Electrochemical and sulfide stress corrosion cracking behaviors of tubing steels in a H 2 S/CO 2 annular environmentLiu et al., 2014
View HTML- Document ID
- 5789982991304178537
- Author
- Liu Z
- Wang X
- Liu R
- Du C
- Li X
- Publication year
- Publication venue
- Journal of materials engineering and performance
External Links
Snippet
The electrochemical and sulfide stress corrosion cracking (SSCC) behaviors of 13Cr stainless steel and P110 steel were investigated in a simulated acidic annular environment with low-temperature and high-pressure H 2 S/CO 2 using electrochemical methods, U-bend …
- 238000005260 corrosion 0 title abstract description 112
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N33/00—Investigating or analysing materials by specific methods not covered by the preceding groups
- G01N33/26—Investigating or analysing materials by specific methods not covered by the preceding groups oils; viscous liquids; paints; inks
- G01N33/28—Oils, i.e. hydrocarbon liquids
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Liu et al. | Electrochemical and sulfide stress corrosion cracking behaviors of tubing steels in a H 2 S/CO 2 annular environment | |
| Zhu et al. | Corrosion of N80 carbon steel in oil field formation water containing CO2 in the absence and presence of acetic acid | |
| Gao et al. | Effect of high temperature on the aqueous H2S corrosion of mild steel | |
| Bai et al. | Effect of amorphous FeS semiconductor on the corrosion behavior of pipe steel in H2S-containing environments | |
| Quej-Ake et al. | Analysis of the physicochemical, mechanical, and electrochemical parameters and their impact on the internal and external SCC of carbon steel pipelines | |
| Zhao et al. | Effect of Temperature on the corrosion behavior of L245NS steel in a CO 2/H 2 S/O 2 multi-component thermal fluid collection and transportation system | |
| Lu et al. | Effect of welding heat input on the corrosion resistance of carbon steel weld metal | |
| Eliyan et al. | Electrochemical investigations on the corrosion behavior and corrosion natural inhibition of API-X100 pipeline steel in acetic acid and chloride-containing CO 2-saturated media | |
| Yin et al. | Corrosion behavior and characteristics of 3Cr steel in coexisting H 2 S-and CO 2-containing solutions | |
| Khaksar et al. | Electrochemical and microstructural analysis of FeS films from acidic chemical bath at varying temperatures, pH, and immersion time | |
| Chen et al. | Failure analysis of corrosion products formed during CO2 pre-corrosion of X70 and 3Cr steels: Effect of oxygen contamination | |
| Liu et al. | Influence of Ru on structure and corrosion behavior of passive film on Ti-6Al-4V alloy in oil and gas exploration conditions | |
| Fan et al. | Penetration of imidazoline derivatives through deposited scale for inhibiting the under-deposit corrosion of pipeline steel | |
| Schott et al. | Monitoring and mitigating corrosion in geothermal systems | |
| Orlikowski et al. | Effect of wet hydrogen sulfide on carbon steels degradation in refinery based on case study | |
| Quej-Ake et al. | The effect of the hydrodynamic and temperature on corrosion rate of API steels exposed to oilfield produced water | |
| Javidi et al. | Inhibitive Performance of Monoethylene Glycol on CO 2 Corrosion of API 5L X52 Steel | |
| Lu et al. | Corrosion control in CO2/H2S-produced water of offshore oil fields | |
| Palencsár et al. | High temperature testing of corrosion inhibitor performance | |
| Qiu et al. | Material Selection for Thermal Inflow Control Device Manufacturing to Minimize the Silica and Calcium Carbonate Scaling Potential | |
| Ma | Corrosion Behavior of Gas Storage Well Pipe Strings in Corrosive H2S–CO2 Environment | |
| Zhao et al. | Effect of chloride concentration on stress corrosion behavior and mechanism of SA516GR70N steel in alkaline Nacl/Na 2 S solution | |
| Deng et al. | pH effect of natural gas hydrate on X80 steel solid—liquid phase scouring corrosion | |
| Wang et al. | Recent progress on the research of steel corrosion behavior and corrosion control in the context of CO2 geological utilization and storage: a review | |
| Hassanzadeh et al. | Investigation of the effect of pH on stress corrosion cracking of API 5L X65 steel by impedance spectroscopy and slow strain rate tensile test |