WO2018108918A1

WO2018108918A1 - Catalyst system for producing polyethylene copolymers in a high temperature solution polymerization process

Info

Publication number: WO2018108918A1
Application number: PCT/EP2017/082434
Authority: WO
Inventors: Noureddine AJELLAL; Anna Fait; Luigi Resconi
Original assignee: Borealis Ag
Priority date: 2016-12-15
Filing date: 2017-12-12
Publication date: 2018-06-21
Also published as: CN110234665A; US11279781B2; JP7130644B2; KR102534541B1; ES2943392T3; JP2020502327A; US20200079887A1; EP3555148B1; CN110234665B; KR20190087636A; EP3555148A1

Abstract

Catalyst system for producing ethylene copolymers in a high temperature solution process, the catalyst system comprising (i) a metallocene complex of formula (I) wherein: M is Hf or a mixture with Zr, provided that more than 50% by moles of the complex of Formula (I) has M = Hf; X is a sigma ligand; R are the same or different from each other and can be saturated linear or branched C₁-C₁₀ alkyl, C₆-C₁₀ aryl, C₄-C₁₀ heteroaryl, C₆-C₂₀ alkylaryl or C₆-C₂₀ arylalkyl groups, which can optionally contain up to 2 heteroatoms or silicon atoms; R¹ is a C₆-C₁₀ aryl or C₆-C₂₀ alkylaryl group optionally containing up to 2 heteroatoms or silicon atoms or a C₄-C₁₀ heteroaryl group; R₂ is a C₄-C₂₀ cycloalkyl group, optionally carrying alkyl substituents in beta-positions, of formula (II) in which R' can be the same or can be different from each other and can be hydrogen or is defined as R and n is 1 to 17 (ii) a boron containing cocatalyst

Description

CATALYST SYSTEM FOR PRODUCING POLYETHYLENE COPOLYMERS IN A HIGH

TEMPERATURE SOLUTION POLYMERIZATION PROCESS

The present invention is related to a new catalysts system, which is able to produce polyethylene copolymers in a high temperature solution polymerization process. The new catalyst system comprises a specifically substituted, bridged hafnocene catalyst complex, comprising a cyclopentadienyl (Cp) ligand, a fluorenyl (Flu) ligand and a specifically covalent bridge connecting the two ligands, along with a boron based cocatalyst. This combination remarkably gives rise to catalyst systems with high productivity combined with high solubility, molecular weight capability and comonomer incorporation ability.

Metallocene catalysts have been used to manufacture polyolefins for many years. Countless academic and patent publications describe the use of these catalysts in olefin polymerization. Metallocenes are now used industrially and polypropylenes as well as polyethylenes are often produced using cyclopentadienyl based catalyst systems with different substitution patterns.

Several of these metallocene catalysts have been described for the use in solution polymerization for producing polyethylene homo- or copolymers.

For example WO 2000024792 describes a catalyst system comprising hafnocene catalyst complex derived from A) a biscyclopentadienyl hafnium organometallic compound having i) at least one unsubstituted cyclopentadienyl ligand or aromatic fused-ring substituted cyclopentadienyl ligand not having additional substitutents on said ligand, ii) one substituted or unsubstituted, aromatic fused-ring substituted cyclopentadienyl ligand, and iii) a covalent bridge connecting the two cyclopentadienyl ligands.

This bridge can be a single carbon substituted with two aryl groups, each of these aryl groups being substituted with a Ci - C20 hydrocarbyl or hydrocarbylsilyl group, whereby at least one of these substituents is a linear C3 or greater substitutent.

In addition the catalyst system comprises an activating cocatalyst, which is preferably a precursor ionic compound comprising a halogenated tetraaryl-substituted Group 13 anion.

Also EP 251 1305 is related to bridged Cp-Flu metallocene complexes. The C-based bridges shown in the Examples are substituted methylene bridges, whereby the substituents are the same (e.g. dimethyl, diphenyl, dibenzyl,-etc) or are linked together to form a ring (e.g. cyclohexylidene). Yano and co-workers (literatures 1 to 4) studied the effect of ligand structure on high temperature ethylene homo-polymerization and copolymerization with various Cp-Flu metallocenes.

1 . A. Yano, M. Sone, S. Hasegawa, M. Sato, A. Akimoto, Macromol. Chem. Phys. 1999, 200, 933.

2. A. Yano, S. Hasegawa, T. Kaneko, M. Sone, M. Sato, A. Akimoto, Macromol. Chem. Phys.

1999, 200, 1542.

3. A. Yano, M. Sone, S. Yamada, S. Hasegawa, M. Sato, A. Akimoto, Journal of Molecular

Catalysis A: Chemical 2000, 156, 133.

4. S. Hasegawa, M. Sone, M. Tanabiki, M. Sato, A. Yano, Journal of Polymer Science: Part A: Polymer Chemistry 2000, 38, 4641.

The main teachings from this work are:

i) For both the Zr and analogue Hf complexes, in C2 homopolymerization and C2/C6 copolymerization, a P i2C bridge provides higher activity and higher Mw compared to a MePhC or Me₂C bridge.

ii) Addition of substituents on the Cp ligand does not significantly change catalyst performance iii) With Zr as the metal, in C2/C6 copolymerization, addition of methyl or ie f-butyl substituents in the 2,7 positions of the Flu ligand increases molecular weight of the copolymer but does not affect comonomer reactivity nor catalyst productivity.

iv) With Hf as the metal, in C2/C6 copolymerization, addition of ie f-butyl substituents in the 2,7 positions of the Flu ligand slightly increases catalyst productivity but molecular weight of the copolymer and comonomer reactivity are hardly affected.

v) Zr complexes are more active than Hf complexes, but the Ph2C(Cp)(Flu)ZrCl2 complex gives lower copolymer Mw compared to its Hf analogue

In none of the above cited literatures and patents the combination of high productivity in combination with high solubility, molecular weight capability and comonomer incorporation ability of the catalyst system is mentioned.

Furthermore the above cited literatures and patents do not address the effect of the steric encumbrance of a bridge being composed of C-atom substituted by an aryl group whereas the second substituent being a non-aryl substituent at higher polymerization temperature on the catalyst performance of a Hafnium complex.

However, for a process for producing ethylene copolymers to be efficient, it is important that the catalyst system used fulfils a set of very strict requirements. Comonomer reactivity for higher comonomers (comonomer incorporation), catalyst molecular weight capability (lowest achievable melt index for a given polymer density, monomer concentration and polymerization temperature) and catalyst thermal stability must ensure the production of copolymers with density down to - 0.850 g/cm³ and a melt index Ml₂ (190°C, 2.16kg) down to -0.3 g/10 min with high productivity (in order to get a maximum of polyethylene produced with as low amount of catalyst as possible).

Solubility of the transition metal complex in aliphatic hydrocarbons is also important to ensure optimal use of the complex in a solution process.

Although a lot of work has been done in the field of metallocene catalysts, there still remains a need to find new catalyst systems for ethylene copolymerization, which are able to produce polymers with desired properties and which have high productivity combined with high solubility, molecular weight capability and comonomer incorporation ability.

As a consequence, the inventors set out to develop a new catalyst system having superior polymerization behaviour than the above mentioned polymerization catalyst systems regarding to productivity, solubility, molecular weight capability and comonomer incorporation ability.

The present inventors have now found a new class of olefin polymerization catalyst systems, which are able to solve the problems disclosed above. In particular, the invention combines the use of special metallocene complexes with a boron cocatalyst.

Summary of Invention

Thus, viewed from one aspect the invention relates to a catalyst system for producing ethylene copolymers in a high temperature solution process, the catalyst system comprising

(i) a metallocene complex of formula (I)

(I)

wherein

M is Hf or a mixture with Zr, provided that more than 50% by moles of the complex of

Formula I has M = Hf

X is a sigma ligand R are the same or different from each other and can be saturated linear or branched Ci- Cio alkyl, C6-C10 aryl, C4-C10 heteroaryl, C6-C20 alkylaryl or C6-C20 arylalkyl groups, which can optionally contain up to 2 heteroatoms or silicon atoms

R¹ is a C6-C10 aryl or C6-C20 alkylaryl group optionally containing up to 2 heteroatoms or silicon atoms or a C4-C10 heteroaryl group

R² is a C4-C20 cycloalkyl group, optionally carrying alkyl substituents in beta-positions, of formula (II)

(II)

in which R' can be the same or can be different from each other and can be hydrogen or is defined as R and n is 1 to 17

and

(ii) a boron containing cocatalyst

Viewed from another aspect the invention provides a process for the preparation of an ethylene copolymer comprising polymerizing ethylene and a C-4-10 alpha-olefin comonomer in a high temperature solution process at a temperature greater than 100°C in the presence of a catalyst comprising:

(i) a metallocene complex of formula (I) as defined above and

(ii) a boron containing cocatalyst.

