KR102151342B1

KR102151342B1 - Oral capsule and manufacturing method of the same

Info

Publication number: KR102151342B1
Application number: KR1020190030289A
Authority: KR
Inventors: 박문수
Original assignee: 박문수
Priority date: 2019-03-18
Filing date: 2019-03-18
Publication date: 2020-09-02

Abstract

The present invention relates to an oral capsule and a method of producing the same. In particular, the oral capsule (1) consists of a core portion (10) containing an oral rinse solution (11) and a shell layer (20), wherein the oral capsule (1) has an average diameter of 15-50 mm. The shell layer (20) comprises: a core portion-shell layer (21); and an outer shell layer (22) which includes one or more through-holes (220) and has a higher elastic strength than that of the core portion-shell layer (21) for improving the strength of the oral capsule. Accordingly, the oral capsule can easily satisfy a desire for oral cleaning without using water, can be conveniently and immediately used in a uniform amount without being weighed; has improved portability due to an improved overall strength of the oral capsule; and can improve productivity.

Description

Oral capsule and manufacturing method of the same

본 발명은 구강 세정액(11)을 포함하는 코어부(10); 및 쉘층(20)으로 이루어진 구강용 캡슐(1)에 있어서, 상기 구강용 캡슐(1)은 평균 입경이 15 내지 50 mm인 것이고, 상기 쉘층(20)은 코어부 쉘층(21)과; 구강용 캡슐의 강도를 개선하기 위하여, 코어부 쉘층(21)보다 높은 탄성강도를 갖고, 하나 또는 하나 이상의 통공(220)을 포함하는 외부 쉘층(22);을 포함하는 구강용 캡슐 및 이의 제조방법에 관한 것이다.The present invention includes a core portion 10 containing an oral cleaning solution (11); And in the oral capsule (1) consisting of a shell layer (20), wherein the oral capsule (1) has an average particle diameter of 15 to 50 mm, the shell layer 20 is a core part shell layer (21); In order to improve the strength of the oral capsule, the outer shell layer 22 has a higher elastic strength than the core shell layer 21, and includes one or more through holes 220; oral capsule and a manufacturing method thereof It is about.

현대인들에게 외모는 가장 대두되는 관심사이다. 외모에 관심이 높아진 만큼 성형이나 화장품 등에 대한 수요가 높아지고 있으며, 더 나아가 교정이나 구취 등 구강에 대한 관심도 높아지고 있는 상황이다. 청결을 중시하는 현대인의 대인관계에 있어서, 치아의 심미감 및 청결함이 중요한 요소로 작용함에 따라, 현대인은 치약과 칫솔, 구강 청정제 등을 항상 휴대하여 치아 건강에 힘쓰고 있다. 또한, 칫솔질을 통해 구취 제거를 하는 것이 현대에서는 자신의 구강을 위한 목적일 뿐만 아니라 타인에 대한 예의라고 생각하는 사람들이 늘어났다. 때문에 수시로 치아 상태나 구취를 확인하여 신경 쓰게 되었으며, 그에 따라 간편하고 쉽게 사용할 수 있는 구강관리 용품들이 많이 발명되었다. Appearance is the most emerging concern for modern people. As interest in appearance increases, demand for plastic surgery and cosmetics is increasing, and further, interest in oral cavity such as correction and bad breath is increasing. In the interpersonal relationship of modern people who value cleanliness, as the aesthetics and cleanliness of teeth act as important factors, modern people always carry toothpaste, toothbrushes, and mouthwashes to strive for dental health. In addition, in modern times, more people think that removing bad breath through brushing is not only a purpose for their oral cavity, but also a courtesy toward others. Because of this, the condition of the teeth or bad breath was checked from time to time, and there were many simple and easy-to-use oral care products.

그 예로, 액상으로 되어 구강 내를 헹구는 구강양치용액이 있다. 구강양치용액은 구강 내 세균 제거뿐만 아니라 구취제거에도 효과가 있는 제품이므로 칫솔질이 어려운 상황에서 대체 용품으로 많은 사람들이 사용하고 있다. 그러나 기존의 구강양치용액은 액상 형태로 용량별 플라스틱 용기에 담아 제작되므로 사용시 용액의 1회분 정량을 맞춰 사용하기 어려울 뿐만 아니라 사용 후에도 용기를 소지하고 있어야 하는 불편함이 있었다. 또한, 기존의 구강양치용액은 가방에 휴대시 용기의 마개 부적합이나 잘못된 취급으로 인해 구강양치용액이 새어나올 수 있고 가방 안의 다른 소지품에 피해를 입힐 수 있는 문제점이 있었다.For example, there is an oral mouthwash solution that is liquid and rinses the oral cavity. Mouthwash solution is a product that not only removes bacteria in the oral cavity but also removes bad breath, so many people use it as an alternative product in situations where brushing is difficult. However, since the existing oral mouthwash solution is produced in a plastic container for each volume in a liquid form, it is difficult to use it in accordance with the amount of one dose of the solution when using it, and there was an inconvenience of having to have the container after use. In addition, when carrying the conventional mouthwash solution in a bag, there is a problem in that the mouthwash solution may leak out due to an improper closure or incorrect handling of the container and cause damage to other belongings in the bag.

본 발명의 일 구현예는 물 없이도 용이하게 구강 청결에 대한 욕구를 해결할 수 있고, 휴대가 간편하며, 개량하지 않고도 즉시 정량 사용이 용이하도록 제작한 구강용 캡슐을 제공하고자 하는 것이다.An embodiment of the present invention is to provide a capsule for oral cavity that can easily solve the desire for oral cleanliness without water, is easy to carry, and is readily used for quantitative use without improvement.

또한, 본 발명의 다른 일 구현예는 상기 본 발명의 일 구현예에 따른 구강용 캡슐의 제조방법을 제공하고자 하는 것이다.In addition, another embodiment of the present invention is to provide a method of manufacturing an oral capsule according to the embodiment of the present invention.

본 발명의 일 구현예는 구강 세정액(11)을 포함하는 코어부(10); 및 쉘층(20)으로 이루어진 구강용 캡슐(1)에 있어서, 상기 구강용 캡슐(1)은 평균 입경이 15 내지 50 mm인 것이고, 상기 쉘층(20)은 코어부 쉘층(21)과; 구강용 캡슐의 강도를 개선하기 위하여, 코어부 쉘층(21)보다 높은 탄성강도를 갖고, 하나 또는 하나 이상의 통공(220)을 포함하는 외부 쉘층(22);을 포함하는 것인 구강용 캡슐을 제공한다.One embodiment of the present invention includes a core portion 10 comprising an oral rinse (11); And in the oral capsule (1) consisting of a shell layer (20), wherein the oral capsule (1) has an average particle diameter of 15 to 50 mm, the shell layer 20 is a core part shell layer (21); In order to improve the strength of the oral capsule, it has an elastic strength higher than that of the core shell layer 21, and an outer shell layer 22 including one or more through holes 220; providing an oral capsule containing do.

