KR101207183B1 - Flame Retardant Polyester Composition with Enhanced Thermal Resistance - Google Patents

Abstract

The present invention is heat-resistant comprising 42 to 80% by weight of polyester, 5 to 30% by weight of phosphorus flame retardant, 1 to 15% by weight of nitrogen-based flame retardant, 0.5 to 5% by weight of layered silicate and 0.1 to 8% by weight of inorganic activator Disclosed is an excellent flame retardant polyester composition. The present invention has the effect of providing an environmentally friendly flame-retardant resin composition excellent in flame retardancy and heat resistance, free color expression at an economical cost.

Polyester, phosphorus flame retardant, nitrogen flame retardant, layered silicate, inorganic activator

Description

Flame Retardant Polyester Composition with Enhanced Thermal Resistance

The present invention relates to a flame retardant polyester composition having excellent heat resistance, and more particularly to a flame retardant polyester composition which is environmentally friendly and excellent in heat resistance by including a non-halogen flame retardant, a nitrogen flame retardant, a layered silicate and an inorganic activator. It is about.

Polyester has excellent mechanical, electrical, physical, and chemical properties, and has been applied to a wide range of fields such as automobiles, electrical, electronic devices, and office equipment. In particular, polybutylene terephthalate (Polybutylene terephthalate) is one of the five general-purpose engineering plastics due to its excellent electrical properties and excellent moldability is increasing its use.

Such polybutylene terephthalate resins have been imparted with flame retardancy by a method of separately adding an organic halogen flame retardant and / or auxiliary flame retardant in a field requiring flame retardancy because of its ability to burn well. However, halogen-based flame retardants containing elemental chlorine or bromine cause problems such as corrosion of the processing equipment and resin decomposition by hydrogen halide. In addition, toxic gases caused by a large amount of halogenated compounds generated in a fire cause personal and property damage. In addition, when the resin composition containing the organic halogen flame retardant and / or flame retardant aid is actually applied, the metal in contact with the molded article may be corroded to hinder the action of the part. For example, the contact metal of an electrical contact component is easily contaminated causing a change in electrical resistance. In addition, thermoplastic resins containing a halogen-based compound and / or an antimony compound-based flame retardant aid bring about a sharp decrease in tracking resistance, which is one of electrical properties.

Meanwhile, some European countries have proposed restrictions on the use of flame retardants, such as polybrominated biphenyls (PBBs) and polybrominated biphenylethers (PBDEs), due to fears of dioxin generation during fire and incineration. In addition, there have been attempts to strictly limit the use of harmful heavy metals, bromine-based flame retardants, and antimony compounds in accordance with environmental stability evaluations in automotive and electrical and electronic components. Therefore, there is an urgent need for the development of technology for non-halogen flame retardants.

Conventionally, as flame retardants of non-halogen flame retardant polybutylene terephthalate, U.S. Pat. Inorganic filler, Japanese Patent Application Laid-open No. Hei 8-259787 discloses a case where phosphoric acid ester and melamine cyanurate, and U.S. Patent No. 3,878,162 are used together with red phosphorus and phosphate ester.

However, such a technique requires a large amount of flame retardant in order to obtain a desirable degree of flame retardancy, which has the disadvantage of causing excessive cost increase, physical property deterioration, heat resistance decrease and electrical property deterioration. In particular, the flame retardant containing red generates phosphine gas even by a small amount of water contact during processing due to the high temperature stability deterioration, the flame retardant composition containing red is limited in the product color due to the red expression by the red itself.

The present inventors have continually researched to solve the above problems, and when the polyester composition comprises a halogen-based flame retardant and phosphorus-based flame retardant, nitrogen-based flame retardant, layered silicate and inorganic activator, The present invention has been completed in recognition of the fact that it exhibits an effective flame retardant increase, does not cost excessively, exhibits balanced physical properties without deteriorating heat resistance, and is free of color expression and environmentally friendly.

Accordingly, it is an object of the present invention to provide an environmentally friendly flame retardant polyester composition that exhibits excellent flame retardancy, exhibits balanced physical properties without excessive cost increase and deterioration of heat resistance, is free of color representation, and excellent in heat resistance.

The above and other objects of the present invention can be achieved by the present invention described below.