Viewed from a further aspect the invention provides an ethylene copolymer made by a process as hereinbefore defined. Detailed Description of the Invention Metallocene Complex

The single site metallocene complex, especially the complexes defined by the formula (I) specified in the present invention, used for manufacture of the ethylene copolymer are asymmetrical, meaning that the two ligands forming the metallocene complex are different. e complex of formula (I)

wherein

M is Hf or a mixture with Zr, provided that more than 50% by moles of the complex of Formula I has M = Hf

X is a sigma ligand

R are the same or different from each other and can be saturated linear or branched Ci-

Cio alkyl, C5-C10 aryl, C6-C20 alkylaryl or C6-C20 arylalkyl groups, which can optionally contain up to 2 heteroatoms or silicon atoms

R¹ is a C6-C10 aryl or C6-C20 alkylaryl group optionally containing up to 2 heteroatoms or silicon atoms or a C4-C10 heteroaryl group is a C4-C20 cycloalkyl group, optionally carrying alkyl substituents in beta-positions, of formula (II)

(II)

in which R' can be the same or can be different from each other and can be hydrogen or is defined as R and n is 1 to 17 In the formula (I) each X, which may be the same or different, is a sigma ligand, preferably a hydrogen atom, a halogen atom, a R³, OR³, OSO2CF3, OCOR³, SR³, NR³ ₂ or PR³ ₂ group wherein R³ is a linear or branched, cyclic or acyclic, Ci-C2o-alkyl, C2-C2o-alkenyl, C2-C20- alkynyl, C6-C2o-aryl, C7-C2o-alkylaryl or C7-C2o-arylalkyl radical; optionally containing heteroatoms belonging to groups 14-16 or is SiR³3, SiHR³2 or S1H2R³. R³ is preferably C1-6- alkyl, phenyl or benzyl group.

The term halogen includes fluoro, chloro, bromo and iodo groups, preferably chloro groups.

More preferably each X is independently a halogen atom or a R³ or OR³ group, whereby R³ is a Ci-6-alkyl, phenyl or benzyl group.

Most preferably X is methyl, benzyl or chlorine group. Preferably both X groups are the same. M is preferably Hf.

R are the same or different from each other and can be saturated linear or branched C1-C10 alkyl, C5-C10 aryl, C6-C20 alkylaryl or C6-C20 arylalkyl groups, which can optionally contain up to 2 heteroatoms or silicon atoms.

Preferably R are the same or different from each other and can be saturated linear or branched C1-C6 alkyl, C6-C10 aryl, C6-C20 alkylaryl or C6-C20 arylalkyl groups, which do not contain heteroatoms or silicon atoms.

More preferably all R are the same and are saturated linear or branched C1-C6 alkyl or C6-C10 aryl, and even more preferred all R are the same and are a saturated linear or branched Ci- C₆ alkyl.

Most preferably all R are the same and are all Ci alkyl groups.

R¹ is a C6-C10 aryl or C6-C20 alkylaryl group optionally containing up to 2 heteroatoms or silicon atoms or a C4-C10 heteroaryl group. C6-C20 alkylaryl group is meant to be an C6-C10 aryl group which is substituted by one or more alkyl groups which may be the same or different, whereby the number of C-atoms in the alkyl group substituents is in a range which leads to C6-C20 alkylaryl groups.

Non limiting examples for R¹ are phenyl, para-tolyl, para-iso-propylphenyl, 3,5-dimethylphenyl, beta-naphthyl, 4-(N,N-dimethylamino)phenyl, 4-pyridyl, beta-thiophenyl, 4-methyl-thiophenyl etc..

Preferably R¹ is a C6-C10 aryl or C6-C12 alkylaryl group, which do not contain heteroatoms or silicon atoms or a C4-C8 heteroaryl group. More preferably R¹ is unsubstituted phenyl (i.e. C6 aryl), or phenyl substituted by one to two C1-C6 alkyl groups(i.e. C7-C18 alkylaryl group).

Even more preferably R¹ is phenyl, para-tolyl or para-iso-propylphenyl. Most preferably R¹ is phenyl or para-iso-propylphenyl

(II)

in which R' can be the same or can be different from each other and can be hydrogen or is defined as R and n is 1 to 17.

Preferably R² is a C4-C10 cycloalkyl group of formula (II), wherein n is 1 to 7 and R' can be the same or can be different from each other and can be hydrogen or saturated linear or branched C1-C6 alkyl or C6-C10 aryl.

More preferably R² is a C4-C10 cycloalkyl group of formula (II), wherein n is 1 to 7 and R' can be the same or can be different from each other and can be hydrogen or saturated linear or branched C1-C4 alkyl group.

Non-limiting examples for R² are cyclobutyl, 3,3-dimethylcyclobutyl, cyclopentyl, cyclohexyl, 3,3,5,5-tetramethylcyclohexyl and the like.

Most preferably R² is a C4-C8 cycloalkyl group of formula (II), wherein n is 1 to 5 and all R' are hydrogen.

Non-limiting examples of complexes of formula (I) are

1 . (Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride

2. (Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dimethyl

3. (Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dibenzyl

4. (Phenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride

5. (Phenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dimethyl

6. (Phenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dibenzyl

7. (Phenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride 8. (Phenyl)(cyclobutyl)methylene(cyclopentadienyl)(2J-di-ie f-butylfluoren-9-y dimethyl

9. (4-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dichloride

10. (4-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dimethyl

1 1 . (4-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dichloride

12. (4-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dimethyl

13. (4-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dichloride

14. (4-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dimethyl

15. (3,5-di-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dichloride

16. (3,5-di-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dimethyl

17. (3,5-di-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dichloride

18. (3,5-di-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dimethyl

19. (3,5-di-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dichloride

20. (3,5-di-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dimethyl

Further preferred examples are the complexes above having dibenzyl as X substituents instead of dimethl or dichloride

Even more preferred are dimethyl and dibenzyl complexes.

Cocatalyst

To form an active catalytic species it is normally necessary to employ a cocatalyst as is well known in the art. The present invention requires the use of a boron containing cocatalyst.

Boron based cocatalysts of interest include boron compounds containing a borate 3⁺ ion, i.e. borate compounds. These compounds generally contain an anion of formula: (Z)₄B- (III) where Z is an optionally substituted phenyl derivative, said substituent being a haloCi-6-alkyl or halo group. Preferred options are fluoro or trifluoromethyl. Most preferably, the phenyl group is perfluorinated.

Such ionic cocatalysts preferably contain a non-coordinating anion such as tetrakis(pentafluorophenyl)borate. Suitable counterions are protonated amine or aniline derivatives or phosphonium ions. These may have the general formula (IV) or (V): NQ₄ ⁺ (IV) or PQ₄ ⁺ (V) where Q is independently H, Ci-6-alkyl, C3-8 cycloalkyl, phenylCi-6-alkylene- or optionally substituted Ph. Optional substituents may be C1 -6-alkyl, halo or nitro. There may be one or more than one such substituent. Preferred substituted Ph groups include therefore para- substituted phenyl, preferably tolyl or dimethylphenyl.

It is preferred if at least one Q group is H, thus preferred compounds are those of formula:

NHQ₃ ⁺ (VI) or PHQ₃ ⁺ (VII) Preferred phenylCi-6-alkyl- groups include benzyl.

Suitable counterions therefore include: methylammonium, anilinium, dimethylammonium, diethylammonium, N-methylanilinium, diphenylammonium, N,N-dimethylanilinium, trimethylammonium, triethylammonium, tri-n-butylammonium, methyldiphenylammonium, p- bromo-N,N- dimethylanilinium or p-nitro-N,N-dimethylanilinium, especially dimethylammonium or N,N-dimethylanilinium. The use of pyridinium as an ion is a further option.

Phosphonium ions of interest include triphenylphosphonium, triethylphosphonium, diphenylphosphonium, tri(methylphenyl)phosphonium and tri(dimethylphenyl)phosphonium. A more preferred counterion is trityl (CP i3⁺) or analogues thereof in which the Ph group is functionalised to carry one or more alkyl groups. Highly preferred borates of use in the invention therefore comprise the tetrakis(pentafluorophenyl)borate ion.

Preferred ionic compounds which can be used according to the present invention include: tributylammoniumtetra(pentafluorophenyl)borate,

tributylammoniumtetra(trifluoromethylphenyl)borate,

tributylammoniumtetra-(4-fluorophenyl)borate,

N,N-dimethylcyclohexylammoniumtetrakis-(pentafluorophenyl)borate,

N,N-dimethylbenzylammoniumtetrakis(pentafluorophenyl)borate,

N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate,

N,N- di(propyl)ammoniumtetrakis(pentafluorophenyl)borate,

di(cyclohexyl)ammoniumtetrakis(pentafluorophenyl)borate, triphenylcarbeniumtetrakis(pentafluorophenyl)borate,

ferroceniumtetrakis(pentafluorophenyl)borate.

Preference is given to triphenylcarbeniumtetrakis(pentafluorophenyl) borate,

N,N- dimethylcyclohexylammoniumtetrakis(pentafluorophenyl)borate,

N,N- dimethylbenzylammoniumtetrakis(pentafluorophenyl)borate or

N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate.

More preferred borates are triphenylcarbeniumtetrakis(pentafluorophenyl) borate and N,N- dimethylaniliniumtetrakis(pentafluorophenyl)borate.

N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate is most preferred.

