JP6450148B2 - Resin composition for sealing organic electroluminescence display element, resin sheet for sealing organic electroluminescence display element, and organic electroluminescence display element - Google Patents
Resin composition for sealing organic electroluminescence display element, resin sheet for sealing organic electroluminescence display element, and organic electroluminescence display element Download PDFInfo
- Publication number
- JP6450148B2 JP6450148B2 JP2014224465A JP2014224465A JP6450148B2 JP 6450148 B2 JP6450148 B2 JP 6450148B2 JP 2014224465 A JP2014224465 A JP 2014224465A JP 2014224465 A JP2014224465 A JP 2014224465A JP 6450148 B2 JP6450148 B2 JP 6450148B2
- Authority
- JP
- Japan
- Prior art keywords
- display element
- organic
- resin
- sealing
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、透明性及びバリア性に優れる有機エレクトロルミネッセンス表示素子封止用樹脂組成物に関する。また、本発明は、該有機エレクトロルミネッセンス表示素子封止用樹脂組成物を用いてなる有機エレクトロルミネッセンス表示素子封止用樹脂シート及び有機エレクトロルミネッセンス表示素子に関する。 The present invention relates to a resin composition for sealing an organic electroluminescence display device having excellent transparency and barrier properties. Moreover, this invention relates to the resin sheet for organic electroluminescent display element sealing which uses this resin composition for organic electroluminescent display element sealing, and an organic electroluminescent display element.
有機エレクトロルミネッセンス（以下、「有機ＥＬ」ともいう）表示素子は、互いに対向する一対の電極間に有機発光材料層が挟持された積層体構造を有し、この有機発光材料層に一方の電極から電子が注入されるとともに他方の電極から正孔が注入されることにより有機発光材料層内で電子と正孔とが結合して発光する。このように有機ＥＬ表示素子は自己発光を行うことから、バックライトを必要とする液晶表示素子等と比較して視認性がよく、薄型化が可能であり、しかも直流低電圧駆動が可能であるという利点を有している。 An organic electroluminescence (hereinafter, also referred to as “organic EL”) display element has a laminated structure in which an organic light emitting material layer is sandwiched between a pair of electrodes facing each other, and the organic light emitting material layer is formed from one electrode on the organic light emitting material layer. When electrons are injected and holes are injected from the other electrode, the electrons and holes are combined in the organic light emitting material layer to emit light. Thus, since the organic EL display element performs self-emission, it has better visibility than a liquid crystal display element that requires a backlight, can be reduced in thickness, and can be driven by a DC low voltage. Has the advantage.
有機ＥＬ表示素子を構成する有機発光材料層や電極は、水分や酸素等により特性が劣化しやすいという問題がある。従って、実用的な有機ＥＬ表示素子を得るためには、有機発光材料層や電極を大気と遮断して長寿命化を図る必要がある。有機発光材料層や電極を大気と遮断する方法としては、封止剤を用いて有機ＥＬ表示素子を封止することが行われている（例えば、特許文献１）。有機ＥＬ表示素子を封止剤で封止する場合、通常、水分や酸素等の透過を充分に抑えるため、有機発光材料層を有する積層体上にパッシベーション膜と呼ばれる無機膜を設け、該無機膜上を封止剤で封止する方法が用いられている。 The organic light-emitting material layer and electrodes constituting the organic EL display element have a problem that the characteristics are easily deteriorated by moisture, oxygen, and the like. Therefore, in order to obtain a practical organic EL display element, it is necessary to extend the life by blocking the organic light emitting material layer and the electrode from the atmosphere. As a method for blocking the organic light emitting material layer and the electrode from the atmosphere, an organic EL display element is sealed with a sealant (for example, Patent Document 1). When sealing an organic EL display element with a sealant, an inorganic film called a passivation film is usually provided on a laminate having an organic light emitting material layer in order to sufficiently suppress the transmission of moisture, oxygen, and the like. A method of sealing the top with a sealant is used.
近年、有機発光材料層から発せられた光を、発光素子を形成した基板面側から取り出すボトムエミッション方式の有機ＥＬ表示素子に代わって、有機発光層の上面側から光を取り出すトップエミッション方式の有機ＥＬ表示素子が注目されている。この方式は、開口率が高く、低電圧駆動となることから、長寿命化に有利であるという利点がある。このようなトップエミッション方式の有機ＥＬ表示素子では、発光層の上面側が透明であることが必要であることから、発光素子の上面側に透明な封止樹脂を介してガラス等の透明防湿性基材を積層することにより封止している（例えば、特許文献２参照）。
しかしながら、このようなトップエミッション方式の有機ＥＬ表示素子では、光の取り出し方向を遮蔽してしまわないようにするために乾燥剤を配置するスペースがなく、充分な防湿効果が得られにくく寿命が短くなるという問題があった。
In recent years, instead of a bottom emission type organic EL display element that extracts light emitted from an organic light emitting material layer from the side of the substrate surface on which the light emitting element is formed, a top emission type organic element that extracts light from the upper surface side of the organic light emitting layer is used. EL display elements have attracted attention. This method has an advantage that it has a high aperture ratio and is driven at a low voltage, which is advantageous for extending the life. In such a top emission type organic EL display element, since the upper surface side of the light emitting layer needs to be transparent, a transparent moisture-proof substrate such as glass is interposed on the upper surface side of the light emitting element via a transparent sealing resin. It seals by laminating | stacking a material (for example, refer patent document 2).
However, in such a top emission type organic EL display element, there is no space for disposing a desiccant so as not to shield the light extraction direction, and it is difficult to obtain a sufficient moisture-proofing effect and the life is short. There was a problem of becoming.
有機ＥＬ表示素子封止用樹脂組成物のバリア性（透湿防止性）を向上させる方法として、樹脂にタルクやシリカ等の無機充填剤を分散させる方法が知られている（例えば、特許文献３）が、樹脂にこのような無機充填剤を分散した組成物は一般的に透明性に劣るものとなる。また、透明性を改善するために無機充填剤の粒子径を可視光線の波長よりも小さくすることも試みられているが、透明性を得られる程度に無機充填剤が分散されたとしても、バリア性が不充分となるという問題があった。 As a method for improving the barrier property (moisture permeation prevention property) of the resin composition for sealing an organic EL display element, a method in which an inorganic filler such as talc or silica is dispersed in the resin is known (for example, Patent Document 3). However, a composition in which such an inorganic filler is dispersed in a resin is generally inferior in transparency. In addition, in order to improve transparency, attempts have been made to make the particle size of the inorganic filler smaller than the wavelength of visible light, but even if the inorganic filler is dispersed to such an extent that transparency can be obtained, the barrier There was a problem that the sex became insufficient.
