PolyJet Materials Data Sheet

MATERIALS SIMULATING ENGINEERING PLASTICS

DIGITAL ABS, GREEN (RGD5160-DM, RGD5161-DM) MADE OF RGD515 & RGD535 |DIGITAL HIGH TEMPERATURE MATERIAL (RGD525)
ABS, IVORY (RGD5130-DM, RGD5131-DM) MADE OF RGD515 & RGD531 ASTM UNITS METRIC UNITS IMPERIAL
ASTM UNITS METRIC UNITS IMPERIAL Tensile strength D-638-03 MPa 70-80 psi 10,000-11,500
Tensile strength D-638-03 MPa 55-60 psi 8000-8700 Elongation at break D-638-05 % 10-15 % 10-15.
Elongation at break D-638-05 % 25-40 % 25-40 Modulus of elasticity D-638-04 MPa 3200-3500 psi 465,000-510,000
Modulus of elasticity D-638-04 MPa 2600-3000 psi 375,000-435,000 Flexural Strength D-790-03 MPa 110-130 psi 16,000-19,000
Flexural Strength D-790-03 MPa 65-75 psi 9,500-11,000 Flexural Modulus D-790-04 MPa 3100-3500 psi 450,000-510,000

Flexural Modulus D-790-04 MPa 1700-2200 psi 245,000-320,000 HDT, oC @ 0.45MPa D-648-06 °C 63-67 °F 145-163

HDT, oC @ 0.45MPa D-648-06 °C 58-68 °F 136-154 HDT, oC @ 0.45MPa after thermal D-648-06 °C 75-80 °F 167-176
post treatment procedure A
HDT, oC @ 0.45MPa after thermal D-648-06 °C 82-90 °F 180-194
post treatment procedure A HDT, oC @ 1.82MPa D-648-07 °C 55-57 °F 131-135

HDT, C @ 0.45MPa after thermal

o
D-648-06 °C 92-95 °F 198-203 Izod Notched Impact D-256-06 J/m 14-16 ft lb/inch 0.262-0.300
post treatment procedure B Water Absorption, % D-570-98 24hr % 1.2-1.4 % 1.2-1.4
HDT, oC @ 1.82MPa D-648-07 °C 51-55 °F 124-131 Tg DMA, E» °C 62-65 °F 144-149
Izod Notched Impact D-256-06 J/m 65-80 ft lb/inch 1.22-1.50 Shore Hardness D Scale D Scale D 87-88 Scale D 87-88
Tg DMA, E» °C 47-53 °F 117-127 Rockwell Hardness Scale M Scale M 78-83 Scale M 78-83
Shore Hardness (D) Scale D Scale D 85-87 Scale D 85-87 Polymerized density ASTM D792 g/cm3 1.17-1.18
Rockwell Hardness Scale M Scale M 67-69 Scale M 67-69 Ash content USP281 % 0.38-0.42 % 0.38-0.42
Polymerized density ASTM D792 g/cm3 1.17-1.18

