The leakage current in epitaxial BiFeO3 capacitors with bottom SrRuO3 and top Pt electrodes, grown by pulsed laser deposition on SrTiO3 (100), SrTiO3 (110), and SrTiO3 (111) substrates, is investigated by current-voltage (I-V) measurements in the 100-300 K temperature range. It is found that the leakage current is interface-limited and strongly dependent on the orientation of the substrate. The potential barriers at the electrode interfaces are estimated to about 0.6, 0.77, and 0.93 eV for the (100), (110), and (111) orientations, respectively. © 2009 American Institute of Physics.

Studies to date on ferromagnet/d-wave superconductor heterostructures focus mainly on the effects at or near the interfaces while the response of bulk properties to heterostructuring is overlooked. Here we use resonant soft x-ray scattering spectroscopy to reveal a novel c-axis ferromagnetic coupling between the in-plane Cu spins in YBa2Cu3O7-x (YBCO) superconductor when it is grown on top of ferromagnetic La0.7Ca0.3MnO3 (LCMO) manganite layer. This coupling, present in both normal and superconducting states of YBCO, is sensitive to the interfacial termination such that it is only observed in bilayers with MnO2 but not with La0.7Ca0.3O interfacial termination. Such contrasting behaviors, we propose, are due to distinct energetic of CuO chain and CuO2 plane at the La0.7Ca0.3O and MnO2 terminated interfaces respectively, therefore influencing the transfer of spin-polarized electrons from manganite to cuprate differently. Our findings suggest that the superconducting/ferromagnetic bilayers with proper interfacial engineering can be good candidates for searching the theorized Fulde-Ferrel-Larkin-Ovchinnikov (FFLO) state in cuprates and studying the competing quantum orders in highly correlated electron systems.

The control of material interfaces at the atomic level has led to novel interfacial properties and functionalities. In particular, the study of polar discontinuities at interfaces between complex oxides lies at the frontier of modern condensed matter research. Here we employ a combination of experimental measurements and theoretical calculations to demonstrate the control of a bulk property, namely ferroelectric polarization, of a heteroepitaxial bilayer by precise atomic-scale interface engineering. More specifically, the control is achieved by exploiting the interfacial valence mismatch to influence the electrostatic potential step across the interface, which manifests itself as the biased-voltage in ferroelectric hysteresis loops and determines the ferroelectric state. A broad study of diverse systems comprising different ferroelectrics and conducting perovskite underlayers extends the generality of this phenomenon.