WO2010045359A2

WO2010045359A2 - Aqueous polyurethaneurea compositions including dispersions and films

Info

Publication number: WO2010045359A2
Application number: PCT/US2009/060677
Authority: WO
Inventors: Hong Liu; Gregory L. Yoder; Jin Li
Original assignee: Invista Technologies S.A R.L.
Priority date: 2008-10-17
Filing date: 2009-10-14
Publication date: 2010-04-22
Also published as: JP2012505958A; KR101907333B1; EP2337818A2; JP5391278B2; CN102257069A; BRPI0914431A2; MX2011003996A; WO2010045359A3; KR20110082572A; US20110201734A1; EP2337818A4; KR20170101314A

Abstract

Included are polyurethaneurea compositions include polyurethaneurea aqueous dispersions. The dispersions may be prepared with solvent or in the absence of any added solvent. Films and other shaped articles may be prepared from the dispersions by a casting a drying method and optionally included with a substrate including paper, fabric or garments. The films exhibit a reduced discoloring or yellowing upon exposure to atmosphere, heat, and UV.

Description

AQUEOUS POLYURETHANEUREA COMPOSITIONS INCLUDING DISPERSIONS AND FILMS

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application claims the benefit of U.S. Provisional Patent Application No. 61/106285 filed October 17, 2008 and is a continuation-in-part of U.S. Patent Application No. 11/780,819 filed on July 20, 2007, which is a continuation-in-part of U.S. Patent Application No. 11/745,668 filed on May 8, 2007, which is a continuation-in-part of U.S. Patent Application No. 11/351 ,967 filed on February 10, 2006, which is a continuation-in- part of U. S Patent Application No. 11/300,229 filed on December 13, 2005, which is a continuation-in-part of 11/253,927 filed on October 19, 2005, which is a continuation-in- part of 11/056,067 fled on February 11 , 2005, now U.S. Patent No. 7,240,371 , all of which are incorporated herein by reference in their entirety.

BACKGROUND OF THE INVENTION

Field of the Invention

[0002] The present invention relates to polyurethaneurea compositions such as aqueous dispersions, films and other shaped articles. Specifically, the present invention relates to optionally solvent-free, aqueous, stable dispersions, which comprise fully formed polyurethaneurea with optionally blocked isocyanate end groups. The dispersions can be formed by prepolymer mixing processes and may be prepared in the absence of added solvent. The films prepared from these compositions exhibit reduced discoloration and/or yellowing on exposure to environmental or process conditions.

Summary of Related Technology

[0003] Polyurethanes (including polyurethaneureas) can be used as adhesives for various substrates, including textile fabrics. Typically, such polyurethanes are either fully formed non-reactive polymers or reactive isocyanate-terminated prepolymers. Such reactive polyurethane adhesives often require extended curing time to develop adequate bonding strength, which can be a disadvantage in manufacturing processes. In addition, the isocyanate groups of the polyurethanes are known to be sensitive to moisture, which limits the storage stability and reduces the shelf life of the product incorporating such polyurethanes.

[0004] Typically, such polymers, when fully formed, are either dissolved in a solvent (solvent borne), dispersed in water (water borne), or processed as thermoplastic solid materials (hot melt). Notably, solvent-based adhesives face ever-tightening health and environmental legislation aimed at reducing volatile organic compound (VOC) and hazardous air pollutant (HAP) emissions. Accordingly, alternatives to conventional solvent-based products may be required in the future.

[0005] Hot-melt adhesives, although environmentally safe and easily applied as films, generally have high set and poor recovery when subject to repeated stretch cycles. Another concern is the discoloration and/or yellowing of the adhesive over time upon exposure to environment or processing conditions. Therefore, adhesives that overcome the performance concerns of hot-melt adhesives are needed. Desirably, such adhesives will also provide other benefits to the fabric such as flexibility, shape retention and air permeability compared to conventional thermoplastic polyurethane and hot-melt adhesives.

SUMMARY OF THE INVENTION

[0006] Some embodiments provide a composition including:

(a) a polyurethaneurea aqueous dispersion comprising a polymer which is the reaction product of:

(1 ) at least one polyol selected from polyethers, polyesters, polycarbonates, and combinations thereof, wherein the polyol has a number average molecular weight of 600 to 4000;

(2) a polyisocyanate comprising at least one aromatic diisocyanate;

(3) optionally a neutralizing agent and a diol compound comprising: (i) hydroxy groups capable of reacting with polyisocyanate, and (ii) at least one carboxylic acid group capable of forming a salt upon neutralization, wherein said at least one carboxylic acid group is incapable of reacting with the polyisocyanate;

(4) a chain extender selected from the group consisting of diamine chain extenders, water, and combinations thereof; and

(5) optionally including a blocking agent for isocyanate;

(6) at least one surface active agent; and (b) an anti-yellowing compound selected from the group consisting of a monoisocyanate, an aliphatic diisocyanate, and combinations thereof.

[0007] In another embodiment is a film cast and dried from a composition comprising

(2) a polyisocyanate comprising at least one aromatic diisocyanate;

(5) optionally including a blocking agent for isocyanate;

(6) at least one surface active agent; and

(b) an anti-yellowing compound selected from the group consisting of a monoisocyanate, an aliphatic diisocyanate, and combinations thereof.

[0008] In a further embodiment is a method for reducing yellowing in a film comprising:

(a) preparing a polyurethaneurea aqueous dispersion comprising a polymer which is the reaction product of:

(2) a polyisocyanate comprising at least one aromatic diisocyanate;

(5) optionally including a blocking agent for isocyanate; (6) at least one surface active agent;

(b) adding to said dispersion an anti-yellowing compound selected from the group consisting of a monoisocyanate, an aliphatic diisocyanate, and combinations thereof; and

(c) preparing a shaped article from said dispersion.

DETAILED DESCRIPTION OF THE INVENTION

[0009] Aqueous polyurethane dispersions falling within the scope of the present invention are provided from particular urethane prepolymers, which also form an aspect of some embodiments.

[0010] In some embodiments, a segmented polyurethaneurea for making a polyurethaneurea dispersion includes: a) a polyol or a polyol copolymer or a polyol mixture of number average molecular weight between 500 to 5000 (such as from about 600 to 4000 and 600 to 3500), including but not limited to polyether glycols, polyester glycols, polycarbonate glycols, polybutadiene glycols or their hydrogenated derivatives, and hydroxy-terminated polydimethylsiloxanes; b) a polyisocyanate including diisocyanates such as aliphatic diisocyanates, aromatic diisocyanates and alicyclic diisocyanates; and c) a diol compound d including: (i) hydroxy groups capable of reacting with polyisocyanate, and (ii) at least one carboxylic acid group capable of forming a salt upon neutralization, wherein the at least one carboxylic acid group is incapable of reacting with the polyisocyanate; d) a chain extending such as water or an diamine chain extender including aliphatic diamine chain extenders or the combination of an aliphatic diamine chain extender with one or more diamines selected from aliphatic diamines and alicyclic diamines having 2 to 13 carbon atoms, or an amino-terminated polyer; and e) optionally a monoalcohol or monoamine, primary or secondary, as a blocking agent or chain terminator; and optionally an organic compound or a polymer with at least three primary or secondary amine groups.

