Li et al., 2021 - Google Patents

Effect of melt flow rate and S/L interface on the P horizontal distribution in silicon

Li et al., 2021

View PDF
Document ID
10916056945597644923
Author
Li P
Hu Z
Wang Z
Wen S
Li J
Jiang D
Tan Y
Publication year
Publication venue
Vacuum

External Links

Snippet

Uniform doping of phosphorus (P) in silicon is always the key and difficult point in the study of n-type solar cells. This paper aims to study the influencing factors for horizontal distribution for P. It is found that the distribution of P in silicon ingot is the results of the …
Continue reading at www.sciencedirect.com (PDF) (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00—Silicon; Compounds thereof
    • C01B33/02—Silicon
    • C01B33/021—Preparation
    • C01B33/027—Preparation by decomposition or reduction of gaseous or vaporised silicon compounds other than silica or silica-containing material
    • C01B33/035—Preparation by decomposition or reduction of gaseous or vaporised silicon compounds other than silica or silica-containing material by decomposition or reduction of gaseous or vaporised silicon compounds in the presence of heated filaments of silicon, carbon or a refractory metal, e.g. tantalum or tungsten, or in the presence of heated silicon rods on which the formed silicon is deposited, a silicon rod being obtained, e.g. Siemens process
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/02—Elements
    • C30B29/06—Silicon
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B11/00—Single-crystal growth by normal freezing or freezing under temperature gradient, e.g. Bridgman-Stockbarger method
    • C30B11/04—Single-crystal growth by normal freezing or freezing under temperature gradient, e.g. Bridgman-Stockbarger method adding crystallising material or reactants forming it in situ to the melt
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B11/00—Single-crystal growth by normal freezing or freezing under temperature gradient, e.g. Bridgman-Stockbarger method
    • C30B11/002—Crucibles or containers for supporting the melt
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B11/00—Single-crystal growth by normal freezing or freezing under temperature gradient, e.g. Bridgman-Stockbarger method
    • C30B11/003—Heating or cooling of the melt or the crystallised material
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B28/00—Production of homogeneous polycrystalline material with defined structure
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B31/00—Carbon; Compounds thereof
    • C01B31/02—Preparation of carbon; Purification; After-treatment
    • C01B31/04—Graphite, including modified graphite, e.g. graphitic oxides, intercalated graphite, expanded graphite or graphene
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL-GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B15/00—Single-crystal growth by pulling from a melt, e.g. Czochralski method
    • C30B15/02—Single-crystal growth by pulling from a melt, e.g. Czochralski method adding crystallising material or reactants forming it in situ to the melt

Similar Documents

Publication Publication Date Title
Tan et al. Removal of aluminum and calcium in multicrystalline silicon by vacuum induction melting and directional solidification
Teng et al. The carbon distribution in multicrystalline silicon ingots grown using the directional solidification process
Yu et al. Local design of the hot-zone in an industrial seeded directional solidification furnace for quasi-single crystalline silicon ingots
Li et al. Effect of melt flow rate and S/L interface on the P horizontal distribution in silicon
Yang et al. A modified vacuum directional solidification system of multicrystalline silicon based on optimizing for heat transfer
Liu et al. Controlling solidification front shape and thermal stress in growing quasi-single-crystal silicon ingots: Process design for seeded directional solidification
Shur et al. Growth of multi-crystalline silicon ingot by improved directional solidification process based on numerical simulation
Liu et al. Global simulation of coupled oxygen and carbon transport in an industrial directional solidification furnace for crystalline silicon ingots: Effect of crucible cover coating
Chen et al. Numerical simulation of the oxygen concentration distribution in silicon melt for different crystal lengths during Czochralski growth with a transverse magnetic field
Zhang et al. Nucleation and bulk growth control for high efficiency silicon ingot casting
Nguyen et al. Effects of the hot zone design during the growth of large size multi-crystalline silicon ingots by the seeded directional solidification process
Teng et al. Numerical investigation of the effect of heat shield shape on the oxygen impurity distribution at the crystal–melt interface during the process of Czochralski silicon crystal growth
Wang et al. Integrated analysis and design optimization of germanium purification process using zone-refining technique
Tan et al. Numerical simulation for parameter optimization of silicon purification by electron beam melting
Dezfoli et al. Modeling of poly-crystalline silicon ingot crystallization during casting and theoretical suggestion for ingot quality improvement
Qiu et al. Process parameters influence on the growth rate during silicon purification by vacuum directional solidification
Wen et al. Determination and controlling of crystal growth rate during silicon purification by directional solidification
Sugunraj et al. Influence of helium gas flow under the retort bottom to control the impurities in grown mc-Si ingot by DS process for photovoltaic application: Numerical simulation
Luo et al. Numerical and experimental study of vacuum directional solidification purification process for SoG-Si in metallurgical route
Qi et al. Effects of furnace pressure on oxygen and carbon coupled transport in an industrial directional solidification furnace for crystalline silicon ingots
Dezfoli Design and optimization of complex single heater for vertical gradient freeze (VGF) grower
Bharathwaj et al. Effect of argon flow rate on mc-silicon ingot grown by DS process for PV application: a numerical investigation of non-metallic impurities
Kesavan et al. Optimizing oxygen impurities using different heater design in the directional solidification of multi-crystalline silicon
Su et al. Numerical analysis and optimization of gas flow and impurity control in directional solidification multi-crystalline Si
Popescu et al. Numerical study of the influence of melt convection on the crucible dissolution rate in a silicon directional solidification process