The flame retardant polyester composition provided by the present invention comprises 42 to 80 wt% polyester, 5 to 30 wt% phosphorus flame retardant, 1 to 15 wt% nitrogen based flame retardant, 0.5 to 5 wt% layered silicate and 0.1 to 0.1 inorganic activator To 8% by weight.

In the above, the phosphorus-based flame retardant is preferably a compound selected from the group consisting of liquid or powdered phosphate ester, phosphate, pyro phosphate, phosphonate, metal-substituted phosphinate and phosphonate.

The nitrogen-based flame retardant synergist is a group of compounds having a triazine structure consisting of melamine, melamine cyanurate and triphenyl isocyanurate, and melamine phosphate, melamine pyrophosphate ( It is preferably selected from the group of nitrogen-phosphorus containing flame retardants consisting of melamine pyrophosphate, ammonium polyphosphate, alkylamine phosphate, and piperazine acid polyphosphate.

The layered silicate is preferably selected from the group consisting of smectite-based materials, vermiculite-based materials, illite-based materials and derivatives thereof.

The inorganic activator is a compound selected from hydrotalcite, aluminum hydrate, magnesium hydrate, calcium hydrate, zinc sulfide, zinc oxide, magnesium calcium carbonate, magnesium carbonate, calcium carbonate, zinc borate, zinc borate hydrate, or magnesium sulfate hydrate. It is preferable.

The flame retardant polyester composition according to the present invention is a resin composition excellent in flame retardancy, free of color expression, excellent in heat resistance, and environmentally friendly. It also exhibits balanced physical properties without excessive cost increase and heat resistance deterioration.

The flame retardant polyester composition according to the present invention is 42 to 80% by weight of polyester, 5 to 30% by weight of phosphorus flame retardant, 1 to 15% by weight of nitrogen-based flame retardant, 0.5 to 5% by weight of layered silicate and 0.1 to 8 inorganic activator Contains weight percent. In the flame retardant polyester composition, excellent flame retardancy is obtained without deteriorating other physical properties such as heat resistance without using a halogen flame retardant in order to impart environmentally friendly flame retardancy.

The polyester used in the composition of the present invention is preferably at least one selected from the group consisting of polyethylene terephthalate, polypropylene terephthalate, polybutylene terephthalate, and the like, in particular, polybutylene terephthalate is preferred, and more Preferably, it is a copolymer which consists of 70-100 weight% of butylene terephthalate units, or the resin compound which contains 70 weight% or more of polybutylene terephthalates. The polybutylene terephthalate may be obtained through polymerization by esterification of butane-1,4-diol and terephthalic acid or transesterification of butane-1,4-diol and dimethyl terephthalate. In the above, the copolymer comprising a butylene terephthalate repeat unit may be formed by transesterification of butylene terephthalate and other comonomers, for example, ethylene terephthalate or propylene terephthalate. The resin blend may also be a mixture of polybutylene terephthalate and other polyalkylene terephthalates such as polyethylene terephthalate or polypropylene terephthalate.

In addition, the polyester composition of the present invention may use a modified polybutylene terephthalate in order to improve the impact strength, polytetramethylene glycol (PTMG), polypropylene glycol (Polypropylene) at the time of polymerization using chemical modification modified polybutylene terephthalate copolymerized with glycol, PPG), polyethylene glycol (PEG), low molecular weight aliphatic polyester, low molecular weight aliphatic polyamide, and the like. ) And modified polybutylene terephthalate may be used.

Examples of the impact modifier include m-acrylonitrile-butadiene-styrene (MBS) having a core of rubber and a shell of plastic, all acrylic rubber, and ethylene-propylene-diene. Ethylene-propylene-diene monomer copolymer (EPDM), styrene-butadiene-styrene (SBS), styrene-isoprene-styrene SIS, styrene-butadiene -butadien, SB), styrene-isoprene rubber, ethylene-vinylacetate (EVA), ethylene-ethyl acrylate (Ethylene ethyl acrylate, EEA), ethylene-vinylalchol, EVOH) copolymer, polybutylene terephtalate (PBT) elastomer, polyethylene terephtalate PET elastomer and nylon (Nylon) elastomer selected from the group The. In addition to the above-mentioned resins, there is no particular limitation as long as the resin can improve the impact strength.

When the modified polybutylene terephthalate is prepared by adding the impact modifier, a compatibilizer or a dispersant may be further added. The compatibilizer or dispersant may include maleic anhydride, oxazoline, or an epoxy group on the terminal group or the side chain. One or more types can be selected from the group which has oligomer and polymer which have. The compatibilizer is represented by a main chain or side chain modification additive, and the main chain is not particularly limited.