It is further possible to add an aluminium alkyl compound. Suitable aluminium alkyl compounds are compounds of the formula (VIII) AIR3 with R being a linear or branched C2-Cs-alkyl group. Preferred aluminium alkyl compounds are triethylaluminium, tri-isobutylaluminium, tri- isohexylaluminium, tri-n-octylaluminium and tri-isooctylaluminium.

Suitable amounts of cocatalyst will be well known to the skilled man. The molar ratio of boron to the metal ion of the metallocene may be in the range 0.5:1 to 10:1 mol/mol, preferably 1 :1 to 10:1 , especially 1 :1 to 5:1 mol/mol.

Even more preferred is a molar ratio of boron to the metal ion of the metallocene from 1 :1 to less than 2:1 mol/mol, e.g from 1 :1 to 1 .8:1 or 1 :1 to 1 .5:1 . Catalyst Manufacture

The metallocene complex of the present invention is used in combination with the cocatalyst(s) as a catalyst system for the polymerization of ethylene and C-4-10 alpha-olefin comonomer in a high temperature solution polymerization process. The catalyst system of the invention may be used as a homogeneous catalyst or heterogeneous catalyst, preferably as homogeneous catalyst system.

Homogeneous or non-supported catalyst systems, suitable for the present invention can be prepared in solution, for example in an hydrocarbon solvent like hexane, cyclohexane, heptane, light naphta or toluene, by contacting the metallocene (as a solid or as a solution) with the cocatalyst(s), for example a borane or a borate salt as slurry in a hydrocarbon diluent or previously dissolved in an aromatic solvent, or preferably can be formed by sequentially adding the catalyst components directly into the polymerization reactor. Polymer

The polymer to be produced using the catalyst system of the invention is copolymer of ethylene and a C4-10 alpha-olefin comonomer, like 1 -butene, 1 -hexene, 4-methyl-1 -pentene, 1 -octene etc. Preferably butene, hexene or octene and more preferably octene is used as comonomer. The comonomer content in such a polymer may be up to 45 mol%, preferably between 1 to 40 mol%, more preferably 1 .5 to 35 mol% and even more preferably 2 to 25 mol%.

The density (measured according to ISO 1 183-187) of the polymers is in the range of 0.850 g/cm³ to 0.930 g/cm³, preferably in the range of 0.850 g/cm³ to 0.920 g/cm³ and more preferably in the range of 0.850 g/cm³ to 0.910 g/cm³.

Mw/Mn value of the polymers of the invention is less than 5, e.g. in the range of 2.0 to 4.5. The melting points (measured with DSC according to ISO 1 1357-3:1999) of the polymers to be produced are below 130°C, preferably below 120°C, more preferably below 1 10°C and most preferably below 100°C

Polymerization

The catalyst system of the present invention is used to produce the above defined ethylene copolymers in a high temperature solution polymerization process at temperatures higher than 100°C.

In view of this invention such process is essentially based on polymerizing the monomer and a suitable comonomer in a liquid hydrocarbon solvent in which the resulting polymer is soluble. The polymerization is carried out at a temperature above the melting point of the polymer, as a result of which a polymer solution is obtained. This solution is flashed in order to separate the polymer from the unreacted monomer and the solvent. The solvent is then recovered and recycled in the process.

A solution polymerization process is known for its short reactor residence times (compared to Gas-phase or slurry processes) allowing, thus, very fast grade transitions and significant flexibility in producing a wide product range in a short production cycle.

According to the present invention the used solution polymerization process is a high temperature solution polymerization process, using a polymerization temperature of higher than 100°C. Preferably the polymerization temperature is at least 1 10°C, more preferably at least 150°C. The polymerization temperature can be up to 250°C. The pressure in the used solution polymerization process according to the invention is preferably in a range of 10 to 100 bar, preferably 15 to 100 bar and more preferably 20 to 100 bar.

The liquid hydrocarbon solvent used is preferably a Cs-12-hydrocarbon which may be unsubstituted or substituted by Ci-₄ alkyl group such as pentane, methyl pentane, hexane, heptane, octane, cyclohexane, methylcyclohexane and hydrogenated naphtha. More preferably unsubstituted C6-io-hydrocarbon solvents are used.

Advantage

The new catalyst systems, comprising component (i) and (ii) can be advantageously used for ethylene copolymerization in high temperature solution polymerization process.

The catalyst systems according to the present invention show high productivity combined with high solubility, molecular weight capability and comonomer incorporation ability, if used for ethylene copolymerization in high temperature solution polymerization process.

Applications

The polymers made by the catalyst system of the invention are useful in all kinds of end articles such as pipes, films (cast or blown films), fibers, moulded articles (e.g. injection moulded, blow moulded, rotomoulded articles), extrusion coatings and so on.

The invention will now be illustrated by reference to the following non-limiting examples

Examples: Methods DSC

Temperature modulated DSC experiments were performed in a TA Instruments Q2000 DSC operated in modulated mode and calibrated with indium, tin and zinc according to ISO 1 1357- 1 . Circa 5 mg of the sample were placed in an aluminium pan. The temperature was initially raised to 180°C and afterwards lowered to -88°C at 10°C/min as in standard DSC. Afterwards the temperature was raised by a temperature modulated scan with heating rate of 2°C/min modulated of 0.32°C every 60 seconds. The glass transition temperature was measured from the reversible heat flow thermogram as the inversion point at transition.

If the polymer composition has been estimated by Tg(DSC) the following internal correlation has been used: C8(wt%)=(Tg(°C) + 19.16)/-1 .059

Zr and Hf determination (ICP-method)

The elementary analysis of a catalyst was performed by taking a solid sample of mass, M, cooling over dry ice. Samples were diluted up to a known volume, V, by dissolving in nitric acid (HNOs, 65 %, 5 % of V) and freshly deionised (Dl) water (5 % of V). The solution was then added to hydrofluoric acid (HF, 40 %, 3 % of V), diluted with Dl water up to the final volume, V, and left to stabilise for two hours.

The analysis was run at room temperature using a Thermo Elemental iCAP 6300 Inductively Coupled Plasma - Optical Emission Spectrometer (ICP-OES) which was calibrated using a blank (a solution of 5 % HNO3, 3 % HF in Dl water), and 6 standards of 0.5 ppm, 1 ppm, 10 ppm, 50 ppm, 100 ppm and 300 ppm of Al, with 0.5 ppm, 1 ppm, 5 ppm, 20 ppm, 50 ppm and 100 ppm of Hf and Zr in solutions of 5 % HN03, 3 % HF in Dl water.

Immediately before analysis the calibration is 'resloped' using the blank and 100 ppm Al, 50 ppm Hf, Zr standard, a quality control sample (20 ppm Al, 5 ppm Hf, Zr in a solution of 5 % HN03, 3 % HF in Dl water) is run to confirm the reslope. The QC sample is also run after every 5th sample and at the end of a scheduled analysis set.

The content of hafnium was monitored using the 282.022 nm and 339.980 nm lines and the content for zirconium using 339.198 nm line. The content of aluminium was monitored via the 167.079 nm line, when Al concentration in ICP sample was between 0-10 ppm (calibrated only to 100 ppm) and via the 396.152 nm line for Al concentrations above 10 ppm.

The reported values are an average of three successive aliquots taken from the same sample and are related back to the original catalyst by inputting the original mass of sample and the dilution volume into the software. Quantification of comonomer content by NMR spectroscopy

Quantitative nuclear-magnetic resonance (NMR) spectroscopy was used to quantify the comonomer content of the polymers.

Quantitative ¹³C{¹H} NMR spectra recorded in the molten-state using a Bruker Advance III 500 NMR spectrometer operating at 500.13 and 125.76 MHz for ¹H and ¹³C respectively. All spectra were recorded using a ¹³C optimised 7 mm magic-angle spinning (MAS) probe-head at 150°C using nitrogen gas for all pneumatics. Approximately 200 mg of material was packed into a 7 mm outer diameter zirconia MAS rotor and spun at 4 kHz. This setup was chosen primarily for the high sensitivity needed for rapid identification and accurate quantification. ^{[11 [21 [31 [41} Standard single-pulse excitation was employed utilising the transient NOE at short recycle delays of 3s ^{[51 [1]} and the RS-HEPT decoupling scheme. ^{[6l [7]} A total of 1024 (1 k) transients were acquired per spectrum. This setup was chosen due to its high sensitivity towards low comonomer contents.

Quantitative ¹³C{¹H} NMR spectra were processed, integrated and quantitative properties determined using custom spectral analysis automation programs. All chemical shifts are internally referenced to the bulk methylene signal (δ+) at 30.00 ppm.^[8]

Characteristic signals corresponding to the incorporation of 1 -octene were observed

[8],[9],[io],[i i],[i2] _anc| g|| comonomer contents calculated with respect to all other monomers present in the polymer.