[0011] The urethane prepolymers of some embodiments, also known as capped glycols, can generally be conceptualized as the reaction product of a polyol, a polyisocyanate, and a compound capable of salt-forming upon neutralization, before the prepolymer is dispersed in water and is chain-extended. Such prepolymers can typically be made in one or more steps, with or without solvents which can be useful in reducing the viscosity of the prepolymer composition. [0012] Depending on whether the prepolymer is dissolved in a less volatile solvent (such as NMP) which will remain in the dispersion; dissolved in a volatile solvent such as acetone or methylethyl ketone (MEK), which can be later removed; or is dispersed in water without any solvent; the dispersion process can be classified in practice as the solvent process, acetone process, or prepolymer mixing process, respectively. The prepolymer mixing process has environmental and economical advantages, and may be used in the preparation of aqueous dispersion with substantially no added solvent.

[0013] In the prepolymer mixing process, it is important that the viscosity of the prepolymer is adequately low enough, with or without dilution by a solvent, to be transported and dispersed in water. One embodiment relates to polyurethaneurea dispersions derived from such a prepolymer, which meet this viscosity requirement and do not have any organic solvent in the prepolymer or in the dispersion. In accordance with the invention, the prepolymer is the reaction product of a polyol, a diisocyanate and a diol compound.

[0014] Some embodiments are solvent-free, stable, aqueous polyurethane dispersions, which can be processed and applied directly as adhesive materials (Ae., without the need of any additional adhesive materials) for coating, bonding, and lamination of to substrates, by conventional techniques. Aqueous polyurethane dispersions may be provided with: essentially no emission of volatile organic materials; acceptable curing time in production; and good adhesion strength, heat resistance, and stretch/recovery properties in finished products and in practical applications.

[0015] In an additional embodiment are shaped articles, such as films, which may be prepared from the aqueous polyurethaneurea dispersion, such as by casting and drying the dispersions. The films which may or may not be adhesive can be coated on a release paper or directly applied to a substrate including textile fabrics for bonding and lamination. The adhesion can be activated, by applying heat and/or pressure onto a substrate and the adhesive film, with a residence time of less than one minute, for example, from about 15 seconds to about 60 seconds. The thus bonded articles have good stretch/recovery properties and are expected to be durable in normal wear and wash cycles.

[0016] As used herein, the term "porous" refers to a substrate that includes voids or holes in the surface or at any point within or through the thickness of the substrate or to any material of which the articles of the present invention may come into contact. [0017] As used herein, the term "pressing" or "pressed" refers to an article that has been subjected to heat and/or pressure to provide a substantially planar structure.

[0018] As used herein, the term "foam" refers to any suitable foam that may be used in fabric construction such as polyurethane foam.

[0019] As used herein, the term "dispersion" refers to a system in which the disperse phase consists of finely divided particles, and the continuous phase can be a liquid, solid or gas.

[0020] As used herein, the term "aqueous polyurethane dispersion" refers to a composition containing at least a polyurethane or polyurethane urea polymer or prepolymer (such as the polyurethane prepolymer described herein), optionally including a solvent, that has been dispersed in an aqueous medium, such as water, including de- ionized water.

[0021] As used herein, the term "solvent," unless otherwise indicated, refers to a nonaqueous medium, wherein the non-aqueous medium includes organic solvents, including volatile organic solvents (such as acetone) and somewhat less volatile organic solvents (such as N-methylpyrrolidone (NMP)).

[0022] As used herein, the term "solvent-free" or "solvent-free system" refers to a composition or dispersion wherein the bulk of the composition or dispersed components has not been dissolved or dispersed in a solvent.

[0023] As used herein, the term shaped article may refer any of a variety of embodiments of a polyurethaneurea composition including, films, tapes, dots, webs, stripes, beads, and foam. A film may describe a sheet material of any shape. A tape may describe a film in narrow strip form, including a narrow strip of from about 0.5 cm to about 3 cm. A film may be in the form of a tape. As used herein, the term "shaped article" refers to a layer comprising an aqueous polyurethane dispersion (such as the aqueous polyurethane dispersion containing the polyurethane prepolymer described herein) that can be directly applied to a substrate or release paper, which can be used for adhesion and/or to form a rigid or an elastic article. [0024] As used herein, the term "article" refers to an article which comprises a dispersion or shaped article and a substrate, for example a textile fabric and release paper, which may or may not have at least one elastic property, in part, due to the application of a dispersion or shaped article as described herein. The article may be in any suitable configuration such as one-dimensional, two-dimensional and/or three- dimensional.

[0025] As used herein, the term "fabric" is meant to include any knitted, woven or nonwoven material. Knitted fabrics may be flat knit, circular knit, warp knit, narrow elastic, or lace. Woven fabrics may be of any construction, for example sateen, twill, plain weave, oxford weave, basket weave, or narrow elastic. Nonwoven materials may be one of meltblown, spun bonded, wet-laid, carded fiber-based staple webs, and the like.

[0026] As used herein, the term "substrate" refers to any material to which the films or dispersions of the present invention may come into contact. A substrate can be substantially one dimensional as is a fiber, two dimensional as in a planar sheet, or a three dimensional article or a bumpy sheet. A planar sheet for example may comprise textile fabric, paper, flocked article, and web. A three dimensional article for example may comprise leather and foam. Other substrates may include wood, paper, plastic, metal, and composites such as concrete, asphalt, gymnasium flooring, and plastic chips.

[0027] As used herein, the term "hard yarn" refers to a yarn which is substantially non-elastic.

[0028] As used herein, the term "molded" article refers to a result by which the shape of an article or shaped article is changed in response to application of heat and/or pressure.

[0029] As used herein, the term "derived from" refers to forming a substance out of another object. For example, a film may be derived from a dispersion which has been dried.

[0030] As used herein, the term "modulus" refers to a ratio of the stress on an item expressed in force per unit linear density or area. [0031] In some embodiments are multiple layer articles which include at least one layer of a polyurethaneurea composition in the form of a film or dispersion. These articles have at least two layers including at least one polyurethaneurea composition. The polyurethaneurea composition may form one of the layers, for example, as a polyurethaneurea composition on a substrate. The polyurethaneurea composition may be in any suitable form such as a film or dispersion. The polyurethaneurea composition may be placed adjacent to or between the layers and also may provide stretch and recovery, increased elastic modulus, adhesion, moldability, shape retention, and flexibility properties for the article. These articles may be formed into fabrics and/or garments.

[0032] In an embodiment where the article includes a multiple layer article including three or more layers where one layer is a film, the film may be an intermediate layer between two fabric layers, between two foam layers, between a fabric layer and a foam layer, or adjacent to a foam layer which is adjacent to a fabric layer. Combinations of these fabric/ foam/ film arrangements are also contemplated. For example, the article may include, in order, a fabric layer, a foam layer, a film layer, a foam layer, and a fabric layer. This article includes two separate fabric layers, two separate foam layers and a film layer. In any of these embodiments, the polyurethaneurea film may be replaced with a polyurethaneurea dispersion. Therefore, the article may include one or more polyurethaneurea film and one or more polyurethaneurea dispersion layer.