本発明は、透明性及びバリア性に優れる有機エレクトロルミネッセンス表示素子封止用樹脂組成物を提供することを目的とする。また、本発明は、該有機エレクトロルミネッセンス表示素子封止用樹脂組成物を用いてなる有機エレクトロルミネッセンス表示素子封止用樹脂シート及び有機エレクトロルミネッセンス表示素子を提供することを目的とする。 An object of this invention is to provide the resin composition for organic electroluminescent display element sealing excellent in transparency and barrier property. Moreover, an object of this invention is to provide the organic electroluminescent display element sealing resin sheet and organic electroluminescent display element which use this organic electroluminescent display element sealing resin composition.
本発明は、ポリイソブチレン骨格を有する樹脂と、炭素数１０以上の脂肪酸で表面処理された層状複水酸化物とを含有する有機エレクトロルミネッセンス表示素子封止用樹脂組成物である。
以下に本発明を詳述する。
The present invention is a resin composition for sealing an organic electroluminescence display element, which contains a resin having a polyisobutylene skeleton and a layered double hydroxide surface-treated with a fatty acid having 10 or more carbon atoms.
The present invention is described in detail below.
本発明者らは、ポリイソブチレン骨格を有する樹脂と、特定の表面処理を施した層状複水酸化物とを組み合わせて用いることにより、高い透明性を保持しながら、優れたバリア性を発現できる有機ＥＬ表示素子封止用樹脂組成物を得ることができることを見出し、本発明を完成させるに至った。 The present inventors use a combination of a resin having a polyisobutylene skeleton and a layered double hydroxide subjected to a specific surface treatment, so that an organic material that can exhibit excellent barrier properties while maintaining high transparency. The present inventors have found that an EL display element sealing resin composition can be obtained and have completed the present invention.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、ポリイソブチレン骨格を有する樹脂を含有する。ポリイソブチレン骨格を有する樹脂は、イソブテンの重合による長鎖状炭化水素によって構成され、バリア性及び接着性が高い。
上述したように、上記ポリイソブチレン骨格を有する樹脂を、特定の表面処理を施した層状複水酸化物と組み合わせて含有することにより、本発明の有機ＥＬ表示素子封止用樹脂組成物は、特に透明性とバリア性とに優れるものとなる。また、上記ポリイソブチレン骨格を有する樹脂は、本発明の有機ＥＬ表示素子封止用樹脂組成物の柔軟性や耐屈曲性を向上させる効果も有する。
The resin composition for sealing an organic EL display device of the present invention contains a resin having a polyisobutylene skeleton. The resin having a polyisobutylene skeleton is composed of long-chain hydrocarbons obtained by polymerization of isobutene, and has high barrier properties and adhesiveness.
As described above, by containing the resin having the polyisobutylene skeleton in combination with a layered double hydroxide subjected to a specific surface treatment, the organic EL display element sealing resin composition of the present invention is particularly It will be excellent in transparency and barrier properties. The resin having the polyisobutylene skeleton also has an effect of improving the flexibility and flex resistance of the organic EL display element sealing resin composition of the present invention.
上記ポリイソブチレン骨格を有する樹脂としては、例えば、イソブテンのホモポリマーや、イソブテンと該イソブテンに対して数重量％の程度のイソプレンとを共重合してなるイソブチレン／イソプレン共重合樹脂や、該イソブチレン／イソプレン共重合樹脂におけるイソプレンに由来する二重結合部位を架橋してなる、いわゆるブチルゴム等が挙げられる。 Examples of the resin having a polyisobutylene skeleton include an isobutene homopolymer, an isobutylene / isoprene copolymer resin obtained by copolymerizing isobutene and isoprene of several weight% with respect to the isobutene, and the isobutylene / Examples thereof include so-called butyl rubber obtained by crosslinking a double bond site derived from isoprene in the isoprene copolymer resin.
上記ポリイソブチレン骨格を有する樹脂全体の重量平均分子量の好ましい下限は１０万、好ましい上限は５０万である。上記ポリイソブチレン骨格を有する樹脂全体の重量平均分子量が１０万未満であると、樹脂の凝集力が不足し、得られる有機ＥＬ表示素子封止用樹脂組成物が接着性に劣るものとなることがある。上記ポリイソブチレン骨格を有する樹脂全体の重量平均分子量が５０万を超えると、得られる有機ＥＬ表示素子封止用樹脂組成物が貼り合わせを行う際の貼付性に劣るものとなることがある。上記ポリイソブチレン骨格を有する樹脂全体の重量平均分子量のより好ましい下限は１１万、より好ましい上限は４０万である。
なお、本明細書において、上記「重量平均分子量」は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）で測定を行い、ポリスチレン換算により求められる値である。ＧＰＣによってポリスチレン換算による重量平均分子量を測定する際に用いるカラムとしては、例えば、Ｓｈｏｄｅｘ ＬＦ−８０４（昭和電工社製）等が挙げられる。
The preferable lower limit of the weight average molecular weight of the whole resin having the polyisobutylene skeleton is 100,000, and the preferable upper limit is 500,000. When the weight average molecular weight of the whole resin having the polyisobutylene skeleton is less than 100,000, the resin cohesive force is insufficient, and the resulting resin composition for sealing an organic EL display element may have poor adhesion. is there. When the weight average molecular weight of the whole resin having the polyisobutylene skeleton exceeds 500,000, the obtained organic EL display element sealing resin composition may be inferior in pasting property when pasting. The minimum with a more preferable weight average molecular weight of the whole resin which has the said polyisobutylene skeleton is 110,000, and a more preferable upper limit is 400,000.
In the present specification, the “weight average molecular weight” is a value determined by polystyrene conversion after measurement by gel permeation chromatography (GPC). As a column used when measuring the weight average molecular weight by polystyrene conversion by GPC, Shodex LF-804 (made by Showa Denko KK) etc. are mentioned, for example.
