KR20130030965A

KR20130030965A - Improved asphalt waterproof sheets and insulation waterproofing method

Info

Publication number: KR20130030965A
Application number: KR1020110094593A
Authority: KR
Inventors: 현흥창; 현우창; 정웅태
Original assignee: 현흥창; 주식회사 다인그룹엔지니어링건축사사무소; 티아이브이건설 주식회사
Priority date: 2011-09-20
Filing date: 2011-09-20
Publication date: 2013-03-28

Abstract

PURPOSE: A rubberized asphalt sheet for waterproofing and an insulation waterproofing method thereof are provided to prevent the generation of a weak part by integrating a rubberized asphalt layer and a waterproofing coating layer. CONSTITUTION: A rubberized asphalt sheet(100) for waterproofing comprises a rubber asphalt layer(101), a polyamide film(102), a fiber fabric(103), and first and second primer coating layers(104,105). An insulation waterproofing method for using a rubberized asphalt sheet comprises the following steps; positioning the rubberized asphalt sheet on a concrete surface by offsetting; adhering a butyl tape to the boundary of the rubberized asphalt sheet for connecting and filing urethane into the offsetting space; and forming a waterproofing coating layer by applying a waterproofing coating material on the surface of the primer coating layer.

Description

Composite asphalt waterproof sheets and composite waterproof insulation method using the same

본 발명은 복합방수용 고무아스팔트 시트 및 이를 이용한 복합방수절연공법에 관한 것으로, 특히, 종래의 복합절연공법의 문제점인 복합방수시트와 도막방수층의 결합력을 향상시키는 폴리아마이드 필름을 사용 도막방수층이 복합방수시트에 영향을 주지 않고 균일한 도막방수층의 형성을 가능케 함으로서 복합방수 시트층과 도막방수층 사이에 프라이머를 사용하지 않아도 우수한 결합력을 만드는 폴리아마이드 필름을 이용한 복합방수용 고무아스팔트 시트 및 이를 이용한 복합방수절연공법에 관한 것이다.The present invention relates to a composite waterproof rubber asphalt sheet and a composite waterproof insulation method using the same, in particular, a composite waterproof sheet using a polyamide film to improve the bonding strength of the composite waterproof sheet and the coating waterproof layer, which is a problem of the conventional composite insulation method Composite waterproof rubber asphalt sheet using polyamide film and excellent composite waterproof insulation method using the polyamide film to make excellent bonding force without using primer between composite waterproof sheet layer and coating waterproof layer by enabling formation of uniform waterproof layer without affecting sheet It is about.

건축물에는 우수 및 지하수의 유입을 차단하여 구조체의 균열이나 내구성의 저하를 미연에 방지하기 위한 방수작업이 필수적으로 요구된다.In buildings, waterproofing is essential to prevent rainwater and groundwater from entering, thus preventing structural cracks and deterioration of durability.

종래의 방수공법은 시공방법에 따라 시트방수, 도막방수, 복합방수로 구분된다. Conventional waterproofing method is divided into sheet waterproof, coating waterproof, composite waterproof according to the construction method.

상기한 도막방수는 액상형의 방수재를 바탕면에 반복하여 도포하는 방법으로서, 액상 자체의 퍼짐성으로 인해 건축물 바탕면의 평활도가 좋지 않으면 균일한 두께의 도막형성이 어렵다는 단점 및 바탕의 습기가 고열에 의하여 증발함으로써 발생하는 부풀림과 들뜸현상이 문제점으로 지적되었으며, 바탕의 크랙에 대한 대응성이 떨어진다는 점 등이 큰 문제점으로 지적되었다.The waterproofing of the coating film is a method of repeatedly applying a liquid-type waterproofing material to the base surface, the smoothness of the base surface of the building due to the spreadability of the liquid itself is difficult to form a coating film of uniform thickness and the moisture of the base due to high temperature The swelling and uplift caused by evaporation were pointed out as problems, and the responsiveness to cracks in the ground was poor.

