Sala et al., 1997 - Google Patents
Viscoelastic effects related to residual thermal stresses in bismaleimide/carbon fiber composite laminatesSala et al., 1997
- Document ID
- 15505031479709247769
- Author
- Sala G
- Di Landro L
- Publication year
- Publication venue
- Polymer composites
External Links
Snippet
This paper studies the effects of the residual stresses which originate in the laminates made of composite materials owing to the curing process, and on stresses affected by time and temperature. In order to sustain high operating temperatures, the polymer composites' …
- 230000035882 stress 0 title abstract description 64
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE, IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
- B29C45/17—Component parts, details or accessories; Auxiliary operations
- B29C45/76—Measuring, controlling or regulating
- B29C45/77—Measuring, controlling or regulating of velocity or pressure of moulding material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE, IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
- B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
- B29C70/28—Shaping operations therefor
- B29C70/40—Shaping or impregnating by compression not applied
- B29C70/42—Shaping or impregnating by compression not applied for producing articles of definite length, i.e. discrete articles
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Shokrieh et al. | Theoretical and experimental studies on residual stresses in laminated polymer composites | |
| Oh et al. | Cure cycle for thick glass/epoxy composite laminates | |
| Manson et al. | Process simulated laminate (PSL): a methodology to internal stress characterization in advanced composite materials | |
| Nawab et al. | Study of variation of thermal expansion coefficients in carbon/epoxy laminated composite plates | |
| Luce et al. | Permeability characterization. Part 2: Flow behavior in multiple‐layer preforms | |
| Templeton | Strength predictions of injection molding compounds | |
| Kashtalyan et al. | Mechanisms of internal damage and their effect on the behavior and properties of cross-ply composite laminates | |
| Chung et al. | Modeling creep in thermoplastic composites | |
| Nghiep Nguyen et al. | Prediction of the elastic—plastic stress/strain response for injection-molded long-fiber thermoplastics | |
| Gower et al. | Determination of ply level residual stresses in a laminated carbon fibre-reinforced epoxy composite using constant, linear and quadratic variations of the incremental slitting method | |
| Chang et al. | Effect of process variables on the quality of compression resin transfer molding | |
| Yoon et al. | Effect of thermal deformation and chemical shrinkage on the process induced distortion of carbon/epoxy curved laminates | |
| Melo et al. | Viscoelastic characterization of transversely isotropic composite laminae | |
| Kim et al. | Numerical analysis of the dimensional stability of thermoplastic composites using a thermoviscoelastic approach | |
| Zhu et al. | Dimensional accuracy of thermoset composites: shape optimization | |
| Hui et al. | Multiscale model of micro curing residual stress evolution in carbon fiber-reinforced thermoset polymer composites | |
| Davidson et al. | Accuracy assessment of the singular-field-based mode-mix decomposition procedure for the prediction of delamination | |
| Sala et al. | Viscoelastic effects related to residual thermal stresses in bismaleimide/carbon fiber composite laminates | |
| Mendels et al. | The influence of internal stresses on the microbond test–I: theoretical analysis | |
| Bolotin | Effect of technological factors on the mechanical reliability of structures made from composites | |
| Corden et al. | The mechanisms of interlaminar cracking in thick resin transfer moulded composite cylinders | |
| Megnis et al. | Micromechanical modeling of viscoelastic response of GMT composite | |
| Konish et al. | Determination of fracture strength in orthotropic graphite-epoxy laminates | |
| Wisnom et al. | Compressive failure due to shear instability: experimental investigation of waviness and correlation with analysis | |
| Miled et al. | Injection molding of fibre reinforced thermoplastics: integration of fibre orientation and mechanical properties computations |