Abstract
Graphene sheets—one-atom-thick two-dimensional layers of sp2-bonded carbon—are predicted to have a range of unusual properties. Their thermal conductivity and mechanical stiffness may rival the remarkable in-plane values for graphite (∼3,000 W m-1 K-1 and 1,060 GPa, respectively); their fracture strength should be comparable to that of carbon nanotubes for similar types of defects1,2,3; and recent studies have shown that individual graphene sheets have extraordinary electronic transport properties4,5,6,7,8. One possible route to harnessing these properties for applications would be to incorporate graphene sheets in a composite material. The manufacturing of such composites requires not only that graphene sheets be produced on a sufficient scale but that they also be incorporated, and homogeneously distributed, into various matrices. Graphite, inexpensive and available in large quantity, unfortunately does not readily exfoliate to yield individual graphene sheets. Here we present a general approach for the preparation of graphene-polymer composites via complete exfoliation of graphite9 and molecular-level dispersion of individual, chemically modified graphene sheets within polymer hosts. A polystyrene–graphene composite formed by this route exhibits a percolation threshold10 of ∼0.1 volume per cent for room-temperature electrical conductivity, the lowest reported value for any carbon-based composite except for those involving carbon nanotubes11; at only 1 volume per cent, this composite has a conductivity of ∼0.1 S m-1, sufficient for many electrical applications12. Our bottom-up chemical approach of tuning the graphene sheet properties provides a path to a broad new class of graphene-based materials and their use in a variety of applications.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on SpringerLink
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Dresselhaus, M. S. & Dresselhaus, G. Intercalation compounds of graphite. Adv. Phys. 51, 1–186 (2002)
Hirata, M., Gotou, T., Horiuchi, S., Fujiwara, M. & Ohba, M. Thin-film particles of graphite oxide 1: High-yield synthesis and flexibility of the particles. Carbon 42, 2929–2937 (2004)
Yu, M. F., Lourie, O., Moloni, K., Kelly, T. F. & Ruoff, R. S. Strength and breaking mechanism of multiwalled carbon nanotubes under tensile load. Science 287, 637–640 (2000)
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004)
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005)
Zhang, Y., Tan, Y.-W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry's phase in graphene. Nature 438, 201–204 (2005)
Zhang, Y., Small, J. P., Amori, M. E. S. & Kim, P. Electric field modulation of galvanomagnetic properties of mesoscopic graphite. Phys. Rev. Lett. 94, 176803 (2005)
Berger, C. et al. Ultrathin epitaxial graphite: two-dimensional electron gas properties and a route toward graphene-based nanoelectronics. J. Phys. Chem. B 108, 19912–19916 (2004)
Stankovich, S. et al. Stable aqueous dispersions of graphitic nanoplatelets via the reduction of exfoliated graphite oxide in the presence of poly(sodium 4-styrenesulfonate). J. Mater. Chem. 16, 155–158 (2006)
Stauffer, D. & Aharnoy, A. Introduction to Percolation Theory (Taylor & Francis, London, 1991)
Ounaies, Z., Park, C., Wise, K. E., Siochi, E. J. & Harrison, J. S. Electrical properties of single wall carbon nanotube reinforced polyimide composites. Compos. Sci. Technol. 63, 1637–1646 (2003)
Chung, D. D. L. Electrical applications of carbon materials. J. Mater. Sci. 39, 2645–2661 (2004)
He, H., Klinowski, J., Forster, M. & Lerf, A. A new structural model for graphite oxide. Chem. Phys. Lett. 287, 53–56 (1998)
Lerf, A., He, H., Forster, M. & Klinowski, J. Structure of graphite oxide revisited. J. Phys. Chem. B 102, 4477–4482 (1998)