[0033] In an embodiment that includes two or more layers, the polyurethaneurea composition may form the external layer. Including the polyurethaneurea composition on an external surface forms many advantageous functions. For example, the polyurethaneurea composition may provide an anchor or area of increased friction to reduce the relative movement between the article including the polyurethaneurea composition and an external substrate. This is particularly useful when the article is an undergarment including a skin-contacting surface (where the wearer's skin is the substrate). Alternatively, the substrate may be outer clothing which is in contact with the polyurethaneurea composition of the inventive article. Where the substrate is outer clothing of a wearer and the article is worn as an undergarment, the article prevents or reduces the relative movement of the outer garment. In addition, an outer garment (e.g. a dress) may include a polyurethaneurea composition to maintain the relative placement of an inner garment (e.g. a slip). [0034] After the layers of fabric, foam, and the polyurethaneurea composition have been selected, they may subsequently be adhered through pressing or molding to form flat or shaped articles. The processes to prepare the pressed and molded articles of some embodiments include the use of pressure and heat as necessary. For example, heat may be applied at about 15O⁰C to about 200⁰C or about 18O⁰C to about 190°C, including about 185⁰C for a sufficient time to achieve a molded article. Suitable times for application of heat include, but are not limited to, from about 30 sec to about 360 sec including from about 45 sec to about 120 sec. Bonding may be effected by any known method, including but not limited to, microwave, infrared, conduction, ultrasonic, pressure application over time (i.e. clamping) and combinations thereof.

[0035] Due the application of heat and pressure to the articles including polyurethaneurea films or dispersion and given that polyurethaneurea films prepared from the dispersions and fabrics are themselves porous materials, it is recognized that the film or dispersion may partially or completely impregnate the fabric or foam of the article. For example, the polyurethaneurea composition may form a layer which is partially separate from the surrounding layers, or may be completely transferred to the surrounding layer or layers to form an integrated article without a distinguishably separate polyurethaneurea composition layer.

[0036] One application of the multi-layer articles of the present invention is body- shaping garments such as brassieres (especially in cups or wings) and men's undergarments. These articles can provide the desirable features of comfort, body shaping and support while still providing comfort, breathability, air permeability, moisture/vapor transport, wicking, and combinations thereof. In the articles of some embodiments of the present invention, the layers may take on predetermined shapes and may be arranged in predetermined orientations relative to each other in the design of a molded or shaped article such as the cups of a brassiere construction. The layers of these fabrics may be used either alone or in combination with other materials that are sewn, glued or otherwise applied to the fabrics.

[0037] In some embodiments there is a system for the construction of a body- shaping garment with integrated shaping ability provided by the fabric. This system of construction may be used in a variety of different garment constructions such as activewear, sportswear, men's and women's intimate apparel such as bras, underwear, panties, shaping garments, legwear and hosiery such as pantyhose, ready-to-wear garments such as denim jeans, camisoles, tailored shirts, and pants among others. This construction may be applied to any formable body area. While many advantages of the fabric constructions are included, it is further recognized that the utility is not limited to garments, but also finds applicability with any shapeable or formable medium, including cushions for furniture which are also subject to movement and potential slipping of a fabric in contact with the shapeable area.

[0038] In order to add additional support and other features, the polyurethaneurea composition may be added to different areas of the article. For example, when a film is used, it may either extend through the entire area of the article or to a selected portion to provide different benefits. For example, a brassiere may include a layered fabric of some embodiments in the cup portion. In the brassiere cup, it can be useful to use a portion of film in the lower portion of the cup for support, in a central portion of the cup for modesty, in the side portion for shaping, or in specific areas for embellishment or decoration.

[0039] Reducing the amount of film in a multi-layer fabric to meet the needs of a fabric may also increase the air permeability of the fabric. As is shown in the examples, the polyurethaneurea compositions derived from the aqueous dispersion described herein provided greater air permeability than those derived from polyurethaneurea solutions. The films cast from the aqueous dispersions also performed better with respect to air permeability in comparison to commercially available thermoplastic polyurethane (TPU) films available from Bemis. Air permeability may also be increased by altering the film to make it porous or to become porous (i.e. "latent" breathability) or by perforating the film.

[0040] Another advantage of the films cast from the aqueous dispersions of some embodiments is with respect to the feel or tactility of the films. They provide a softer feel compared to silicone rubber or the commercially available TPU films while maintaining the desired friction to reduce movement that is a further advantage for skin contact applications. Also lower bending modulus gives better drape and fabric hand.

[0041] The polyurethaneurea compositions provide additional benefits especially as compared to commercially available thermoplastic polyurethaneurea compositions, when used in a garment. These benefits include shape retention, shaping ability, adhesion, maintaining a fraction of the substrates, moisture management, and vapor permeability. [0042] The polyurethaneurea compositions may be added in other constructions depending on the desired function which may be a visual aesthetic. The polyurethaneurea films or dispersions may be added to an article, fabric or garment to be molded into a design, to adhere embellishments such as decorative fabrics and glitter, in the form of a label or logo, and combinations thereof.

[0043] Depending on the desired effect of the polyurethaneurea composition when applied as a film or dispersion from the aqueous dispersion described herein, the weight average molecular weight of the polymer in the film may vary from about 40,000 to about 250,000, including from about 40,000 to about 150,000; from about 100,000 to about 150,000; and about 120,000 to about 140,000.

[0044] In some embodiments, the polyurethaneurea composition may act as an adhesive to attach two or more layers of fabric or foam, or to attach a layer of fabric to foam. One suitable method for accomplishing this is to apply a dispersion to a layer by any suitable method. Methods for applying the dispersions of some embodiments include spraying, kissing, printing, brushing, dipping, padding, dispensing, metering, painting, and combinations thereof. This may be followed by application of heat and/or pressure.

[0045] Other adhesives may be included in the multiple layer articles of some embodiments of the invention. Examples of adhesives include thermoset or thermoplastic adhesives, pressure sensitive adhesives, hot melt adhesives, and combinations thereof. The adhesive may be used to adhere the different layers and may be applied to any of the fabric, foam or polyurethaneurea films or dispersion. Moreover, the polyurethaneurea aqueous dispersions may also be used as an adhesive to adhere more than one layer of any fabric, foam or polyurethaneurea film as described in some embodiments.

[0046] As described above, there are a variety of fabric constructions that are useful for the articles of the present invention. Furthermore, the polyurethane composition may be either a film or a dispersion in any of these embodiments. In addition, the polyurethaneurea composition may provide structural properties, flexibility, adhesion, or any combination of these. The order of layer arrangement may be (1) fabric layer, foam layer, polyurethaneurea composition layer; (2) fabric layer, foam layer, polyurethaneurea composition layer, foam layer, fabric layer; (3) fabric layer, polyurethaneurea composition layer, fabric layer; (4) foam layer, polyurethaneurea layer, foam layer; (5) foam layer, polyurethaneurea composition layer; (6) fabric layer, polyurethaneurea layer; or any combination of these which may be combined to achieve more layers in the fabric construction. An adhesive may be included to adhere any of the layers, including wherein the polyurethaneurea composition is the adhesive.

[0047] A variety of different fibers and yarns may be used with the fabrics of some embodiments. These include cotton, wool, acrylic, polyamide (nylon), polyester, spandex, regenerated cellulose, rubber (natural or synthetic), bamboo, silk, soy or combinations thereof.

The components of the polyurethaneurea compositions are described in more detail below:

[0048] Polyol components suitable as a starting material for preparing urethane prepolymers, according to the invention, are polyether glycols, polycarbonate glycols, and polyester glycols of number average molecular weight of about 600 to about 3,500 or about 4,000.