In addition, polycarbonate, polyethylene terephthalate, phenol resin, or the like may be blended for the purpose of toughening polyester, improving appearance, or improving fluidity. Can be blended with Also. Premodified polybutylene terephthalate may be used, or pure polybutylene terephthalate and other resins may be added and mixed together before melt kneading.

The content of the polyester is preferably 42 to 80% by weight, more preferably 50 to 70% by weight based on the total composition.

The composition of the present invention comprises a halogen-based flame retardant or a phosphorus-based flame retardant that is not in order to impart environmentally friendly flame retardant. The phosphorus flame retardant may be at least one compound selected from the group consisting of liquid or powdered phosphate esters, phosphates chemically similar to the phosphate esters, pyrophosphate, phosphonates, metal-substituted phosphinates and phosphonates. . As the phosphate ester compound, triphenyl phosphate (TPP), trixylenyl phosphate (TXP), tricresyl phosphate (TCP), etc. may be mainly used as monomers having an aromatic group. Resorcinyl diphenyl phosphate (RDP), phenyl diresorcinyl phosphate, cresyl diphenyl phosphate, xylenyl diphenyl phosphate Xylenyl diphenyl phosphate), phenyl di (isopropylphenyl) phosphate, and the like may be used. Oligomers or polyphosphates more than dimers can be used. In the present invention, phosphorus-based flame retardants other than those mentioned above may be used alone or in combination of one or more thereof. In addition to the above-mentioned phosphate ester compounds, a phosphorus nitrogen composite flame retardant, a phosphazine compound, or the like can also be used. The compounds may be in liquid or solid form.

The content of the phosphorus flame retardant is preferably 5 to 30% by weight based on the total composition, since the effect of synergistic flame retardation is lowered at less than 5% by weight, and heat resistance is lowered at more than 30% by weight. More preferably, it is 7-20 weight%.

Nitrogen-based flame retardants used in the present invention include nitrogen-containing flame retardants or nitrogen-phosphorus-containing flame retardants. Nitrogen-containing flame retardants include compounds having a triazine structure, such as melamine, melamine cyanurate and triphenyl isocyanurate, and nitrogen-phosphorus-containing flame retardants include melamine phosphate, Melamine pyrophosphate, ammonium polyphosphate, ammonium polyphosphate, alkylamine phosphate, alkylamine phosphate, piperazine acid polyphosphate, and the like, may be used alone or in combination. In addition, various nitrogen-based flame retardants and / or intumescent additives (e.g., polyhydric compounds such as dipentaerythritol, starch, dextrin, inorganic acids, etc.) may be used alone or in combination of two or more thereof. Can be. The content of the nitrogen-based flame retardant increasing agent is preferably 1 to 15% by weight of the total resin composition, and most preferably in an amount of 2 to 12% by weight.

The composition of the present invention comprises a layered silicate for improving heat resistance and delaying combustion. The layered silicate may be a layered illite such as montmorillonite, nontronite, batellite, boneconscote, hectorite, saponite, or kniteite, smectite-based material, vermiculite-based material, or radicalite. System substances and derivatives thereof. The layered silicates may be used alone or in combination. More preferred are montmorillonite, nontronite, baydelite, vonconscote, hectorite, saponite and kenite.

The content of the layered silicate is preferably 0.5 to 5% by weight based on the total composition, since the flame retardant synergistic effect is lowered at less than 0.5% by weight, and the rigidity is lowered when it exceeds 5% by weight. More preferably, it is 1-4 weight%.

The composition of the present invention includes an inorganic activator for the flame retardant activation in addition to the non-halogen flame retardant as described above, specific examples of the inorganic activator include hydrotalcite, aluminum hydrate, magnesium hydrate, calcium hydrate, zinc sulfide, zinc oxide , Magnesium calcium carbonate, magnesium carbonate, calcium carbonate, zinc borate, zinc borate hydrate, or magnesium sulfate hydrate.

The content of the inorganic activator is preferably 0.1 to 8% by weight based on the total composition, since the flame retardant activation effect is lowered at less than 0.1% by weight, and the decomposition of the resin is promoted when it is more than 8% by weight. More preferably, it is 0.3-5 weight%.