Hirata, M., Gotou, T. & Ohba, M. Thin-film particles of graphite oxide 2: Preliminary studies for internal micro fabrication of single particle and carbonaceous electronic circuits. Carbon 43, 503–510 (2005)
Szabo, T., Szeri, A. & Dekany, I. Composite graphitic nanolayers prepared by self-assembly between finely dispersed graphite oxide and a cationic polymer. Carbon 43, 87–94 (2005)
Kovtyukhova, N. I. et al. Layer-by-layer assembly of ultrathin composite films from micron-sized graphite oxide sheets and polycations. Chem. Mater. 11, 771–778 (1999)
Kotov, N. A., Dekany, I. & Fendler, J. H. Ultrathin graphite oxide-polyelectrolyte composites prepared by self-assembly. Transition between conductive and non-conductive states. Adv. Mater. 8, 637–641 (1996)
Cassagneau, T., Guerin, F. & Fendler, J. H. Preparation and characterization of ultrathin films layer-by-layer self-assembled from graphite oxide nanoplatelets and polymers. Langmuir 16, 7318–7324 (2000)
Vaia, R. A. & Wagner, H. D. Framework for nanocomposites. Mater. Today 7, 32–37 (2004)
Du, X. S., Xiao, M., Meng, Y. Z. & Hay, A. S. Novel synthesis of conductive poly(arylene disulfide)/graphite nanocomposite. Synth. Met. 143, 129–132 (2004)
Liu, P. & Gong, K. Synthesis of polyaniline-intercalated graphite oxide by an in situ oxidative polymerization reaction. Carbon 37, 706–707 (1999)
Stankovich, S., Piner, R. D., Nguyen, S. T. & Ruoff, R. S. Synthesis and exfoliation of isocyanate-treated graphene oxide nanoplatelets. Carbon (in the press)
McLachlan, D. S. et al. AC and DC percolative conductivity of single wall carbon nanotube polymer composites. J. Polym. Sci. B 43, 3273–3287 (2005)
Chen, G., Weng, W., Wu, D. & Wu, C. PMMA/graphite nanosheets composite and its conducting properties. Eur. Polym. J. 39, 2329–2335 (2003)
Garboczi, E. J., Snyder, K. A., Douglas, J. F. & Thorpe, M. F. Geometrical percolation threshold of overlapping ellipsoids. Phys. Rev. E 52, 819–828 (1995)
Grossiord, N., Loos, J. & Koning, C. E. Strategies for dispersing carbon nanotubes in highly viscous polymers. J. Mater. Chem. 15, 2349–2352 (2005)
Ramasubramaniam, R., Chen, J. & Liu, H. Homogeneous carbon nanotube polymer composites for electrical applications. Appl. Phys. Lett. 83, 2928–2930 (2003)
Olson, D. W. USGS Mineral Commodity Summaries. http://minerals.usgs.gov/minerals/pubs/commodity/graphite/graphmcs06.pdf (2006).
Titelman, G. I. & Bron, S. Method of Manufacturing of Graphite Oxide (GO) P1391–P1392 (Research Disclosure 500, IMI TAMI Institute for Research & Development Ltd., Haifa, 2005).
Acknowledgements
SEM was done at the Electron Probe Instrumentation Centre at Northwestern University. This work was funded by the NASA University Research, Engineering and Technology Institute on Bio-Inspired Materials (BIMat) and by the NSF NIRT grant ‘Nanostructured carbons from self-assembled block copolymer precursors: From synthesis and characterization to devices’. We appreciate J. A. Ibers and A. L. Ruoff for critically reading an early version of this manuscript.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Competing interests
Reprints and permissions information is available at npg.nature.com/reprintsandpermissions. The authors declare no competing financial interests.
Supplementary information
Supplementary Notes
This file contains Supplementary Methods 1 and 2 (Composite samples preparation via hot pressing; Nanofillers made from graphite oxide by two competing methods: chemical reduction and thermal expansion.) and Supplementary Discussion (Explanation of electron diffraction patterns). (PDF 321 kb)
Rights and permissions
About this article
Cite this article
Stankovich, S., Dikin, D., Dommett, G. et al. Graphene-based composite materials. Nature 442, 282–286 (2006). https://doi.org/10.1038/nature04969
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1038/nature04969
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.