Product description
Designation and range of application
DILLIMAX 690 can be delivered in three qualities:
Basic (B) with minimum impact values down to -20 C (-4 F):
Steel number 1.8931 - S690Q according to EN 10025-6
Tough (T) with minimum impact values down to -40 C (-40 F):
Steel number 1.8928 - S690QL according to EN 10025-6
Extra tough (E) with minimum impact values down to -60 C (-76 F):
Steel number 1.8988 - S690QL1 according to EN 10025-6
DILLIMAX 690 B
DILLIMAX 690 T
DILLIMAX 690 E
DILLIMAX 690 can be delivered in thicknesses from 6 to 200 mm ( to 8 in.), according to the
dimensional program. Dimensions, which deviate from the usual dimensional program, may be possible
on request.
DILLIMAX 690 fulfils the requirements of EN 10025-6.
Chemical composition
For the ladle analysis, the following limiting values in % are applicable:
DILLIMAX 690
B,T,E
Si
Mn
Cr
Ni
Mo
V+Nb
0.18 0.50 1.60 0.020 0.010 1.50 1.80 0.60 0.10 0.004
1/4
DILLIMAX 690
Delivery condition
Water quenched and tempered according to EN 10025-6.
100 (4)
Tensile strength
Rm [MPa] (ksi) 1)
690 (100)
150 (6)
4)
200 (8)
4)
Minimum elongation
A5 [%]
A2in.3) [%]
14
15
670 (97)
4)
14
15
630 (91)
4)
14
15
610 (88)
4)
14
15
Specimen direction
Basic (B)
-20 C (-4 F) 1)
-40 C(-40 F) 1)
-60 C (-76 F) 1)
longitudinal / transverse
40/30 (30/22)
30/27 (22/20)
longitudinal / transverse
50/35 (37/26)
40/30 (30/22)
30/27 (22/20)
longitudinal / transverse
60/40 (44/30)
50/35 (37/26)
40/30 (30/22)
30/27 (22/20)
The specified minimum value is the average of 3 tests. Only one individual value is permitted to be below this minimum value, and
no more than 30%. For plate thicknesses below 12 mm the test can be carried out on Charpy-V test specimens with reduced width;
the minimum width must be 5 mm. The minimum impact value will be decreased proportionally.
Testing
Tensile and impact tests will be performed according to EN 10025-6 once per heat and 40 t. Tests on
every heat treated plate may be possible on request.
The specimens for the tensile test are prepared according to EN 10025-6. Testing is carried out on
specimens of gauge length L0 = 5.65S0 or L0 = 5d0, in accordance with EN ISO 6892-1.
Tensile tests according to ASTM A370 may be agreed.
The impact test will be carried out on Charpy-V-specimens in accordance with EN 10045-1. Unless
otherwise agreed, the test will be performed at the lowest temperature of the corresponding quality on
transverse test specimens taken as follows:
for plate thicknesses < 40 mm: the test specimen shall be taken in such a way that one side is not
further away than 2 mm from a rolled surface.
for plate thicknesses 40 mm: of the plate thickness.
Unless otherwise agreed, the test results are documented in a certificate 3.1 in accordance with
EN 10204.
Identification of plates
Unless otherwise agreed, the marking is carried out via steel stamps with at least the following
information:
steel grade (e.g. DILLIMAX 690 B, T or E)
heat number
number of mother plate and individual plate
the manufacturers symbol
inspectors sign
1)
2)
3)
4)
2/4
DILLIMAX 690
Processing
The entire processing and application techniques are of fundamental importance to the reliability of
products made from this steel. The user should ensure that his design, construction and processing
methods are aligned with the material, correspond to the state-of-the-art that the fabricator has to comply
with and are suitable for the intended use. The customer is responsible for the selection of the material.
The recommendations of the EN 1011-2 (Welding) and CEN/TR 10347 (Forming) as well as
recommendations regarding job safety in accordance with national rules should be observed.
Cold forming
Cold forming means forming below the maximum allowable stress relief temperature (560 C/1040 F).
DILLIMAX 690 can be cold formed with regard to its high yield strength. Flame cut or sheared edges in
the bending area should be ground before cold forming. Cold forming is related to a hardening of the steel
and to a decrease in toughness. Depending on the relevant design code this can result in the need of
larger bending radiuses than indicated in the chart. For larger cold forming amounts we recommend you
to consult the steel producer prior to ordering.
During the processing, the necessary safety measures have to be taken, so that nobody will be exposed
to a danger by a possible fracture of the work piece during the forming process.
The following geometries can usually be achieved by cold forming without the formation of surface
defects (where t is the plate thickness):
Transverse direction
Longitudinal direction
3t
9t
Hot forming
If the temperature of 560 C (1040 F) is exceeded, the initial tempering will be altered so that the
mechanical properties are affected.
To regain the initial properties new quenching and tempering become necessary. However, water
quenching of a formed workpiece or component will often be less effective than the original quenching in
the plate mill so that the fabricator may not be able to reestablish the properties required and therefore
hot forming may not be suitable. In this respect we recommend you to contact the steel producer prior to
ordering, in all cases where hot forming is required.
Finally, it is the fabricators responsibility to obtain the required values of the steel through an
appropriate heat treatment.
DILLIMAX 690
Heat treatment
If a stress relieving has to be considered because of constructional regulations, constructive reasons or
because it is necessary for the fabrication, please consult us. The properties of structural components
can be altered by a stress relief heat treatment.
Detailed instructions for flame cutting, welding, machining and about the structural properties of the
DILLIMAX are provided in the technical information MAKE SAVINGS WITH HIGH STRENGTH STEELS
- DILLIMAX.
Tolerances
Unless otherwise agreed, the tolerances will be in accordance with EN 10029, with class A for thickness
and table 4, steel group H, for the maximum flatness deviation. Smaller flatness deviations may be
possible on request prior to order.
Surface quality
Unless otherwise agreed, the specifications will be in accordance with EN 10163-2, class A2.
General note
If particular requirements are demanded and not covered in this data sheet, please contact us with the
specifications for our review and agreement prior to ordering. The information in this data sheet is a
product description. This data sheet is updated at occasion demands. The latest version is available from
the mill or as download at www.dillinger.de.
Distribution
For your local representative
please contact our coordination office in Dillingen:
Telephone: +49 6831 47 22 23
Fax:
+49 6831 47 33 50
or the internet:
http://www.dillinger.de/dh/kontakt/weltweit/index.shtml.en
DILLIMAX 690