[0049] Examples of polyether polyols that can be used include those glycols with two or more hydroxy groups, from ring-opening polymerization and/or copolymerization of ethylene oxide, propylene oxide, trimethylene oxide, tetrahydrofuran, and 3- methyltetrahydrofuran, or from condensation polymerization of a polyhydric alcohol, preferably a diol or diol mixtures, with less than 12 carbon atoms in each molecule, such as ethylene glycol, 1 ,3-propanediol, 1 ,4-butanediol, 1 ,5-pentanediol 1 ,6-hexanediol, neopentyl glycol, 3-methyl-1 ,5-pentanediol, 1 ,7-heptanediol, 1 ,8-octanediol, 1 ,9- nonanediol, 1 ,10-decanediol and 1 ,12-dodecanediol. A linear, bifunctional polyether polyol is preferred, and a poly(tetramethylene ether) glycol of molecular weight of about 1 ,700 to about 2, 100, such as Terathane® 1800 (Invista) with a functionality of 2, is particularly preferred in the present invention.

[0050] Examples of polyester polyols that can be used include those ester glycols with two or more hydroxy groups, produced by condensation polymerization of aliphatic polycarboxylic acids and polyols, or their mixtures, of low molecular weights with no more than 12 carbon atoms in each molecule. Examples of suitable polycarboxylic acids are malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, undecanedicarboxylic acid, and dodecanedicarboxylic acid. Examples of suitable polyols for preparing the polyester polyols are ethylene glycol, 1 ,3-propanediol, 1 ,4-butanediol, 1 ,5-pentanediol 1 ,6-hexanediol, neopentyl glycol, 3-methyl-1 ,5- pentanediol, 1 ,7-heptanediol, 1 ,8-octanediol, 1 ,9-nonanediol, 1 ,10-decanediol and 1 ,12- dodecanediol. A linear bifunctional polyester polyol with a melting temperature of about 5°C to about 5O⁰C is preferred.

[0051] Examples of polycarbonate polyols that can be used include those carbonate glycols with two or more hydroxy groups, produced by condensation polymerization of phosgene, chloroformic acid ester, dialkyl carbonate or diallyl carbonate and aliphatic polyols, or their mixtures, of low molecular weights with no more than 12 carbon atoms in each molecule. Examples of suitable polyols for preparing the polycarbonate polyols are diethylene glycol, 1 ,3-propanediol, 1 ,4-butanediol, 1 ,5-pentanediol, 1 ,6-hexanediol, neopentyl glycol, 3-methyl-1 ,5-pentanediol, 1 ,7-heptanediol, 1 ,8-octanediol, 1 ,9- nonanediol, 1 ,10-decanediol and 1 ,12-dodecanediol. A linear, bifunctional polycarbonate polyol with a melting temperature of about 5°C to about 50⁰C is preferred.

Polyisocyanates

[0052] Examples of suitable polyisocyanate components include diisocyanates such as 1 ,6-diisocyanatohexane, 1 ,12-diisocyanatododecane, isophorone diisocyanate, trimethyl-hexamethylenediisocyanates, 1 ,5-diisocyanato-2-methylpentane, diisocyanato- cyclohexanes, methylene-bis(4-cyclohexyl isocyanate), tetramethyl-xylenediisocyanates, bis(isocyanatomethyl) cyclohexanes, toluenediisocyanates, methylene bis(4-phenyl isocyanate), phenylenediisocyanates, xylenediisocyanates, and a mixture of such diisocyanates. For example the diisocyanate may be an aromatic diisocyanate such phenylenediisocyanate, tolylenediisocyanate (TDI), xylylenediisocyanate, biphenylenediisocyanate, naphthylenediisocyanate, diphenylmethanediisocyanate (MDI), and combinations thereof.

[0053] The polyisocyanate component, suitable as another starting material for making urethane prepolymers according to the invention, can be an isomer mixture of diphenylmethane diisocyanate (MDI) containing 4,4'-methylene bis(phenyl isocyanate) and 2,4'- methylene bis(phenyl isocyanate) in the range of 4,4'-MDI to 2,4'-MDI isomer ratios of between about 65:35 to about 35:65, preferably in the range of about 55:45 to about 45:55 and more preferably at about 50:50. Examples of suitable polyisocyanate components include Mondur® ML (Bayer), Lupranate® Ml (BASF), and Isonate® 50 O, P' (Dow Chemical).

Anti-yellowinq Compound

[0054] The anti-yellowing compound useful in some embodiments includes an aliphatic or aromatic isocyanate (mono-functional), an aliphatic diisocyanate, or a combination thereof.

[0055] The anti-yellowing compound can be added to the dispersion at any convenient time after formation of the dispersion. One suitable addition method is adding and mixing the anti-yellowing compound with the dispersion. The anti-yellowing compound can be added in any effective amount to achieve improved properties such as reduction of yellowing of the resulting films, such as from about 0.1 % to about 1.5% by weight of the dispersion, including from about 0.3% to about 1.0% and about 0.5%.

Monoisocvanate

[0056] The monoisocyanates useful with the present invention include aliphatic monoisocyanates, cycloaliphatic isocyanates. Specifically included are compounds of the formula R-N=C=O, where are is aliphatic or cylcoaliphatic such as ethyl-, propyl-, butyl-, pentyl-, hexyl, cyclohexyl-, etc. as well as aromatic monoisocyanates. Aliphatic polyisocyanates have been used in polyurethane applications to reduce yellowing due to the absence of an aromatic group. In the present invention, a monoisocyanate is added to a polyurethaneurea dispersion prepared with an aromatic polyisocyanate and surprisingly results in a composition that has a significant reduction in yellowing of films cast and dried from the dispersion. Yellowing can result from exposure to environmental or process conditions such as heat, NO2, and UV, among others.

[0057] A non-limiting list of suitable monoisocyanates include: 1-methyl-decyl isocyanate, 2-chloroethyl isocyanate, 2-ethylhexyl isocyanate, 2-methylcyclohexyl isocyanate, 3-(triethoxysilyl)propyl isocyanate, 3-chloropropyl isocyanate, 3-isopropenyl- a,a-dimethylbenzyl isocyanate, 3-methylcyclohexyl isocyanate, 4-methycyclohexyl isocyanate, 6-chlorohexyl isocyanate, benzyl isocyanate, cycloheptyl isocyanate, cycloheptyl isocyanate, cyclohexyl isocyanate, cyclohexanemethyl isocyanate, cyclooctyl isocyanate, decyl isocyanate, dodecyl isocyanate, isocyanatoacetic acid n-butyl ester, isopropyl isocyanate, n-hepyl isocyanate, n-hexyl isocyanate, nonyl isocyanate, octadecyl isocyanate, octyl isocyanate, pentyl isocyanate, phenethyl isocyanate, trans-4- methycyclohexyl isocyanate, α-methylbenzyl isocyanate, (3- isocyanatopropyl)triethoxysilane, ethyl 6-isocyanatohexanoate, ethyl 3- isocyanatopropionate, 1-tetradecyl isocyanate, and combinations thereof. An example of a suitable aromatic monoisocyanate includes phenyl isocyanate, which may be used alone or in combination with other aromatic or aliphatic isocyanates.

Aliphatic diisocyanates

[0058] A variety of different aliphatic diisocyanates are also useful with the present invention and may be used alone, or in combinations with other aliphatic diisocyanates or a monoisocyanate.

