Nothing Special   »   [go: up one dir, main page]
Scribd Logo
Upload

Welcome to Scribd!

  • 72 views

    Data Sheet ECP PP R20TK

    Uploaded by

    Đình Long Trịnh
    This document provides product information for ECP PP R20T, a plastic compound manufactured in Vietnam containing 20% talc powder for injection molding applications. It has a melt flow rate of 6 g/10 min and a density of 1.07 g/cm3. The compound has a tensile strength of 31 MPa, elongation at break over 20%, flexural strength of 46 MPa, and flexural modulus of 1682 MPa. It meets Vietnam safety standards for food and medical applications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Data Sheet ECP PP R20TK

    Uploaded by

    Đình Long Trịnh
    72 views2 pages
    This document provides product information for ECP PP R20T, a plastic compound manufactured in Vietnam containing 20% talc powder for injection molding applications. It has a melt flow rate of 6 g/10 min and a density of 1.07 g/cm3. The compound has a tensile strength of 31 MPa, elongation at break over 20%, flexural strength of 46 MPa, and flexural modulus of 1682 MPa. It meets Vietnam safety standards for food and medical applications.

    Original Description:

    Original Title

    Data sheet ECP PP R20TK

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides product information for ECP PP R20T, a plastic compound manufactured in Vietnam containing 20% talc powder for injection molding applications. It has a melt flow rate of 6 g/10 min and a density of 1.07 g/cm3. The compound has a tensile strength of 31 MPa, elongation at break over 20%, flexural strength of 46 MPa, and flexural modulus of 1682 MPa. It meets Vietnam safety standards for food and medical applications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    72 views2 pages

    Data Sheet ECP PP R20TK

    Uploaded by

    Đình Long Trịnh
    This document provides product information for ECP PP R20T, a plastic compound manufactured in Vietnam containing 20% talc powder for injection molding applications. It has a melt flow rate of 6 g/10 min and a density of 1.07 g/cm3. The compound has a tensile strength of 31 MPa, elongation at break over 20%, flexural strength of 46 MPa, and flexural modulus of 1682 MPa. It meets Vietnam safety standards for food and medical applications.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    PRODUCT INFORMATION AND DATA SHEET

    PRODUCTION NAME: PP COMPOUND


    PRODUCT GRADE: ECP PP R20T

    About Product
    This product is one kinds of plastic compound. It is manufactured by extruder machine and the
    most modern technology represent in Vietnam.
    General Description
    ECP PP R20T is product compound plastic PP with 20% talc powder use for injection molding
    applications.

    Technical Analysis
    PHYSICAL PROPERTIES ASTM/ Method Units Values
    Melt Flow Rate (230°C/2.16kg) D 1238 g/10 min 6
    Density D 792 g/cm³ 1.07
    MECHANICAL
    Tensile Strength at Break D 638 MPa 31
    Elongation at Break D 638 % >20
    Flexural Strength D 790 MPa 46
    Flexural Modulus D 790 MPa 1682
    Izod Impact Strength, Notched D 256 kJ/m2 5

    Mold shrinkage 50x70x3 mm % 1.2 – 1.5


    THERMAL

    DeflectionTemperatureunderLoadat0.45MPa D 648 ºC 120

    Flammability UL 94 HB

    Properties:
    Appearance (Surface color) : pellet form
    Processing temperature : 180 - 230 oC
    Pellet Size : 3x3 (±0.3) mm
    Packing : 20 kgs per PP bag
    Storage : Keep at dry condition
    Medical norm
    Attain the Safety Norm for Health and Foodstuff issued by Vietnam Directorate for Standards and Quality allow the decision
    3339/2001/QĐ-BYT promulgated by Vietnam Ministry of Health.
    Safety apply for handling process. No healthy damage infected.

    Caution: This product information is based on our general experience and does not constitute a specification. Since many
    factors affect the use of our products, no warranty is given or implied with respect to this information or patent infringement. We do
    not accept liability for any loss or damage arising from the use of this information. All sales are subject to our Standard Terms and
    Conditions of Sale.

    QC Department

    You might also like