아울러, 상기한 시트방수는 상기 도막방수의 단점 중 방수층 두께 확보와 크랙에 대한 대응성에 대한 문제를 해결하기는 하였으나, 복잡한 구조물의 모서리나 돌출부의 밀실한 방수층의 확보에 어렵다는 단점이 있다. In addition, the above-mentioned sheet waterproofing has solved the problem of securing the thickness of the waterproof layer and the correspondence to cracks among the disadvantages of the waterproofing of the coating film, but has a disadvantage in that it is difficult to secure the tight waterproof layer of the corners or protrusions of the complex structure.

따라서, 종래의 방수시공 중 상기한 도막방수와 시트방수를 결합하여 양자의 단점을 보완하고 장점을 상승시킨 것이 복합방수공법이다.Therefore, the combined waterproofing and sheet waterproofing of the conventional waterproof construction to complement the disadvantages of both of them and increase the advantages is a composite waterproofing method.

상기한 복합방수공법은 고무화 아스팔트류, 합성고분자계 등으로 제작된 베이스 시트를 바탕면에 부착하고 그 위에 액상의 도막방수재를 도포하는 방법이다.The composite waterproof method is a method of attaching a base sheet made of rubberized asphalt, synthetic polymers, etc. to the base surface and applying a liquid coating waterproofing material thereon.

복합방수공법에서 상기한 통상의 베이스 시트를 그대로 사용하게 되면, 베이스 시트와 액상의 도막방수재가 제대로 부착되지 않거나 부착된 후에도 들뜨게 되는 문제점이 있었다.When the conventional base sheet is used as it is in the composite waterproofing method, there is a problem that the base sheet and the liquid coating waterproofing material are not properly attached or are excited after being attached.

이러한 문제점은 베이스 시트와 액상의 도막방수재의 재료적 특성이 서로 다르기 때문에 물성이 서로 반목하는데 기인하고 있다.This problem is attributable to the fact that the physical properties of the base sheet and the liquid coating waterproofing material are different from each other.

이러한 문제를 해결하기 위하여 베이스 시트와 액상의 도막방수재 사이에 부착 및 결속력을 증대시키는 매개체로서 부직포를 부착한 베이스 시트가 개발된 바 있으나, 이러한 개량 베이스 시트에 액상의 도막방수재를 도포하면 부직포로 도막방수재가 다량 흡수되므로 원하는 도막방수층의 두께을 구성하기 못하는 새로운 문제가 발생하게 된다. In order to solve this problem, a base sheet with a nonwoven fabric has been developed as a medium for increasing adhesion and binding force between the base sheet and the liquid film waterproofing material. However, when the liquid film waterproofing material is applied to such an improved base sheet, the film is coated with a nonwoven fabric. Since a large amount of waterproof material is absorbed, a new problem may occur that does not constitute a desired thickness of the coating layer.

한편, 종래의 복합방수공법에서는 베이스 시트로 고무아스팔트 시트가 많이 사용하고 있는데, 고무아스팔트 시트 자체의 점착력이 떨어져 프라이머 처리된 바탕면에 부착되었으나, 이와 같은 방법은 프라이머 도포작업으로 인한 재료와 인건비의 비용문제, 프라이머 도포 후 시간적인 지연문제가 있었다. Meanwhile, in the conventional composite waterproofing method, rubber asphalt sheets are frequently used as a base sheet, but the adhesive force of the rubber asphalt sheet itself is lowered and thus attached to the primer-treated base surface. There was a cost problem and a time delay after primer application.

따라서, 점착력을 활용하거나 고무계 점착제를 이용하는 정도에 머물기 때문에 바탕면에의 부착력이 그다지 우수하지 못하였고, 나아가 저온에서 부착력이 현저히 떨어진다는 문제가 있어 종래의 고무아스팔트 시트와 다름없이 프라이머 처리된 바탕면에 부착하여 사용하는 것이 일반적이었다.Therefore, the adhesive force to the base surface is not very good because the adhesive force or the pressure-sensitive adhesive remains on the base surface, and furthermore, there is a problem in that the adhesive force is significantly lowered at low temperatures. It was common to attach to and use it.