상기 코어부 쉘층(21)은 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민 (triethanolamine alginate)에 2가 이상의 양이온성 금속염 용액을 반응시켜 제조되는 것이고, 상기 외부 쉘층(22)은 젤라틴, 글리세린, D-소르비톨액, 및 나트륨셀룰로우즈설페이트를 포함하는 것을 사용하여 제조되는 것이고, 상기 코어부 쉘층(21)의 2가 이상의 양이온성 금속염과 상기 외부 쉘층(22)의 나트륨셀룰로우즈설페이트가 서로 결합하여, 상기 코어부 쉘층(21) 및 외부 쉘층(22)이 보다 견고한 결합을 갖게 할 수 있다.The core part shell layer 21 is prepared by reacting a divalent or higher cationic metal salt solution with gellan gum, alginic acid, and triethanolamine alginate, and the outer shell layer 22 is gelatin, glycerin, It is prepared by using a D-sorbitol solution and sodium cellulose sulfate, and the divalent or higher cationic metal salt of the core part shell layer 21 and sodium cellulose sulfate of the outer shell layer 22 are each By combining, the core part shell layer 21 and the outer shell layer 22 may have a more rigid bond.

상기 외부 쉘층(22)의 통공(220)은 결정 셀룰로오스, D-만니톨 및 알파화된 옥수수 전분을 포함하는 타액 붕괴성 조성물(221)로 채워지는 것일 수 있다.The through hole 220 of the outer shell layer 22 may be filled with a saliva-disintegrating composition 221 including crystalline cellulose, D-mannitol, and gelatinized corn starch.

본 발명의 다른 일 구현예는 구강 세정액(11)에 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민 (triethanolamine alginate)의 혼합 용액을 투입하여 혼합한 후, 상기 혼합액을 2가 이상의 양이온성 금속염 용액에 투입하여, 반응시킴으로써, 구강 세정액(11)을 포함하는 코어부 쉘층(21)을 제조하는 단계; 및 상기 제조된 구강 세정액(11)을 포함하는 코어부 쉘층(21)의 표면에, 외부 쉘층 제조용 노즐(223)을 이용하여, 젤라틴, 글리세린, D-소르비톨액, 및 나트륨셀룰로우즈설페이트를 포함하는 외부 쉘층 제조용 용액(222)을 토출 및 코팅시킴으로써, 코어부(10)에 구강 세정액(11)을 포함하고, 쉘층(20)으로서 코어부 쉘층(21) 및 외부 쉘층(22)을 포함하는 구강용 캡슐(1)을 제조하는 단계를 포함하고; 상기 외부 쉘층 제조용 용액(222)을 노즐(223)을 이용하여, 토출하는 공정은 비연속적으로 수행됨으로써, 하나 또는 하나 이상의 통공(220)을 포함하는 외부 쉘층(22)을 형성하는 것인 구강용 캡슐의 제조방법을 제공한다.In another embodiment of the present invention, after mixing by adding a mixed solution of gellan gum, alginic acid, and triethanolamine alginate to the oral rinse 11, the mixed solution is mixed with a divalent or higher cationic metal salt solution. Injecting into, by reacting, preparing a core part shell layer 21 containing the oral rinse (11); And gelatin, glycerin, D-sorbitol solution, and sodium cellulose sulfate on the surface of the core part shell layer 21 containing the prepared oral rinse solution 11, using a nozzle 223 for producing an outer shell layer. By discharging and coating the solution 222 for manufacturing an outer shell layer, the oral cavity including the oral cleaning solution 11 and the shell layer 20 as the core portion 10 and the outer shell layer 21 and the outer shell layer 22 Including the step of preparing a capsule (1); The process of discharging the outer shell layer manufacturing solution 222 using the nozzle 223 is performed discontinuously, thereby forming an outer shell layer 22 including one or more through holes 220 It provides a method of manufacturing a capsule.

본 발명의 일 구현예에 따른 구강용 캡슐은 용이하게 깨물어 터트림으로써, 구강 세정액으로 입안을 헹굴수 있도록 되므로, 직장이나 학교에서 또는 여행시 물 없이도 구강 청결에 대한 욕구를 간편하게 해결할 수 있고, 개량하지 않고도 즉시 정량 사용이 용이하며, 1회용 포장으로 용기를 들고 다닐 필요없이, 외부활동 및 여행 등에서 필요한 만큼의 캡슐만 준비함으로써 휴대성이 높아지고, 장시간 밖에 있을 경우에도 구강 청결에 대한 욕구를 쉽게 해결할 수 있는 효과가 있다.The oral capsule according to an embodiment of the present invention is easily bitten and burst, so that the mouth can be rinsed with an oral rinse solution, so that the desire for oral cleanliness can be easily solved at work, school, or without water when traveling, It is easy to quantify and use immediately without improvement, and it is easy to use as a single-use packaging, without having to carry a container, and by preparing only as many capsules as necessary for outdoor activities and travel, it increases portability and facilitates the need for oral cleanliness even when outside for a long time There is an effect that can be solved.

또한, 본 발명의 일 구현예에 따른 구강용 캡슐은 자체 강도가 개선되어, 평균 입경이 15 내지 50 mm 범위로 상당히 큰 크기의 구강용 캡슐을 제조할 수 있고, 휴대시, 외부의 충격에 의해 파괴되는 문제점을 해결할 수 있게 되므로, 휴대성이 더욱 개선되는 효과가 있다.In addition, the oral capsule according to an embodiment of the present invention has improved its own strength, so that the average particle diameter is in the range of 15 to 50 mm, so that a considerably large size of the oral capsule can be manufactured. Since it is possible to solve the problem of destruction, there is an effect of further improving portability.

또한, 본 발명의 다른 일 구현예에 따른 구강용 캡슐의 제조방법은 구강용 캡슐의 자체 강도를 개선하는 효과가 있기 때문에, 제조과정 중에 구강용 캡슐이 파괴되는 것을 방지하여, 생산성을 향상시킬 수 있는 효과가 있다. In addition, since the method for manufacturing an oral capsule according to another embodiment of the present invention has an effect of improving the strength of the oral capsule, it is possible to improve productivity by preventing the oral capsule from being destroyed during the manufacturing process. There is an effect.

