Htoo et al., 2016 - Google Patents
Variation of local stress ratio and its effect on notch fatigue behavior of 2024-T4 aluminum alloyHtoo et al., 2016
- Document ID
- 11486560708698379555
- Author
- Htoo A
- Miyashita Y
- Otsuka Y
- Mutoh Y
- Sakurai S
- Publication year
- Publication venue
- International Journal of Fatigue
External Links
Snippet
Fatigue tests and finite element analysis of notched specimen were carried out to investigate the variation of local stress ratio at notch root and its influence on fatigue strength. The S–N curve of 2024-T4 aluminum alloy was kinked at the critical nominal stress amplitude, above …
- 229910000838 Al alloy 0 title abstract description 23
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/025—Geometry of the test
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/0202—Control of the test
- G01N2203/0212—Theories, calculations
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
- G01N2203/006—Crack, flaws, fracture or rupture
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0014—Type of force applied
- G01N2203/0016—Tensile or compressive
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Htoo et al. | Variation of local stress ratio and its effect on notch fatigue behavior of 2024-T4 aluminum alloy | |
| Gao et al. | Fatigue life of 7075-T651 aluminium alloy treated with vibratory stress relief | |
| Shen et al. | On the correlation between hardness and tensile strength in particle reinforced metal matrix composites | |
| Bao | Dependence of ductile crack formation in tensile tests on stress triaxiality, stress and strain ratios | |
| Xue et al. | Micromechanisms of multistage fatigue crack growth in a high-strength aluminum alloy | |
| Lacarac et al. | Fatigue crack growth from plain and cold expanded holes in aluminium alloys | |
| Boyce et al. | Mechanical relaxation of localized residual stresses associated with foreign object damage | |
| Htoo et al. | Notch fatigue behavior of Ti-6Al-4V alloy in transition region between low and high cycle fatigue | |
| Kalatehmollaei et al. | An asymmetric elastic–plastic analysis of the load-controlled rotating bending test and its application in the fatigue life estimation of wrought magnesium AZ31B | |
| Oberwinkler | Modeling the fatigue crack growth behavior of Ti-6Al-4V by considering grain size and stress ratio | |
| Zhang et al. | Elastic–plastic finite element analysis and experimental study of short and long fatigue crack growth | |
| Moćko et al. | Analysis of deformation history and damage initiation for 6082-T6 aluminium alloy loaded at classic and symmetric Taylor impact test conditions | |
| Gerin et al. | Beneficial effect of prestrain due to cold extrusion on the multiaxial fatigue strength of a 27MnCr5 steel | |
| Kermanidis et al. | Prediction of crack growth following a single overload in aluminum alloy with sheet and plate microstructure | |
| Kossakowski | Microstructural failure criteria for S235JR steel subjected to spatial stress states | |
| Nečemer et al. | Low cycle fatigue behaviour of ductile aluminium alloys using the inelastic energy approach | |
| Mahmoudi et al. | Using local out-of-plane compression (LOPC) to study the effects of residual stress on apparent fracture toughness | |
| Amsterdam et al. | The influence of strain-induced damage on the mechanical response of open-cell aluminum foam | |
| Tzamtzis et al. | Improvement of fatigue crack growth resistance by controlled overaging in 2024‐T3 aluminium alloy | |
| Oberwinkler et al. | Importance of local microstructure for damage tolerant light weight design of Ti–6Al–4V forgings | |
| He et al. | Analysis of Forging Cracks during Hot Compression of Powder Metallurgy Nickel‐Based Superalloy on Simulation and Experiment | |
| McMaster et al. | Predictions of fatigue crack growth in aluminium alloy 2024–T351 using constraint factors | |
| DING et al. | A low‐cycle fatigue life prediction model of ultrafine‐grained metals | |
| Buciumeanu et al. | Fatigue life predictions including the Bauschinger effect | |
| Falkowska et al. | Fatigue life of 316L steel sinters of varying porosity under conditions of uniaxial periodically variable loading at a fixed stress amplitude |