LUPOX TE5100

Injection Molding, PBT+PC+GF10%

Description Application
High Tensile/Flexural strength, Dimensional Stability Automotive(Roof Rack)

Properties Test Condition Test Method Unit Typical Value

Physical
Specific Gravity ASTM D792 - 1.29
Molding Shrinkage ASTM D955 % 0.6 ~ 0.9
Melt Flow Rate 250℃/5kg ASTM D1238 g/10min 14
Water Absorption 23℃, 24hrs ASTM D570 % 0.08

Mechanical
Tensile Strength, 3.2mm ASTM D638
@ Break 5mm/min kg/cm 2 880
Tensile Elongation, 3.2mm ASTM D638
@ Yield 5mm/min % -
@ Break 5mm/min % 3.0
Flexural Strength, 6.4mm 5mm/min ASTM D790 kg/cm 2 1,350
Flexural Modulus, 6.4mm 5mm/min ASTM D790 kg/cm 2 42,000
IZOD Impact Strength, 6.4mm ASTM D256
(Notched) 23℃ kg·cm/cm 9.7
-30℃ kg·cm/cm 7.5

Thermal
Melt Temperature ASTM D3418 ℃ 223
Heat Deflection Temperature, 6.4mm ASTM D648
(Unannealed) 18.6kg ℃ 120
4.6kg ℃ -
Flammability UL94 class -
Relative Temperature Index UL 746B
Electrical ℃ -
Mechanical with Impact ℃ -
Mechanical without Impact ℃ -

Electrical
Comparative Tracking Index(CTI) Solution A UL 746 PLC -
Volume Resistivity 23℃ ASTM D257 Ohm·cm -
Arc Resistance 23℃ ASTM D495 PLC -
Dielectric Strength, 1mm 23℃ ASTM D149 kV/mm -
Note) All properties, except melt flow rate are measured on injection molulded specimens and after 48 hours storage at 23℃, 50% relative humidty.

Updated : 1-Jul-14
The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee,
expressed or implied, (i) that the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG
Chem materials, products, recommendations or advice. Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the
typical values should be regarded as reference values only and not as binding minimum values. Each user bear full responsibility for making its own determination as to the
suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each user must identify and perform all tests and analyses necessary to
assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use conditions. The data contained herein can be
changed without notice as a result of the quality improvement of the products.
 LUPOX TE5100
Injection Molding, PBT+PC+GF10%

Description Application
High Tensile/Flexural strength, Dimensional Stability Automotive(Roof Rack)

Processing Guide (Injection Molding)

Processing Parameters Unit Value

Drying Temperature ℃ 120
Drying Time hrs 4~5
Maximum Moisture Content % 0.02
Melt Temperature ℃ 260 ~ 270
Rear ℃ 250 ~ 260
Cylinder Temperature Middle ℃ 250 ~ 260
Front ℃ 255 ~ 265
Nozzle Temperature ℃ 260 ~ 270
Mold Temperature ℃ 60 ~ 80
Back Pressure kg/cm 2 -
Screw Speed rpm -
Note) Back Pressure & Screw Speed are only mentioned as general guidelines.
These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.

Updated : 1-Jul-14

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee,
expressed or implied, (i) that the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG
Chem materials, products, recommendations or advice. Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the
typical values should be regarded as reference values only and not as binding minimum values. Each user bear full responsibility for making its own determination as to the
suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each user must identify and perform all tests and analyses necessary to
assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use conditions. The data contained herein can be
changed without notice as a result of the quality improvement of the products.