도 1은 본 발명의 일 구현예에 따른 구강용 캡슐의 모식도 및 모식적 단면도를 나타낸 것이다.
도 2는 외부 쉘층(22)의 통공(220)을 타액 붕괴성 조성물(221)로 채운 본 발명의 일 구현예에 따른 구강용 캡슐의 모식도를 나타낸 것이다.
도 3은 본 발명의 일 구현예에 따른 구강용 캡슐을 제조하는데 적합한 제조장치의 노즐부의 일 구현예를 나타내는 모식적 종단면도이다.1 is a schematic view and a schematic cross-sectional view of an oral capsule according to an embodiment of the present invention.
2 is a schematic view of a capsule for oral cavity according to an embodiment of the present invention in which the through hole 220 of the outer shell layer 22 is filled with a saliva-disintegrating composition 221.
3 is a schematic longitudinal sectional view showing an embodiment of a nozzle part of a manufacturing apparatus suitable for manufacturing an oral capsule according to an embodiment of the present invention.

이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구범위의 범주에 의해 정의될 뿐이다.Hereinafter, embodiments of the present invention will be described in detail. However, this is presented as an example, and the present invention is not limited thereby, and the present invention is only defined by the scope of the claims to be described later.

본 발명의 일 구현예는 구강 세정액(11)을 포함하는 코어부(10); 및 쉘층(20)으로 이루어진 구강용 캡슐(1)에 있어서, 상기 구강용 캡슐(1)은 평균 입경이 15 내지 50 mm인 것이고, 상기 쉘층(20)은 코어부 쉘층(21)과; 구강용 캡슐의 강도를 개선하기 위하여, 코어부 쉘층(21)보다 높은 탄성강도를 갖고, 하나 또는 하나 이상의 통공(220)을 포함하는 외부 쉘층(22);을 포함하는 것인 구강용 캡슐을 제공한다. 이러한 본 발명의 일 구현예에 따른 구강용 캡슐의 모식도 및 모식적 단면도를 도 1에 나타내었다.One embodiment of the present invention includes a core portion 10 comprising an oral rinse (11); And in the oral capsule (1) consisting of a shell layer (20), wherein the oral capsule (1) has an average particle diameter of 15 to 50 mm, the shell layer 20 is a core part shell layer (21); In order to improve the strength of the oral capsule, it has an elastic strength higher than that of the core shell layer 21, and an outer shell layer 22 including one or more through holes 220; providing an oral capsule containing do. A schematic diagram and a schematic cross-sectional view of an oral capsule according to an embodiment of the present invention are shown in FIG. 1.

이러한 본 발명의 일 구현예에 따른 구강용 캡슐은 입안에 넣고, 깨물기만 하면, 외부 쉘층(22)에 포함되는 하나 또는 하나 이상의 통공(220)을 통하여, 구강 세정액(11)이 터져나와, 용이하게 입안을 헹굴수 있게 하는 효과가 있다.Such an oral capsule according to an embodiment of the present invention is put in the mouth and bite, and the oral cleaning liquid 11 bursts through one or more through holes 220 included in the outer shell layer 22, and is easily It has the effect of allowing you to rinse your mouth thoroughly.

또한, 본 발명의 일 구현예에 따른 구강용 캡슐은 종래의 구강 세정액을 포함하는 연질 캡슐과 대비하여, 구강용 캡슐(1)의 강도가 보강되는 효과가 있다. 이로써, 평균 입경이 15 내지 50 mm 범위로 상당히 큰 크기의 구강용 캡슐을 제조할 수 있고, 휴대시, 외부의 충격에 의해 파괴되는 문제점을 해결할 수 있게 되므로, 휴대성이 더욱 개선되는 효과가 있다. 또한, 제조과정 중에 구강용 캡슐이 파괴되는 것을 방지하여, 생산성이 향상되는 효과가 있다. In addition, the oral capsule according to an embodiment of the present invention has an effect of reinforcing the strength of the oral capsule 1 as compared to a soft capsule including a conventional oral cleaning solution. Thereby, it is possible to manufacture a capsule for oral cavity having a fairly large size with an average particle diameter in the range of 15 to 50 mm, and when carrying, it is possible to solve the problem of being destroyed by an external impact, so that portability is further improved. . In addition, there is an effect of improving productivity by preventing the oral capsule from being destroyed during the manufacturing process.

본 발명의 일 구현예에 따른 구강용 캡슐(1)은 구강 세정액(11)을 포함하는 코어부(10); 및 쉘층(20)으로 이루어진다. 이러한 구강용 캡슐(1)은 평균 입경이 15 내지 50 mm인 것으로 제조될 수 있는 바, 한입 크기로 제조되어, 편리하게 입안에 넣고, 입안을 헹굴수 있게 하는 효과가 있다.The oral capsule 1 according to an embodiment of the present invention includes a core portion 10 including an oral cleaning solution 11; And a shell layer 20. These oral capsules (1) can be manufactured to have an average particle diameter of 15 to 50 mm, and are manufactured in a bite size, and are conveniently placed in the mouth and have the effect of allowing the mouth to be rinsed.

상기 쉘층(20)은 코어부 쉘층(21)과; 구강용 캡슐의 강도를 개선하기 위하여, 코어부 쉘층(21)보다 높은 탄성강도를 갖는 외부 쉘층(22)을 포함한다.The shell layer 20 includes a core part shell layer 21; In order to improve the strength of the oral capsule, it includes an outer shell layer 22 having a higher elastic strength than the core shell layer 21.

보다 구체적으로, 상기 외부 쉘층(22)의 탄성강도는 코어부 쉘층(21)의 탄성강도 대비 1 내지 70 % 높은 것일 수 있다. 이로써, 종래보다 상당히 큰 크기의 구강용 캡슐을 제조하면서도, 구강용 캡슐(1)의 강도가 보강될 수 있는 것이다. 상기 코어부 쉘층(21)과; 외부 쉘층(22)의 탄성강도의 차이만으로도 구강용 캡슐의 강도는 현저하게 개선될 수 있다. More specifically, the elastic strength of the outer shell layer 22 may be 1 to 70% higher than the elastic strength of the core part shell layer 21. Thus, while manufacturing a capsule for oral cavity of a significantly larger size than the conventional, the strength of the capsule for oral cavity (1) can be reinforced. The core part shell layer 21; The strength of the oral capsule can be remarkably improved only by the difference in the elastic strength of the outer shell layer 22.

보다 더 구체적으로, 상기 외부 쉘층(22)의 탄성강도는 90 내지 150 N인 것이고, 상기 코어부 쉘층(21)의 탄성강도는 50 내지 100 N인 것으로 제조함으로써, 상기한 효과를 더욱 개선할 수 있다.More specifically, by manufacturing that the elastic strength of the outer shell layer 22 is 90 to 150 N, and the elastic strength of the core shell layer 21 is 50 to 100 N, the above effect can be further improved. have.

