1051R - 1057R

HIGH PRODUCTIVE
SURFACER

PRODUCT DESCRIPTION FEATURES

High Productive Surfacer White (1051R) and
High Productive Surfacer Black (1057R) are 01 Combines excellent filling properties with
excellent vertical stability.
highly productive surfacers that can be used as
sanding surfacers and as maxi fillers for all
Cromax topcoats. They provide a good
02 Suitable for fast air dry or quick curing with
minimal IR power.
performance with no edge mapping. By adding
High Productive Accelerator AZ1050, the
03 Helps bodyshops focus on saving time and
energy while supporting high throughput.
surfacers help to deliver increased productivity
through air-drying. 04 It has a dedicated and unique High
Productive Accelerator AZ1050.

05 For increased productivity, use with XK203

and AZ1050 in a 5:1:2 mixing ratio.
Very productive ValueShade surfacer
06 Aids productivity with an easy dry-to-sand in
30 minutes air dry at 20°C.
Developed by Cromax®,
ValueShade® delivers the
optimal undercoat for every
07 As a sanding surfacer, it can be applied up
to 3 coats in wet on wet application when
topcoat colour. used with AZ1050.

08 Part of the ValueShade concept.

AN AXALTA COATING SYSTEMS BRAND 1 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues
TECHNICAL DATA SHEET
1051R - 1057R
HIGH PRODUCTIVE SURFACER
Product preparation - application STANDARD SANDING VOC

It is strongly recommended to use appropriate personal protection equipment during application to

avoid respiratory, skin and eye irritation.

Steel, galvanised steel and soft aluminium sanded and cleaned and coated with 1K Wash Primer or
Epoxy Primer. In addition, for small sand through areas, pre-treatment wipes can be used.
Old or original paintwork well sanded and cleaned.
OEM Primer (e-coat), sanded and cleaned.
Surfaces pretreated with 2K polyester products and then finely sanded and cleaned.
Glass fibre polyester substrates, free of release agents, sanded and cleaned.
VS1 VS2 VS3 VS4 VS5 VS6 VS7
1051R 100 93 83 65 35 10 -
1057R - 7 17 35 65 90 100
Standard
Volume Weight
1051R / 1057R 7 100
AR7305 / XK203 / XK205 1 11
XB383 2.5 21

Pot life at 20°C: 1 hr

Spray nozzle Spray pressure

Compliant 1.6 - 1.8 1.5 - 2 bar inlet pressure
HVLP 1.6 - 1.8 0.7 bar atomisation pressure
see manufacturer’s instructions
2 - 3 coats intermediate and final flash-off: 5 min - 10 min

AR7305 / XK203 / XK205

20 °C 1 hr
60 - 65 °C 25 min
Guideline for short wave IR equipment
Half power: 10 min

P500

2K Topcoat
Basecoat + Clearcoat

VOC compliant 2004/42/IIB(c)(540) 540: The EU limit value for this product (product category: IIB(c)) in ready to use form is
maximum 540 g/l of VOC. The VOC content of this product in ready to use form is maximum 540 g/l.

AN AXALTA COATING SYSTEMS BRAND 2 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues
TECHNICAL DATA SHEET
1051R - 1057R
HIGH PRODUCTIVE SURFACER
Product preparation - application STANDARD SANDING HS/MS

It is strongly recommended to use appropriate personal protection equipment during application to

avoid respiratory, skin and eye irritation.

Steel, galvanised steel and soft aluminium sanded and cleaned and coated with 1K Wash Primer or
Epoxy Primer. In addition, for small sand through areas, pre-treatment wipes can be used.
Old or original paintwork well sanded and cleaned.
OEM Primer (e-coat), sanded and cleaned.
Surfaces pretreated with 2K polyester products and then finely sanded and cleaned.
Glass fibre polyester substrates, free of release agents, sanded and cleaned.
VS1 VS2 VS3 VS4 VS5 VS6 VS7
1051R 100 93 83 65 35 10 -
1057R - 7 17 35 65 90 100
Hs Ms
Volume Weight Volume Weight
1051R / 1057R 5 100 4 100
1010R / 125S - - 1 17
256S 1 14 - -
1025R - - 1 15
XB383 1.5 18 - -

