Basinox 904L is an electrode suitable for welding stainless and heat resistant steels like Ni-Cr-Mo stainless steel with low carbon content. It provides very good resistance to intergranular and pitting corrosion and is particularly suitable for materials like URANUS B6, AISI 904L. The all-weld metal has typical compositions of around 0.027% C, 1.7% Mn, 0.5% Si, and 21% Cr, 24.6% Ni, 4.8% Mo. As-welded weld metal has mechanical properties like a yield strength over 310 MPa and tensile strength over 520 MPa.
Basinox 904L is an electrode suitable for welding stainless and heat resistant steels like Ni-Cr-Mo stainless steel with low carbon content. It provides very good resistance to intergranular and pitting corrosion and is particularly suitable for materials like URANUS B6, AISI 904L. The all-weld metal has typical compositions of around 0.027% C, 1.7% Mn, 0.5% Si, and 21% Cr, 24.6% Ni, 4.8% Mo. As-welded weld metal has mechanical properties like a yield strength over 310 MPa and tensile strength over 520 MPa.
Basinox 904L is an electrode suitable for welding stainless and heat resistant steels like Ni-Cr-Mo stainless steel with low carbon content. It provides very good resistance to intergranular and pitting corrosion and is particularly suitable for materials like URANUS B6, AISI 904L. The all-weld metal has typical compositions of around 0.027% C, 1.7% Mn, 0.5% Si, and 21% Cr, 24.6% Ni, 4.8% Mo. As-welded weld metal has mechanical properties like a yield strength over 310 MPa and tensile strength over 520 MPa.
Basinox 904L is an electrode suitable for welding stainless and heat resistant steels like Ni-Cr-Mo stainless steel with low carbon content. It provides very good resistance to intergranular and pitting corrosion and is particularly suitable for materials like URANUS B6, AISI 904L. The all-weld metal has typical compositions of around 0.027% C, 1.7% Mn, 0.5% Si, and 21% Cr, 24.6% Ni, 4.8% Mo. As-welded weld metal has mechanical properties like a yield strength over 310 MPa and tensile strength over 520 MPa.
MMA Electrodes Stainless and Heat resistant steels Basinox 904L is suitable for the welding of Ni-Cr-Mo stainless steel with a low carbon content. Very good resistance to intergranular and pitting corrosion. It is particularly suitable for URANUS B6 - NSCD - HU7 - HU9, AISI 904L. Efficiency 150%.
Classification Approvals Grades
AWS A5.4: E 385-15 EN 1600: E Z 20 25 5 CuL B 12
Analysis of all-weld metal (Typical values in %)
C Mn Si P S Cr Ni Mo Nb Cu N Ferrite 0.027 1.70 0.50 0.030 0.025 21 24.60 4.80 - 1.50 - -
All-weld metal Mechanical Properties
Yield Tensile Elongation Impact Energy Heat Treatment Strength Strength ISO - V (J) Hardness A5 (%) N/mm2 N/mm2 20°C As Welded 310 520 30 47 -