본 발명의 명세서에 있어서, "탄성강도"라 함은 242±20 ℃, 49±10 % RH에서 250 N 피로시험기(INSTRON사, E1000)를 사용하여 10 mm/min의 속도로 하중을 가해 최대 압축 하중(탄성 강도; N)을 측정한 것을 의미한다.In the specification of the present invention, "elastic strength" refers to maximum compression by applying a load at a speed of 10 mm/min using a 250 N fatigue tester (INSTRON, E1000) at 242±20°C and 49±10% RH. It means the measurement of the load (elastic strength; N).

본 발명의 일 구현예에 따른 구강용 캡슐(1)의 쉘층(20)에 포함되는 코어부 쉘층(21)과; 외부 쉘층(22)은 상기한 특징을 가지는 것이라면 당분야에 일반적으로 알려진 제조성분 및 제조방법에 의하여 제조될 수 있는 바, 그 구체적인 제조성분 및 제조방법에 대해서는 특별히 한정하지 않는다.The core part shell layer 21 included in the shell layer 20 of the oral capsule 1 according to an embodiment of the present invention; As long as the outer shell layer 22 has the above characteristics, it can be manufactured by generally known manufacturing components and manufacturing methods in the art, and specific manufacturing components and manufacturing methods thereof are not particularly limited.

보다 구체적인 예를 들면, 상기 코어부 쉘층(21)은 2가 이상의 양이온성 금속염을 포함하는 것이고, 상기 외부 쉘층(22)은 나트륨셀룰로우즈설페이트를 포함하는 것을 사용함으로써, 상기 코어부 쉘층(21)의 2가 이상의 양이온성 금속염과 상기 외부 쉘층(22)의 나트륨셀룰로우즈설페이트가 서로 결합하여, 상기 코어부 쉘층(21) 및 외부 쉘층(22)이 보다 견고한 결합을 갖게할 수 있다.For a more specific example, the core part shell layer 21 contains a cationic metal salt of divalent or higher, and the outer shell layer 22 is made of sodium cellulose sulfate, so that the core part shell layer 21 ) And sodium cellulose sulfate of the outer shell layer 22 are bonded to each other, so that the core part shell layer 21 and the outer shell layer 22 may have a more robust bond.

보다 더 구체적으로, 상기 코어부 쉘층(21)은 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민(triethanolamine alginate)에 2가 이상의 양이온성 금속염 용액을 반응시켜 제조되는 것일 수 있다. 상기 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민(triethanolamine alginate)은 각각 1: 1 내지 5: 1 내지 2의 중량비율로 혼합한 것을 15 내지 20 중량%의 농도로 정제수에 혼합하여, 수용액의 형태로 사용할 수 있다. More specifically, the core part shell layer 21 may be prepared by reacting a divalent or higher cationic metal salt solution with gellan gum, alginic acid, and triethanolamine alginate. The gellan gum, alginic acid and alginic acid triethanolamine alginate are mixed in a weight ratio of 1: 1 to 5: 1 to 2, respectively, and mixed in purified water at a concentration of 15 to 20% by weight, Can be used in form.

이어서, 상기 수용액과 구강 세정액(11)의 혼합물을 2가 이상의 양이온성 금속염 용액에 반응시키면, 코어부 쉘층(21)에 둘러싸인 구강 세정액(11)을 제조할 수 있게 된다. Subsequently, when the mixture of the aqueous solution and the oral rinse 11 is reacted with a divalent or higher cationic metal salt solution, the oral rinse 11 surrounded by the core part shell layer 21 can be prepared.

이 때, 상기 2가 이상의 양이온성 금속염 용액은 5 내지 10 중량%의 농도의 수용액인 것을 사용하는 것이 좋다. 또한, 상기 2가 이상의 양이온성 금속염으로는 당분야에서 일반적으로 사용되는 것으로 그 종류를 특별히 한정하지 않지만, 예를 들면, 젖산칼슘, 염화마그네슘, 황산마그네슘, 염화칼슘, 황산칼슘, 염화아연, 황산아연 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상인 것을 사용할 수 있다. 보다 구체적으로 코어부 쉘층(21)의 탄성강도를 고려하여, 젖산칼슘 및 염화칼슘을 1: 2 중량 비율로 혼합한 것을 사용하는 것이 좋다. At this time, the divalent or higher cationic metal salt solution is preferably an aqueous solution having a concentration of 5 to 10% by weight. In addition, the divalent or higher cationic metal salt is generally used in the art, and its kind is not particularly limited, but, for example, calcium lactate, magnesium chloride, magnesium sulfate, calcium chloride, calcium sulfate, zinc chloride, zinc sulfate And one or more selected from the group consisting of a mixture thereof may be used. More specifically, in consideration of the elastic strength of the core shell layer 21, it is preferable to use a mixture of calcium lactate and calcium chloride in a ratio of 1:2 by weight.

이러한 쉘층(20)으로서 코어부 쉘층(21)만을 가지는 경우, 그 강도가 너무 약하여, 터지기 쉽고, 이로써 제조시 생산성이 저하되는 문제점이 있을 수 있다. 또한, 제조된 구강용 캡슐(1)의 휴대성이 나빠지는 문제점이 있을 수 있다. 따라서, 보다 높은 탄성 강도를 갖는 외부 쉘층(22)으로 구강용 캡슐(1)의 강도를 더욱 보강할 수 있게 되었다.In the case of having only the core part shell layer 21 as such a shell layer 20, the strength is too weak, it is easy to burst, and thus there may be a problem that productivity is lowered during manufacture. In addition, there may be a problem that the portability of the manufactured oral capsule 1 is deteriorated. Therefore, it is possible to further reinforce the strength of the oral capsule 1 with the outer shell layer 22 having a higher elastic strength.

이러한 상기 외부 쉘층(22)은 젤라틴, 글리세린, D-소르비톨액, 및 나트륨셀룰로우즈설페이트를 포함하는 것일 수 있다. 보다 구체적으로 젤라틴 40 내지 70 중량%, 글리세린 15 내지 35 중량%, D-소르비톨액 10 내지 20 중량%, 및 나트륨셀룰로우즈설페이트 1 내지 10 중량%를 포함하는 것일 수 있다. The outer shell layer 22 may include gelatin, glycerin, D-sorbitol liquid, and sodium cellulose sulfate. More specifically, it may include 40 to 70% by weight of gelatin, 15 to 35% by weight of glycerin, 10 to 20% by weight of D-sorbitol solution, and 1 to 10% by weight of sodium cellulose sulfate.

이러한 상기 코어부 쉘층(21) 및 외부 쉘층(22)은 건조후의 평균 두께가 각각 0.3 내지 0.7 mm 범위가 되도록 제작될 수 있다. The core part shell layer 21 and the outer shell layer 22 may be manufactured such that the average thickness after drying is in the range of 0.3 to 0.7 mm, respectively.