上記ポリイソブチレン骨格を有する樹脂は、重量平均分子量の異なる複数の樹脂を含有することが好ましく、重量平均分子量が２０万〜５０万である樹脂と、重量平均分子量が２万〜１５万である樹脂とからなることがより好ましい。上記ポリイソブチレン骨格を有す
る樹脂として、重量平均分子量が５０万を超える樹脂や重量平均分子量が２万未満である樹脂を含有すると、得られる有機ＥＬ表示素子封止用樹脂組成物の接着性や貼り合わせを行う際の貼付性が低下することがある。上記ポリイソブチレン骨格を有する樹脂として、重量平均分子量が２０万〜５０万である樹脂と、重量平均分子量が２万〜１５万である樹脂との混合物を用いることで、樹脂の凝集力を保った状態で良好な貼付性を得ることができる。
The resin having a polyisobutylene skeleton preferably contains a plurality of resins having different weight average molecular weights, a resin having a weight average molecular weight of 200,000 to 500,000, and a resin having a weight average molecular weight of 20,000 to 150,000. More preferably, it consists of: When the resin having a polyisobutylene skeleton contains a resin having a weight average molecular weight of more than 500,000 or a resin having a weight average molecular weight of less than 20,000, the adhesiveness and adhesion of the resulting resin composition for sealing an organic EL display element Adhesiveness when performing the alignment may be reduced. By using a mixture of a resin having a weight average molecular weight of 200,000 to 500,000 and a resin having a weight average molecular weight of 20,000 to 150,000 as the resin having the polyisobutylene skeleton, the cohesive strength of the resin was maintained. Good pastability can be obtained in the state.
上記ポリイソブチレン骨格を有する樹脂が、上記重量平均分子量が２０万〜５０万である樹脂と、上記重量平均分子量が２万〜１５万である樹脂とからなる場合、含有割合としては、重量比で、上記重量平均分子量が２０万〜５０万である樹脂：上記重量平均分子量が２万〜１５万である樹脂＝１：１〜１：９であることが好ましい。上記重量平均分子量が２０万〜５０万である樹脂と、上記重量平均分子量が２万〜１５万である樹脂との含有割合がこの範囲であることにより、得られる有機ＥＬ表示素子封止用樹脂組成物が特に接着性及び貼付性に優れるものとなる。 When the resin having the polyisobutylene skeleton is composed of a resin having a weight average molecular weight of 200,000 to 500,000 and a resin having a weight average molecular weight of 20,000 to 150,000, the content ratio is as follows: The resin having a weight average molecular weight of 200,000 to 500,000: The resin having a weight average molecular weight of 20,000 to 150,000 is preferably 1: 1 to 1: 9. Resin for sealing an organic EL display element obtained by the content ratio of the resin having a weight average molecular weight of 200,000 to 500,000 and the resin having a weight average molecular weight of 20,000 to 150,000 in this range. The composition is particularly excellent in adhesiveness and sticking property.
上記重量平均分子量が２０万〜５０万である樹脂のうち市販されているものとしては、例えば、Ｏｐｐａｎｏｌ Ｂ３０ＳＦ、Ｏｐｐａｎｏｌ Ｂ５０、Ｏｐｐａｎｏｌ Ｂ５０ＳＦ（いずれもＢＡＳＦ社製）等が挙げられる。
上記重量平均分子量が２万〜１５万である樹脂のうち市販されているものとしては、例えば、Ｏｐｐａｎｏｌ Ｂ１０ＳＦＮ、Ｏｐｐａｎｏｌ Ｂ１０Ｎ、Ｏｐｐａｎｏｌ Ｂ１１ＳＦＮ、Ｏｐｐａｎｏｌ Ｂ１２ＳＦＮ、Ｏｐｐａｎｏｌ Ｂ１２Ｎ、Ｏｐｐａｎｏｌ Ｂ１３ＳＦＮ、Ｏｐｐａｎｏｌ Ｂ１４ＳＦＮ、Ｏｐｐａｎｏｌ Ｂ１４Ｎ、Ｏｐｐａｎｏｌ Ｂ１５ＳＦＮ、Ｏｐｐａｎｏｌ Ｂ１５Ｎ（いずれもＢＡＳＦ社製）、テトラックス ３Ｔ、テトラックス ４Ｔ、テトラックス ５Ｔ、テトラックス ６Ｔ、ハイモール ４Ｈ、ハイモール ５Ｈ、ハイモール ５．５Ｈ、ハイモール ６Ｈ（いずれもＪＸ日鉱日石エネルギー社製）等が挙げられる。
Examples of commercially available resins having a weight average molecular weight of 200,000 to 500,000 include Oppanol B30SF, Opanol B50, Opanol B50SF (all manufactured by BASF).
Examples of commercially available resins having a weight average molecular weight of 20,000 to 150,000 include, for example, Oppanol B10SFN, Opanol B10N, Opanol B11SFN, Opanol B12SFN, Opanol B12N, OppolB13PFN, OpPolB13SFN, B15SFN, Oppanol B15N (all manufactured by BASF), Tetrax 3T, Tetrax 4T, Tetrax 5T, Tetrax 6T, Highmall 4H, Highmall 5H, Highmall 5.5H, Highmall 6H (all JX Nikko) Nisseki Energy Co., Ltd.).
本発明の有機ＥＬ表示素子封止用樹脂組成物全体１００重量部中における上記ポリイソブチレン骨格を有する樹脂の含有量の好ましい下限は３０重量部、好ましい上限は９０重量部である。上記ポリイソブチレン骨格を有する樹脂の含有量が３０重量部未満であると、得られる有機ＥＬ表示素子封止用樹脂組成物を用いて樹脂シートを形成する際、シートの強度が乏しく、作業性が低下することがある。上記ポリイソブチレン骨格を有する樹脂の含有量が９０重量部を超えると、得られる有機ＥＬ表示素子封止用樹脂組成物が白濁し、透明性に劣るものとなることがある。上記ポリイソブチレン骨格を有する樹脂の含有量のより好ましい下限は４０重量部、より好ましい上限は８０重量部である。 The minimum with preferable content of the resin which has the said polyisobutylene frame | skeleton in 100 weight part of resin composition for organic EL display element sealing of this invention is 30 weight part, and a preferable upper limit is 90 weight part. When the content of the resin having a polyisobutylene skeleton is less than 30 parts by weight, when the resin sheet is formed using the obtained resin composition for sealing an organic EL display element, the strength of the sheet is poor, and the workability is low. May decrease. If the content of the resin having a polyisobutylene skeleton exceeds 90 parts by weight, the resulting resin composition for sealing an organic EL display element may become cloudy and may be inferior in transparency. The minimum with more preferable content of resin which has the said polyisobutylene skeleton is 40 weight part, and a more preferable upper limit is 80 weight part.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、炭素数１０以上の脂肪酸で表面処理された層状複水酸化物を含有する。以下、炭素数１０以上の脂肪酸で表面処理された層状複水酸化物を「本発明にかかる層状複水酸化物」といい、未処理の層状複水酸化物を単に「層状複水酸化物」という。
本発明にかかる層状複水酸化物を、上記ポリイソブチレン骨格を有する樹脂と組み合わせて含有することにより、本発明の有機ＥＬ表示素子封止用樹脂組成物は、透明性及びバリア性に優れるものとなる。
The resin composition for sealing an organic EL display device of the present invention contains a layered double hydroxide surface-treated with a fatty acid having 10 or more carbon atoms. Hereinafter, the layered double hydroxide surface-treated with a fatty acid having 10 or more carbon atoms is referred to as “layered double hydroxide according to the present invention”, and the untreated layered double hydroxide is simply “layered double hydroxide”. That's it.
