use combined with a laying cement …
Continue reading at link.springer.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/03—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on magnesium oxide, calcium oxide or oxide mixtures derived from dolomite
    • C04B35/04—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on magnesium oxide, calcium oxide or oxide mixtures derived from dolomite based on magnesium oxide
    • C04B35/043—Refractories from grain sized mixtures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5427—Particle size related information expressed by the size of the particles or aggregates thereof millimeter or submillimeter sized, i.e. larger than 0,1 mm
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/66—Monolithic refractories or refractory mortars, including those whether or not containing clay
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B7/00—Hydraulic cements
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21B—MANUFACTURE OF IRON OR STEEL
    • C21B7/00—Blast furnaces
    • C21B7/04—Blast furnaces with special refractories

Similar Documents

Publication Publication Date Title
Chen et al. Degradation mechanisms of alumina-chromia refractories for secondary copper smelter linings
Ko Role of spinel composition in the slag resistance of Al2O3–spinel and Al2O3–MgO castables
CN107140957A (en) A kind of Zinc volatilization kiln pink fused alumina Mg-Al spinel brick and preparation method thereof
EP2792656B1 (en) Method for producing a silicon carbide whisker-reinforced refractory ceramic composition
Slovikovskii Rotary kiln corrosion-erosion-resistant linings
Banerjee Properties of refractories
Hino et al. Fatigue failure behavior of Al2O3–SiO2 system bricks under compressive stress at room and high temperatures
Jiao et al. Properties and Application of a New Type Carbon Composite Brick Used for Blast Furnace Hearth
Slovikovskii et al. Creation of high-efficiency promising refractory materials and constructions for the lining of metallurgical units
Srivastava et al. The effect of mechanochemically activated MgO in Al2O3–MgO–C refractory. Part I: Formulation and properties
Slovikovskii et al. More durable lining for horizontal copper-nickel converters
Varga et al. Abrasive wear of ceramic wear protection at ambient and high temperatures
Bounziová et al. Testing magnesia-carbon bricks for oxidation resistance
Slovikovskii et al. Efficient Corrosion/Erosion-Resistant Linings for Rotary Kilns
CN105745184A (en) Blast furnace hearth lining structure
US3125454A (en) Insulating compositions
Ovčačík et al. Technology of refractory materials and heat insulating materials
Qiang et al. Novel Flexibilizer for Cement Rotary Kiln Bricks
Slovikovskii et al. Durable Structures for the Lining of Electric-Arc Furnaces Used to Make Ferronickel and Granular Mattes
Primachenko et al. Advanced refractory articles and materials for the metallurgical industry
Slovikovskii et al. Trouble-Free Construction of a Large Diameter Waelz Kiln Lining with Increased Life
Wynn et al. Improved Monolithic Materials for Lining Aluminum Holding & Melting Furnaces
Lindstad Maintenance and major repairs of tap-holes and tapping spouts
Maistry Analysis of torpedo ladle refractories experiencing premature failure at the spout
Petrov et al. Optimization and Design of a New Torpedo Lining