또한, 상기 외부 쉘층(22)은 하나 또는 하나 이상의 통공(220)을 포함함으로써, 구강용 캡슐의 자체 강도를 더욱 개선할 수 있다. 뿐만 아니라, 상기 통공(220)은 탄성강도가 상대적으로 약한 부분이기 때문에 이러한 통공(220)을 통하여, 구강 세정액(11)이 터져나오는 통로 역할을 하게 되고, 이로써, 용이하게 입안을 헹굴수 있게 하는 효과가 있는 것이다. 만약 이러한 통공이 없는 경우에는 외부 쉘층(22)의 탄성강도가 너무 높아 구강내에서 깨물어도 구강용 캡슐이 잘 터지지 않는 문제점이 있을 수 있다.In addition, the outer shell layer 22 may further improve the strength of the oral capsule by including one or more through holes 220. In addition, since the through hole 220 has a relatively weak elastic strength, through the through hole 220, it serves as a passage through which the oral cleaning solution 11 bursts, thereby allowing the mouth to be easily rinsed. It works. If there is no such hole, the elastic strength of the outer shell layer 22 is too high, and there may be a problem that the oral capsule does not burst well even if bitten in the oral cavity.

이러한 통공은 그 크기를 특별히 제한하지는 않으나, 상기한 효과를 고려하여, 평균 직경이 0.5 내지 3 mm 범위가 되도록 제작하는 것이 좋다.The size of these through holes is not particularly limited, but in consideration of the above-described effect, it is preferable to manufacture so that the average diameter is in the range of 0.5 to 3 mm.

또한, 상기 외부 쉘층(22)의 통공(220)은 타액 붕괴성 조성물(221)로 채워지는 것일 수 있다. 이러한 외부 쉘층(22)의 통공(220)을 타액 붕괴성 조성물(221)로 채운 본 발명의 일 구현예에 따른 구강용 캡슐의 모식도는 도 2에 나타내었다. 상기 통공(220)은 탄성강도가 상대적으로 약한 부분이기 때문에 이러한 통공(220)을 타액 붕괴성 조성물(221)로 채움으로써, 구강용 캡슐(1)의 강도를 더욱 개선할 수 있는 효과가 있다. 또한, 상기 타액 붕괴성 조성물(221)을 타액으로 용이하게 녹인 후, 통공(220)이 노출되면, 구강용 캡슐(1)을 깨물어 터트림으로써, 구강 세정액(11)으로 용이하게 입안을 헹굴수 있게 하는 효과가 있는 것이다. In addition, the through hole 220 of the outer shell layer 22 may be filled with the saliva-disintegrating composition 221. A schematic diagram of a capsule for oral cavity according to an embodiment of the present invention in which the through hole 220 of the outer shell layer 22 is filled with the saliva-disintegrating composition 221 is shown in FIG. 2. Since the through hole 220 has a relatively weak elastic strength, by filling the through hole 220 with the saliva-disintegrating composition 221, the strength of the oral capsule 1 can be further improved. In addition, after easily dissolving the saliva-disintegrating composition 221 with saliva, when the through hole 220 is exposed, the oral capsule 1 is bitten and burst, so that the mouth can be easily rinsed with the oral cleaning solution 11 It has the effect of making it possible.

보다 구체적으로 상기 타액 붕괴성 조성물(221)은 타액에 의하여 용이하게 용해되는 성분이라면 그 조성물을 특별히 한정하지 않으나, 예를 들면, 결정 셀룰로오스, D-만니톨 및 알파화된 옥수수 전분을 포함하는 것을 사용하여, 상기한 효과를 더욱 개선할 수 있다. 보다 구체적으로 상기 조성물은 결정 셀룰로오스 100 중량부에 대하여, D-만니톨 300 내지 500 중량부 및 알파화된 옥수수 전분 10 내지 80 중량부의 비율로 혼합되는 것이 좋다. More specifically, the saliva-disintegrating composition 221 is not particularly limited as long as it is a component that is easily dissolved by saliva, but, for example, it is used that contains crystalline cellulose, D-mannitol, and alpha corn starch. Thus, the above effect can be further improved. More specifically, the composition is preferably mixed in a ratio of 300 to 500 parts by weight of D-mannitol and 10 to 80 parts by weight of gelatinized corn starch based on 100 parts by weight of crystalline cellulose.

또한, 상기 알파화 전분이란, 전분을 가열 처리하여 알파화한 것으로, 일본 의약품 첨가물 규격에 기재된 것을 사용할 수 있다. 평균 알파화도는 70 ∼ 80 ％인 것을 사용하는 것이 좋다. 시판되는 것으로는, 예를 들어, 알파화 전분 swelstar PD-1 (아사히카세이 케미컬즈 제조) 을 사용할 수 있다 In addition, the above-described gelatinized starch is obtained by heat treatment of starch to be gelatinized, and those described in the Japanese pharmaceutical additive standard can be used. It is preferable to use an average degree of gelatinization of 70 to 80%. As a commercially available thing, for example, gelatinized starch swelstar PD-1 (manufactured by Asahi Kasei Chemicals) can be used.

본 발명에서 사용되는 상기 구강 세정액(11)은 당분야에서 일반적으로 사용되는 것으로 그 종류를 특별히 한정하지 않는다. 다만, 액상의 구강 세정액(11)을 담지하면서도, 개선된 강도를 가질 수 있는 바, 예를 들면, 유지, 청량화제, 감미제, pH조절제, 염화세틸피리디늄, 및 안식향나트륨을 포함하는 구강 세정 조성물; 및 정제수를 1: 50 내지 90 부피비율로 혼합한 것을 사용할 수 있다.The oral rinse liquid 11 used in the present invention is generally used in the art, and the type is not particularly limited. However, a bar that can have improved strength while supporting a liquid oral rinse (11), for example, an oral cleaning composition containing fats and oils, a refreshing agent, a sweetener, a pH adjusting agent, cetylpyridinium chloride, and sodium benzoate ; And purified water may be mixed in a volume ratio of 1: 50 to 90.