본 발명은 상기한 종래의 문제를 해결하고자 안출된 것으로서, 복합방수공법에서 고무아스팔트층과 도막방수층의 결합력이 향상되게 함으로써, 고무아스팔트층과 도막방수층의 일체화를 도모함은 물론 균일한 도막방수층의 형성을 가능케 하는 복합방수용 고무아스팔트 시트 및 이를 이용한 복합방수절연공법를 제공하는데 그 목적이 있다.The present invention has been made to solve the above-mentioned conventional problems, by improving the bonding force of the rubber asphalt layer and the film waterproof layer in the composite waterproof method, to achieve the integration of the rubber asphalt layer and the film waterproof layer as well as to form a uniform film waterproof layer It is an object of the present invention to provide a composite waterproof rubber asphalt sheet and a composite waterproof insulation method using the same.

상기한 목적은, 고무아스팔트층과; 상기 고무아스팔트층 상부에 부착되고, 내용제성과 치수안정성이 우수한 폴리아마이드 필름과; 상기 고무아스팔트층과 폴리아마이드 필름 사이의 폴리아마이드 필름 하면에 부착되는 섬유포와; 상기 폴리아마이드 필름의 표면에 프라이머가 도포되어 형성되는 제1프라이머코팅층과; 상기 섬유포 하면에 프라이머가 도포되어 형성되는 제2프라이머코팅층을 포함하는 것을 특징으로 하는 복합방수용 고무아스팔트 시트에 의해 달성된다.The above object is a rubber asphalt layer; A polyamide film attached to an upper portion of the rubber asphalt layer and having excellent solvent resistance and dimensional stability; A fiber cloth attached to a lower surface of the polyamide film between the rubber asphalt layer and the polyamide film; A first primer coating layer formed by coating a primer on a surface of the polyamide film; It is achieved by a composite waterproof rubber asphalt sheet comprising a second primer coating layer formed by applying a primer on the lower surface of the fiber cloth.

여기서, 상기 제1프라이머코팅층과 제2프라이머코팅층을 형성하는 프라이머는 주제와 경화제로 이루어진 2성분형으로, 상기 주제는 염화 폴리올레핀 20%~25% 중량%, 용제 75%~80 중량%를 포함하여 구성되고, 상기 경화제는 폴리이소시아네이트 100 중량%로 이루어진다.Here, the primer for forming the first primer coating layer and the second primer coating layer is a two-component type consisting of a main body and a curing agent, the main body 20% to 25% by weight of polyolefin chloride, including 75% to 80% by weight solvent And the curing agent consists of 100% by weight of polyisocyanate.

그리고, 상기 고무아스팔트층 하부면에 0.3mm~0.5mm 크기의 세모래를 함침시켜 이루어진 세모래층(10)을 더 포함하는 것이 바람직하다.In addition, the rubber asphalt layer preferably further includes a three-sand layer 10 formed by impregnating three-sand of 0.3 mm to 0.5 mm in size.

