Facility for stress corrosion cracking of irradiated specimens in supercritical water

Teysseyre et al., 2007

Document ID
15686814728444650737
Author
Teysseyre S
Peng Q
Becker C
Was G
Publication year
Publication venue
Journal of Nuclear Materials

External Links

Snippet

This paper presents the capability to conduct stress corrosion cracking experiments on neutron-irradiated material in supercritical water for application to the GenIV supercritical water reactor concept. The Irradiated Materials Testing Laboratory (IMTL) is dedicated to …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N23/00—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons
    • G01N23/02—Investigating or analysing materials by the use of wave or particle radiation not covered by G01N21/00 or G01N22/00, e.g. X-rays or neutrons by transmitting the radiation through the material
    • G—PHYSICS
    • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
    • G21C—NUCLEAR REACTORS
    • G21C17/00—Monitoring; Testing ; Maintaining
    • G21C17/02—Devices or arrangements for monitoring coolant or moderator
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N3/60—Investigating resistance of materials, e.g. refractory materials, to rapid heat changes
    • G—PHYSICS
    • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
    • G21C—NUCLEAR REACTORS
    • G21C19/00—Arrangements for treating, for handling, or for facilitating the handling of, fuel or other materials which are used within the reactor, e.g. within its pressure vessel

Similar Documents

Publication Publication Date Title
Dong et al. Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water
Moss et al. Accelerated stress corrosion crack initiation of alloys 600 and 690 in hydrogenated supercritical water
Stuckert et al. Results of the QUENCH-LOCA experimental program at KIT
Garnier et al. Irradiation creep of SA 304L and CW 316 stainless steels: Mechanical behaviour and microstructural aspects. Part I: Experimental results
Teysseyre et al. Facility for stress corrosion cracking of irradiated specimens in supercritical water
Kozsda-Barsy et al. Post-test examinations on Zr-1% Nb claddings after ballooning and burst, high-temperature oxidation and secondary hydriding
Hesterberg et al. Effects of post-irradiation annealing on the IASCC susceptibility of neutron-irradiated 304L stainless steel
Gusarov et al. Assessment of creep in reactor-irradiated CuCrZr alloy intended for the ITER first wall panels
Grosse et al. Neutron imaging investigations of the secondary hydriding of nuclear fuel cladding alloys during loss of coolant accidents
Chopra et al. Crack growth rates and fracture toughness of irradiated austenitic stainless steels in BWR environments.
Féron et al. Stress corrosion cracking of Alloy 600: overviews and experimental techniques
Hein et al. Final Results from the CARINA Project on Crack Initiation and Arrest of Irradiated German RPV Steels for Neutron Fluences in the Upper Bound
Wan et al. Analysis method of Charpy V-notch impact data before and after electron beam welding reconstitution
JP5226975B2 (en) Stress corrosion cracking monitoring method and monitoring device therefor
JPH0634786A (en) Method of estimating life expectancy of component constituting light water reactor and device therefor
Grosse Neutron radiography: a powerful tool for fast, quantitative and non-destructive determination of hydrogen concentration and distribution in zirconium alloys
Stuckert et al. Results of the LOCA Bundle Test QUENCH-L5 with Pre-hydrogenated Optimised ZIRLOTM Claddings (SR-7738)
Teysseyre et al. Irradiation Assisted Stress Corrosion Cracking Susceptibility of Alloy X-750 Exposed to BWR Environments
Kussmaul et al. Assurance of the pressure vessel integrity with respect to irradiation embrittlement: Activities in the Federal Republic of Germany
Georgy Experiment for determination of residual stresses in pipes
Murugan et al. Irradiation testing of structural materials in fast breeder test reactor
Shaber Investigation of Fatigue and Creep-Fatigue Crack Growth in Alloy 709 at Elevated Temperatures
Teysseyre et al. Assessing SCC and IASCC of austenitic alloys for application to the SCWR concept
Alexandreanu et al. Performance Testing of Additively Manufactured 316L Stainless Steel in Light Water Reactor Environment
Ashida et al. Facilities For Crack Growth Testing of Neutron-Irradiated Alloys In LWR Environments