Diols

[0059] Diol compounds which may be included in some embodiments, include at least one diol compound with: (i) two hydroxy groups capable of reacting with the polyisocyanates; and (ii) at least one carboxylic acid group capable of forming salt upon neutralization and incapable of reacting with the polyisocyanates (b). Typical examples of diol compounds having a carboxylic acid group, include 2,2-dimethylopropionic acid (DMPA), 2,2-dimethylobutanoic acid, 2,2-dimethylovaleric acid, and DMPA initiated caprolactones such as CAP A® HC 1060 (Solvay). DMPA is preferred in the present invention.

Neutralizing Agents

[0060] Neutralizing agents should be included when an acidic diol is included. Examples of suitable neutralizing agents to convert the acid groups to salt groups include: tertiary amines (such as triethylamine, N,N-diethylmethylamine, N-methylmorpholine, N,N-diisopropylethylamine, and triethanolamine) and alkali metal hydroxides (such as lithium, sodium and potassium hydroxides). Primary and/or secondary amines may be also used as the neutralizing agent for the acid groups. The degrees of neutralization are generally between about 60% to about 140%, for example, in the range of about 80% to about 120% of the acid groups. Chain Extenders

[0061] The chain extenders useful with the present invention include diamine chain extenders and water. Many examples of useful chain extenders are known by those of ordinary skill in the art. Examples of suitable diamine chain extenders include: 1 ,2- ethylenediamine, 1 ,4-butanediamine, 1 ,6-hexamethylenediamine, 1 ,12-dodecanediamine, 1 ,2-propanediamine, 2-methyl~1 ,5-pentanediamine, 1 ,2-cyclohexanediamine, 1 ,4- cyclohexanediamine, 4,4'-methylene-bis(cyclohexylamine), isophorone diamine, 2,2- dimethyl-1 ,3-propanediamine, mefa-tetramethylxylenediamine, and Jeffamine® (Texaco) of molecular weight less than 500.

Surface Active Agents

[0062] Examples of suitable surface active agents (surfactants) include: anionic, cationic, or nonionic dispersants or surfactants, such as sodium dodecyl sulfate, sodium dioctyl sulfosuccinate, sodium dodecylbenzenesulfonate, ethoxylated alkylphenols such as ethoxylated nonylphenols, and ethoxylated fatty alcohols, lauryl pyridinium bromide, polyether phosphates and phosphate esters, modified alcohol-ethoxylates, and combinations thereof.

Blocking Agents

[0063] The blocking agent for isocyanate groups may be either a monofunctional alcohol or a monofunctional amine. The blocking agent may be added at any time prior to formation of the prepolymer, during the formation of the prepolymer, or after the formation of the prepolymer including before and after dispersing the prepolymer into an aqueous medium such as deionized water. In some embodiments, the blocking agent is optional, or may be excluded. In other embodiments, based on the weight of the prepolymer, the blocking agent may be included in an amount from about 0.05% to about 10.0%, including about 0.1% to about 6.0% and about 1.0% to about 4.0%. Based on the weight of the final dispersion, the blocking agent may be present in an amount from about 0.01 % to about 6.0%, including about 0.05% to about 3%, and about 0.1% to about 1.0%.

[0064] The inclusion of a blocking agent permits control over the weight average molecular weight of the polymer in the dispersion as well as providing control over the polymer molecular weight distribution. The effectiveness of the blocking agent to provide this control depends on the type of the blocking agent and when the blocking agent is added during the preparation of the dispersion. For example, a monofunctional alcohol may be added prior to the formation of the prepolymer, during or after the formation of the prepolymer. The monofunctional alcohol blocking agent may also be added to the aqueous medium into which the prepolymer is dispersed, or immediately following the dispersion of the prepolymer into the aqueous medium. However, when control over the polymer molecular weight and the molecular weight distribution in the final dispersion is desired, the monofunctional alcohol may be most effective if added and reacted as part of the prepolymer before it is dispersed. If the monofunctional alcohol is added to the aqueous medium during or after dispersing the prepolymer, its effectiveness in controlling the polymer molecular weight will be reduced due to the competing chain extension reaction.

[0065] Examples of monofunctional alcohols useful with the present invention include at least one member selected from the group consisting of aliphatic and cycloaliphatic primary and secondary alcohols with 1 to 18 carbons, phenol, substituted phenols, ethoxylated alkyl phenols and ethoxylated fatty alcohols with molecular weight less than about 750, including molecular weight less than 500, hydroxyamines, hydroxymethyl and hydroxyethyl substituted tertiary amines, hydroxymethyl and hydroxyethyl substituted heterocyclic compounds, and combinations thereof, including furfuryl alcohol, tetrahydrofurfuryl alcohol, N-(2-hydroxyethyl)succinimide, 4-(2-hydroxyethyl)morpholine, methanol, ethanol, butanol, neopentyl alcohol, hexanol, cyclohexanol, cyclohexanemethanol, benzyl alcohol, octanol, octadecanol, N,N-diethylhydroxylamine, 2- (diethylamino)ethanol, 2-dimethylaminoethanol, and 4-piperidineethanol, and combinations thereof.

[0066] When a monofunctional amine compound, such as a monofunctional dialkyl amine is used as a blocking agent for isocyanate groups, it may also be added at any time during preparation of the dispersion, desirably the monofunctional amine blocking agent is added to the water medium during or after the prepolymer dispersion. For example, the monofunctional amine blocking agent can be added to the water mixture immediately after the prepolymer is dispersed.

[0067] Examples of suitable mono-functional dialkylatnine blocking agents include: N,N-diethylamine, N-ethyl-N-propylamine, N,N-diisopropylamine, N-te/t-butyl-N- methylamine, N-ferf-butyl-N-benzylamine, N.N-dicyclohexylaminβ, N-ethyl-N- isopropylamine, N-te/f-butyl-N-isopropylamine, N-isopropyl-N-cyclohexylamine, N-ethyl- N-cyclohexylamine, N,N-diethanolamine, and 2,2,6,6-tetramethylpiperidine. The molar ratio of the amine blocking agent to the isocyanate groups of the prepolymer prior to dispersion in water generally should range from about 0.05 to about 0.50, for example from about 0.20 to about 0.40. Catalysts may be used for the de-blocking reactions.

[0068] Optionally at least one polymeric component (MVY > about 500), with at least three or more primary and/or secondary amino groups per mole of the polymer, may be added to the water medium after the prepolymer is dispersed and the blocking agent is added. Examples of the suitable polymeric component include polyethylenimine, poly(vinylamine), poly(allylamine), and poly(amidoamine) dendrimers, and combinations thereof.

Other Additives

[0069] Examples of suitable antifoaming or defoaming or foam controlling agents include: Additive 65 and Additive 62 (silicone based additives from Dow Corning), FoamStar® I 300 (a mineral oil based, silicone free defoamer from Cognis) and Surfynol™ DF 110L (a high molecular weight acetylenic glycol non-ionic surfactant from Air Products & Chemicals).

[0070] Examples of suitable rheological modifiers include: hydrophobically-modified ethoxylate urethanes (HEUR), hydrophobically-modified alkali swellable emulsions (HASE), and hydrophobically-modified hydroxy-ethyl cellulose (HMHEC).