한편, 상기한 목적은, 콘크리트 바탕면에 제1항에 의한 다수 개의 복합방수용 고무아스팔트 시트를 서로 소정거리 이격배치하여 바탕면이 일부 노출되게 하는 단계와; 신축적으로 수축이완하며, 저온과 고온에서 반고체상태로서 방수층을 이루는 부틸고무층과, 이 부틸고무층 상부에서 부틸고무층 보다 넓게 유리섬유가 부착되어 이루어진 부틸테이프를 서로 이격배치된 다수 개의 복합방수용 고무아스팔트 시트의 테두리에 부착하여 서로 연결시키는 단계와; 상기 어느 하나의 고무아스팔트 시트와 인접한 다른 고무아스팔트 시트 사이의 이격공간에 우레탄을 충진시키는 단계와; 상기 부틸테이프에 의해 바탕면 상부에 연결설치된 복합방수용 고무아스팔트 시트의 제1프라이머코팅층 상부에 도막방수재를 도포하여 도막방수층을 형성하는 단계를 포함하는 것을 특징으로 하는 복합방수용 고무아스팔트 시트의 복합방수절연공법에 의해 달성된다.On the other hand, the above object, the step of placing a plurality of composite waterproofing rubber asphalt sheet according to claim 1 spaced apart from each other by a predetermined distance on the concrete base surface; A plurality of composite waterproof rubber asphalt sheets which are spaced apart from each other by butyl rubber layer, which is elastically relaxed and semi-solid at low temperature and high temperature, forming a waterproof layer, and butyl tape formed by attaching glass fiber on the upper part of the butyl rubber layer more broadly than butyl rubber layer. Attaching to the edges of each other and connecting them to each other; Filling a urethane in a space between the rubber asphalt sheet and another rubber asphalt sheet adjacent thereto; Composite waterproof insulation of the composite waterproof rubber asphalt sheet comprising the step of coating the coating film waterproofing material on the first primer coating layer of the composite waterproof rubber asphalt sheet connected to the upper base surface by the butyl tape to form a coating waterproof layer It is achieved by the method.

본 발명은 고무아스팔트 시트와 도막방수층의 결합력을 향상시킴은 물론 균일한 도막방수층의 형성이 용이하고, 바탕면과 고무아스팔트 시트가 절연된 상태로 시공되도록 함으로써, 고무아스팔트 시트 또는 고무아스팔트층이 바탕면의 거동에 대하여 역학적인 구조변화가 발생하지 않게 된다.The present invention not only improves the bonding force between the rubber asphalt sheet and the waterproofing layer, but also facilitates the formation of a uniform coating waterproofing layer, and allows the rubber asphalt sheet or the rubber asphalt layer to be ground in a state where the ground surface and the rubber asphalt sheet are insulated. There is no dynamic structural change in the behavior of the face.

따라서, 바탕면 거동과 이에 순응하는 고무아스팔트 시트 또는 고무아스팔트층에 항상 발생하는 드레인 부위 및 취약부위와 같은 위험요소를 사전에 방지할 수 있는 효과를 가진다. Therefore, there is an effect that can prevent in advance the risk factors such as the drain portion and the vulnerable portion that always occurs in the base surface behavior and the rubber asphalt sheet or rubber asphalt layer conforming thereto.

도 1은 복합방수용 고무아스팔트 시트의 구조를 도시한 도면.
도 2는 복합방수용 고무아스팔트 시트가 바탕면에 시공되는 상태를 도시한 도면.
도 3은 복합방수용 고무아스팔트 시트가 바탕면에 시공되는 상태를 도시한 도면.1 is a view showing the structure of a composite waterproof rubber asphalt sheet.
Figure 2 is a view showing a state in which a composite waterproof rubber asphalt sheet is installed on the base surface.
Figure 3 is a view showing a state in which the composite waterproof rubber asphalt sheet is constructed on the base surface.

본 발명은 도 1에 도시된 바와 같이 고무아스팔트층(101), 폴리아마이드 필름(102), 섬유포(103), 제1프라이머코팅층(104), 제2프라이머코팅층(105)으로 구성된다.1, the rubber asphalt layer 101, the polyamide film 102, the fiber cloth 103, the first primer coating layer 104, and the second primer coating layer 105 are formed.

상기한 고무아스팔트층(101)은 방수시트에 사용되는 점착성을 가지는 통상의 고무아스팔트를 말한다.The rubber asphalt layer 101 refers to a conventional rubber asphalt having adhesiveness used for a waterproof sheet.

그리고, 상기 고무아스팔트층(101) 상부에는 폴리아마이드 필름(102)을 부착하되, 이 폴리아마이드 필름(102)과 고무아스팔트층(101) 사이에는 섬유포(103)가 개입되어 부착될 수 있게 한다.In addition, the polyamide film 102 is attached to the rubber asphalt layer 101, but the fiber cloth 103 is interposed between the polyamide film 102 and the rubber asphalt layer 101.