Pot life at 20°C: 1 hr

Spray nozzle Spray pressure

Compliant 1.6 - 1.8 1.5 - 2 bar inlet pressure
HVLP 1.6 - 1.8 0.7 bar atomisation pressure
see manufacturer’s instructions
2 - 3 coats intermediate and final flash-off: 5 min - 10 min

1010R / 125S / 256S

20 °C 1 hr
60 - 65 °C 25 min
Guideline for short wave IR equipment
Half power: 10 min

P500

2K Topcoat
Basecoat + Clearcoat

VOC compliant 2004/42/IIB(c)(540) 540: The EU limit value for this product (product category: IIB(c)) in ready to use form is
maximum 540 g/l of VOC. The VOC content of this product in ready to use form is maximum 540 g/l.

AN AXALTA COATING SYSTEMS BRAND 3 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues
TECHNICAL DATA SHEET
1051R - 1057R
HIGH PRODUCTIVE SURFACER
Product preparation - application STANDARD MAXI MS

It is strongly recommended to use appropriate personal protection equipment during application to

avoid respiratory, skin and eye irritation.

Steel, galvanised steel and soft aluminium sanded and cleaned and coated with 1K Wash Primer or
Epoxy Primer. In addition, for small sand through areas, pre-treatment wipes can be used.
Old or original paintwork well sanded and cleaned.
OEM Primer (e-coat), sanded and cleaned.
Surfaces pretreated with 2K polyester products and then finely sanded and cleaned.
Glass fibre polyester substrates, free of release agents, sanded and cleaned.
VS1 VS2 VS3 VS4 VS5 VS6 VS7
1051R 100 93 83 65 35 10 -
1057R - 7 17 35 65 90 100
Standard
Volume Weight
1051R / 1057R 4 100
1010R / 125S 1 17
1025R 0.5 8
AB385 / XB387 1 15

Pot life at 20°C: 45 min

Spray nozzle Spray pressure

Compliant 1.6 - 1.8 1.5 - 2 bar inlet pressure
HVLP 1.6 - 1.8 0.7 bar atomisation pressure
see manufacturer’s instructions
2 - 3 coats with intermediate flash-off: 5 min - 10 min
final flash-off: 30 min

1010R / 125S
20 °C 1 hr - 1 hr 30 min
60 - 65 °C 30 min
Guideline for short wave IR equipment
Half power: 10 min

P500

2K Topcoat
Basecoat + Clearcoat

VOC compliant 2004/42/IIB(c)(540) 540: The EU limit value for this product (product category: IIB(c)) in ready to use form is
maximum 540 g/l of VOC. The VOC content of this product in ready to use form is maximum 540 g/l.

AN AXALTA COATING SYSTEMS BRAND 4 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues
TECHNICAL DATA SHEET
1051R - 1057R
HIGH PRODUCTIVE SURFACER
Product preparation - application STANDARD ACCELERATED

It is strongly recommended to use appropriate personal protection equipment during application to

avoid respiratory, skin and eye irritation.

Steel, galvanised steel and soft aluminium sanded and cleaned and coated with 1K Wash Primer or
Epoxy Primer. In addition, for small sand through areas, pre-treatment wipes can be used.
Old or original paintwork well sanded and cleaned.
OEM Primer (e-coat), sanded and cleaned.
Surfaces pretreated with 2K polyester products and then finely sanded and cleaned.
Glass fibre polyester substrates, free of release agents, sanded and cleaned.
VS1 VS2 VS3 VS4 VS5 VS6 VS7
1051R 100 93 83 65 35 10 -
1057R - 7 17 35 65 90 100
Standard
Volume Weight
1051R / 1057R 5 100
XK203 1 15
AZ1050 2 25

Pot life at 20°C: 20 min

Spray nozzle Spray pressure

Compliant 1.6 - 1.8 1.5 - 2 bar inlet pressure
HVLP 1.6 - 1.8 0.7 bar atomisation pressure
see manufacturer’s instructions
2 - 3 coats intermediate flash-off not needed

AZ1050
20 °C 30 min
P500

2K Topcoat
Basecoat + Clearcoat

VOC compliant 2004/42/IIB(c)(540) 540: The EU limit value for this product (product category: IIB(c)) in ready to use form is
maximum 540 g/l of VOC. The VOC content of this product in ready to use form is maximum 540 g/l.