MATERIALS SIMULATING STANDARD PLASTICS

TRANSPARENT MATERIALS TRANSPARENT MATERIALS

RGD720 VEROCLEAR RGD810
ASTM UNITS METRIC UNITS IMPERIAL ASTM UNITS METRIC UNITS IMPERIAL
Tensile strength D-638-03 MPa 50-65 psi 7250-9450 Tensile strength D-638-03 MPa 50-65 psi 7250-9450
Elongation at break D-638-05 % 15-25 % 15-25 Elongation at break D-638-05 % 10-25 % 10-25
Modulus of elasticity D-638-04 MPa 2000-3000 psi 290,000-435,000 Modulus of elasticity D-638-04 MPa 2000-3000 psi 290,000-435,000
Flexural Strength D-790-03 MPa 80-110 psi 12000-16000 Flexural Strength D-790-03 MPa 75-110 psi 11000-16000
Flexural Modulus D-790-04 MPa 2700-3300 psi 390,000-480,000 Flexural Modulus D-790-04 MPa 2200-3200 psi 320,000-465,000
HDT, oC @ 0.45MPa D-648-06 °C 45-50 °F 113-122 HDT, oC @ 0.45MPa D-648-06 °C 45-50 °F 113-122
HDT, oC @ 1.82MPa D-648-07 °C 45-50 °F 113-122 HDT, oC @ 1.82MPa D-648-07 °C 45-50 °F 113-122
Izod Notched Impact D-256-06 J/m 20-30 ft lb/inch 0.375-0.562 Izod Notched Impact D-256-06 J/m 20-30 ft lb/inch 0.375-0.562
Water Absorption D-570-98 24hr % 1.5-2.2 % 1.5-2.2 Water Absorption D-570-98 24hr % 1.1-1.5 % 1.1-1.5
Tg DMA, E» °C 48-50 °F 118-122 Tg DMA, E» °C 52-54 °F 126-129
Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86 Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86
Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76 Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76
Polymerized density ASTM D792 g/cm3 1.18-1.19 Polymerized density ASTM D792 g/cm3 1.18-1.19
Ash content USP281 % 0.01-0.02 % 0.01-0.02 Ash content USP281 % 0.02-0.06 % 0.02-0.06
Find material properties for color materials on the Color Digital Materials Data Sheet.
 RIGID OPAQUE MATERIALS RIGID OPAQUE MATERIALS
VEROPUREWHITE RGD837, VEROGRAY RGD850, VEROBL ACKPLUS RGD875, VEROBLUE RGD840
VEROWHITEPLUS RGD835, VEROYELLOW RGD836, VEROCYAN RGD841, ASTM UNITS METRIC UNITS IMPERIAL
VEROMAGENTA RGD851 Tensile strength D-638-03 MPa 50-60 psi 7250-8700
ASTM UNITS METRIC UNITS IMPERIAL Elongation at break D-638-05 % 15-25 % 15-25
Tensile strength D-638-03 MPa 50-65 psi 7250-9450
Modulus of elasticity D-638-04 MPa 2000-3000 psi 290,000-435,000
Elongation at break D-638-05 % 10-25 % 10-25
Modulus of elasticity D-638-04 MPa 2000-3000 psi 290,000-435,000 Flexural Strength D-790-03 MPa 60-70 psi 8700-10200
Flexural Strength D-790-03 MPa 75-110 psi 11000-16000 Flexural Modulus D-790-04 MPa 1900-2500 psi 265,000-365,000
Flexural Modulus D-790-04 MPa 2200-3200 psi 320,000-465,000 HDT, °C @ 0.45MPa D-648-06 °C 45-50 °F 113-122
HDT, °C @ 0.45MPa D-648-06 °C 45-50 °F 113-122
HDT, °C @ 1.82MPa D-648-07 °C 45-50 °F 113-122
HDT, °C @ 1.82MPa D-648-07 °C 45-50 °F 113-122
Izod Notched Impact D-256-06 J/m 20-30 ft lb/inch 0.375-0.562 Izod Notched Impact D-256-06 J/m 20-30 ft lb/inch 0.375-0.562
Water Absorption D-570-98 24hr % 1.1-1.5 % 1.1-1.5 Water Absorption D-570-98 24hr % 1.5-2.2 % 1.5-2.2
Tg DMA, E» °C 52-54 °F 126-129 Tg DMA, E» °C 48-50 °F 118-122
Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86
Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86
Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76
Polymerized density ASTM D792 g/cm3 1.17-1.18 Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76
Ash content VeroGray, USP281 % 0.23-0.26 % 0.23-0.26 Polymerized density ASTM D792 g/cm3 1.18-1.19
VeroWhitePlus Ash content USP281 % 0.21-0.22 % 0.21-0.22
Ash content VeroBlackPlus USP281 % 0.01-0.02 % 0.01-0.02