여기서, 상기 폴리아마이드 필름(102)은 도막이 용제에 잠겨도 잘 변화되지 않는 성질을 가진다.Here, the polyamide film 102 has a property that does not change well even when the coating film is immersed in the solvent.

즉, 내용제 시험에서 규정된 용제에 침적하여 도막에 주름, 팽창, 균열, 벗겨짐 또는 색, 광택의 변화가 없는 것으로서, 점착성이 증가된 것이다.That is, there is no wrinkle, swelling, cracking, peeling or change of color or gloss in the coating film by immersing in the solvent specified in the solvent test, and the adhesiveness is increased.

그리고, 상기 폴리아마이드 필름(102)은 치수안정성이 우수한 것으로서, 비바람, 햇볕과 같은 외부환경에도 변형이 일어나진 않으므로, 최초의 크기가 환경에 무관하게 변화하지 않으므로, 방수시트의 균일한 성능의 보장이 더욱 용이하다는 것이다.In addition, since the polyamide film 102 is excellent in dimensional stability, deformation does not occur even in an external environment such as rain or sunshine, and thus the initial size does not change regardless of the environment, thereby ensuring uniform performance of the waterproof sheet. This is even easier.

즉, 기존의 필름지는 열을 받거나 비바람을 맞아 혹은 햇볕에 장시간 노출되었을 경우 변형이 일어나서 오그라들거나 뒤틀림 현상이 일어나기도 하며, 이로 인하여, 최초 생산 시의 크기였던 치수가 불안정할 개연성이 있으며, 이에 따라, 방수시트의 구조에서는 필름의 변형 및 치수의 불안정성은 방수층 즉, 고무아스팔트층(101)의 방수성을 저하시키는 문제로 발전할 수 있다는 것이다.That is, the conventional film paper is deformed or warped due to deformation or deformation when subjected to heat, weather, or long-term exposure to the sun. As a result, the size at the time of initial production is likely to be unstable. In the structure of the waterproof sheet, the deformation of the film and the instability of the dimension may develop into a problem of reducing the waterproofness of the waterproof layer, that is, the rubber asphalt layer 101.

그러나, 본 발명의 폴리아마이드 필름(102)은 상기한 바와 같이 내용제성과 치수안정성이 우수하므로 외부환경으로부터의 변형이 발생하지 않으므로, 고무아스팔트층(101)의 변형과 결합력의 약화를 미연에 방지하고 강한 결합구조를 가질 수 있게 되는 것이다.However, since the polyamide film 102 of the present invention has excellent solvent resistance and dimensional stability as described above, deformation from the external environment does not occur, thereby preventing deformation of the rubber asphalt layer 101 and weakening of the bonding force in advance. It will be able to have a strong coupling structure.

여기서, 상기 폴리아마이드 필름(102)의 표면에는 프라이머를 도포하여 제1프라이머코팅층(104)을 형성한다.Here, a primer is applied to the surface of the polyamide film 102 to form a first primer coating layer 104.

즉, 고무아스팔트층(101)과 도막방수층은 서로 친화성이 없기 때문에 고무아스팔트층(101)과 방수시공 시 도포되는 도막방수층(106)은 서로 접착되지 않아 분리되기 마련이므로, 폴리아마이드 필름(102)에 프라이머를 코팅하여 제1프라이머코팅층(104)이 형성되게 하고, 이 제1프라이머코팅층(104)이 고무아스팔트층(101)과 도막방수층의 결합매개가 되도록 하고 있는 것이다.That is, since the rubber asphalt layer 101 and the waterproofing layer are not compatible with each other, the rubber asphalt layer 101 and the waterproofing layer 106 applied during waterproofing are not bonded to each other and are separated from each other, so that the polyamide film 102 The first primer coating layer 104 is formed by coating a primer, and the first primer coating layer 104 is a bonding medium between the rubber asphalt layer 101 and the coating waterproof layer.

