Novel method for preparing controllable nanoporous a-Fe2O3 and its reactivity to SCR de-NOx

Liu et al., 2017

View PDF
Document ID
15896533455652707899
Author
Liu H
Zhang Z
Li Q
Chen T
Zhang C
Chen D
Zhu C
Jiang Y
et al.
Publication year
Publication venue
Aerosol and Air Quality Research

External Links

Snippet

ABSTRACTControllable nanoporous hematite (CNH, α-Fe2O3) was prepared by thermal treatment of α-FeOOH at different temperatures, and the SCR activity of the prepared α- Fe2O3 was evaluated. XRD (X-ray diffraction), HRTEM (high-resolution transmission …
Continue reading at aaqr.org (PDF) (other versions)

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS, COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/02—Solids
    • B01J35/10—Solids characterised by their surface properties or porosity
    • B01J35/1052—Pore diameter
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS, COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
    • B01J23/76—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
    • B01J23/84—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J23/889—Manganese, technetium or rhenium
    • B01J23/8892—Manganese
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
    • B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
    • B01D53/9404—Removing only nitrogen compounds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS, COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/02—Impregnation, coating or precipitation
    • B01J37/0201—Impregnation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/74—General processes for purification of waste gases; Apparatus or devices specially adapted therefor
    • B01D53/86—Catalytic processes
    • B01D53/8621—Removing nitrogen compounds
    • B01D53/8625—Nitrogen oxides
    • B01D53/8628—Processes characterised by a specific catalyst
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS, COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/08—Heat treatment

Similar Documents

Publication Publication Date Title
Liu et al. Novel method for preparing controllable nanoporous a-Fe2O3 and its reactivity to SCR de-NOx
Xue et al. Cu-ZSM-5 catalyst impregnated with Mn–Co oxide for the selected catalytic reduction of NO: physicochemical property–catalytic activity relationship and in situ DRIFTS study for the reaction mechanism
Li et al. The enhanced Zn resistance of Mn/TiO2 catalyst for NH3-SCR reaction by the modification with Nb
Yuan et al. Montmorillonite based porous clay heterostructures modified with Fe as catalysts for selective catalytic reduction of NO with propylene
Li et al. ZSM-5-supported V-Cu bimetallic oxide catalyst for remarkable catalytic oxidation of toluene in coal-fired flue gas
Hu et al. In situ DRIFTs investigation of the low-temperature reaction mechanism over Mn-doped Co3O4 for the selective catalytic reduction of NO x with NH3
Li et al. Effect of aluminum on the catalytic performance and reaction mechanism of Mn/MCM-41 for NH3-SCR reaction
Gong et al. Enhancement of the NH3-SCR property of Ce-Zr-Ti by surface and structure modification with P
Lu et al. Low temperature selective catalytic reduction of NOX with NH3 by activated coke loaded with FexCoyCezOm: the enhanced activity, mechanism and kinetics
Zhou et al. Iron based monolithic catalysts supported on Al2O3, SiO2, and TiO2: A comparison for NO reduction with propane
Zhou et al. Surface properties and reactivity of Fe/Al2O3/cordierite catalysts for NO reduction by C2H6: Effects of calcination temperature
Gong et al. Facile synthesis of porous α-Fe2O3 nanostructures from MIL-100 (Fe) via sacrificial templating method, as efficient catalysts for NH3-SCR reaction
Xu et al. Effectively promote catalytic performance by adjusting W/Fe molar ratio of FeWx/Ce0. 68Zr0. 32O2 monolithic catalyst for NH3-SCR
Xu et al. Facile preparation of high-performance Fe-doped Ce–Mn/TiO 2 catalysts for the low-temperature selective catalytic reduction of NO x with NH 3
Qiao et al. MnOx location on MnOx-ZSM-5 to influence the catalytic activity for selective catalytic reduction of NOx by NH3
Xu et al. Promotional effects of Titanium additive on the surface properties, active sites and catalytic activity of W/CeZrOx monolithic catalyst for the selective catalytic reduction of NOx with NH3
Zhang et al. One pot synthesis of a highly efficient mesoporous ceria–titanium catalyst for selective catalytic reduction of NO
Bai et al. Investigation of the interactions in CeO 2–Fe 2 O 3 binary metal oxides supported on ZSM-5 for NO removal by CO in the presence of O 2, SO 2 and steam
Nie et al. Tailored temperature window of MnOx-CeO2 SCR catalyst by addition of acidic metal oxides
Du et al. Effects of ferric and manganese precursors on catalytic activity of Fe-Mn/TiO 2 catalysts for selective reduction of NO with ammonia at low temperature
Weiman et al. Mesoporous MnOx–CeO 2 composites for NH 3-SCR: the effect of preparation methods and a third dopant
Cheng et al. Effect of ceria loading on Zr-pillared clay catalysts for selective catalytic reduction of NO with NH 3
Li et al. Characterization and SCR performance of nano-structured iron-manganese oxides: Effect of annealing temperature
Yang et al. Effect of initial support particle size of MnO x/TiO 2 catalysts in the selective catalytic reduction of NO with NH 3
Song et al. Catalytic hydrolysis of HCN on ZSM-5 modified by Fe or Nb for HCN removal: surface species and performance