By including the layered double hydroxide according to the present invention in combination with the resin having the polyisobutylene skeleton, the resin composition for sealing an organic EL display device of the present invention has excellent transparency and barrier properties. Become.
上記層状複水酸化物としては、ハイドロタルサイト類、パイロオーライト類、ハイドロカルマイト等が挙げられる。なかでも、下記式（Ｉ）で表される不定比化合物が好ましい。 Examples of the layered double hydroxide include hydrotalcites, pyroaulites, hydrocalumite and the like. Of these, non-stoichiometric compounds represented by the following formula (I) are preferable.
式（Ｉ）中、Ｍ２＋は、Ｍｇ２＋、Ｚｎ２＋、Ｃａ２＋、Ｆｅ２＋、Ｍｎ２＋、Ｃｏ２＋
、Ｎｉ２＋、及び、Ｃｕ２＋からなる群より選択される少なくとも１種の２価金属イオンであり、Ｍ３＋は、Ａｌ３＋、Ｆｅ３＋、Ｃｒ３＋、及び、Ｃｏ３＋からなる群より選択される少なくとも１種の３価金属イオンであり、Ａｎ−は、ｎ価のアニオンを示し、ｘは、０＜ｘ≦１／３の範囲の数であり、ｍは、０≦ｍ≦２の範囲の数である。
In formula (I), M 2+ is Mg 2+ , Zn 2+ , Ca 2+ , Fe 2+ , Mn 2+ , Co 2+.
, Ni 2+, and, at least one divalent metal ion selected from the group consisting of Cu 2+, M 3+ is, Al 3+, Fe 3+, Cr 3+, and is selected from the group consisting of Co 3+ is at least one trivalent metal ion, a n-represents an n-valent anion, x is a number in the range of 0 <x ≦ 1/3, m is in the range of 0 ≦ m ≦ 2 Is the number of
上記式（Ｉ）において、Ａｎ−としては、具体的には例えば、ＯＨ−、ＣＯ３ ２−、ＳＯ４ ２−、ＮＯ３ −、Ｃｌ−、Ｆ−、Ｂｒ−、Ｆｅ（ＣＮ）６ ３−、酢酸イオン、シュウ酸イオン、サリチル酸イオン等が挙げられる。 In the above formula (I), A n-, specifically, for example, OH -, CO 3 2-, SO 4 2-, NO 3 -, Cl -, F -, Br -, Fe (CN) 6 3- , acetate ion, oxalate ion, salicylate ion and the like.
上記層状複水酸化物としては、上記式（Ｉ）で表される不定比化合物のなかでも、下記式（ＩＩ）で表される不定比化合物がより好ましい。 As the layered double hydroxide, among the non-stoichiometric compounds represented by the above formula (I), the non-stoichiometric compound represented by the following formula (II) is more preferable.
式（ＩＩ）中、Ｍ２＋は、Ｍｇ２＋及び／又はＺｎ２＋であり、Ａｎ−はｎ価のアニオンを示し、ｘは０＜ｘ≦１／３の範囲の数であり、ｍは０≦ｍ≦２の範囲の数である。 Wherein (II), M 2+ is Mg 2+ and / or Zn 2+, A n-represents an n-valent anion, x is a number in the range of 0 <x ≦ 1/3, m is 0 The number is in the range of ≦ m ≦ 2.
上記層状複水酸化物としては、上記式（ＩＩ）で表される不定比化合物のなかでも、Ａｎ−がＯＨ−及び／又はＣＯ３ ２−であるものが更に好ましい。 As the layered double hydroxide, Among non-stoichiometric compound represented by the formula (II), A n-is OH - ones and / or CO 3 2-is more preferred.
上記層状複水酸化物は、天然品でも合成品でもよいが、不純物による透明性の低下や有機ＥＬ表示素子への汚染の影響を抑制し易いことから、合成層状複水酸化物が好ましい。
上記合成層状複水酸化物のうち市販されているものとしては、例えば、アルカマイザー１、アルカマイザー２、アルカマイザー３、アルカマイザー４、アルカマイザー５、ＤＨＴ−４Ａ（いずれも協和化学工業社製）、ＳＴＡＢＩＡＣＥ ＨＴ−１、ＳＴＡＢＩＡＣＥ ＨＴ−７、ＳＴＡＢＩＡＣＥ ＨＴ−Ｐ（いずれも堺化学工業社製）等が挙げられる。
The layered double hydroxide may be a natural product or a synthetic product, but a synthetic layered double hydroxide is preferred because it is easy to suppress the effect of transparency deterioration due to impurities and contamination of the organic EL display element.
Examples of commercially available synthetic layered double hydroxides include Alkamizer 1, Alkamizer 2, Alkamizer 3, Alkamizer 4, Alkamizer 5, and DHT-4A (all manufactured by Kyowa Chemical Industry Co., Ltd.). ), STABIACE HT-1, STABIACE HT-7, and STABIACE HT-P (all manufactured by Sakai Chemical Industry Co., Ltd.).
本発明にかかる層状複水酸化物は、上記層状複水酸化物が炭素数１０以上の脂肪酸で表面処理されている。
上記炭素数１０以上の脂肪酸としては、例えば、ステアリン酸、オレイン酸、エルカ酸、パルミチン酸、ラウリン酸、オレイン酸、リノール酸等が挙げられる。
In the layered double hydroxide according to the present invention, the layered double hydroxide is surface-treated with a fatty acid having 10 or more carbon atoms.
Examples of the fatty acid having 10 or more carbon atoms include stearic acid, oleic acid, erucic acid, palmitic acid, lauric acid, oleic acid, linoleic acid and the like.
上記層状複水酸化物を上記炭素数１０以上の脂肪酸にて表面処理する方法としては、湿式法や乾式法等、従来公知の表面処理法を用いることができる。
上記湿式法を用いる場合、具体的には、上記層状複水酸化物のスラリーに、溶液やエマルジョンの状態とした上記炭素数１０以上の脂肪酸を加え、必要に応じて１００℃までの温度に加熱しながら、充分に撹拌して混合した後、濾過し、水洗し、乾燥する方法を用いることができる。
また、上記乾式法を用いる場合、具体的には、上記層状複水酸化物に、溶液やエマルジョンの状態とした上記炭素数１０以上の脂肪酸を加え、ヘンシェルミキサー等の混合装置を用いて、必要に応じて加熱しながら、充分に混合する方法を用いることができる。
As a method of surface-treating the layered double hydroxide with the fatty acid having 10 or more carbon atoms, a conventionally known surface treatment method such as a wet method or a dry method can be used.