이러한 본 발명의 일 구현예에 따른 구강용 캡슐은 용이하게 깨물어 터트림으로써, 구강 세정액으로 입안을 헹굴수 있도록 되므로, 직장이나 학교에서 또는 여행시 물 없이도 구강 청결에 대한 욕구를 간편하게 해결할 수 있고, 개량하지 않고도 즉시 정량 사용이 용이하며, 1회용 포장으로 용기를 들고 다닐 필요없이, 외부활동 및 여행 등에서 필요한 만큼의 캡슐만 준비함으로써 휴대성이 높아지고, 장시간 밖에 있을 경우에도 구강 청결에 대한 욕구를 쉽게 해결할 수 있는 효과가 있다.The oral capsule according to the embodiment of the present invention is easily bitten and burst, so that the mouth can be rinsed with an oral rinse solution, so that the desire for oral cleanliness can be easily solved at work, school, or without water when traveling. , It is easy to use immediately without improvement, and it is easy to use in a single-use package, without the need to carry a container, and by preparing only as many capsules as necessary for outdoor activities and travel, etc., portability increases, and the desire for oral cleanliness even when outside for a long time There is an effect that can be easily resolved.

본 발명의 다른 일 구현예는 구강 세정액(11)에 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민 (triethanolamine alginate)의 혼합 용액을 투입하여 혼합한 후, 상기 혼합액을 2가 이상의 양이온성 금속염 용액에 투입하여, 반응시킴으로써, 구강 세정액(11)을 포함하는 코어부 쉘층(21)을 제조하는 단계; 및 상기 제조된 구강 세정액(11)을 포함하는 코어부 쉘층(21)의 표면에, 외부 쉘층 제조용 노즐(223)을 이용하여, 젤라틴, 글리세린, D-소르비톨액, 및 나트륨셀룰로우즈설페이트를 포함하는 외부 쉘층 제조용 용액(222)을 토출 및 코팅시킴으로써, 코어부(10)에 구강 세정액(11)을 포함하고, 쉘층(20)으로서 코어부 쉘층(21) 및 외부 쉘층(22)을 포함하는 구강용 캡슐(1)을 제조하는 단계를 포함하고; 상기 외부 쉘층 제조용 용액(222)을 노즐(223)을 이용하여, 토출하는 공정은 비연속적으로 수행됨으로써, 하나 또는 하나 이상의 통공(220)을 포함하는 외부 쉘층(22)을 형성하는 것인 구강용 캡슐의 제조방법을 제공한다. 이러한 본 발명의 일 구현예에 따른 구강용 캡슐을 제조하는데 적합한 제조장치의 노즐부의 일 구현예를 나타내는 모식적 종단면도를 도 3에 나타내었다. 이러한 본 발명의 다른 일 구현예에 따른 구강용 캡슐의 제조방법에서 사용되는 성분 및 함량 등의 기술적인 특징은 상기 본 발명의 일 구현예에 따른 구강용 캡슐을 설명하면서 기술한 바와 같다.In another embodiment of the present invention, after mixing by adding a mixed solution of gellan gum, alginic acid, and triethanolamine alginate to the oral rinse 11, the mixed solution is mixed with a divalent or higher cationic metal salt solution. Injecting into, by reacting, preparing a core part shell layer 21 containing the oral rinse (11); And gelatin, glycerin, D-sorbitol solution, and sodium cellulose sulfate on the surface of the core part shell layer 21 containing the prepared oral rinse solution 11, using a nozzle 223 for producing an outer shell layer. By discharging and coating the solution 222 for manufacturing an outer shell layer, the oral cavity including the oral cleaning solution 11 and the shell layer 20 as the core portion 10 and the outer shell layer 21 and the outer shell layer 22 Including the step of preparing a capsule (1); The process of discharging the outer shell layer manufacturing solution 222 using the nozzle 223 is performed discontinuously, thereby forming an outer shell layer 22 including one or more through holes 220 It provides a method of manufacturing a capsule. Fig. 3 is a schematic longitudinal sectional view showing an embodiment of a nozzle part of a manufacturing apparatus suitable for manufacturing an oral capsule according to an embodiment of the present invention. Technical features, such as ingredients and contents, used in the method of manufacturing an oral capsule according to another embodiment of the present invention are as described while describing the oral capsule according to the embodiment of the present invention.

이러한 본 발명의 다른 일 구현예에 따른 구강용 캡슐의 제조방법은 평균 입경이 15 내지 50 mm인 것이고, 상기 쉘층(20)은 코어부 쉘층(21)과; 구강용 캡슐의 강도를 개선하기 위하여, 코어부 쉘층(21)보다 높은 탄성강도를 갖고, 하나 또는 하나 이상의 통공(220)을 포함하는 외부 쉘층(22);을 포함하는 구강용 캡슐을 제조할 수 있다. 이러한 본 발명의 다른 일 구현예에 따른 구강용 캡슐의 제조방법은 구강용 캡슐의 자체 강도를 개선하는 효과가 있기 때문에, 제조과정 중에 구강용 캡슐이 파괴되는 것을 방지하여, 생산성을 향상시킬 수 있는 효과가 있다. In the method of manufacturing the oral capsule according to another embodiment of the present invention, the average particle diameter is 15 to 50 mm, and the shell layer 20 includes a core part shell layer 21; In order to improve the strength of the oral capsule, it has an elastic strength higher than that of the core shell layer 21, and an outer shell layer 22 including one or more through holes 220; can be prepared for oral capsules including have. Since the method of manufacturing an oral capsule according to another embodiment of the present invention has the effect of improving the strength of the oral capsule, it prevents the oral capsule from being destroyed during the manufacturing process, thereby improving productivity. It works.

이하, 실시예를 통하여 본 발명의 구성 및 작용효과를 보다 구체적으로 설명한다. 그러나, 본 발명이 이들 실시예에만 한정되는 것이 아님은 당업자에게 있어서 자명한 사실이다.Hereinafter, the configuration and effects of the present invention will be described in more detail through examples. However, it is obvious to those skilled in the art that the present invention is not limited to these examples.

실시예Example

홍화씨유 72 중량%, 페퍼민트향 11 중량%, 윈터그린 2.3 중량%, 아스파탐 1.5 중량%, 구연산 2.7 중량%, 염화세틸피리디늄 3.5 중량%, 및 안식향나트륨 7 중량%을 포함하는 구강 세정 조성물; 및 정제수를 1: 86 부피비율로 혼합함으로써, 구강 세정액(11)을 준비하였다.An oral cleaning composition comprising 72% by weight of safflower seed oil, 11% by weight of peppermint, 2.3% by weight of winter green, 1.5% by weight of aspartame, 2.7% by weight of citric acid, 3.5% by weight of cetylpyridinium chloride, and 7% by weight of sodium benzoate; And purified water in a volume ratio of 1:86 to prepare an oral rinse solution (11).

한편, 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민 (triethanolamine alginate)이 각각 1: 2: 1의 중량비율로 혼합한 혼합 용액을 약 18 중량%의 농도로 정제수에 혼합하여, 수용액을 준비하였다.Meanwhile, a mixed solution of gellan gum, alginic acid, and triethanolamine alginate in a weight ratio of 1: 2: 1 was mixed with purified water at a concentration of about 18% by weight, to prepare an aqueous solution. .