Characteristic signals resulting from isolated 1 -octene incorporation i.e. EEOEE comonomer sequences, were observed. Isolated 1 -octene incorporation was quantified using the integral of the signal at 38.32 ppm. This integral is assigned to the unresolved signals corresponding to both _*B6 and _*βΒ6Β6 sites of isolated (EEOEE) and isolated double non-consecutive

(EEOEOEE) 1 -octene sequences respectively. To compensate for the influence of the two _*βΒ6Β6 sites the integral of the ββΒ6Β6 site at 24.7 ppm is used:

O = Ι,Β6+,βΒ6Β6 - 2 ^* ΙββΒ6Β6

Characteristic signals resulting from consecutive 1-octene incorporation, i.e. EEOOEE comonomer sequences, were also observed. Such consecutive 1 -octene incorporation was quantified using the integral of the signal at 40.48 ppm assigned to the ααΒ6Β6 sites accounting for the number of reporting sites per comonomer:

00 = 2 ^* ΙααΒ6Β6

Characteristic signals resulting from isolated non-consecutive 1 -octene incorporation, i.e. EEOEOEE comonomer sequences, were also observed. Such isolated non-consecutive 1 - octene incorporation was quantified using the integral of the signal at 24.7 ppm assigned to the ββΒ6Β6 sites accounting for the number of reporting sites per comonomer: OEO = 2 ^* ΙββΒ6Β6

Characteristic signals resulting from isolated triple-consecutive 1 -octene incorporation, i.e. EEOOOEE comonomer sequences, were also observed. Such isolated triple-consecutive 1 - octene incorporation was quantified using the integral of the signal at 41 .2 ppm assigned to the ααγΒ6Β6Β6 sites accounting for the number of reporting sites per comonomer:

OOO = 3/2 ^* ΙααγΒ6Β6Β6

With no other signals indicative of other comonomer sequences observed the total 1 -octene comonomer content was calculated based solely on the amount of isolated (EEOEE), isolated double-consecutive (EEOOEE), isolated non-consecutive (EEOEOEE) and isolated triple-consecutive (EEOOOEE) 1 -octene comonomer sequences:

Ototai = O + 00 + OEO + 000

Characteristic signals resulting from saturated end-groups were observed. Such saturated end-groups were quantified using the average integral of the two resolved signals at 22.84 and 32.23 ppm. The 22.84 ppm integral is assigned to the unresolved signals corresponding to both 2B6 and 2S sites of 1 -octene and the saturated chain end respectively. The 32.23 ppm integral is assigned to the unresolved signals corresponding to both 3B6 and 3S sites of 1 -octene and the saturated chain end respectively. To compensate for the influence of the 2B6 and 3B6 1 -octene sites the total 1 -octene content is used:

S =(1/2 )^*( I2S+2B6 + I3S+3B6 - 2*Ototal)

The ethylene comonomer content was quantified using the integral of the bulk methylene (bulk) signals at 30.00 ppm. This integral included the γ and 4B6 sites from 1 -octene as well as the δ⁺ sites. The total ethylene comonomer content was calculated based on the bulk integral and compensating for the observed 1 -octene sequences and end-groups:

Etotai = (1/2 )^*[ Ibuik + 2^*0 + 1 ^*00 + 3ΌΕ0 + 0^*000 + 3^*S ]

It should be noted that compensation of the bulk integral for the presence of isolated triple- incorporation (EEOOOEE) 1 -octene sequences is not required as the number of under and over accounted ethylene units is equal.

The total mole fraction of 1 -octene in the polymer was then calculated as:

fO = ( Ototai / ( Etotai + Ototai )

The total comonomer incorporation of 1 -octene in weight percent was calculated from the mole fraction in the standard manner:

0 [wt%] = 100 ^* ( fO ^* 1 12.21 ) / ( (fO ^* 1 12.21 ) + ((1 -fO) ^* 28.05) )

[1 ] Klimke, K., Parkinson, M., Piel, C, Kaminsky, W., Spiess, H.W., Wilhelm, M., Macromol. Chem. Phys. 2006;207:382.

[2] Parkinson, M., Klimke, K., Spiess, H.W., Wilhelm, M., Macromol. Chem. Phys. 2007;208:2128. [3] Castignolles, P., Graf, R., Parkinson, M., Wilhelm, M., Gaborieau, M., Polymer 50 (2009) 2373

[4] NMR Spectroscopy of Polymers: Innovative Strategies for Complex Macromolecules, Chapter 24, 401 (201 1 )

[5] Pollard, M., Klimke, K., Graf, R., Spiess, H.W., Wilhelm, M., Sperber, O., Piel, C, Kaminsky, W., Macromolecules 2004;37:813.

[6] Filip, X., Tripon, C, Filip, C, J. Mag. Resn. 2005, 176, 239

[7] Griffin, J.M., Tripon, C, Samoson, A., Filip, C, and Brown, S.P., Mag. Res. in Chem. 2007 45, S1 , S198

[8] J. Randall, Macromol. Sci., Rev. Macromol. Chem. Phys. 1989, C29, 201.

[9] Liu, W., Rinaldi, P., Mcintosh, L, Quirk, P., Macromolecules 2001 , 34, 4757

[10] Qiu, X., Redwine, D., Gobbi, G., Nuamthanom, A., Rinaldi, P., Macromolecules 2007, 40, 6879

[1 1] Busico, V., Carbonniere, P., Cipullo, R., Pellecchia, R., Severn, J., Talarico, G., Macromol. Rapid Commun. 2007, 28, 1 128

[12] Zhou, Z., Kuemmerle, R., Qiu, X., Redwine, D., Cong, R., Taha, A., Baugh, D. Winniford, B., J. Mag. Reson. 187 (2007) 225

GPC: Molecular weight averages, molecular weight distribution, and polydispersity index (M_n,

Molecular weight averages (Mw, Mn), Molecular weight distribution (MWD) and its broadness, described by polydispersity index, PDI= Mw/Mn (wherein Mn is the number average molecular weight and Mw is the weight average molecular weight) of the polymer were determined by high temperature size exclusion chromatography (HT-SEC) on a Polymer Laboratories PLXT- 20 Rapid GPC Polymer Analysis System (including pump, refractive index detector and viscosity detector) at 160°C with 3 PLgel Olexis (300 x 7.5 mm, Polymer Laboratories) columns in series. 1 ,2,4-Trichlorobenzene containing butylated hydroxytoluene (0.5 g/L) and Irganox 1010 (20 mg/L) was used as eluent at a flow rate of 1 .0 mL/min. The molecular weights were calculated with respect to polyethylene standards (Polymer Laboratories, Mp = 5.310 up to Mp = 1 .510.000 g/mol). A Polymer Laboratories PL XT-220 robotic sample handling system was used as autosampler. The concentration of the samples was between 2 and 4 mg polymer / mL of TCB.

Determination of the relative comonomer reactivity ratio R

Ethylene concentration in liquid phase can be considered constant since total pressure is kept constant by feeding ethylene during polymerization. The Cs C2 ratio in solution at the end of the polymerization is calculated by subtracting the amount of octene incorporated in the polymer from the measured composition of the latter (%wt 1 -octene)

The reactivity ratio, R, for each catalyst is then calculated as:

R= [(C8 C2)pol] [(Ce/C2)average in liquid phase]

Where (C8/C2) average in liquid phase IS Calculated aS ((C8/C2)final +(C8 C2)feed) 2 Solubility of the hafnium complex in hexane

Procedure for the solubility test:

All experiments were carried out under inert atmosphere in a septum bottle.

1 . Inside the glovebox, 10.5 mg of complex was weighted in a septum bottle. 2. 1 g of hexane was added to the solid complex

3. After stirring for 20h at room temperature, solution is checked

4. if no insoluble material is observed, repeat steps 1 and 3 until you reach saturation and insoluble materials are observed. Chemicals

Ν,Ν-Dimethylanilinium Tetrakis(pentafluorophenyl)borate (AB) (CAS 1 18612-00-3) was purchased from Boulder. 1 -octene as co-monomer (99%, Sigma Aldrich) was dried over molecular sieves and degassed with nitrogen before use.

Heptane and decane (99.9 %, Sigma Aldrich) were dried over molecular sieves and degassed with nitrogen before use.

Catalyst Preparation Examples a) Complex preparation:

Inventive Complex (IC)

(Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dimethyl

Step 1 : 6-Phenyl-6-cyclohexylfulvene

To a solution of sodium ethoxide obtained from 6.1 1 g (267.7 mmol) of sodium metal and 160 ml of dry ethanol 22.0 g (332.8 mmol) of cyclopentadiene was added dropwise over 10 min and the resulting red solution was stirred 0.5 h at room temperature. Then, 25.0 g (132.8 mmol) of phenyl cyclohexyl ketone was added and the resulting dark-red mixture was stirred 22 h at room temperature. Then, it was poured into 1000 ml of water. After acidification with 2 M HCI to pH ca. 6.5, the product was extracted with 500 ml of dichloromethane. The organic layer was separated, dried over Na2S0₄ and concentrated under a reduced pressure. The product was isolated by flash-chromatography on silica gel 60 (40-63 urn, 800 ml; eluent: hexane). This procedure gave 22.09 g (70%) of 6-phenyl-6-cyclohexylfulvene as a light-red oil which completely solidified upon storage at -30°C.

Anal. calc. for Ci₈H₂₀: C, 91.47; H, 8.53. Found: C, 91.79; H, 8.72.