여기서, 상기 제1프라이머코팅층(104)을 형성하는 프라이머는, 주제와 경화제로 이루어진 2성분형으로, 상기 주제는 염화 폴리올레핀 20%~25% 중량%, 용제 75%~80 중량%를 포함하여 구성되고, 상기 경화제는 폴리이소시아네이트 100 중량%로 구성한다.Here, the primer for forming the first primer coating layer 104 is a two-component type consisting of a main body and a curing agent, the main body is composed of 20% to 25% by weight of polyolefin chloride, 75% to 80% by weight solvent And the curing agent comprises 100% by weight of polyisocyanate.

상기 프라이머는 2액형으로 이루어지므로 경화제에 의한 주제의 경화과정에서 폴리아마이드 필름(102) 위에 안정적으로 코팅층을 형성시킬 수 있게 되고, 특히, 상기와 같은 프라이머를 사용하면 도막방수재로 우레탄을 적용하는 경우 도막방수층과 일체 결합하는데 더욱 유리한 효과를 발휘할 것이데, 이는 경화제로 우레탄의 주원료와 동일한 폴리이소시아네이트를 사용하였는 바 제1프라이머코팅층(104)이 우레탄 도막방수층과 친화성을 발휘하며, 여기서, 상기 폴리아마이드 필름(102)은 상기한 바와 같이 내용제성과 치수안정성이 우수하므로 외부환경으로부터의 변형이 발생하지 않으므로, 제1프리어머코팅층과의 결합력이 우수하고 변형이 발생하지 않으므로 시공 후에도 제1프라이머코팅층(104)이 폴리아마이드 필름(102)에 안정적으로 결합된 상태를 유지할 수 있게 된다.Since the primer is made of a two-component type, it is possible to stably form a coating layer on the polyamide film 102 in the curing process of the main body by a curing agent, and in particular, when using the primer as described above, when urethane is applied as a coating waterproof It will have a more advantageous effect of integrally bonding with the coating film waterproofing layer, since the same polyisocyanate as the main raw material of urethane is used as the curing agent, and thus the first primer coating layer 104 exhibits affinity with the urethane coating film waterproofing layer, wherein the poly Since the amide film 102 is excellent in solvent resistance and dimensional stability as described above, no deformation from the external environment occurs, and thus, the first primer coating layer is excellent even after construction because of excellent bonding force with the first primer coating layer and no deformation. 104 is stably bonded to the polyamide film 102 Will be able to maintain.

한편, 도 1에 도시된 바와 같이 상기 폴리아마이드 필름(102) 하부에 섬유포(103)가 부착되도록 하고, 상기 섬유포(103) 아래에 제2프라이머코팅층(105)을 형성한다.Meanwhile, as shown in FIG. 1, the fiber cloth 103 is attached to the lower portion of the polyamide film 102, and a second primer coating layer 105 is formed below the fiber cloth 103.

상기 섬유포(103)로는 타폴린 직포와 같은 것을 채택할 수 있으며, 이와 같은 섬유포(103)의 채택으로 폴리아마이드 필름(102)과 고무아스팔트층(101)과의 부착면적이 확대되어 부착력향상과 결속력의 향상을 기대할 수 있게 된다. The fiber cloth 103 may be adopted, such as a tarpaulin woven fabric, and by adopting the fiber cloth 103, the adhesion area between the polyamide film 102 and the rubber asphalt layer 101 is increased, thereby improving adhesion and binding force. We can expect improvement of.

또한, 상기 제2프라이머코팅층(105)은 고무아스팔트층(101)에 개입 또는 융화하면서 섬유포(103)가 고무아스팔트층(101)에 합지되는 것을 보완한다.In addition, the second primer coating layer 105 compensates for the fiber cloth 103 being laminated to the rubber asphalt layer 101 while intervening or melting in the rubber asphalt layer 101.