When the wet method is used, specifically, the fatty acid having 10 or more carbon atoms in the form of a solution or emulsion is added to the slurry of the layered double hydroxide, and heated to a temperature of up to 100 ° C. as necessary. However, a method of sufficiently stirring and mixing, followed by filtering, washing with water and drying can be used.
When using the dry method, specifically, the fatty acid having 10 or more carbon atoms in the form of a solution or emulsion is added to the layered double hydroxide, and it is necessary to use a mixing device such as a Henschel mixer. A method of sufficiently mixing while heating can be used.
上記層状複水酸化物を上記炭素数１０以上の脂肪酸にて表面処理する方法において、上記炭素数１０以上の脂肪酸は、上記層状複水酸化物に対して、０．１〜１５重量％の範囲で使用することが好ましく、０．５〜５重量％の範囲で使用することがより好ましい。 In the method of surface-treating the layered double hydroxide with the fatty acid having 10 or more carbon atoms, the fatty acid having 10 or more carbon atoms is in a range of 0.1 to 15% by weight with respect to the layered double hydroxide. It is preferable to use in the range of 0.5 to 5% by weight.
一般に、無機充填剤の平均粒子径が可視光の波長と同等となると、光の散乱を生じるために得られる組成物の透明性が低下するが、本発明の有機ＥＬ表示素子封止用樹脂組成物では、可視光の波長と同等の平均粒子径を有する本発明にかかる層状複水酸化物を、公知の
分散装置を用いて上記ポリイソブチレン骨格を有する樹脂中に分散させた場合でも、高い透明性が得られる。
In general, when the average particle diameter of the inorganic filler is equal to the wavelength of visible light, the transparency of the composition obtained to cause light scattering decreases, but the organic EL display element sealing resin composition of the present invention Even when the layered double hydroxide according to the present invention having an average particle diameter equivalent to the wavelength of visible light is dispersed in the resin having the polyisobutylene skeleton using a known dispersing device, it is highly transparent. Sex is obtained.
本発明にかかる層状複水酸化物の平均粒子径の好ましい下限は２０ｎｍ、好ましい上限は１０００ｎｍである。本発明にかかる層状複水酸化物の平均粒子径が２０ｎｍ未満であると、バリア性が充分に発揮されないことがある。本発明にかかる層状複水酸化物の平均粒子径が１０００ｎｍを超えると、得られる有機ＥＬ表示素子封止用樹脂組成物が透明性に劣るものとなることがある。本発明にかかる層状複水酸化物の平均粒子径のより好ましい下限は１００ｎｍ、より好ましい上限は８００ｎｍである。
なお、本発明にかかる層状複水酸化物の平均粒子径は、動的光散乱式粒子径測定装置（大塚電子社製、「ＥＬＳＺ−１０００Ｓ」）等を用いて測定することができる。
The minimum with a preferable average particle diameter of the layered double hydroxide concerning this invention is 20 nm, and a preferable upper limit is 1000 nm. When the average particle size of the layered double hydroxide according to the present invention is less than 20 nm, the barrier property may not be sufficiently exhibited. When the average particle diameter of the layered double hydroxide according to the present invention exceeds 1000 nm, the obtained resin composition for sealing an organic EL display element may be inferior in transparency. The minimum with a more preferable average particle diameter of the layered double hydroxide concerning this invention is 100 nm, and a more preferable upper limit is 800 nm.
In addition, the average particle diameter of the layered double hydroxide according to the present invention can be measured using a dynamic light scattering particle diameter measuring apparatus (“ELSZ-1000S” manufactured by Otsuka Electronics Co., Ltd.) or the like.
本発明にかかる層状複水酸化物の含有量は、上記ポリイソブチレン骨格を有する樹脂１００重量部に対して、好ましい下限が１０重量部、好ましい上限が１５０重量部である。本発明にかかる層状複水酸化物の含有量が１０重量部未満であると、得られる有機ＥＬ表示素子封止用樹脂組成物がバリア性に劣るものとなることがある。本発明にかかる層状複水酸化物の含有量が１５０重量部を超えると、得られる有機ＥＬ表示素子封止用樹脂組成物が透明性に劣るものとなることがある。本発明にかかる層状複水酸化物の含有量のより好ましい下限は４０重量部、より好ましい上限は１２０重量部である。 The content of the layered double hydroxide according to the present invention is preferably 10 parts by weight with respect to 100 parts by weight of the resin having the polyisobutylene skeleton, and 150 parts by weight with respect to the preferred upper limit. When the content of the layered double hydroxide according to the present invention is less than 10 parts by weight, the resulting resin composition for sealing an organic EL display element may be inferior in barrier properties. When content of the layered double hydroxide concerning this invention exceeds 150 weight part, the resin composition for organic EL display element sealing obtained may become inferior to transparency. The minimum with more preferable content of the layered double hydroxide concerning this invention is 40 weight part, and a more preferable upper limit is 120 weight part.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、得られる有機ＥＬ表示素子封止用樹脂組成物の接着性を向上させること等を目的として、粘着付与樹脂を含有してもよい。
上記粘着付与樹脂としては、例えば、テルペン樹脂、変性テルペン樹脂、クマロン樹脂、インデン樹脂、石油樹脂等が挙げられる。
上記変性テルペン樹脂としては、例えば、水素添加テルペン樹脂、テルペンフェノール共重合樹脂、芳香族変性テルペン樹脂等が挙げられる。
上記石油樹脂としては、例えば、脂肪族系石油樹脂、水添脂環式石油樹脂、芳香族系石油樹脂、脂肪族芳香族共重合系石油樹脂、脂環族系石油樹脂、ジシクロペンタジエン系石油樹脂及びその水素化物等が挙げられる。
なかでも、上記粘着付与樹脂としては、樹脂組成物の接着性、耐透湿性、相溶性等の観点から、テルペン樹脂、芳香族変性テルペン樹脂、テルペンフェノール共重合樹脂、水添脂環式石油樹脂、芳香族系石油樹脂、脂肪族芳香族共重合系石油樹脂、脂環族系石油樹脂が好ましく、脂環族系石油樹脂がより好ましく、脂環族飽和炭化水素樹脂、脂環族不飽和炭化水素樹脂が更に好ましく、シクロヘキシル環（即ち、シクロヘキサン環）含有飽和炭化水素樹脂、ジシクロペンタジエン変性炭化水素樹脂が特に好ましい。これらの粘着付与樹脂は、単独で用いられてもよいし、２種以上が併用されてもよい。
The resin composition for sealing an organic EL display element of the present invention may contain a tackifier resin for the purpose of improving the adhesiveness of the obtained resin composition for sealing an organic EL display element.