¹H NMR (CDCIs): 5 7.35-7.29 (m, 3H), 7.19-7.14 (m, 2H), 6.71 (dt, J = 5.4 Hz, J = 1 .6 Hz, 1 H), 6.54 (dt, J = 5.4 Hz, J = 1 .6 Hz, 1 H), 6.36 (dt, J = 5.3 Hz, J = 1 .5 Hz, 1 H), 5.74 (dt, J = 5.3 Hz, J = 1 .7 Hz, 1 H), 3.10 (tt, J = 1 1 .8 Hz, J = 3.2 Hz, 1 H), 1.85-1.73 (m, 4H), 1 .66 (dm, J = 13.2 Hz, 1 H), 1.37 (qt, J = 12.9 Hz, 3.2 Hz, 2H), 1.30 (qd, J = 12.4 Hz, 3.2 Hz, 2H), 1.06 (qt, J = 12.9 Hz, 3.7 Hz, 1 H).

Step 2: Phenyl-cyclohexyl-cyclopentadienyl-(2,7-di-tert-butylfluoren-9-yl)methane

1. "BuLi, THF

To a solution of 26.0 g (93.38 mmol) of 2,7-di-ie/f-butylfluorene in 250 ml of THF cooled to - 50°C 38.4 ml (93.31 mmol) of 2.43 M "BuLi in hexanes was added in one portion. This mixture was stirred overnight at room temperature. To the resulting orange solution a solution of 22.09 g (93.46 mmol) of 6-phenyl-6-cyclohexylfulvene in 200 ml of THF was added at room temperature in one portion. After stirring overnight at room temperature the dark-red reaction mixture was cooled in an ice-bath and then quenched with a solution of 8.8 ml of 12 M HCI in 100 ml of water. The resulting orange mixture was diluted with 1000 ml of water and then extracted with 500 ml of ether. The organic layer was separated and dried over Na2S0₄. Removal of the solvents under vacuum gave orange oil, which was dissolved in 250 ml of n- hexane, and the resulting solution was slowly evaporated in vacuo to volume ca. 50 ml. The obtained suspension was diluted with 200 ml of n-hexane and filtered off (G3) to give 33.17 g (69%) of 1 -phenyl-1 -cyclohexyl-1 -cyclopentadienyl-1 -(2 ,7-di-fe/f-butylfluorenyl)methane as a white powder.

Anal. calc. for C39H46: C, 90.99; H, 9.01. Found: C, 91.34; H, 9.38.

¹H NMR (CDCIs): 5 8.18-6.16 (set of multiplets, sum 12H), 6.02-4.86 (set of singlets, sum 3H), 3.57-0.13 (set of singlets and multiplets, sum 31 H).

Step 3: (Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ieri-butylfluoren-9- yl)hafnium dichloride

To a solution of 10.17 g (19.76 mmol) of 1 -phenyl-1 -cyclohexyl-1 -cyclopentadienyl-1 -(2,7-di- ie/f-butylfluoren-9-yl)methane in 250 ml of ether cooled to -78°C 15.8 ml (39.5 mmol) of 2.5 M "BuLi in hexanes was added in one portion. This mixture was stirred overnight at room temperature. The resulting light-orange solution with orange precipitate was cooled to -50°C, and 6.33 g (19.76 mmol) of HfCU was added. The formed mixture was stirred for 24 h at room temperature and then evaporated to dryness. The residue was stirred with 100 ml of warm toluene, the formed suspension was filtered through a glass frit (G4), and the filtrate was evaporated to ca. 35 ml. Precipitated overnight at room temperature white solid was filtered off (G4) and discarded. The mother liquor was evaporated to ca. 20 ml, and 20 ml of n-hexane was added to the residue. Yellow solid precipitated overnight at -30°C was filtered off (G3) and dried in vacuo to give 3.20 g of (phenyl)(cyclohexyl)methylene (cyclopentadienyl)(2,7-di- ie f-butylfluoren-9-yl) hafnium dichloride. The mother liquor was evaporated to dryness, and the residue was dissolved in 25 ml of n-hexane. Solid precipitated from this solution overnight at -30°C was collected and dried in vacuo. This procedure gave additional 0.60 g of the target complex. Thus, the total yield of (phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f- butylfluoren-9-yl) hafnium dichloride isolated in this synthesis was 3.80 g (25%).

Anal. calc. for C, 61.46; H, 5.82. Found: C, 61 .37; H, 6.10.

¹H NMR (CDCIs): δ 8.02 (d, J = 8.8 Hz, 1 H), 7.95 (d, J = 8.8 Hz, 1 H), 7.76 (d, J = 7.8 Hz, 1 H), 7.68 (s, 1 H), 7.63 (dd, J = 8.8 Hz, J = 1 .2 Hz, 1 H), 7.57-7.51 (m, 2H), 7.48 (dd, J = 8.8 Hz, J = 1 .6 Hz, 1 H), 7.45-7.41 (m, 1 H), 7.39 (ddd, J = 7.5 Hz, J = 7.5 Hz, J = 1.0 Hz, 1 H), 6.36-6.31 (m, 1 H), 6.21 -6.16 (m, 1 H), 5.96 (s, 1 H), 5.76-5.71 (m, 1 H), 5.55-5.50 (m, 1 H), 3.26 (t, J = 1 1.5 Hz, 1H), 2.33 (d, J= 12.9 Hz, 1H), 2.14 (d, J= 12.3 Hz, 1H), 1.94-1.83 (m, 2H), 1.16 (d, J = 13.2 Hz, 1H), 1.66-1.56 (m, 1H), 1.53-1.40 (m, 1H), 1.41 (s, 9H), 1.40-1.30 (m, 1H), 1.12-1.01 (m, 1H), 0.96 (s, 9H), 0.91-0.79 (m, 1H). Step 4: (Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ieri-butylfluoren-9- yl)hafnium dimeth l

To a solution of 3.80 g (4.99 mmol) of (phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7- di-ief-butylfluoren-9-yl)hafnium dichloride in a mixture of 50 ml of toluene and 50 ml of ether 7.0 ml (14.77 mmol) of 2.11 M MeMgBr in ether was added. The resulting mixture was refluxed for 30 min and then evaporated to ca.25 ml. The obtained mixture was heated to 80-90°C and filtered while hot through glass frit (G4) to remove insoluble magnesium salts. The filter cake was additionally washed with 5 x 20 ml of warm n-hexane. The combined filtrate was evaporated almost to dryness, and then 20 ml of n-hexane was added to the residue. The resulting mixture was filtered once again through a glass frit (G4). The mother liquor was evaporated to dryness, and the residue was dissolved in 7 ml of n-hexane. Yellow powder precipitated from this solution overnight at -30°C was collected and dried in vacuum.

This procedure gave 3.05 g (88%) of pure (phenyl)(cyclohexyl)methylene(cyclopentadienyl)

(2,7-di-ief-butylfluoren-9-yl)hafnium dimethyl. Anal. calc. for C₄iH₅₀Hf: C, 68.27; H, 6.99. Found: C, 68.49; H, 7.22.

¹H NMR (CDCIs): δ 8.08 (d, J = 8.6 Hz, 1 H), 7.98 (d, J = 8.9 Hz, 1 H), 7.73 (d, J = 7.6 Hz, 1 H), 7.58-7.48 (m, 3H), 7.45 (td, J= 7.6 Hz, J = 1.5 Hz, 1H), 7.38-7.28 (m, 3H), 6.28-6.21 (m, 1H), 6.12-6.06 (m, 1H), 5.86 (s, 1H), 5.62-5.55 (m, 1 H), 5.33-5.27 (m, 1H), 3.06 (t, J= 11.5 Hz, 1H), 2.28 (d, J= 12.8 Hz, 1H), 2.10 (d, J= 12.3 Hz, 1H), 1.90-1.75 (m, 2H), 1.70 (d, J= 13.3 Hz, 1H), 1.65-1.20 (m, 1H), 1.48-1.33 (m, 1H), 1.40 (s, 9H), 1.31-1.16 (m, 1H), 1.08-0.92 (m, 1H), 0.95 (s, 9H), 0.77-0.62 (m, 1H), -1.79 (s, 3H), -1.93 (s, 3H).¹³C{¹H} NMR (CDCIs,): δ 150.30, 147.62, 140.00, 132.05, 129.17, 127.31, 126.95, 126.75, 124.03, 123.70, 122.93, 122.79, 120.91, 120.54, 119.29, 117.90, 116.35, 115.93, 112.41, 111.17, 109.62, 101.41,99.72,76.78, 57.85, 43.58, 38.06, 37.13, 35.47, 34.72, 31.56, 30.72, 29.02, 28.27, 27.36, 26.91, 26.70. Comparative Complex 1 (CC1 ):

(Phenyl)(1 -hexyl)methylene(cyclopentadienyl)(2J-di-ie f-butylfluoren-9-yl)h dimethyl Step 1 : 6-Phenyl-6-hexylfulvene

To a solution of 23.8 g (125.1 mmol) of 1 -phenylheptan-1 -one in 50 ml of THF cooled in an ice-bath, a solution of 25.4 g (150 mmol, 1 .2 equiv.) of cyclopentadienylmagnesium bromide in 150 ml of THF was added dropwise. The resulting mixture was refluxed for 3 h, then stirred overnight at room temperature, then cooled in an ice-bath and then quenched with 10% HCI to pH~5-6. This mixture was extracted with 3x150 ml of hexane; the combined organic extract was dried over Na2S0₄ and then evaporated to dryness to give a dark-red oil. The product was isolated by flash-chromatography on silica gel 60 (40-63 μηη; eluent: hexane-ethyl acetate = 100:1 , vol.). This procedure gave 14.25 g (48%) of 6-phenyl-6-hexylfulvene as reddish oil. Anal. calc. for Ci₈H₂₂: C, 90.70; H, 9.30. Found: C, 90.87; H, 9.27.