본 발명에 따른 도 1과 같은 구조의 고무아스팔트 시트는 섬유포(103) 표면에 합성수지액을 부은 상태에서 폴리아마이드 필름(102)을 적층 형성하고, 그 위와 아래로 프라이머를 롤 코팅하여 제1프라이머코팅층(104)과 제2프라이머코팅층(105)을 적층형성하여 필름형태로 완성한 후 이를 고무아스팔트층(101) 위에 부착하는 방법으로 제작 완성할 수 있다.The rubber asphalt sheet having the structure as shown in FIG. 1 according to the present invention is formed by laminating a polyamide film 102 in a state in which a synthetic resin solution is poured onto the surface of the fiber cloth 103, and coating a primer on and below the first primer coating layer. The 104 and the second primer coating layer 105 may be laminated to form a film, and then manufactured and completed by attaching the 104 and second primer coating layers 105 on the rubber asphalt layer 101.

한편, 본 발명에 따른 고무아스팔트 시트(100)는 상기 고무아스팔트층(101) 하부면에 0.3mm ~ 0.5mm 크기의 세모래를 함침시켜 세모래층을 형성함으로써, 고무아스팔트층(101) 하부면의 점착력을 약화시킴과 동시에 바탕면으로부터의 절연성을 향상시킬 수 있게 된다.On the other hand, the rubber asphalt sheet 100 according to the present invention by impregnating the fine sand of 0.3mm ~ 0.5mm size on the lower surface of the rubber asphalt layer 101 to form a three-sand layer, the lower surface of the rubber asphalt layer 101 It is possible to weaken the adhesive force and at the same time improve the insulation from the base surface.

상기한 바와 같이 이루어진 본 발명에 따른 복합방수용 고무아스팔트 시트의 복합방수절연공법을 설명하면 다음과 같다.Referring to the composite waterproof insulation method of the composite waterproof rubber asphalt sheet according to the present invention made as described above are as follows.

먼저, 콘크리트 바탕면에 상기한 바와 같이 본 발명에 따른 다수 개의 복합방수용 고무아스팔트 시트(100)를 서로 소정거리 이격배치하여 도 2에 도시된 바와 같이 일정한 공간(A)가 형성될 수 있게 함으로써, 바탕면이 일부 노출되게 하는 단계를 수행한다.First, by placing a plurality of composite waterproofing rubber asphalt sheet 100 according to the present invention on a concrete base surface spaced apart from each other by a predetermined distance so that a constant space (A) can be formed, as shown in FIG. Perform the step of partially exposing the base surface.

그리고, 상기한 바와 같이 서로 이격배치된 다수 개의 복합방수용 고무아스팔트 시트(100)의 테두리에 부틸테이프(200)를 부착하여 서로 연결시키는 단계를 수행한다.As described above, the butyl tape 200 is attached to the edges of the plurality of composite waterproof rubber asphalt sheets 100 spaced apart from each other, thereby connecting to each other.

여기서, 상기 부틸테이프(200)는, 부틸고무층(201)과 유리섬유(202)로 구성되며, 부틸고무층(201)은 신축적으로 수축이완이 자유로우며, 저온과 고온에서 반고체 상태를 유지한다.Here, the butyl tape 200 is composed of a butyl rubber layer 201 and a glass fiber 202, the butyl rubber layer 201 is freely shrinkage and relaxation freely, and maintains a semi-solid state at low and high temperatures.

그리고, 상기 부틸고무층(201)의 상부에는 도 2와 도 3에 도시된 바와 같이 부틸고무층(201) 보다 넓은 면적으로 성형된 유리섬유(202)를 부착하여 도 2와 같이 테두리에 여유 면적이 만들어지게 한 것이다.In addition, as shown in FIGS. 2 and 3, the butyl rubber layer 201 is attached to the glass fiber 202 formed in a wider area than the butyl rubber layer 201, thereby making a free area on the edge as shown in FIG. It is lost.

즉, 도 2에 도시된 상기 고무아스팔트 시트(100)의 테두리 영역(B)에는 부틸테이프(200)가 부착되어지는 것이다.That is, the butyl tape 200 is attached to the edge region B of the rubber asphalt sheet 100 illustrated in FIG. 2.