상기 준비된 구강 세정액(11)에 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민 (triethanolamine alginate)의 혼합 용액을 투입하여 혼합한 후, 상기 혼합액을, 젖산칼슘 및 염화칼슘을 1: 2 중량 비율로 혼합한 2가 이상의 양이온성 금속염의 약 8 중량%의 농도의 수용액에 투입하여, 반응시킴으로써, 구강 세정액(11)을 포함하는 코어부 쉘층(21)을 제조하였다.After adding and mixing a mixed solution of gellan gum, alginic acid, and triethanolamine alginate to the prepared oral rinse 11, the mixed solution was mixed with calcium lactate and calcium chloride in a ratio of 1: 2 The core part shell layer 21 containing the oral rinse 11 was prepared by adding and reacting in an aqueous solution having a concentration of about 8% by weight of a divalent or higher cationic metal salt.

이어서, 상기 제조된 구강 세정액(11)을 포함하는 코어부 쉘층(21)을 도 3에 도시된 장치에 공급하고, 외부 쉘층 제조용 노즐(223)에는 젤라틴, 글리세린, D-소르비톨액, 및 나트륨셀룰로우즈설페이트를 포함하는 외부 쉘층 제조용 용액(222)을 공급하였다. 이 때, 상기 외부 쉘층 제조용 용액(222)은 젤라틴 55 중량%, 글리세린 25 중량%, D-소르비톨액 17 중량%, 및 나트륨셀룰로우즈설페이트 3 중량%를 포함하는 것을 사용하였다. 상기한 장치를 이용하여, 상기 외부 쉘층 제조용 용액(222)을 1회 비연속적으로 토출하여, 상기 제조된 구강 세정액(11)을 포함하는 코어부 쉘층(21)의 표면을 하나의 통공(220)을 포함하도록 코팅시킴으로써, 코어부(10)에 구강 세정액(11)을 포함하고, 쉘층(20)으로서 코어부 쉘층(21) 및 외부 쉘층(22)을 포함하는 구강용 캡슐(1)을 제조하였다. Subsequently, the core part shell layer 21 containing the prepared oral rinse solution 11 is supplied to the device shown in FIG. 3, and the nozzle 223 for manufacturing the outer shell layer includes gelatin, glycerin, D-sorbitol solution, and sodium cellulose. A solution 222 for preparing an outer shell layer containing Rhodes sulfate was supplied. At this time, the solution 222 for preparing the outer shell layer was used as containing 55% by weight of gelatin, 25% by weight of glycerin, 17% by weight of D-sorbitol solution, and 3% by weight of sodium cellulose sulfate. Using the above-described device, the outer shell layer preparation solution 222 is discontinuously discharged once, so that the surface of the core part shell layer 21 containing the prepared oral cleaning solution 11 is provided with a single through hole 220 By coating so as to include, the oral cavity capsule (1) including the oral cleaning solution 11 in the core portion 10 and comprising the core portion shell layer 21 and the outer shell layer 22 as the shell layer 20 was prepared. .

이렇게 제조된 구강용 캡슐은 평균 입경이 약 32.1 mm인 것을 확인할 수 있었다.It was confirmed that the oral capsule thus prepared had an average particle diameter of about 32.1 mm.

비교예 1(코어부 쉘층만을 포함하는 구강용 캡슐)Comparative Example 1 (oral capsule containing only the core part shell layer)

상기 실시예와 동일하게, 홍화씨유 72 중량%, 페퍼민트향 11 중량%, 윈터그린 2.3 중량%, 아스파탐 1.5 중량%, 구연산 2.7 중량%, 염화세틸피리디늄 3.5 중량%, 및 안식향나트륨 7 중량%을 포함하는 구강 세정 조성물; 및 정제수를 1: 86 부피비율로 혼합함으로써, 구강 세정액(11)을 준비하였다.Same as the above example, safflower seed oil 72% by weight, peppermint flavor 11% by weight, winter green 2.3% by weight, aspartame 1.5% by weight, citric acid 2.7% by weight, cetylpyridinium chloride 3.5% by weight, and sodium benzoate 7% by weight included Oral cleaning composition; And purified water in a volume ratio of 1:86 to prepare an oral rinse solution (11).

상기 준비된 구강 세정액(11)에 젤란검, 알긴산(alginic acid) 및 알긴산트리에탄올아민 (triethanolamine alginate)의 혼합 용액을 투입하여 혼합한 후, 상기 혼합액을, 젖산칼슘 및 염화칼슘을 1: 2 중량 비율로 혼합한 2가 이상의 양이온성 금속염의 약 8 중량%의 농도의 수용액에 투입하여, 반응시킴으로써, 코어부(10)에 구강 세정액(11)을 포함하고, 쉘층(20)으로서 코어부 쉘층(21)만을 갖는 구강용 캡슐을 제조하였다. After adding and mixing a mixed solution of gellan gum, alginic acid, and triethanolamine alginate to the prepared oral rinse 11, the mixed solution was mixed with calcium lactate and calcium chloride in a ratio of 1: 2 Into an aqueous solution having a concentration of about 8% by weight of a divalent or higher cationic metal salt and reacting, the oral rinse solution 11 is included in the core 10, and only the core shell layer 21 is used as the shell layer 20. A capsule for oral cavity was prepared.

이로써, 코어부 쉘층만을 포함하는 구강용 캡슐을 제조하였다.(통공은 존재하지 않음.) 이렇게 제조된 구강용 캡슐은 평균 입경이 약 34.3 mm인 것을 확인할 수 있었다.As a result, an oral capsule including only the core part shell layer was prepared. (No pores were present.) It was confirmed that the oral capsule thus prepared had an average particle diameter of about 34.3 mm.