¹H NMR (CDCIs): δ 7.37-7.30 (m, 5H), 6.63 (ddd, J = 5.3 Hz, J = 2.0 Hz, J = 1.5 Hz, 1 H), 6.55 (ddd, J = 5.3 Hz, J = 2.0 Hz, J = 1.5 Hz, 1 H), 6.46 (ddd, J = 5.3 Hz, J = 2.0 Hz, J = 1.5 Hz, 1 H), 6.10 (ddd, J = 5.3 Hz, J = 2.0 Hz, J = 1.5 Hz, 1 H), 2.90 (t, J = 7.6 Hz, 2H), 1.47-1 .36 (m, 2H), 1 .34-1 .15 (m, 6H), 0.83 (t, J = 6.9 Hz, 3H). ¹³C{¹H} NMR (CDCIs): δ 154.81 , 143.31 , 140.87, 131 .71 , 131 .32, 129.42, 127.97, 127.73, 123.86, 120.90, 36.25, 31 .51 , 29.54, 29.13, 22.46, 13.97.

Step 2: (Phenyl)(1 -hexyl)methylene(cyclopentadienyl)(2,7-di-ieri-butylfluoren-9- yl)hafnium dichloride

"BuLi, THF

To a solution of 14.88 g (53.44 mmol) of 2,7-di-ie/f-butylfluorene in 200 ml of THF cooled to -50°C 21 .4 ml (53.5 mmol) of 2.5 M "BuLi in hexanes was added in one portion. This mixture was stirred overnight at room temperature. The resulting reddish solution was cooled to -50°C, and a solution of 14.25 g (59.78 mmol) of 6-phenyl-6-hexylfulvene in 200 ml of THF was added in one portion. After stirring overnight at room temperature the dark-red reaction mixture was cooled in an ice-bath and then quenched with a solution of 5 ml of 12 M HCI in 200 ml of water. The resulting yellow mixture was extracted with 400 ml of dichloromethane. The organic layer was separated, and the aqueous one was extracted with 150 ml of dichloromethane. The combined organic extract was dried over Na2S0₄ and filtered through a pad of silica gel 60 (40-63 μηη) which was additionally washed by 2x50 ml of dichloromethane. The combined filtrate was evaporated to dryness to give 29.1 g of phenyl-(1 -hexyl)-cyclopentadienyl-(2,7-di- ie f-butylfluoren-9-yl)methane which was used without further purification. To a solution of 16.2 g (31 .35 mmol) of phenyl-(1 -hexyl)-cyclopentadienyl-(2,7-di-ie f-butylfluorenyl)methane (as prepared above) in 250 ml of ether cooled to -78°C, 25.0 ml (62.5 mmol) of 2.5 M "BuLi in hexanes was added in one portion. The formed mixture was stirred overnight at room temperature and then cooled to -50°C, and 10.04 g (31 .35 mmol) of HfCI₄ was added. The obtained mixture was stirred for 24 h at room temperature and then evaporated to dryness. The residue was stirred with 200 ml of warm toluene, and the formed suspension was filtered through a glass frit (G4). The filtrate was evaporated to ca. 40 ml. Yellow crystalline material precipitated from this mixture over a week at -30°C was separated, washed with 3x15 ml of a mixture of toluene and hexane (1 :3, vol.) and dried in vacuum. This procedure gave 14.2 g (59%) of (phenyl)(1 -hexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)-]hafnium dichloride. Anal. calc. for CsgHUeC Hf: C, 61.30; H, 6.07. Found: C, 61.53; H, 6.26.

¹H NMR (CDCIs): δ 8.01 (d, J = 8.9 Hz, 1H), 7.95 (d, J = 8.9 Hz, 1H), 7.82 (dm, J = 7.9 Hz, 1H), 7.70 (s, 1H), 7.66-7.58 (m, 2H), 7.58-7.52 (m, 1H), 7.52-7.46 (m, 1H), 7.44-7.36 (m, 2H), 6.36-6.30 (m, 1H), 6.23-6.17 (m, 1H), 6.13 (s, 1H), 5.80-5.74 (m, 1H), 5.55-5.49 (m, 1H), 3.13- 2.97 (m, 1H), 2.80-2.65 (m, 1H), 1.64-1.44 (m, 3H), 1.40 (s, 9H), 1.36-1.18 (m, 5H), 0.99 (s, 9H), 0.85 (t, J =7.9 Hz, 3H).¹³C{¹H} NMR (CDC ,): δ 152.11, 149.53, 143.32, 130.53, 128.46, 128.26, 127.17, 127.05, 124.17, 124.14, 123.97, 123.49, 122.63, 120.25, 119.84, 119.65, 118.84, 118.79, 117.87, 116.58, 114.58, 99.64 (two resonances), 77.83, 53.68, 41.28, 35.42, 34.84, 31.88, 31.11, 30.51 , 29.75, 24.03, 22.63, 14.05.

Step 3: (Phenyl)(1 -hexyl)methylene(cyclopentadienyl)(2,7-di-ieri-butylfl

yl)hafnium dimethyl

To a solution of 3.82 g (5.0 mmol) of (phenyl)(1-hexyl)methylene(cyclopentadienyl)(2,7-di-ief- butylfluoren-9-yl)hafnium dichloride in a mixture of 50 ml of toluene and 50 ml of ether 7.0 ml (14.77 mmol) of 2.11 M MeMgBr in ether was added. The resulting mixture was refluxed for 30 min and then evaporated to ca.25 ml. The obtained solution was heated to 80-90°C and filtered while hot through glass frit (G3) to remove insoluble magnesium salts. The filter cake was additionally washed with 2x20 ml of toluene. The combined filtrate was evaporated to dryness, and 20 ml of hexane was added to the residue. The resulting suspension was filtered once again through a glass frit (G4). The filtrate was evaporated to dryness, and the residue was dissolved in 7 ml of hexane. Yellow powder precipitated from this solution overnight at -40°C was collected and dried in vacuum. This procedure gave 2.55 g (71%) of pure (phenyl)(1-hexyl)methylene(cyclopentadienyl)(2,7-di-ief-butylfluoren-9-yl)hafnium dimethyl. Anal. calc. for C₄iH₅₂Hf: C, 68.08; H, 7.25. Found: C, 68.11 ; H, 7.46.

¹H NMR (CDCIs): δ 8.07 (d, J = 8.9 Hz, 1H), 7.98 (d, J = 8.9 Hz, 1H), 7.81 (dm, J = 7.9 Hz, 1H), 7.63-7.56 (m, 2H), 7.53-7.43 (m, 2H), 7.38-7.30 (m, 3H), 6.28-6.21 (m, 1H), 6.14-6.08 (m, 1H), 6.03 (s, 1H), 5.65-5.59 (m, 1H), 5.34-5.28 (m, 1H), 2.92-2.81 (m, 1H), 2.59-2.48 (m, 1H), 1.52-1.40 (m, 3H), 1.38 (s, 9H), 1.34-1.17 (m, 5H), 0.97 (s, 9H), 0.84 (t, J = 7.0 Hz, 3H), -1.76 (s, 3H), -1.90 (s, 3H).¹³C{¹H} NMR (CDC ,): δ 150.18, 147.73, 144.31 , 130.72, 128.04, 127.90, 127.20, 126.59, 124.49, 123.74, 122.90, 122.73, 121.01, 120.61, 119.11, 117.56, 116.32, 1 15.83, 1 12.85, 1 1 1 .08, 109.58, 100.94, 100.57, 76.51 , 53.50, 41 .19, 38.16, 37.39, 35.32, 34.75, 31 .93, 31 .35, 30.75, 29.86, 24.12, 22.68, 14.08.

Comparative Complex 2 (CC2):

(Phenyl)(isopropyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)^ dimethyl Step 1 : 6-lsopropyl- -phenylfulvene

To a solution of 14.82 g (100 mmol) of isopropyl phenyl ketone in 40 ml of THF cooled in an ice-bath a solution of 20.3 g (120 mmol, 1 .2 equiv.) of cyclopentadienylmagnesium bromide in 120 ml of THF was added dropwise. The resulting mixture was refluxed for 3 h, then stirred overnight at room temperature, finally, cooled in an ice-bath and quenched with 10% HCI to pH~5-6. This mixture was extracted with 3x150 ml of hexane, and the combined organic extract was dried over Na2S0₄. Removal of the solvent under vacuum gave a dark-red oil. The product was isolated by flash-chromatography on silica gel 60 (40-63 μηη; eluent: hexane). This procedure gave 8.32 g (42%) of 6-isopropyl-6-phenylfulvene as a light orange oil, which completely crystallized during storage at -30°C.