Examples of the tackifying resin include terpene resins, modified terpene resins, coumarone resins, indene resins, and petroleum resins.
Examples of the modified terpene resin include a hydrogenated terpene resin, a terpene phenol copolymer resin, and an aromatic modified terpene resin.
Examples of the petroleum resin include aliphatic petroleum resins, hydrogenated alicyclic petroleum resins, aromatic petroleum resins, aliphatic aromatic copolymer petroleum resins, alicyclic petroleum resins, and dicyclopentadiene petroleum. Examples thereof include resins and hydrides thereof.
Among these, as the tackifying resin, from the viewpoints of adhesiveness, moisture resistance, compatibility, etc. of the resin composition, terpene resin, aromatic modified terpene resin, terpene phenol copolymer resin, hydrogenated alicyclic petroleum resin Aromatic petroleum resins, aliphatic aromatic copolymer petroleum resins, alicyclic petroleum resins are preferred, alicyclic petroleum resins are more preferred, alicyclic saturated hydrocarbon resins, alicyclic unsaturated carbonization A hydrogen resin is more preferable, and a cyclohexyl ring (that is, cyclohexane ring) -containing saturated hydrocarbon resin and dicyclopentadiene-modified hydrocarbon resin are particularly preferable. These tackifier resins may be used alone or in combination of two or more.
上記テルペン樹脂のうち市販されているものとしては、例えば、ＹＳレジンＰＸ、ＹＳレジンＰＸＮ（いずれもヤスハラケミカル社製）等が挙げられる。
上記芳香族変性テルペン樹脂のうち市販されているものとしては、例えば、ＹＳレジンＴＯ、ＴＲシリーズ（いずれもヤスハラケミカル社製）等が挙げられる。
上記水素添加テルペン樹脂のうち市販されているものとしては、例えば、クリアロンＰ、クリアロンＭ、クリアロンＫシリーズ（いずれもヤスハラケミカル社製）等が挙げられる。
上記テルペンフェノール共重合樹脂のうち市販されているものとしては、例えば、ＹＳポリスター２０００、ＹＳポリスターＵ、ＹＳポリスターＴ、ＹＳポリスターＳ、マイティエースＧ（いずれもヤスハラケミカル社製）等が挙げられる。
上記水添脂環式石油樹脂のうち市販されているものとしては、例えば、Ｅｓｃｏｒｅｚ５３００シリーズ、５６００シリーズ（いずれもエクソンモービル社製）等が挙げられる。上記芳香族系石油樹脂のうち市販されているものとしては、例えば、ＥＮＤＥＸ１５５（
イーストマン社製）等が挙げられる。
上記脂肪族芳香族共重合系石油樹脂のうち市販されているものとしては、例えば、ＱｕｉｎｔｏｎｅＤ１００（日本ゼオン社製）等が挙げられる。
上記脂環族系石油樹脂のうち市販されているものとしては、例えば、Ｑｕｉｎｔｏｎｅ１３２５、Ｑｕｉｎｔｏｎｅ１３４５（いずれも日本ゼオン社製）、アルコン Ｐ−９０、アルコン Ｐ−１００、アルコン Ｐ−１２５、アルコン Ｐ−１４０（いずれも荒川化学社製）等が挙げられる。
Examples of commercially available terpene resins include YS resin PX and YS resin PXN (both manufactured by Yasuhara Chemical Co., Ltd.).
As what is marketed among the said aromatic modified terpene resins, YS resin TO, TR series (all are made by Yashara Chemical Co., Ltd.) etc. are mentioned, for example.
Examples of commercially available hydrogenated terpene resins include Clearon P, Clearon M, Clearon K series (all manufactured by Yasuhara Chemical Co., Ltd.) and the like.
Examples of commercially available terpene phenol copolymer resins include YS Polystar 2000, YS Polyster U, YS Polyster T, YS Polyster S, Mighty Ace G (all manufactured by Yasuhara Chemical Co., Ltd.) and the like.
Examples of commercially available hydrogenated alicyclic petroleum resins include Escorez 5300 series and 5600 series (both manufactured by ExxonMobil). Among the above-mentioned aromatic petroleum resins, those commercially available include, for example, ENDEX 155 (
Eastman) and the like.
As what is marketed among the said aliphatic aromatic copolymerization petroleum resin, QuintoneD100 (made by Nippon Zeon) etc. are mentioned, for example.
Examples of commercially available alicyclic petroleum resins include Quintone 1325, Quintone 1345 (all manufactured by Nippon Zeon Co., Ltd.), Archon P-90, Archon P-100, Archon P-125, Archon P-140. (Both manufactured by Arakawa Chemical Co., Ltd.).
上記粘着付与樹脂は、本発明の有機ＥＬ表示素子封止用樹脂組成物をシート上に成形する場合に、積層工程でシートを軟化させ、かつ、所望の耐熱性を有するシートを得る観点から、軟化点の好ましい下限が５０℃、好ましい上限が１５０℃、より好ましい下限が６０℃、より好ましい上限が１２０℃、更に好ましい下限が７０℃、更に好ましい上限が１００℃である。
なお、上記軟化点は、ＪＩＳ Ｋ ２２０７に従い、環球法により測定される。
From the viewpoint of softening the sheet in the laminating step and obtaining a sheet having desired heat resistance when the tackifying resin is molded on the sheet of the organic EL display element sealing resin composition of the present invention, The preferred lower limit of the softening point is 50 ° C., the preferred upper limit is 150 ° C., the more preferred lower limit is 60 ° C., the more preferred upper limit is 120 ° C., the still more preferred lower limit is 70 ° C., and the still more preferred upper limit is 100 ° C.
The softening point is measured by the ring and ball method according to JIS K 2207.
