Yu et al., 2015 - Google Patents
Fabrication of graphene oxide–alumina hybrids to reinforce the anti-corrosion performance of composite epoxy coatingsYu et al., 2015
- Document ID
- 11853402798362315375
- Author
- Yu Z
- Di H
- Ma Y
- Lv L
- Pan Y
- Zhang C
- He Y
- Publication year
- Publication venue
- Applied surface science
External Links
Snippet
Graphene oxide–alumina (GO–Al 2 O 3) sheet hybrids were fabricated using GO as a precursor, then anchoring Al 2 O 3 on GO sheets with the help of 3- aminopropyltriethoxysilane. The structure of hybrids can be measured by FT-IR, XPS, XRD …
- 229920000647 polyepoxide 0 title abstract description 49
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B31/00—Carbon; Compounds thereof
- C01B31/02—Preparation of carbon; Purification; After-treatment
- C01B31/04—Graphite, including modified graphite, e.g. graphitic oxides, intercalated graphite, expanded graphite or graphene
- C01B31/0438—Graphene
- C01B31/0446—Preparation
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B31/00—Carbon; Compounds thereof
- C01B31/02—Preparation of carbon; Purification; After-treatment
- C01B31/0206—Nanosized carbon materials
- C01B31/022—Carbon nanotubes
- C01B31/0253—After-treatments
- C01B31/0266—Sorting
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B31/00—Carbon; Compounds thereof
- C01B31/02—Preparation of carbon; Purification; After-treatment
- C01B31/0206—Nanosized carbon materials
- C01B31/0293—Other structures, e.g. nano-onions, nano-scrolls, nano-horns, nano-cones or nano-walls
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K3/00—Use of inorganic ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Yu et al. | Fabrication of graphene oxide–alumina hybrids to reinforce the anti-corrosion performance of composite epoxy coatings | |
| Ma et al. | Fabrication of silica-decorated graphene oxide nanohybrids and the properties of composite epoxy coatings research | |
| Zhou et al. | Designing reduced graphene oxide/zinc rich epoxy composite coatings for improving the anticorrosion performance of carbon steel substrate | |
| Di et al. | Graphene oxide decorated with Fe3O4 nanoparticles with advanced anticorrosive properties of epoxy coatings | |
| Sun et al. | The role of graphene loading on the corrosion-promotion activity of graphene/epoxy nanocomposite coatings | |
| Wu et al. | π-π interaction between fluorinated reduced graphene oxide and acridizinium ionic liquid: Synthesis and anti-corrosion application | |
| Kumar et al. | Thermo-mechanical and anti-corrosive properties of MWCNT/epoxy nanocomposite fabricated by innovative dispersion technique | |
| Wan et al. | Synthesis of PDA-BN@ f-Al2O3 hybrid for nanocomposite epoxy coating with superior corrosion protective properties | |
| Yu et al. | RGO modified ZnAl-LDH as epoxy nanostructure filler: A novel synthetic approach to anticorrosive waterborne coating | |
| Song et al. | Graphitic carbon nitride (g-C3N4) interfacially strengthened carbon fiber epoxy composites | |
| Qiang et al. | GO-functionalized MXene towards superior anti-corrosion coating | |
| Liu et al. | Comparative tribological and corrosion resistance properties of epoxy composite coatings reinforced with functionalized fullerene C60 and graphene | |
| Zhang et al. | h-BN decorated with Fe3O4 nanoparticles through mussel-inspired chemistry of dopamine for reinforcing anticorrosion performance of epoxy coatings | |
| Qing et al. | A facile method to prepare superhydrophobic fluorinated polysiloxane/ZnO nanocomposite coatings with corrosion resistance | |
| Wang et al. | An organic/inorganic composite multi-layer coating to improve the corrosion resistance of AZ31B Mg alloy | |
| Wu et al. | Ti3C2Tx@ CNF nanohybrid improving the corrosion resistance of waterborne epoxy coating under 15 MPa alternating hydrostatic pressure | |
| Yu et al. | Preparation of graphene oxide modified by titanium dioxide to enhance the anti-corrosion performance of epoxy coatings | |
| Wang et al. | A cost-effective method for preparing mechanically stable anti-corrosive superhydrophobic coating based on electrochemically exfoliated graphene | |
| Wen et al. | Corrosion resistance performance of the self-assembled reduction of graphene/silane composite films | |
| Qian et al. | Superdurable fiber-reinforced composite enabled by synergistic bridging effects of MXene and carbon nanotubes | |
| Di et al. | Anchoring calcium carbonate on graphene oxide reinforced with anticorrosive properties of composite epoxy coatings | |
| Chu et al. | Graphene oxide film as a protective barrier for Mg alloy: Worse or better is dependent on a chemical reduction process | |
| Pan et al. | Corrosion control by carbon-based nanomaterials: a review | |
| Jing et al. | Molybdenum disulfide with poly (dopamine) and epoxy groups as an efficiently anticorrosive reinforcers in epoxy coating | |
| Zhang et al. | Interfacial engineering in PDMS/graphene composites via anchoring polypyrrole nanowires to enhance its electro-photo thermal performance |