Anal. calc. for Ci₅Hi₆: C, 91 .78; H, 8.22. Found: C, 92.00; H, 8.41.

¹H NMR (CDCIs): δ 7.36-7.30 (m, 3H), 7.21 -7.15 (m, 2H), 6.70 (ddd, J = 5.3 Hz, J = 1 .9 Hz, J = 1 .5 Hz, 1 H), 6.54 (ddd, J = 5.3 Hz, J = 1 .9 Hz, J = 1 .5 Hz, 1 H), 6.37 (ddd, J = 5.3 Hz, J = 1.9 Hz, J = 1 .5 Hz, 1 H), 5.77 (ddd, J = 5.3 Hz, J = 1 .9 Hz, J = 1.5 Hz, 1 H), 3.50 (sept, J = 7.0 Hz, 1 H), 1.14 (d, J = 7.0 Hz, 6H). ¹³C{¹H} NMR (CDC ): δ 159.82, 143.03, 138.92, 132.14, 130.72, 129.20, 127.19, 126.98, 124.36, 120.22, 33.72, 22.13. Step 2: (Phenyl)(isopropyl)methylene(cyclopentadienyl)(2,7-di-ieri-butylfluoren-9- yl)hafnium dichloride

To a solution of 1 1 .77 g (42.27 mmol) of 2,7-di-ie f-butylfluorene in 250 ml of ether cooled to -50°C, 17.4 ml (42.28 mmol) of 2.43 M "BuLi in hexanes was added in one portion. This mixture was stirred overnight at room temperature. The resulting orange solution was cooled to -50°C, and a solution of 8.30 g (42.29 mmol) of 6-isopropyl-6-phenylfulvene in 150 ml of ether was added in one portion. After stirring overnight at room temperature the dark-red reaction mixture was cooled to -50°C, and 17.4 ml (42.28 mmol) of 2.43 M "BuLi in hexanes was added in one portion. This mixture was stirred overnight at room temperature. The resulting dark-red solution was cooled to -50°C, and 13.55 g (42.3 mmol) of HfCU was added. The formed mixture was stirred for 24 h at room temperature, then it was evaporated to dryness, and the residue was treated with 150 ml of warm toluene. This mixture was filtered while hot through glass frit (G4), the filtrate was evaporated to ca. 50 ml, and 80 ml of n-hexane was added to the residue. Precipitated solid was filtered and discarded. The mother liquor was evaporated almost to dryness, and the residue was triturated with 70 ml of n-hexane. Orange- yellow precipitate was filtered to give 5.80 g (ca. 19%) of (phenyl)(isopropyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride with ca. 90% purity. The analytically pure sample (2.51 g, 8%) was obtained by recrystallization of crude product from toluene.

Anal. calc. for CseHUoC Hf: C, 59.88; H, 5.58. Found: C, 60.07; H, 5.73.

¹H NMR (CDCIs): δ 8.01 (d, J = 8.8 Hz, 1 H), 7.95 (d, J = 8.9 Hz, 1 H), 7.78 (dm, J = 7.8 Hz, 1 H), 7.69 (s, 1 H), 7.62 (d, J = 8.9 Hz, 1 H), 7.59-7.51 (m, 2H), 7.49 (dd, J = 8.8 Hz, J = 1 .2 Hz, 1 H), 7.47-7.36 (m, 2H), 6.37-6.30 (m, 1 H), 6.22-6.16 (m, 1 H), 5.99 (br.s, 1 H), 5.75-5.69 (m, 1 H), 5.57-5.51 (m, 1 H), 3.69 (sept, J = 6.7 Hz, 1 H), 1 .39 (s, 9H), 1.31 (d, J = 6.7 Hz, 3H), 1 .05 (d, J = 6.7 Hz, 3H), 0.97 (s, 9H). ¹³C{¹H} NMR (CDCIs,): δ 152.22, 149.49, 137.95, 131 .85, 129.31 , 127.77, 127.42, 124.1 1 , 124.06, 123.96, 123.43, 122.28, 120.46, 1 19.93, 1 19.81 , 1 18.99, 1 18.56, 1 18.52, 1 16.70, 1 15.03, 100.10, 99.06, 78.64, 58.17, 35.40, 34.84, 32.74, 31.1 1 , 30.51 , 18.34, 17.89. Step 3: (Phenyl)(isopropyl)methylene(cyclopentadienyl)(2,7-di-ieri-butylfluoren-9- yl)hafnium dimethyl

To a solution of 3.3 g (ca. 4.6 mmol) of crude (phenyl)(isopropyl)methylene(cyclo- pentadienyl)(2,7-di-fe/f-butylfluoren-9-yl)hafnium dichloride (residue after recrystallization from toluene) in a mixture of 30 ml of toluene and 15 ml of ether, 6.5 ml (17.55 mmol) of 2.7 M MeMgBr in ether was added. The resulting mixture was stirred overnight at room temperature. Most of ether was distilled off, and the resulting mixture was filtered through glass frit (G4) to remove insoluble magnesium salts. The filtrate was evaporated to ca. 15 ml and filtered again through glass frit (G4). The mother liquor was evaporated to ca. 5 ml, 15 ml of n-hexane was added, and the resulting slightly turbid solution was filtered through glass frit (G4). Yellow powder precipitated from the filtrate overnight at -30°C was collected and dried in vacuum. This procedure gave 1.46 g (ca. 47%) of (phenyl)(isopropyl)methylene(cyclopentadienyl)(2,7- di-ie f-butylfluoren-9-yl) hafnium dimethyl.

Anal. calc. for CssHUeHf: C, 66.99; H, 6.81. Found: C, 67.14; H, 7.02.

¹H NMR (CDCIs): δ 8.09 (d, J = 8.8 Hz, 1 H), 7.99 (d, J = 8.8 Hz, 1 H), 7.75 (dm, J = 7.9 Hz, 1 H), 7.57 (br.s, 1 H), 7.56-7.44 (m, 3H), 7.39-7.29 (m, 3H), 6.27-6.23 (m, 1 H), 6.13-6.08 (m, 1 H), 5.88 (br.d, J = 1 .0 Hz, 1 H), 5.59-5.55 (m, 1 H), 5.33-5.29 (m, 1 H), 3.55-3.43 (m, 1 H), 1 .38 (s, 9H), 1 .22 (d, J = 6.7 Hz, 3H), 0.97-0.93 (s and d, sum 12H), -1.79 (s, 3H), -1.92 (s, 3H). Complex elemental analysis (ICP method):

Comparative Example CO

Diphenylmethylene(cyclopentadienyl)(2,7-di-ferf-butylfluoren-9-yl)hafnium dimethyl

Diphenylmethylene(cyclopentadienyl)(2J-di-ie f-butylfluoren-9-yl)hafni dicloride was synthesized according to the literature: Hopf, A, Kaminsky, W., Catalysis Communications

To a solution of 3.78 g (5.0 mmol) of Diphenylmethylene(cyclopentadienyl)(2,7-di-ie f- butylfluoren-9-yl)hafnium dichloride in a mixture of 50 ml of toluene and 50 ml of ether, 7.0 ml (14.77 mmol) of 2.1 1 M MeMgBr in ether was added. The resulting mixture was refluxed for 30 min and then evaporated to ca. 25 ml. The obtained mixture was heated to 80-90 °C and filtered while hot through glass frit (G4) to remove insoluble magnesium salts. The filter cake was additionally washed with 5 x 20 ml of warm hexane. The combined filtrate was evaporated to ca. 5 ml, and then 20 ml of hexane was added to the residue. Yellow powder precipitated from this solution was collected and dried in vacuum. This procedure gave 3.14 g (88%) of pure diphenylmethylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dimethyl. Anal. calc. for C₄i H₄₄Hf: C, 68.85; H , 6.20. Found: C, 69.10; H , 6.37.

¹ H NMR (CDCIs): δ 8.07 (d, J = 8.9 Hz, 2H), 7.95 (br.d, J = 7.9 Hz, 2H), 7.85 (br.d, J = 7.9 Hz, 2H), 7.44 (dd, J = 8.9 Hz, J = 1 .5 Hz, 2H), 7.37 (td, J = 7.6 Hz, J = 1 .2 Hz, 2H), 7.28 (td, J = 7.6 Hz, J = 1 .2 Hz, 2H), 7.24-7.17 (m, 2H), 6.26 (s, 2H), 6.20 (t, J = 2.7 Hz, 2H), 5.45 (t, J = 2.7 Hz, 2H), 1 .03 (s, 18H), -1 .90 (s, 6H). ¹³C{¹ H} NMR (CDCIs,): δ 148.46, 145.75, 129.69, 128.63, 128.46, 126.73, 126.54, 123.29, 122.62, 120.97, 1 18.79, 1 16.09, 1 1 1 .68, 107.76, 101 .56, 76.47, 57.91 , 37.61 , 34.88, 30.84. b) Polymerization procedure

Polymerization tests have been performed in 125ml_ reactors equipped with a bottom valve, at 160°C and 30 barg as total pressure. Different C8/C2 weight ratios in the liquid phase and different catalyst loadings have been tested to find the optimal amount to guarantee almost constant temperature and pressure during the 10 minutes of polymerization.