上記粘着付与樹脂の含有量は、良好なバリア性を維持する観点から、上記ポリイソブチレン骨格を有する樹脂１００重量部に対して、好ましい下限が５重量部、好ましい上限が５０重量部である。上記粘着付与樹脂の含有量が５重量部未満であると、接着性を向上させる効果が充分に発揮されないことがある。上記粘着付与樹脂の含有量が５０重量部を超えると、得られる有機ＥＬ表示素子封止用樹脂組成物がバリア性に劣るものとなることがある。上記粘着付与樹脂の含有量のより好ましい下限が１０重量部、より好ましい上限が４０重量部である。 From the viewpoint of maintaining good barrier properties, the content of the tackifying resin is preferably 5 parts by weight with respect to 100 parts by weight of the resin having the polyisobutylene skeleton, and 50 parts by weight with respect to the preferable upper limit. When the content of the tackifying resin is less than 5 parts by weight, the effect of improving the adhesiveness may not be sufficiently exhibited. When content of the said tackifying resin exceeds 50 weight part, the resin composition for organic EL display element sealing obtained may become inferior to barrier property. A more preferable lower limit of the content of the tackifier resin is 10 parts by weight, and a more preferable upper limit is 40 parts by weight.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、シランカップリング剤を含有することが好ましい。上記シランカップリング剤は、本発明の有機ＥＬ表示素子封止用樹脂組成物と被着体との接着性を向上させる役割を有する。 The organic EL display element sealing resin composition of the present invention preferably contains a silane coupling agent. The said silane coupling agent has a role which improves the adhesiveness of the resin composition for sealing an organic EL display element of this invention, and a to-be-adhered body.
上記シランカップリング剤は特に限定されず、一般的にポリオレフィン系樹脂と相溶可能な公知のシランカップリング剤を用いることができる。
上記シランカップリング剤としては、具体的には例えば、３−グリシドキシプロピルトリメトキシシラン、３−グリシドキシプロピルメチルジメトキシシラン、３−グリシドキシプロピルメチルジメトキシシラン、２−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、３−エチル−［（トリエトキシシリルプロポキシ）メチル］オキセタン、ビニルトリメトキシシラン、ビニルトリエトキシシラン、３−メルカプトプロピルトリメトキシシラン、３−メルカプトプロピルメチルジメトキシシラン、３−アミノプロピルトリメトキシシラン、３−アミノプロピルトリエトキシシラン等が挙げられる。これらのシランカップリング剤は、単独で用いられてもよいし、２種以上が併用されてもよい。
The said silane coupling agent is not specifically limited, Generally the well-known silane coupling agent compatible with polyolefin resin can be used.
Specific examples of the silane coupling agent include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 2- (3,4). -Epoxycyclohexyl) ethyltrimethoxysilane, 3-ethyl-[(triethoxysilylpropoxy) methyl] oxetane, vinyltrimethoxysilane, vinyltriethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-mercaptopropylmethyldimethoxysilane, Examples include 3-aminopropyltrimethoxysilane and 3-aminopropyltriethoxysilane. These silane coupling agents may be used independently and 2 or more types may be used together.
上記シランカップリング剤の含有量は、上記ポリイソブチレン骨格を有する樹脂１００重量部に対して、好ましい下限が０．１重量部、好ましい上限が５重量部である。上記シランカップリング剤の含有量が０．１重量部未満であると、得られる有機ＥＬ表示素子封止用樹脂組成物の接着性を向上させる効果が充分に発揮されないことがある。上記シランカップリング剤の含有量が５重量部を超えると、得られる有機ＥＬ表示素子封止用樹脂組成物が、バリア性に劣るものとなったり、余剰のシランカップリング剤がブリードアウトし、接着性を損なったりすることがある。上記シランカップリング剤の含有量のより好ましい下限は０．３重量部、より好ましい上限は２重量部である。 The content of the silane coupling agent is preferably 0.1 parts by weight and preferably 5 parts by weight with respect to 100 parts by weight of the resin having the polyisobutylene skeleton. When the content of the silane coupling agent is less than 0.1 parts by weight, the effect of improving the adhesiveness of the obtained organic EL display element sealing resin composition may not be sufficiently exhibited. When the content of the silane coupling agent exceeds 5 parts by weight, the resulting organic EL display element sealing resin composition becomes inferior in barrier properties, or excess silane coupling agent bleeds out, Adhesiveness may be impaired. The minimum with more preferable content of the said silane coupling agent is 0.3 weight part, and a more preferable upper limit is 2 weight part.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、界面活性剤を含有してもよい。上記界面活性剤を含有することにより、本発明の有機ＥＬ表示素子封止用樹脂組成物をシート状に成形する際の塗布後の平坦性を向上させることができる。
上記界面活性剤は、消泡剤等の機能を有していてもよい。
The resin composition for sealing an organic EL display element of the present invention may contain a surfactant. By containing the surfactant, the flatness after coating when the organic EL display element sealing resin composition of the present invention is formed into a sheet can be improved.
The surfactant may have a function such as an antifoaming agent.
上記界面活性剤としては、例えば、フッ素系、シリコーン系、アクリル系等のものが挙げられる。なかでも、フッ素系界面活性剤、シリコーン系界面活性剤が好ましく、フッ素系界面活性剤がより好ましい。
上記界面活性剤は、単独で用いられてもよいし、２種以上が組み合わせて用いられてもよい。
Examples of the surfactant include fluorine-based, silicone-based, acrylic-based and the like. Of these, fluorine-based surfactants and silicone-based surfactants are preferable, and fluorine-based surfactants are more preferable.
The said surfactant may be used independently and 2 or more types may be used in combination.
上記フッ素系界面活性剤としては、末端、主鎖及び側鎖の少なくともいずれかの部位にフルオロアルキル基又はフルオロアルキレン基を有する化合物を好適に用いることができ、具体的には例えば、１，１，２，２−テトラフロロオクチル（１，１，２，２−テトラフロロプロピル）エーテル、１，１，２，２−テトラフロロオクチルヘキシルエーテル、オクタエチレングリコールジ（１，１，２，２−テトラフロロブチル）エーテル、ヘキサエチレングリコール（１，１，２，２，３，３−ヘキサフロロペンチル）エーテル、オクタプロピレングリコールジ（１，１，２，２−テトラフロロブチル）エーテル、ヘキサプロピレングリコールジ（１，１，２，２，３，３−ヘキサフロロペンチル）エーテル、パーフロロドデシルスルホン酸ナトリウム、１，１，２，２，８，８，９，９，１０，１０−デカフロロドデカン、１，１，２，２，３，３−ヘキサフロロデカン、フルオロアルキルベンゼンスルホン酸ナトリウム、フルオロアルキルホスホン酸ナトリウム、フルオロアルキルカルボン酸ナトリウム、フルオロアルキルポリオキシエチレンエーテル、ジグリセリンテトラキス（フルオロアルキルポリオキシエチレンエーテル）、フルオロアルキルアンモニウムヨージド、フルオロアルキルベタイン、フルオロアルキルポリオキシエチレンエーテル、パーフルオロアルキルポリオキシエタノール、パーフルオロアルキルアルコキシレート、フッ素系アルキルエステル等が挙げられる。 As the fluorosurfactant, a compound having a fluoroalkyl group or a fluoroalkylene group in at least one of the terminal, main chain and side chain can be preferably used. Specifically, for example, 1,1 , 2,2-tetrafluorooctyl (1,1,2,2-tetrafluoropropyl) ether, 1,1,2,2-tetrafluorooctyl hexyl ether, octaethylene glycol di (1,1,2,2- Tetrafluorobutyl) ether, hexaethylene glycol (1,1,2,2,3,3-hexafluoropentyl) ether, octapropylene glycol di (1,1,2,2-tetrafluorobutyl) ether, hexapropylene glycol Di (1,1,2,2,3,3-hexafluoropentyl) ether, perfluorododecyl sulfonate Lilium, 1,1,2,2,8,8,9,9,10,10-decafluorododecane, 1,1,2,2,3,3-hexafluorodecane, sodium fluoroalkylbenzenesulfonate, fluoroalkyl Sodium phosphonate, sodium fluoroalkylcarboxylate, fluoroalkyl polyoxyethylene ether, diglycerin tetrakis (fluoroalkyl polyoxyethylene ether), fluoroalkyl ammonium iodide, fluoroalkyl betaine, fluoroalkyl polyoxyethylene ether, perfluoroalkyl poly Examples include oxyethanol, perfluoroalkyl alkoxylates, and fluorine alkyl esters.
