    This document provides information on a halogen free flame retardant thermoplastic compound intended for use in tight and semitight buffer fiber cables. The compound offers excellent mechanical properties from -20 to +90°C with high fire resistance and good processing conditions. Physical property data and testing results are provided, along with processing guidelines for extrusion of the compound into cable jacketing. Storage and packaging information is also included.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    TDS 01ofg V08 en

    Uploaded by

    DenisTaras
    69 views2 pages
    This document provides information on a halogen free flame retardant thermoplastic compound intended for use in tight and semitight buffer fiber cables. The compound offers excellent mechanical properties from -20 to +90°C with high fire resistance and good processing conditions. Physical property data and testing results are provided, along with processing guidelines for extrusion of the compound into cable jacketing. Storage and packaging information is also included.

    Original Description:

    Original Title

    TDS_01OFG_V08_EN

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on a halogen free flame retardant thermoplastic compound intended for use in tight and semitight buffer fiber cables. The compound offers excellent mechanical properties from -20 to +90°C with high fire resistance and good processing conditions. Physical property data and testing results are provided, along with processing guidelines for extrusion of the compound into cable jacketing. Storage and packaging information is also included.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    69 views2 pages

    TDS 01ofg V08 en

    Uploaded by

    DenisTaras
    This document provides information on a halogen free flame retardant thermoplastic compound intended for use in tight and semitight buffer fiber cables. The compound offers excellent mechanical properties from -20 to +90°C with high fire resistance and good processing conditions. Physical property data and testing results are provided, along with processing guidelines for extrusion of the compound into cable jacketing. Storage and packaging information is also included.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    HZ Geral 01OFG

    PRODUCT APPLICATION
    Halogen free flame retardant thermoplastic compound to be used as tight and semitight buffer fibre
    cables. This compound combines excellent mechanical properties, -20 to +90ºC and high fire resistance,
    with excellent processing conditions. Low shrinkage and good extralength fibre. Good gel and chemical
    resistance.

    PHYSICAL PROPERTIES UNIT VALUE TOLERANCE TEST METHOD


    Density (23±2 ºC) g/cm3 1,44 ± 0,02 ISO 1183 A
    Hardness (23±2 ºC) shore D/15s 56 ±2 ISO 868
    Tensile strenght (23±2 ºC) M Pa 14 Typical value CEI 60811-1-1
    Elongation at break (23±2 ºC) % 170 Typical value CEI 60811-1-1
    Elongation after aging % variation 30 max. MI (100ºC - 168h)
    Tensile strenght after aging % variation 30 max. MI (100ºC - 168h)
    Melt flow index (21,6 Kg/150ºC) g/10' 9 ±3 ISO 1133
    Conductivity microS.mm-1 0,8 Typical value EN 50267-2-2
    Water Absortion (10d at 70ºC) mg/cm² 0,3 max. CEI 60811-1-3
    Pellet Length mm 2,8 max. MI
    Heat deformation test (6h, 80ºC) % variation 5 max. Internal method

    FLAMMABILITY UNIT VALUE TOLERANCE TEST METHOD


    Limiting Oxygen Index % 33 Typical value ASTM D 2863
    Halogen Content % 0 Typical value CEI 60754-1
    pH pH 4,5 min. EN 50267-2-2

    CHEMICAL RESISTANCE UNIT VALUE TOLERANCE TEST METHOD


    TS after immersion in oil (IRM 902) % variation -12 max. Oil(IRM 902) - 70ºC-4h
    Elong. after immersion in oil (IRM902) % variation -5 max. Oil(IRM 902) - 70ºC-4h

    The typical values reported in the table have obtained from measurements made in pressed plates, on extruded samples or pellets.

    Color: Natural

    Packing: The compound can be supplied in bags of aluminum or polyethylene (of 20 or 25 kg), in big bags (of 750 the 2000 kg).

    Storage: The product must be stored at room temperature between 10 and 50ºC and relative humidity less then 70%.
    The container must be kept tightly closed to prevent moisture absorption or contamination.
    The container must be kept in a dry cool and well ventilated place. Avoid direct sun light and direct heat exposure.
    Maximum recommended storage time in the original package and without being open: 9 months from the delivery date. We
    recomend always to dry the compound before use.

    CABOPOL - Polymer Compounds, S.A. Telf. +351 244 498 151 Nº 5106
    Apartado 39 EC Porto de Mós Fax: +351 244 481 970 Version 08
    2481-917, Porto de Mós, Portugal cabopol@mekkin.pt Date 11/06/2019

    MOD.CTC/05
    PROCESSING GUIDE
    Extrusion line L/D 24D-25D
    Color masterbatch PE, EVA base
    Wire section (sqm)
    Tooling Pressure DDR 1,6; lip diameter +1,5/1 mm core.
    Semi-pressure or a tube DDR 1,5 - 2; DRB=1
    Die diameter Die same diameter as outer or -0,2mm
    Screw design compression ratio Low compression 1.1,5 with flat end trnsport. High compression also
    possible need adjust temperature profile increase temperature.
    Screw cooling Not mandatory, if possible 120ºC
    Copper heating (ºC) Not mandatory or 80ºC- 100ºC
    Pre-dry material before extrusion Not mandatory if time after production < 3 months
    Moisture level (ppm) < 600
    Cooling Water Ambient water cooling
    Screen packs 40, 60 mesh or free flow open ring
    Extruder Z1(°C) 130-140
    Extruder Z2(°C) 140-150
    Extruder Z3(°C) 155
    Extruder Z4(°C) 160
    Neck Z5(°C) 160
    Head Z6(°C) 165-170
    Die Z7(°C) 175
    Melt temperature (°C) 155-165
    Speed extrusion (m/min) 300m/min D 3,0 mm;100m/min D 20mm
    Surface If not smooth with die droll, use flame to improve
    Notes Screw design halogen free - low compression; control temperature as better
    as possible but not mandatory. Adjust temperatures base on L/D and
    number of zones. Porosity come for the shear or moisture control melt not to
    pass 175ºC.

    Disclaimer
    Once removed from its original package, the material shall be used immediately. Cabopol, SA assumes no responsibility for any non-
    conformities of the material resulting from its incorrect storage and/or handling.

    All values expressed in this data sheet were obtained under controlled conditions according to our knowledge and are valid only for those same
    conditions. Therefore, the information contained in this document is believed to be accurate and reliable. However, no warranty, expressed or
    implied, is given as to the suitability, accuracy, reliability or completeness of the information made available. The information provided herein
    does not hold Cabopol liable for damages or penalties resulting from following our suggestions or recommendations, and it is the responsibility
    of the user to ensure of the conformity of the material to the intended application and to the specific regulations that apply to each case.

    This document contains confidential and / or privileged information. If you are not the intended recipient or the person authorized to receive this
    document, you should not use, copy or disclose any information contained therein or take any action based on this information.

    CABOPOL - Polymer Compounds, S.A. Telf. +351 244 498 151 Nº 5106
    Apartado 39 EC Porto de Mós Fax: +351 244 481 970 Version 08
    2481-917, Porto de Mós, Portugal cabopol@mekkin.pt Date 11/06/2019

    MOD.CTC/05

    You might also like