Flame-retardant polyester composition as described above is a silicone-based flame retardant, lubricant, antioxidant, light stabilizer, hydrolysis stabilizer, mold release agent, pigment, antistatic agent, conductivity imparting agent, EMI shielding agent, magnetic imparting agent, mineral within the range that physical properties are not damaged It may further include one or more additives selected from the group consisting of fillers, crosslinking agents, antibacterial agents, processing aids, metal deactivators, depressants, fluorine-based antidropping agents, abrasion resistant antiwear agents, coupling agents, and the like, to impart other physical properties.

The compositions of the present invention are first mixed with the above additives in a super mixer, and then a conventional twin-screw extruder, single-screw extruder, roll-mills, kneader After kneading by melt kneading using one of a variety of mixing processing equipment such as) or a banbury mixer, pellets were obtained by a pelletizer, and then sufficiently dried in a dehumidifying dryer or a hot air dryer, followed by injection molding to measure physical properties.

In addition, the present invention provides an electrical component, an electronic component, an automotive component, and an industrial molded article including the flame retardant polyester composition having excellent heat resistance as described above.

Hereinafter, the present invention will be described in more detail with reference to the following examples, but the scope of the present invention is not limited to the examples.

[Examples 1 to 6 and Comparative Examples 1 to 4]

After mixing according to the ingredients and contents shown in Table 1, the mixture was mixed well by a super mixer, melt-kneaded in a twin-screw extruder, pelletized, dried, injection-molded, and sufficiently conditioned at room temperature. Physical properties of the specimens were measured in the following manners and the results are shown in Table 1.

◎ Tensile strength and elongation: It was measured by ASTM D638 method.

◎ Heat deflection temperature (HDT): measured by ASTM D648 method using a load of 18.6kgf / cm ² .

◎ Izod Impact was measured by ASTM D256 method.

◎ Flame retardancy: Measured by UL 94 test, a method defined by Underwriter's Laboratory Inc. of the United States, which remains after 10 seconds of flame infection of the burner on a vertically sized specimen. It is a method of evaluating flame retardancy from time or drip. Afterflaming time is the length of time that the specimen continues flame-burning after the ignition source is far away, and the surface of the drip is dripping from the specimen about 300 mm below the bottom of the specimen. Determined by complexation by water, the flame retardancy grade is divided according to the table below.

division V2 V1 V0 HB Residual flame time of each sample 30 seconds or less 30 seconds or less Less than 10 seconds Flame retardant 5 Total residue time of the sample 250 seconds or less 250 seconds or less 50 seconds or less Ignition of cotton by drip has exist none none

◎ Tracking Resistance: Insulator may cause current on the surface between two electrodes due to contamination or corrosion, and to measure the resistance of the insulator against such electric current, and test the standard pollutants by ASTM D2863 method. The highest voltage (CTI) without tracking after dropping on was measured.

◎ Color Representation: Compared with natural colors.

◎ Phosphine gas generation amount: The generation amount of phosphine gas after heating at 150 ° C. for 1 hour was measured.

      * PBT: GP-2000 (LG Chemical Products)

      * PET: BB-8055 (SK Chemicals)

      * Layered silicate: Cloisite 44A (SCP product)

      * Inorganic activator 1: hydrotalcite (DHT, Kyowa product)

      * Inorganic activator 2: Zinc oxide (ZEHUI product)

As shown in Table 1, Examples including a non-halogen flame retardant, nitrogen-based flame retardant, layer silicate and inorganic activator are Comparative Example 1 containing a halogen flame retardant, Comparative Example comprising an inorganic and inorganic activator 2, and Comparative Example 3, which contains a non-halogen flame retardant but does not include a layered silicate, compared to Comparative Example 4, which includes a non-halogen flame retardant, a layered silicate and an inorganic activator but does not include a nitrogen-based flame retardant It can be seen that it exhibits effective flame retardancy without generating gas, and that physical properties of tensile strength, elongation, heat deformation temperature, impact strength and tracking resistance are not lowered compared to the comparative example, and color expression is free.