• Activation procedure

Ν,Ν-dimethylanilinium tetrakis(pentafluorophenyl) borate has been used for all experiments. TEA (7x10^"2 mol/kg in Isopar E) has been used as the scavenger for all the experiments and its amount has been optimised together with the B/Hf ratio based on a specific design of experiments (DoE). Activation is carried out by dissolving separately the complex and the activator in 4 mL of toluene. The borate solution is then injected in the reactor feeding line followed by the complex solution and the two are let in contact for few seconds before the injection into the reactor by nitrogen overpressure.

· Polymerization procedure

The reactor is filled with the desired amount of solvent (isopar E), scavenger (optimised amount 0.035 mmol TEA) and 1 -octene. Solvent and monomers amounts are chosen to have an initial liquid volume at the polymerization conditions of 80mL.

The reactor is then heated up and carefully pressurised with ethylene (25-28 bar-g). When conditions are stable, the ethylene pressure is adjusted to 30 bar-g and the mixture is allowed to stir at 750 rpm during 10 minutes in order to determine the residual ethylene uptake.

After this time the catalyst (dissolved with 4mL of toluene) and the cocatalyst (also dissolved with 4 mL toluene) are combined in the injection line and immediately injected in the reactor by nitrogen overpressure. Pressure is then kept constant by feeding ethylene and after 10 minutes polymerization is quenched by adding a killing agent (either EtOH or C02). Then the reactor is vented, the temperature is decreased and the vessel is opened. The solution is discharged in an aluminium pan containing few milligrams (-500 ppm related to the copolymer produced) of Irganox 1076. The pan is then placed under a well-ventilated fume hood until the volatiles are evaporated. The collected residual material is analysed by HT-SEC and DSC according to the methods reported in the polymer characterisation paragraph.

Table 1 : Ethylene/1 -octene solution co-polymerisation productivity results

Inventive Examples IE1 - IE3 and Comparative Examples CE1 - CE6

Table 1 shows based on the productivity results, that the cyclohexyl as substituent in the bridge (IC) results in higher productivity compared to hexyl (CC1 ) or isopropyl (CC2) as substituent in the bridge when activated using borate AB as co-catalyst (Error! Reference source not found.)- The catalyst system IC/AB displayed highest productivity with 1 1 1 kg-PO/g-cat for a catalyst loading of 0.07 mg and residence time 10 min.

For same C8 content (or same average C8/C2), no significant clear differences on molecular weight capability and reactivity can be observed between the three complexes (Figures 2-4)

The performance of the IC/AB catalyst system was further investigated by carrying out a set of experiments following the design of experiments (DoE) methodology. The two factors TEA amount and B/Hf ratio was used (see Table 2). In those set of experiments the effect on productivity and polymer properties (Mw and C8 incorporation) has been evaluated.

Polymerisation temperature was 160°C and total pressure 30 barg. Results are reported in Table 2, best productivity was obtained for 35 μηηοΙ TEA and 1 .5 B/Hf molar ratio.

Table 2: Ethylene/1 -octene solution co-polymerisation polymerisation results for IC/AB system IE2 and IE 4 to IE12

Solubility of the complex in aliphatic hydrocarbons is also an important property, since the complex is preferably fed into the reactor as a solution in such a solvent. This feeding mode ensures higher accuracy in the catalyst concentration in the reactor and better activation efficiency.

The solubility of the inventive complex in hexane is shown in Table 3.

Table 3 Solubility of hafnium complexes in hexane

As is shown in Table 3, complex IC has a higher solubility compared to complex CO.

Claims

Claims:

1. Catalyst system for producing ethylene copolymers in a high temperature solution process, the catalyst system comprising

(i) a metallocene complex of formula (I)

wherein

X is a sigma ligand

R are the same or different from each other and can be saturated linear or branched Ci- Cio alkyl, C6-C10 aryl, C4-C10 heteroaryl, C6-C20 alkylaryl or C6-C20 arylalkyl groups, which can optionally contain up to 2 heteroatoms or silicon atoms

(II)

in which R' can be the same or can be different from each other and can be hydrogen or is defined as R and n is 1 to 17 and

(ii) a boron containing cocatalyst

2. Catalyst system according to claim 1 , wherein in the formula (I)

M is Hf

X is hydrogen atom, a halogen atom, a R³, OR³, OSO2CF3, OCOR³, SR³, NR³ ₂ or PR³ ₂ group wherein R³ is a linear or branched, cyclic or acyclic, Ci-C2o-alkyl, C2-C2o-alkenyl,

C2-C2o-alkynyl, C6-C2o-aryl, C7-C2o-alkylaryl or C7-C2o-arylalkyl radical; optionally containing heteroatoms belonging to groups 14-16 or is SiR³3, SiHR³2 or S1H2R³

R are the same or different from each other and can be saturated linear or branched C1-C6 alkyl, C6-C10 aryl, C6-C20 alkylaryl or C6-C20 arylalkyl groups, which do not contain heteroatoms or silicon atoms

R¹ is a C6-C10 aryl or C6-C12 alkylaryl group, which do not contain heteroatoms or silicon atoms, or a C4-C8 heteroaryl group

R² is a C4-C10 cycloalkyl group of formula (II)

in which R' can be the same or can be different from each other and can be hydrogen or saturated linear or branched C1-C6 alkyl or C6-Cioaryl and n is 1 to 7

3. Catalyst system according to claim 2, wherein in the formula (I)

M is Hf

X is independently a halogen atom or a R³ or OR³ group, whereby R³ is a Ci-6-alkyl, phenyl or benzyl group

R are the same and are saturated linear or branched C1-C6 alkyl or C6-C10 aryl, and even more preferred all R are the same and are a saturated linear or branched C1-C6 alkyl

R¹ is unsubstituted phenyl or phenyl substituted by one to two C1-C6 alkyl groups

R² is a C4-C10 cycloalkyl group of formula (II)

in which all R' can be the same or can be different from each other and can be hydrogen or saturated linear or branched C1-C4 alkyl and n is 1 to 7

4. Catalyst system according to claim 2, wherein in the formula (I) M is Hf

X is independently a methyl, benzyl or chlorine group

R are the same and are all Ci alkyl groups

R¹ is phenyl, para-tolyl or para-iso-propylphenyl

R² is a C4-C8 cycloalkyl group of formula (II)

in which all R' are hydrogen and n is 1 to 5

Catalyst system according to anyone of the preceding claims, wherein the metallocene complex of formula (I) is selected from the group of

(Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride

(Phenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dibenzyl

(Phenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride

(Phenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dimethyl

(Phenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dibenzyl

(Phenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dichloride

(Phenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9-yl)hafnium dimethyl

(4-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dichloride

(4-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dimethyl

(4-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dichloride

(4-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dimethyl

(4-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dichloride

(4-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-9- yl)hafnium dimethyl

(3,5-di-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dichloride

(3,5-di-isopropylphenyl)(cyclohexyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dimethyl

(3,5-di-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dichloride

(3,5-di-isopropylphenyl)(cyclopentyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dimethyl

(3,5-di-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren- 9-yl)hafnium dichloride

(3,

5-di-isopropylphenyl)(cyclobutyl)methylene(cyclopentadienyl)(2,7-di-ie f-butylfluoren-

9-yl)hafnium dimethyl

or the corresponding dibenzyl complexes

6. Catalyst system according to any of preceding claims, whereby the catalyst system is a homogeneous or non-supported catalyst systems, which can be prepared in solution, by contacting the metallocene complex of Formula (I), as a solid or as a solution, with the cocatalyst in a hydrocarbon diluent or previously dissolved in an aromatic solvent, or which can be formed by sequentially adding the catalyst components directly into the polymerization reactor.

7. A catalyst system as claimed in any preceding claim wherein said optional boron containing cocatalyst comprises an anion of formula:

(Z)₄B- (III)

where Z is an optionally substituted phenyl derivative, said substituent being a halo-Ci-6- alkyl or halo group, preferably

triphenylcarbeniumtetrakis(pentafluorophenyl) borate,

N,N-dimethylcyclohexylammoniumtetrakis(pentafluorophenyl)borate,

N,N- dimethylbenzylammoniumtetrakis(pentafluorophenyl)borate, or

N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate.

8. Use of a catalyst system as defined in claim 1 to 7 in a high temperature solution process at a temperature greater than 100°C for copolymerizing ethylene and a C4-10 alpha-olefin comonomer.

9. Process for the preparation of an ethylene copolymer comprising polymerizing ethylene and a C-4-10 alpha-olefin comonomer in a high temperature solution process at a temperature greater than 100°C in the presence of a catalyst comprising:

(i) a metallocene complex of formula (I) as defined in any of preceding claims 1 to 5 and

(ii) a boron containing cocatalyst.

10. Process according to claim 9, wherein the polymerization is performed

a) at a polymerization temperature of at least 1 10°C,

b) a pressure in the range of 10 to 100 bar and

c) in a liquid hydrocarbon solvent selected from the group of C5-i2-hydrocarbons, which may be unsubstituted or substituted by Ci-₄ alkyl group 11. Ethylene copolymer obtained by a polymerization process according to claim 9 or 10.