AN AXALTA COATING SYSTEMS BRAND 5 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues
TECHNICAL DATA SHEET
1051R - 1057R
HIGH PRODUCTIVE SURFACER
Products
1051R High Productive Surfacer - VS1
1057R High Productive Surfacer - VS7

1010R High Solids Activator Fast

125S Standard Activator
256S Activator Fast
AR7305 High Performance Activator
XK203 Low Emission Activator Fast
XK205 Low Emission Activator

1025R High Solids Surfacer Thinner

AB385 MS HI-Temp Thinner
AZ1050 High Productive Accelerator
XB383 Standard Thinner
XB387 HI-Temp Thinner

Product mix
Mixing ratios with special agents are available in the productmix table on ChromaWeb and in the
specific TDS.

ISO 5: 25 - 30 s at 20°C
DIN 4: 22 - 25 s at 20°C

70 - 200 µm

Theoretical 380 - 400 m²/l at 1 micron dry film thickness

coverage Due to different activator characteristics and different mixing ratios of the ready-to-use mixture in
some TDS versions, the theoretical coverage calculation may vary.
Note: The practical material consumption depends on several factors, e.g. geometry of the object,
surface formation, application method, spray gun setting, inlet pressure, etc.

Clean after use with a suitable solventbased guncleaner.

AN AXALTA COATING SYSTEMS BRAND 6 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues
TECHNICAL DATA SHEET
1051R - 1057R
HIGH PRODUCTIVE SURFACER
Remarks
. Material has to be at room temperature (18-25°C) before use.
. Surplus ready for use material should not be returned to original can.
. When isolating certain spots - even on problem substrates - the best results are achieved with a
medium film thickness of 80-120µm in 2 coats, after either air drying overnight or force drying/IR
drying. With problem substrates, careful pretreatment is necessary and the Surfacer must be
applied to the entire area.
. Allow additional time for preheating up to panel temperature.
. The use of 2K Wash Primer underneath the surfacer is allowed, when the surfacer is intended to
be forced dried or dried overnight.
. Mix thoroughly by hand before placing the can on mixing machine.
. Surfacer has to be applied over the complete panel or overall car if the OEM paintwork is not well
cured. Spot repairing or sand throughs of the surfacer can result in spot marking or lifting when
applying a basecoat.
. The use of high performance activators will positively influence the adhesion and stonechip
performance of the complete paint system.
. Force drying of High Productive Surfacer 105xR with AZ1050 is possible with short wave I.R. for 5
minutes at half power, or 5 minutes at 60°C-65°C oven bake.
. For Semi-Flexible systems 10% 805R Flexible Additive can be added to the base material.
Activator and Thinner ratios remain equal.

Consult Safety Data Sheet prior to use. Observe the precautionary notices displayed on the container.
All other products referred to in the refinish build up are from our Cromax product range. System properties will not be valid
when the related material is used in combination with any other materials or additives which are not part of our Cromax
product range, unless explicitly indicated otherwise.

For professional use only! The information provided in this documentation has been carefully selected and arranged by us.
It is based upon our best knowledge on the subject at the date of issuance. The Information is given for information
purposes only. We are not liable for its correctness, accuracy and completeness. It is up to the user to check the
information with regard to up-to-dateness and suitability for his intended purpose. The intellectual property in this
Information, including patents, trademarks and copyrights, is protected. All rights reserved. The relevant Material Safety
Data Sheet and Warnings displayed on the product label need to be observed. We may modify and/ or discontinue
operation of all or portions of this Information at any time in our sole discretion, without notice and assume no responsibility
to update the Information. All rules set forth in this clause shall apply accordingly for any future changes and amendments.

AN AXALTA COATING SYSTEMS BRAND 7 of 7 | EN 105xR - 33 | 17.01.2024

This Technical Data Sheet supersedes all previous issues