또한, 상기한 바와 같이 부틸테이프(200)가 고무아스팔트 시트(100)에 부착되어 도 3과 같이 서로연결된 상태가 이루어지면, 어느 하나의 고무아스팔트 시트(100)와 인접한 다른 고무아스팔트 시트(100) 사이의 이격공간에 도 3에 도시된 바와 같이 우레탄(107)을 충진시키는 단계를 수행한다.In addition, as described above, when the butyl tape 200 is attached to the rubber asphalt sheet 100 and connected to each other as shown in FIG. 3, the other rubber asphalt sheet 100 adjacent to any one rubber asphalt sheet 100 is provided. Filling the space between the urethane 107 as shown in Figure 3 is performed.

상기한 바와 같이 상기 부틸테이프(200)에 의해 바탕면(108) 상부에 다수 개의 복합방수용 고무아스팔트 시트(100)가 연결설치되면, 상부면에 노출된 제1프라이머코팅층(104) 상부에 도막방수재를 도포하여 도막방수층(106)을 형성하는 단계를 수행함으로써, 방수시공이 완료될 수 있는 것이다.As described above, when a plurality of composite waterproof rubber asphalt sheets 100 are installed on the base surface 108 by the butyl tape 200, the coating waterproofing material is disposed on the first primer coating layer 104 exposed on the top surface. By performing the step of forming a coating waterproof layer 106 by applying, the waterproof construction can be completed.

100 : 고무아스팔트 시트 101 : 고무아스팔트층
102 : 폴리아마이드 피름 103 : 섬유포
104 : 제1프라이머코팅층 105 : 제2프라이머코팅층
106 : 도막방수층 107 : 우레탄
108 : 바탕면100: rubber asphalt sheet 101: rubber asphalt layer
102 polyamide film 103: fiber cloth
104: first primer coating layer 105: second primer coating layer
106: coating film waterproofing layer 107: urethane
108: ground plane

Claims

Rubber asphalt layer;
A polyamide film attached to an upper portion of the rubber asphalt layer and having excellent solvent resistance and dimensional stability;
A fiber cloth attached to a lower surface of the polyamide film between the rubber asphalt layer and the polyamide film;
A first primer coating layer formed by coating a primer on a surface of the polyamide film;
Composite waterproof rubber asphalt sheet, characterized in that it comprises a second primer coating layer formed by applying a primer on the lower surface of the fiber cloth.

The method of claim 1,
The primer forming the first primer coating layer and the second primer coating layer is a two-component type consisting of a main body and a curing agent, the main body is composed of 20% to 25% by weight of polyolefin chloride, 75% to 80% by weight solvent , The hardener is composed of 100% by weight of polyisocyanate rubber asphalt sheet for composite waterproof.

The method according to claim 1 or 2,
Composite waterproof rubber asphalt sheet, characterized in that it further comprises a three-sand layer (10) made by impregnating the fine sand of 0.3mm ~ 0.5mm size on the lower surface of the rubber asphalt layer.

Placing a plurality of composite waterproof rubber asphalt sheets according to claim 1 spaced apart from each other by a predetermined distance on a concrete base surface to partially expose the base surface;
A plurality of composite waterproof rubber asphalt sheets which are spaced apart from each other by butyl rubber layer, which is elastically relaxed and semi-solid at low temperature and high temperature, forming a waterproof layer, and butyl tape formed by attaching glass fiber on the upper part of the butyl rubber layer more broadly than butyl rubber layer. Attaching to the edges of each other and connecting them to each other;
Filling a urethane in a space between the rubber asphalt sheet and another rubber asphalt sheet adjacent thereto;
Composite waterproof insulation of the composite waterproof rubber asphalt sheet comprising the step of coating the coating film waterproofing material on the first primer coating layer of the composite waterproof rubber asphalt sheet connected to the upper base surface by the butyl tape to form a coating waterproof layer Method.