[0071] Other additives that may be optionally included in the aqueous dispersion or in the prepolymer include: anti-oxidants, UV stabilizers, colorants, pigments, crosslinking agents, phase change materials (i.e., Outlast®, commercially available from Outlast Technologies, Boulder, Colorado), antimicrobials, minerals (i.e., copper), microencapsulated well-being additives (i.e., aloe vera, vitamin E gel, aloe vera, sea kelp, nicotine, caffeine, scents or aromas), nanoparticles (i.e., silica or carbon), calcium carbonate, flame retardants, antitack additives, chlorine degradation resistant additives, vitamins, medicines, fragrances, electrically conductive additives, and/or dye-assist agents. Other additives which may be added to the prepolymer or the aqueous dispersion comprise adhesion promoters, anti-static agents, anti-cratering agents, anti- crawling agents, optical brighteners, coalescing agents, electroconductive additives, luminescent additives, flow and leveling agents, freeze-thaw stabilizers, lubricants, organic and inorganic fillers, preservatives, texturizing agents, thermochromic additives, insect repellants, and wetting agents.

[0072] Optional additives may be added to the aqueous dispersion before, during, or after the prepolymer is dispersed.

[0073] The aqueous polyurethaneurea dispersions of some embodiments may be prepared on a commercial scale, for example, in batches greater than about 500 gallons or greater than about 1000 gallons. The dispersions may be made with or without the addition of an organic solvent. In a commercial scale preparation of an aqueous polyurethaneurea, the prepolymer may include a monofunctional alcohol blocking agent. Stable dispersions may be prepared with these prepolymers in the absence of added solvent. Examples of prepolymer compositions (shown on a weight percent basis based on the weight of the total prepolymer composition) are given in Table 1.

[0074] The polyurethaneurea aqueous dispersions of some embodiments may include a variety of different compositions as described hereinabove. Suitable methods of preparation are illustrated in the Examples below. Compositions useful for the dispersions of some embodiments are set forth in Table 2. Any of the compositions in Tables 1 and 2 may be prepared on a commercial scale as described above.

[0075] In the prepolymer mixing process, the prepolymer can be prepared by mixing starting materials, namely the polyol, the polyisocyanate and the diol compound together in one step and by reacting at temperatures of about 5O⁰C to about 100⁰C for adequate time until all hydroxy groups are essentially consumed and a desired %NCO of the isocyanate group is achieved. Alternatively, this prepolymer can be made in two steps by first reacting a polyol with excess polyisocyanate, followed by reacting with a diol compound until a final desired %NCO of the prepolymer is achieved. For example, the %NCO may range from about 1.3 to about 6.5, such as from about 1.8 to about 2.6. Significantly, no organic solvent is necessary, but may be added or mixed with the starting materials before, during or after the reaction. Optionally, a catalyst may be used to facilitate the prepolymer formation.

[0076] In some embodiments, the prepolymer includes a polyol, a polyisocyanate, and a diol which are combined together and provided in the following ranges of weight percentages, based on the total weight of the prepolymer about 34% to about 89% of polyol, including from about 61% to about 80%; about 10% to about 59% of polyisocyanate, including from about 18% to about 35%; and about 1.0% to about 7.0% of diol compound, including from about 2.0% to about 4.0%. A monofunctional alcohol may be included with the prepolymer in order to control the weight average molecular weight of the polyurethaneurea polymer in the complete dispersion.

[0077] The prepolymer prepared from the polyol, polyisocyanate, diol compound and optionally a blocking agent such as a monofunctional alcohol, may have a bulk viscosity (with or without solvent present) below about 6,000 poises, including below about 4,500 poises, measured by the falling ball method at 40⁰C. This prepolymer, containing carboxylic acid groups along the polymer chains (from the diol compound), can be dispersed with a high-speed disperser into a de-ionized water medium that includes: at least one neutralizing agent, to form an ionic salt with the acid; at least one surface active agent (ionic and/or non-ionic dispersant or surfactant); and, optionally, at least one chain extension component. Alternatively, the neutralizing agent can be mixed with the prepolymer before being dispersed into the water medium. At least one antifoam and/or defoam agent a^'nd/or at least one rheological modifier can be added to the water medium before, during, or after the prepolymer is dispersed.

[0078] Polyurethane aqueous dispersions falling within the scope of the present invention may have a wide range of solids contents depending on the desired end use of the dispersion. Examples of suitable solids contents for the dispersions of some embodiments include from about 10% to about 50% by weight, for example from about 30% to about 45% by weight.

[0079] The viscosity of polyurethane aqueous dispersions may also be varied in a broad range from about 10 centipoises to about 100,000 centipoises depending on the processing and application requirements. For example, in one embodiment, the viscosity is in the range of about 500 centipoises to about 30,000 centipoises. The viscosity may be varied by using an appropriate amount of thickening agent, such as from about 0 to about 2.0 wt%, based on the total weight of the aqueous dispersion.

[0080] In the solvent process or acetone process, an organic solvent may also be used in the preparation of films and dispersions of some embodiments. The organic solvent may be used to lower the prepolymer viscosity through dissolution and dilution and/or to assist the dispersion of solid particles of the diol compound having a carboxylic acid group such as 2,2-dimethylopropionic acid (DMPA) to enhance the dispersion quality. It may also serve the purposes of improving the film uniformity such as reducing streaks and cracks in the coating/film-forming process.

[0081] The solvents selected for these purposes are substantially or completely non- reactive to isocyanate groups, stable in water, and have a good solubilizing ability for DMPA, the formed salt of DMPA and thethylamine, and the prepolymer. Examples of suitable solvents include N-methylpyrrolidone, N-ethylpyrrolidone, dipropylene glycol dimethyl ether, propylene glycol n-butyl ether acetate, N,N-dimethylacetamide, N, N- dimethylformamide, 2-propanone (acetone) and 2-butanone (methylethylketone or MEK).

[0082] In the solvent process, the amount of solvent added to the films/dispersion of some embodiments may vary. When a solvent is include, suitable ranges of solvent include amounts of less than 50% by weight of the dispersion. Smaller amounts may also be used such as less than 20% by weight of the dispersion, less than 10% by weight of the dispersion, less than 5% by weight of the dispersion and less than 3% by weight of the dispersion.

[0083] In the acetone process, a greater amount of solvent may be added to the prepolymer composition prior to the preparation of the dispersion. Alternatively, the prepolymer may be prepared in the solvent. The solvent may also be removed from the dispersion after dispersion of the prepolymer such as under vacuum.

[0084] There are many ways to incorporate the organic solvent into the dispersion at different stages of the manufacturing process, for example:

1 ) The solvent can be added to and mixed with the prepolymer after the polymerization is completed prior to transferring and dispersing the prepolymer, the diluted prepolymer containing the carboxylic acid groups (from the diol compound) in the backbone and isocyanate groups at the chain ends is neutralized and chain extended while it is dispersed in water.

2) The solvent can be added and mixed with other ingredients such as polyol, polyisocyanate and diol compound to make a prepolymer in the solution, and then this prepolymer containing the carboxylic acid groups in the backbone and isocyanate groups at the chain ends in the solution is dispersed in water and at the same time it is neutralized and chain extended. 3) The solvent can be added with a neutralized salt of a diol compound and a neutralizing agent amd mixed with a polyol and polyisocyanate to make the prepolymer prior to dispersion.