비교예 2(외부 쉘층만을 포함하는 구강용 캡슐)Comparative Example 2 (oral capsule containing only the outer shell layer)

이어서, 상기 제조된 구강 세정액(11)을 도 3에 도시된 장치에 공급하고, 외부 쉘층 제조용 노즐(223)에는 젤라틴, 글리세린, D-소르비톨액, 및 나트륨셀룰로우즈설페이트를 포함하는 외부 쉘층 제조용 용액(222)을 공급하였다. 이 때, 상기 외부 쉘층 제조용 용액(222)은 젤라틴 55 중량%, 글리세린 25 중량%, D-소르비톨액 17 중량%, 및 나트륨셀룰로우즈설페이트 3 중량%를 포함하는 것을 사용하였다. 상기한 장치를 이용하여, 상기 외부 쉘층 제조용 용액(222)을 토출하여, 상기 제조된 구강 세정액(11)을 포함하도록 외부 쉘층(22)을 형성함으로써, 코어부(10)에 구강 세정액(11)을 포함하고, 쉘층(20)으로서 외부 쉘층(22)만을 갖는 구강용 캡슐을 제조하였다. Subsequently, the prepared oral rinse solution 11 is supplied to the apparatus shown in FIG. 3, and the nozzle 223 for manufacturing the outer shell layer includes gelatin, glycerin, D-sorbitol solution, and sodium cellulose sulfate. Solution 222 was supplied. At this time, the solution 222 for preparing the outer shell layer was used as containing 55% by weight of gelatin, 25% by weight of glycerin, 17% by weight of D-sorbitol solution, and 3% by weight of sodium cellulose sulfate. By using the above-described device, by discharging the outer shell layer preparation solution 222 to form the outer shell layer 22 to contain the prepared oral washing solution 11, the oral washing solution 11 in the core portion 10 Including, to prepare an oral capsule having only the outer shell layer 22 as the shell layer 20.

이로써, 쉘층으로서 외부 쉘층만을 포함하는 구강용 캡슐을 제조하였다.(통공은 존재하지 않음.) 이렇게 제조된 구강용 캡슐은 평균 입경이 약 32.4 mm인 것을 확인할 수 있었다.As a result, an oral capsule including only an outer shell layer as a shell layer was prepared. (No pores were present.) It was confirmed that the oral capsule thus prepared had an average particle diameter of about 32.4 mm.

시험예Test example

상기 실시예 및 비교예에서 제조된 구강용 캡슐에 대하여, 각각의 탄성강도를 측정하였다. 이 때, 상기 탄성강도는 242±20 ℃, 49±10 % RH에서 250 N 피로시험기(INSTRON사, E1000)를 사용하여 10 mm/min의 속도로 하중을 가해 최대 압축 하중(탄성 강도; N)을 측정하였다.For the oral capsules prepared in Examples and Comparative Examples, the elastic strength of each was measured. At this time, the elastic strength is the maximum compressive load (elastic strength; N) by applying a load at a speed of 10 mm/min using a 250 N fatigue tester (INSTRON, E1000) at 242±20°C and 49±10% RH. Was measured.

탄성강도(N)Elastic strength (N) 실시예 Example 142142 비교예 1Comparative Example 1 9292 비교예 2 Comparative Example 2 138138

상기 표 1의 결과에서 확인할 수 있는 바와 같이, 본 발명의 일 구현예에 따른 구강용 캡슐은 비교예 1 및 2와 대비하여 우수한 탄성강도를 갖는 바, 평균 입경이 약 32.9 mm의 상당히 큰 크기에도 우수한 탄성강도를 갖는 것을 확인할 수 있었다. 이로써, 구강 세정액의 저장 안정성을 향상시킬 수 있을 것으로 기대되는 바, 휴대성이 더욱 개선될 것으로 기대된다.As can be seen from the results of Table 1, the oral capsule according to an embodiment of the present invention has excellent elastic strength compared to Comparative Examples 1 and 2, and the average particle diameter is about 32.9 mm. It was confirmed that it has excellent elastic strength. As a result, it is expected that the storage stability of the oral rinse solution can be improved, and portability is expected to be further improved.

1: 구강용 캡슐
10: 코어부 20: 쉘층
11: 구강 세정액
21: 코어부 쉘층 22: 외부 쉘층
220: 통공
221: 타액 붕괴성 조성물
222: 외부 쉘층 제조용 용액
223: 외부 쉘층 제조용 노즐
3: 냉각액1: oral capsule
10: core part 20: shell layer
11: oral rinse
21: core part shell layer 22: outer shell layer
220: through hole
221: saliva disintegrating composition
222: solution for preparing an outer shell layer
223: nozzle for manufacturing an outer shell layer
3: coolant

Claims

A core part 10 comprising an oral cleaning liquid 11 obtained by mixing an oral cleaning composition and purified water in a volume ratio of 1: 50 to 90; And in the oral capsule (1) consisting of the shell layer (20), the oral capsule (1) will have an average particle diameter of 15 to 50 mm,
The shell layer 20 includes a core part shell layer 21; In order to improve the strength of the oral capsule, it has an elastic strength higher than that of the core part shell layer 21, and the outer shell layer 22 including one or more through holes 220; to include;
The oral capsule is a mixture of gellan gum, alginic acid, and alginic acid triethanolamine alginate in an oral rinse (11) in a weight ratio of 1: 1 to 5: 1 to 2, respectively, 15 to 20% by weight 5 to 10% by weight of a divalent or higher cationic metal salt in which calcium lactate and calcium chloride are mixed in a ratio of 1: 2 by mixing the mixture with purified water at the concentration of and mixing the mixture prepared in the form of an aqueous solution. Preparing a core part shell layer (21) comprising an oral rinse (11) by adding it to a divalent or higher cationic metal salt solution which is an aqueous solution having a concentration of and reacting; And
On the surface of the core part shell layer 21 containing the prepared oral washing liquid 11, using a nozzle 223 for producing an outer shell layer, gelatin 40 to 70% by weight, glycerin 15 to 35% by weight, D-sorbitol solution By discharging and coating a solution 222 for preparing an outer shell layer containing 10 to 20% by weight, and 1 to 10% by weight of sodium cellulose sulfate, the core part 10 contains the oral rinse solution 11, and the shell layer ( 20) is manufactured by a manufacturing method comprising the step of manufacturing an oral capsule (1) comprising a core portion shell layer (21) and an outer shell layer (22);
The process of discharging the outer shell layer manufacturing solution 222 using the nozzle 223 is performed discontinuously to form the outer shell layer 22 including one or more through holes 220; The through hole 220 of the outer shell layer 22 is filled with a saliva-disintegrating composition 221 comprising 300 to 500 parts by weight of D-mannitol and 10 to 80 parts by weight of gelatinized corn starch based on 100 parts by weight of crystalline cellulose. Is;
The divalent or higher cationic metal salt of the core part shell layer 21 and sodium cellulose sulfate of the outer shell layer 22 are bonded to each other, so that the core part shell layer 21 and the outer shell layer 22 are bonded to each other. To have;
The elastic strength of the outer shell layer 22 is 1 to 70% higher than that of the core shell layer 21, the elastic strength of the outer shell layer 22 is 90 to 150 N, and the core shell layer 21 ) Of 50 to 100 N (“elastic strength” refers to 242±20 ℃, 49±10% RH using a 250 N fatigue tester (INSTRON, E1000) at a speed of 10 mm/min. It is the maximum compressive load (elastic strength; N) measured by applying a load;
The core part shell layer 21 and the outer shell layer 22 have an average thickness after drying in the range of 0.3 to 0.7 mm, respectively.

delete