RUBBER-LIKE MATERIALS
SIMUL ATED POLYPROPYLENE MATERIALS
TANGOBL ACKPLUS FL X980 AND TANGOPLUS FL X930
DURUS WHITE RGD430
ASTM UNITS METRIC UNITS IMPERIAL
ASTM UNITS METRIC UNITS IMPERIAL
Tensile strength D-638-03 MPa 20-30 psi 2900-4350 Tensile strength D-412 MPa 0.8-1.5 psi 115-220
Elongation at break D-638-05 % 40-50 % 40-50 Elongation at break D-412 % 170-220 % 170-220
Modulus of elasticity D-638-04 MPa 1000-1200 psi 145,000-175,000 Compressive set D-395 % 4-5 % 4-5
Flexural Strength D-790-03 MPa 30-40 psi 4350-5800 Shore Hardness (A) D-2240 Scale A 26-28 Scale A 26-28
Flexural Modulus D-790-04 MPa 1200-1600 psi 175,000-230,000 Tensile Tear resistance D-624 Kg/cm 2-4. Lb/in 18-22
HDT, °C @ 0.45MPa D-648-06 °C 37-42 °F 99-108
Polymerized density ASTM D792 g/cm3 1.12-1.13
HDT, °C @ 1.82MPa D-648-07 °C 32-34 °F 90-93
Izod Notched Impact D-256-06 J/m 40-50 ft lb/inch 0.749-0.937
Water Absorption D-570-98 24hr % 1.5-1.9 % 1.5-1.9 TANGOBL ACK FL X973
Tg DMA, E» °C 35-37 °F 95-99 ASTM UNITS METRIC UNITS IMPERIAL
Shore Hardness (D) Scale D Scale D 74-78 Scale D 74-78 Tensile strength D-412 MPa 1.8-2.4 psi 115-350
Rockwell Hardness Scale M Scale M no data Scale M no data
Elongation at break D-412 % 45-55 % 45-55
Polymerized density ASTM D792 g/cm3 1.15-1.17
Compressive set D-395 % 0.5-1.5 % 0.5-1.5
Ash content USP281 % 0.10-0.12 % 0.1-0.12
Shore Hardness (A) D-2240 Scale A 60-62 Scale A 60-62
Tensile Tear resistance D-624 Kg/cm 3-5 Lb/in 18-24
RIGUR RGD450
Polymerized density ASTM D792 g/cm3 1.14-1.15
ASTM UNITS METRIC UNITS IMPERIAL
Tensile strength D-638-03 MPa 40-45 psi 5800-6500
Elongation at break D-638-05 % 20-35 % 20-35 TANGOGRAY FL X950
Modulus of elasticity D-638-04 MPa 1700-2100 psi 246,000 – 305,000 ASTM UNITS METRIC UNITS IMPERIAL
Flexural Strength D-790-03 MPa 52-59 psi 7500 - 8500
Tensile strength D-412 MPa 3-5 psi 435-725
Flexural Modulus D-790-04 MPa 1500-1700 psi 217,000 – 246,000
Elongation at break D-412 % 45-55 % 45-55
HDT, °C @ 0.45MPa D-648-06 °C 49-54 °F 120-129
Compressive set D-395 % 0.5-1.5 % 0.5-1.5
HDT, °C @ 1.82MPa D-648-07 °C 45-50 °F 113-122
Izod Notched Impact D-256-06 J/m 30-35 ft lb/inch 0.561-0.656 Shore Hardness (A) D-2240 Scale A 73-77 Scale A 73-77
Tg DMA, E» °C 48-52 °F 118-126 Tensile Tear resistance D-624 Kg/cm 8-12 Lb/in 50-60
Shore Hardness (D) Scale D Scale D 80-84 Scale D 80-84 Polymerized density ASTM D792 g/cm3 1.16-1.17
Rockwell Hardness Scale M Scale M 58-62 Scale M 58-62
Polymerized density ASTM D792 g/cm3 1.20-1.21
Ash content USP281 % 0.3-0.4 % 0.3-0.4

The data included in this brochure is for your information purposes only and should not be considered specific advice to any particular customer project. Each customer is responsible for the design, functioning and all other decisions with regards to its particular projects and systems. The sale and provision of the products described
in this brochure are subject to terms and conditions outlined in Stratasys’ selling policies, contracts between the parties or Stratasys’ Terms and Conditions of Sale. This brochure is not intended to and does not enlarge or add to any such contract or terms.
© 2014, 2015, 2016 Stratasys Ltd. All rights reserved. Stratasys, Stratasys logo, Objet, For a 3D World, Objet24,Objet30, Objet 30 Pro, Objet30 OrthoDesk, Objet Studio, Quadra, QuadraTempo, FullCure, SHR, Eden, Eden250, Eden260, Eden260V, Eden 330, Eden350, Eden350V, Eden500V, Job Manager, CADMatrix,Connex,
Objet260 Connex, Connex350, Connex500, Objet1000, Rigur, Alaris, Alaris30, PolyLog, TangoBlack,TangoGray, TangoPlus, TangoBlackPlus, VeroBlue, VeroBlack, VeroBlackPlus, VeroClear, VeroDent,VeroGray, VeroWhite, VeroWhitePlus, VeroPureWhite, Durus, Digital Materials, PolyJet, Polyjet Matrix, Digital ABS and ObjetGreen are
trademarks or registered trademarks of Stratasys Ltd. and/or its subsidiaries or affiliates and may be registered in certain jurisdictions. All other trademarks belong to their respective owners. MSS_PJ_PJMaterialsDataSheet_0916a