4) The solvent can be mixed with TEA, and then added to the formed prepolymer prior to dispersion.

5) The solvent can be added and mixed with the polyol, followed by the addition of the diol compound and netralizing agent, and then the polyisocyanate in sequence to a neutralized prepolymer in solution prior to dispersion.

6) The solvent may also be removed from the dispersion, especially in the case of the acetone process.

[0085] The aqueous polyurethane dispersions of the some embodiments are particularly suitable for adhesive shaped articles, which can be used for fabric bonding, lamination, and adhesion purposes when applied with heat and pressure for a relatively short period of time. Pressures, can for example, range from about atmospheric pressure to about 60 psi and times can range from less than about one second to about 30 minutes in accordance with the bonding method used.

[0086] Such shaped articles may be made by coating the dispersion onto a release paper and drying to remove water at temperatures below about 100°C through commercially available processes to form a film on the paper. This film can be a single layer or multiple layers. The multi-layer films can be formed from the same dispersion or different dispersion, adhered together by a lamination process or sequential coating process or direct coating process. The formed film sheets can be slit into strips of desired width and wound-up into spools for later use in applications to form stretch articles, for example textile fabrics. Examples of such applications include: stitch-less or seamless garment constructions; seam seal and reinforcement; labels and patches bonding to garments; and localized stretch/recovery enhancement. The adhesion bonding can be developed in the temperature range of from about 100⁰C to about 200⁰C, such as from about 13O⁰C to about 200°C, for example, from about 140°C to about 180⁰C, in a period of 0.1 seconds to several minutes, for example, less than about one minute. Typical bonding machines are Sew Free (commercially available from SewSystems in Leicester, England), Macpi hemming machine (commercially available from the Macpi Group in Brescia, Italy), Framis hot air welding machine (commercially available from Framis Italy, s p. a. in Milano, Italy). This bonding is expected to be strong and durable when exposed to repeated wear, wash, and stretch in a textile fabric garment.

[0087] The coating, dispersion, film or shaped article may be pigmented or colored and also may be used as a design element.

[0088] In addition, articles with laminated films or dispersions can be molded. For example, fabric can be molded under conditions appropriate for the hard yarn in the fabric. Also, molding may be possible at temperature which will mold the shaped article or dispersion, but below temperatures suitable for molding the hard yarn.

[0089] Lamination can be carried out to secure a polyurethaneurea dispersion shaped article prepared from a polyurethaneurea dispersion to a fabric using any method wherein heat is applied to the laminate surface. Methods of heat application include, for example, ultrasonic, direct heat, indirect heat, and microwave. Such direct lamination may provide an advantage in view of other methods used in the art in that the shaped article may not only bond to the a substrate via a mechanical interaction but also via a chemical bond. For example, if the substrate has any reactive hydrogen functional groups, such groups may react with the isocyanate and hydroxyl groups on the dispersion or shaped article, thereby providing a chemical bond between the substrate and the dispersion or shaped article. Such chemical bonding of the dispersion or shaped article to the substrate can give a much stronger bond. Such bonding may occur in dry shaped articles that are cured onto a substrate or in wet dispersions that are dried and cured in one step. Materials without an active hydrogen include polypropylene fabrics and anything with a fluoropolymer or a silicone based surface. Materials with an active hydrogen include, for example, nylon, cotton, polyester, wool, silk, cellulosics, acetates, metals, and acrylics. Additionally, articles treated with acid, plasma, or another form of etching may have active hydrogens for adhesion. Dye molecules also may have active hydrogens for bonding.

[0090] Methods and means for applying the polyurethaneurea compositions of some embodiments include, but are not limited to: roll coating (including reverse roll coating); use of a metal tool or knife blade (for example, pouring a dispersion onto a substrate and then casting the dispersion into uniform thickness by spreading it across the substrate using a metal tool, such as a knife blade); spraying (for example, using a pump spray bottle); dipping; painting; printing; stamping; and impregnating the article. These methods can be used to apply the dispersion directly onto a substrate without the need of further adhesive materials and can be repeated if additional/heavier layers are required. The dispersions can be applied to any fabrics of knits, wovens or nonwovens made from synthetic, natural, or synthetic/natural blended materials for coating, bonding, lamination and adhesion purposes. The water in the dispersion can be eliminated with drying during the processing (for example, via air drying or use of an oven), leaving the precipitated and coalesced polyurethane layer on the fabrics to form an adhesive bond.

[0091] Where additional control of the particle size is desired, or where the dispersion includes larger particles that are not useful for certain applications of the dispersions, the dispersions may be filtered. Useful types of filters include self-cleaning wiped filters such as those available by Russell Finex, Pineville, NC and Eaton Filtration, Elizabeth, NJ. These filters wipe the surface of the filtration media to remove deposited solids during the filtration process.

[0092] A film of some embodiments may be affixed to a substrate or self-supporting (meaning that the film maintains its structure in the absence of a substrate). These films are formed as a result of casting and drying the dispersions. The dispersions may be cast and dried on a substrate of any suitable material including, but not limited to, textiles; fabrics, including wovens and knits; nonwovens; leather (real or synthetic); paper; metal; plastic; and scrim.

[0093] At least one coagulant may optionally be used to control or to minimize penetration of dispersions according to the invention into a fabric or other article. Examples of coagulants that may be used include calcium nitrate (including calcium nitrate tetrahydrate), calcium chloride, aluminum sulfate (hydrated), magnesium acetate, zinc chloride (hydrated) and zinc nitrate.

[0094] An example of a tool that can be used for applying dispersions is a knife blade. The knife blade can be made of metal or any other suitable material. The knife blade can have a gap of a predetermined width and thickness. The gap may range in thickness, for example, from 0.2 mils to 50 mils, such as a thickness of 5 mils, 10 mils, 15 mils, 25 mils, 30 mils, or 45 mils.

[0095] The thickness of the films, solutions, and dispersions may vary depending on the application. In the case of dry shaped articles, the final thickness may, for example, range from about 0.1 mil to about 250 mil, such as from about 0.5 mil to about 25 mil, including from about 1 to about 6 mil (one mil = one thousandth of an inch). Additional examples of suitable thicknesses include about 0.5 mil to about 12 mil, about 0.5 to about 10 mil, and about 1.5 mil to about 9 mil.

[0096] For aqueous dispersions, suitable amounts are described by the weight of the dispersion over unit area. The amount used may, for example, range from about 2.5 g/m² to about 6.40 kg/m², such as from about 12.7 to about 635 g/m², including from about 25.4 to about 152.4 g/m².

[0097] Types of planar sheets and tapes that can be coated with dispersions and shaped articles falling within the scope of the present invention include, but are not limited to: textile fabrics, including wovens and knits; nonwovens; leather (real or synthetic); paper, including specially coated "release papers," waxed papers and silicone coated papers; metal; plastic; and scrim.

[0098] End articles that can be produced using the dispersions and shaped articles falling within the scope of the present invention include, but are not limited to: apparel, which includes any type of garment or article of clothing; knitted gloves; upholstery; hair accessories; bed sheets; carpet and carpet backing; conveyor belts; medical applications, such as stretch bandages; personal care items, including incontinence and feminine hygiene products; and footwear. Articles coated with dispersion or covered with film or tape may be used as sound suppression articles.

[0099] Non-elastic fabrics laminated to shaped articles can have improved stretch and recovery and improved molding properties.