Claims (14)

42 to 80 wt% polyester, 5 to 30 wt% phosphorus flame retardant, 1 to 15 wt% nitrogen based flame retardant, 0.5 to 4 wt% layered silicate and 0.1 to 8 wt% inorganic activator, The polyester is a copolymer comprising 70 to 100% by weight of butylene terephthalate repeating unit or a resin mixture consisting of 70 to 100% by weight of polybutylene terephthalate and the remaining polyalkylene terephthalate, Flame-retardant polyester composition characterized in that the phosphorus flame retardant is a compound selected from the group consisting of liquid or powdered phosphate ester, phosphate, pyro phosphate, phosphonate, metal-substituted phosphinate and phosphonate. delete The method of claim 1, In the copolymer including the butylene terephthalate repeat unit, the remaining repeat unit is an ethylene terephthalate repeat unit or a propylene terephthalate repeat unit, and the remaining polyalkylene terephthalate in the resin mixture is polyethylene terephthalate or polypropylene terephthalate. Flame retardant polyester composition, characterized in that. The method of claim 1, The copolymer including the butylene terephthalate repeating unit is a butylene terephthalate monomer, polytetramethylene glycol (PTMG), polypropylene glycol (PPG), polyethylene glycol (PE), low Flame retardant polyester composition, characterized in that formed by copolymerizing at least one comonomer selected from the group consisting of a molecular weight aliphatic polyester, and a low molecular weight aliphatic polyamide. delete The method of claim 1, The phosphate ester is triphenyl phosphate (TPP), trixylenyl phosphate (TXP), tricresyl phosphate (TCP), resorcinyl diphenyl phosphate (RDP) , Phenyl diresorcinyl phosphate, Cresyl diphenyl phosphate, Xylenyl diphenyl phosphate, Phenyl di (isopropylphenyl) phosphate phosphate), and oligomers or polyphosphates of at least two dimers thereof. The method of claim 1, The nitrogen-based flame retardant synergist is a group of compounds having a triazine structure consisting of melamine, melamine cyanurate and triphenyl isocyanurate, and melamine phosphate, melamine pyrophosphate ( Flame-retardant polyester, characterized in that selected from the group of nitrogen-phosphorous flame retardant consisting of melamine pyrophosphate, ammonium polyphosphate, alkylamine phosphate, and piperazine acid polyphosphate Composition. The method of claim 1, The layered silicate is selected from the group consisting of smectite-based materials, vermiculite-based materials, illite-based materials and derivatives thereof. 9. The method of claim 8, The smectite-based material is selected from the group consisting of montmorillonite, nontronite, batellite, vonconscote, hectorite, saponite and keniteite, and the layered illite-based material is redicite Flame retardant polyester composition. The method of claim 1, The inorganic activator is selected from the group consisting of hydrotalcite, aluminum hydrate, magnesium hydrate, calcium hydrate, zinc sulfide, zinc oxide, magnesium calcium carbonate, magnesium carbonate, calcium carbonate, zinc borate, zinc borate hydrate, or magnesium sulfate hydrate. Flame retardant polyester composition characterized in that it further comprises one or more additives. The method of claim 1, The flame retardant polyester composition is a silicone flame retardant, lubricant, antioxidant, light stabilizer, hydrolysis stabilizer, mold release agent, pigment, antistatic agent, conductivity imparting agent, EMI shielding agent, magnetic imparting agent, mineral filler, crosslinking agent, antibacterial agent, processing aid, metal Flame retardant polyester composition characterized in that it further comprises at least one additive selected from the group consisting of an inactivating agent, a depressant, a fluorine-based anti-dropping agent, a friction wear-resistant agent, and a coupling agent. The method of claim 1, The flame retardant polyester composition is a flame retardant polyester composition, characterized in that it further comprises an impact modifier. The method of claim 12, The impact modifiers are m-acrylonitrile-butadiene-styrene (MBS) having a core structure of rubber and a shell plastic, and all acrylic rubber and ethylene-propylene-diene monomers. Ethylene-propylene-diene monomer copolymer (EPDM), styrene-butadien-styrene (SBS), styrene-isoprene-styrene SIS, styrene-butadiene butadien, SB), styrene-isoprene rubber, ethylene-vinylacetate (EVA), ethylene-ethyl acrylate (Ethylene ethyl acrylate, EEA), ethylene-vinylalchol, EVOH) copolymer, polybutylene terephtalate (PBT) -based elastomer, polyethylene terephtalate PET-based elastomer and nylon (Nylon) elastomer selected from the group consisting of Flame retardant polyester composition, characterized in that. 14. A part made from a material comprising a flame retardant polyester composition according to any one of claims 1, 3, 4 or 6-13.