Komori et al., 2002 - Google Patents
Approach for the fabrication of MgB 2 superconducting tape with large in-field transport critical current densityKomori et al., 2002
View PDF- Document ID
- 8553396363546805383
- Author
- Komori K
- Kawagishi K
- Takano Y
- Fujii H
- Arisawa S
- Kumakura H
- Fukutomi M
- Togano K
- Publication year
- Publication venue
- Applied physics letters
External Links
Snippet
The letter reports the fabrication of MgB 2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The tape was prepared by depositing MgB 2 film on a …
- 238000004519 manufacturing process 0 title abstract description 9
Classifications
-
- H—ELECTRICITY
- H01—BASIC ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H01L39/00—Devices using superconductivity; Processes or apparatus peculiar to the manufacture or treatment thereof or of parts thereof
- H01L39/24—Processes or apparatus peculiar to the manufacture or treatment of devices provided for in H01L39/00 or of parts thereof
- H01L39/2419—Processes or apparatus peculiar to the manufacture or treatment of devices provided for in H01L39/00 or of parts thereof the superconducting material comprising copper oxide
- H01L39/2422—Processes for depositing or forming superconductor layers
- H01L39/2454—Processes for depositing or forming superconductor layers characterised by the substrate
- H01L39/2461—Intermediate layers, e.g. for growth control
-
- H—ELECTRICITY
- H01—BASIC ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H01L39/00—Devices using superconductivity; Processes or apparatus peculiar to the manufacture or treatment thereof or of parts thereof
- H01L39/24—Processes or apparatus peculiar to the manufacture or treatment of devices provided for in H01L39/00 or of parts thereof
- H01L39/2419—Processes or apparatus peculiar to the manufacture or treatment of devices provided for in H01L39/00 or of parts thereof the superconducting material comprising copper oxide
- H01L39/2464—After-treatment, e.g. patterning
-
- H—ELECTRICITY
- H01—BASIC ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H01L39/00—Devices using superconductivity; Processes or apparatus peculiar to the manufacture or treatment thereof or of parts thereof
- H01L39/02—Details
- H01L39/12—Details characterised by the material
- H01L39/125—Ceramic materials
- H01L39/126—Ceramic materials comprising copper oxide
-
- H—ELECTRICITY
- H01—BASIC ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H01L39/00—Devices using superconductivity; Processes or apparatus peculiar to the manufacture or treatment thereof or of parts thereof
- H01L39/24—Processes or apparatus peculiar to the manufacture or treatment of devices provided for in H01L39/00 or of parts thereof
- H01L39/2419—Processes or apparatus peculiar to the manufacture or treatment of devices provided for in H01L39/00 or of parts thereof the superconducting material comprising copper oxide
- H01L39/248—Processes peculiar to the manufacture or treatment of filaments or composite wires
-
- H—ELECTRICITY
- H01—BASIC ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H01L39/00—Devices using superconductivity; Processes or apparatus peculiar to the manufacture or treatment thereof or of parts thereof
- H01L39/22—Devices comprising a junction of dissimilar materials, e.g. Josephson-effect devices
- H01L39/223—Josephson-effect devices
- H01L39/225—Josephson-effect devices comprising high Tc ceramic materials
-
- H—ELECTRICITY
- H01—BASIC ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
- H01L39/00—Devices using superconductivity; Processes or apparatus peculiar to the manufacture or treatment thereof or of parts thereof
- H01L39/14—Permanent superconductor devices
- H01L39/143—Permanent superconductor devices comprising high Tc ceramic materials
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Komori et al. | Approach for the fabrication of MgB 2 superconducting tape with large in-field transport critical current density | |
| Goyal et al. | Strengthened, biaxially textured Ni substrate with small alloying additions for coated conductor applications | |
| Matsumoto et al. | High critical current density YBa2Cu3O7− δ tapes prepared by the surface-oxidation epitaxy method | |
| Cai et al. | Structural and magnetotransport properties of YBa2Cu3O7− δ∕ Y2O3 quasimultilayers | |
| Hänisch et al. | Electrical transport properties of Bi 2 Sr 2 Ca 2 Cu 3 O 1 0+ δ thin film [001] tilt grain boundaries | |
| Zhang et al. | Superconductivity of disordered NbN films deposited on magnesium oxide and oxidized silicon substrates | |
| Yamada et al. | Development of cost-effective HTS superconductor.: Simple heat treatment and low-cost substrate Ni/NiO | |
| He et al. | High‐current superconducting Tl1Ba2Ca2Cu3Oy thick films on polycrystalline Ag by spin coating | |
| Goyal et al. | Optimal, Nanodefect Configurations via Strain-Mediated Assembly for Optimized Vortex-Pinning in Superconducting Wires from 5K-77K | |
| Richter et al. | Resistivity, Hall effect, and anisotropic superconducting coherence lengths of HgBa2CaCu2O6 thin films with different morphology | |
| Miura et al. | Superconducting properties in SmBa 2 Cu 3 O y films with high density of BaHfO 3 Nanorods fabricated with a seed layer | |
| Fournier-Lupien et al. | Effect of annealing on HTS tapes with a cerium oxide layer inserted between the REBaCuO and silver layers | |
| Xu et al. | Relevant pinning for ab-plane Jc enhancement of MOCVD REBCO coated conductors | |
| Oh et al. | Enhanced Pinning Properties of GdBa2Cu3O7-δ Films With the Gd 2O3 Nanoparticles | |
| US5232904A (en) | Materials having a zero resistance transition temperature above 200 K and method for maintaining the zero resistance property | |
| Usagawa et al. | Nonlinear I–V characteristics and proximity effects for PrBa 2 Cu 3 O 7− δ/YBa 2 Cu 3 O 7− δ bilayered structures grown on (001) YBa 2 Cu 3 O 7− δ single crystal substrates | |
| Kang et al. | Oxygen annealing and superconductivity of HgBa2Ca2Cu3O8+ y thin films | |
| Boffa et al. | Influence of film thickness on the critical current of YBa/sub 2/Cu/sub 3/O/sub 7-x/thick films on Ni-V biaxially textured substrates | |
| Vossen | Thin Films for Emerging Applications | |
| Hashimoto et al. | Fabrication of YBa2Cu3O7 Superconducting Film on {100}< 001> Textured Cu Tape via Conductive Buffer Layers | |
| Yoo et al. | The growth of YBCO films with high critical current at reduced pressures using the BaF2 ex situ process | |
| Yao | Development of Multifilamentary 122-Type IBS Tapes | |
| Carlson et al. | LaNiO3 buffer layers for high critical current density YBa2Cu3O7− δ and Tl2Ba2CaCu2O8− δ films | |
| Fuger et al. | Evaluation of current transport properties of GdBa2Cu3O7− δ coated conductors over a wide range of temperature and external magnetic fields | |
| Zhang et al. | Microwave surface resistance of nickel and zinc doped YBCO single crystals in the ab plane |