[0100] Articles comprising shaped articles, film, tape, or aqueous polyurethane dispersion may be molded. The articles may be made with multiple layers of substrate and shaped article, film, tape, or dispersion. The multi-layered articles also may be molded. Molded and non-molded articles may have different levels of stretch and recovery. The molded articles may comprise a body shaping or body supporting garment, such as a brassiere.

[0101] Examples of apparel or garments that can be produced using the dispersions and shaped articles falling within the scope of the present invention, include but are not limited to: undergarments, brassieres, panties, lingerie, swimwear, shapers, camisoles, hosiery, sleepwear, aprons, wetsuits, ties, scrubs, space suits, uniforms, hats, garters, sweatbands, belts, activewear, outerwear, rainwear, cold-weather jackets, pants, shirtings, dresses, blouses, mens and womens tops, sweaters, corsets, vests, knickers, socks, knee highs, dresses, blouses, aprons, tuxedos, bisht, abaya, hijab, jilbab, thoub, burka, cape, costumes, diving suit, kilt, kimono, jerseys, gowns, protective clothing, sari, sarong, skirts, spats, stola, suits, straitjacket, toga, tights, towel, uniform, veils, wetsuit, medical compression garments, bandages, suit interlinings, waistbands, and all components therein.

[0102] Methods for performing and overcoming common problems in reverse roll coating are described in Walter, et al., "Solving common coating flaws in Reverse Roll Coating," AIMCAL Fall Technical Conference (October 26-29, 2003), the entire disclosure of which is incorporated herein by reference.

[0103] Another aspect of the invention is an article comprising the shaped article and a substrate wherein the shaped article and the substrate are attached to form a laminate whereby coefficient of friction of the elastic laminate is greater than that of the substrate alone. Examples of this are a waistband with a coating or film comprising the aqueous polyurethane dispersion which prevents slippage of the garment from another garment such as a blouse or shirt, or alternately prevents slippage of the waistband on the skin of the garment wearer.

[0104] Another aspect of the invention is an article comprising a polyurethaneurea composition and a substrate wherein the modulus of the shaped article varies along the length, or alternately the width, of the article. For example, a substrate such as fabric can be treated with two feet (61 cm) of a polyurethaneurea composition such as a one inch (2.5 cm) wide adhesive tape. An additional layer of adhesive can be applied by painting three two inches (5 cm) by one inch segments along the length of the one inch wide adhesive tape to form composite structure.

[0105] Shaped article, for example, films of the aqueous polyurethaneurea dispersions, may have the following properties: set after elongation of from about 0 to 10%, for example from about 0 to

5%, typically from about 0 to about 3%, elongation of about 400 to about 800%, and tenacity of about 0.5 to about 3 Mpa.

[0106] Laminates prepared from articles and substrates may have the following properties: peel strength after 50 washes wherein at least 50% of the strength is maintained from the same before washing, air permeability of at least about 0 to about 0.5 cfm, and moisture vapor permeability of at least about 0 to about 300 g/m2 over 24h.

Examples

[0107] Color measurements are made on samples of film with a Datacolor Spectraflash Model SF-300 colorimeter (Datacolor International, Lawrenceville, NJ) using a D65/10 degree illuminant. Measurements are reported using the international standard color measurement method promulgated by "Commission Internationale de L'Eclairage" (Paris, France), (International Society for Illumination/Lighting), ("CIE") using standard color coordinates of the CIELAB L*a*b* color space: "L" designates the lightness coordinate; "a" designates the red/green coordinate (+a indicating red and -a indicating green); and "b" designates the yellow/blue coordinate (+b indicating yellow and -b indicating blue).

[0108] Samples were prepared by obtaining a polyurethaneurea solution of the average molecular weights listed in Table 3, below. The anti-yellowing agents were then added in the amounts listed. Films were then cast and dried on MYLAR® sheets and dried. Before and after exposure Fume (at 50 ⁰C for 24 hours), NO2 (at room temperature for 24 hours), and UV (at room temperature for 8 hours), as indicated, the color change was measured as is shown. The films prepared from compositions including the anti-yellowing agent showed a noticeable improvement in whiteness/reduction in yellowing as shown. In addition, the consisting in whiteness was improved regardless of the polymer composition.

[0109] While there have been described what are presently believed to be the preferred embodiments of the invention, those skilled in the art will realize that changes and modifications may be made thereto without departing from the spirit of the invention, and it is intended to include all such changes and modifications as fall within the true scope of the invention.

Claims

What is claimed is:

1. A composition comprising;

(1) at least one polyol selected from polyethers, polyesters, polycarbonates, and combinations thereof, wherein the polyol has a number average molecular weight of 600 to 4000;

(2) a polyisocyanate comprising at least one aromatic diisocyanate;

(5) optionally including a blocking agent for isocyanate;

(6) at least one surface active agent; and

2. The composition of claim 1 , wherein said a blocking agent for isocyanate groups is included and comprises at least one monofunctional alcohol.

3. The composition of claim 1 , wherein said anti-yellowing compound is selected from the group consisting of cyclohexyl isocyanate, phenyl isocyanate, ethyl isocyanate, ethyl isocyanatoacetate and combinations thereof.

4. The composition of claim 1 , wherein said anti-yellowing compound is present in an amount of about 1 % to about 15% by weight of the dispersion.

5. The composition of claim 1 , wherein said anti-yellowing compound is present in an amount of about 3% to about 10% by weight of the dispersion.

6. A film cast and dried from a composition comprising

(2) a polyisocyanate comprising at least one aromatic diisocyanate;

(5) optionally including a blocking agent for isocyanate;

(6) at least one surface active agent; and

7. The composition of claim 6, wherein said a blocking agent for isocyanate groups is included and comprises at least one monofunctional alcohol.

8. The composition of claim 6, wherein said compound is selected from the group consisting of cyclohexyl isocyanate, phenyl isocyanate, ethyl isocyanate, ethyl isocyanatoacetate and combinations thereof.

9. The composition of claim 6, wherein said monoisocyanate is present in an amount of about 1 % to about 15% by weight of the dispersion.

10. The composition of claim 6, wherein said monoisocyanate is present in an amount of about 3% to about 10% by weight of the dispersion.

11. A method for reducing yellowing in a film comprising:

(a) preparing a polyurethaneurea aqueous dispersion comprising a polymer which is the reaction product of: (1 ) at least one polyol selected from polyethers, polyesters, polycarbonates, and combinations thereof, wherein the polyol has a number average molecular weight of 600 to 4000;

(2) a polyisocyanate comprising at least one aromatic diisocyanate;

(5) optionally including a blocking agent for isocyanate;

(6) at least one surface active agent;

(c) preparing a shaped article from said dispersion.

12. The method of claim 11 , wherein said a blocking agent for isocyanate groups is included and comprises at least one monofunctional alcohol.

13. The method of claim 11 , wherein said anti-yellowing compound is selected from the group consisting of cyclohexyl isocyanate, phenyl isocyanate, ethyl isocyanate, ethyl isocyanatoacetate and combinations thereof.

14. The method of claim 11 , wherein said anti-yellowing compound is present in an amount of about 1 % to about 15% by weight of the dispersion.

15. The method of claim 11 , wherein said anti-yellowing compound is present in an amount of about 3% to about 10% by weight of the dispersion.