また、上記フッ素系界面活性剤のうち市販されているものとしては、例えば、ＢＭ−１０００、ＢＭ−１１００（いずれもＢＭ ＣＨＥＭＩＥ社製）、メガファックＦ１４２Ｄ、メガファックＦ１７２、メガファックＦ１７３、メガファックＦ１８３、メガファックＦ１７８、メガファックＦ１９１、メガファックＦ４７１、メガファックＦ４７６（いずれもＤＩＣ社製）、フロラードＦＣ１７０Ｃ、ＦＣ−１７１、ＦＣ−４３０、ＦＣ−４３１（いずれも住友スリーエム社製）、サーフロンＳ−１１２、サーフロンＳ−１１３、サーフロンＳ−１３１、サーフロンＳ−１４１、サーフロンＳ−１４５、サーフロンＳ−３８２、サーフロンＳＣ−１０１、サーフロンＳＣ−１０２、サーフロンＳＣ−１０３、サーフロンＳＣ−１０４、サーフロンＳＣ−１０５、サーフロンＳＣ−１０６（いずれも旭硝子社製）、エフトップＥＦ３０１、エフトップＥＦ３０３、エフトップＥＦ３５２（いずれも三菱マテリアル電子化成社製）、フタージェントＦＴ−１００、フタージェントＦＴ−１１０、フタージェントＦＴ−１４０Ａ、フタージェントＦＴ−１５０、フタージェントＦＴ−２５０、フタージェントＦＴ−２５１、フタージェントＦＴＸ−２５１、フタージェントＦＴＸ−２１８、フタージェントＦＴ−３００、フタージェントＦＴ−３１０、フタージェントＦＴ−４００Ｓ（いずれもネオス社製）等が挙げられる。 Examples of commercially available fluorosurfactants include BM-1000, BM-1100 (all manufactured by BM CHEMIE), MegaFuck F142D, MegaFuck F172, MegaFuck F173, MegaFuck. F183, Megafuck F178, Megafuck F191, Megafuck F471, Megafuck F476 (all manufactured by DIC), Florard FC170C, FC-171, FC-430, FC-431 (all manufactured by Sumitomo 3M), Surflon S -112, Surflon S-113, Surflon S-131, Surflon S-141, Surflon S-145, Surflon S-382, Surflon SC-101, Surflon SC-102, Surflon SC-103, Surflon SC-104, Surf SC-105, Surflon SC-106 (all manufactured by Asahi Glass Co., Ltd.), Ftop EF301, Ftop EF303, Ftop EF352 (all manufactured by Mitsubishi Materials Denka Kasei), Aftergent FT-100, Aftergent FT-110 , Aftergent FT-140A, Aftergent FT-150, Aftergent FT-250, Aftergent FT-251, Aftergent FTX-251, Aftergent FTX-218, Aftergent FT-300, Aftergent FT-310, After Gento FT-400S (all manufactured by Neos) and the like can be mentioned.
また、上記シリコーン系界面活性剤としては、ポリエーテル変性ポリジメチルシロキサン、ポリエステル変性ポリジメチルシロキサンが好ましく、ポリエーテル変性ポリジメチルシロキサンがより好ましい。 Moreover, as said silicone type surfactant, polyether modified polydimethylsiloxane and polyester modified polydimethylsiloxane are preferable, and polyether modified polydimethylsiloxane is more preferable.
上記シリコーン系界面活性剤のうち市販されているものとしては、例えば、ＢＹＫ−３５４、ＢＹＫ−３００、ＢＹＫ−３０２、ＢＹＫ−３０６、ＢＹＫ−３０７、ＢＹＫ−３１０、ＢＹＫ−３１３、ＢＹＫ−３１５、ＢＹＫ−３２０、ＢＹＫ−３２２、ＢＹＫ−３２３、ＢＹＫ−３２５、ＢＹＫ−３３０、ＢＹＫ−３３１、ＢＹＫ−３３３、ＢＹＫ−３４２、ＢＹＫ−３４５、ＢＹＫ−３４６、ＢＹＫ−３４７、ＢＹＫ−３４８、ＢＹＫ−３４９、ＢＹＫ−３７０、ＢＹＫ−３７８、ＢＹＫ−３４５５（いずれもビックケミー・ジャパン社製）、サーフロンＳ−６１１（ＡＧＣセイミケミカル社製）、トーレシリコーンＤＣ３ＰＡ、トーレシリコーンＤＣ７ＰＡ、トーレシリコーンＳＨ１１ＰＡ、トーレシリコーンＳＨ２１ＰＡ、トーレシリコーンＳＨ２８ＰＡ、トーレシリコーンＳＨ２９ＰＡ、トーレシリコーンＳＨ３０ＰＡ、トーレシリコーンＳＨ−１９０、トーレシリコーンＳＨ−１９３、トーレシリコーンＳＺ−６０３２、トーレシリコーンＳＦ−８４２８、トーレシリコーンＤＣ−５７、トーレシリコーンＤＣ−１９０（いずれも東レ・ダウコーニング・シリコーン社製）、ＴＳＦ−４４４０、ＴＳＦ−４３００、ＴＳＦ−４４４５、ＴＳＦ−４４４６、ＴＳＦ−４４６０、ＴＳＦ−４４５２（いずれもモメンティブ・パフォーマンス・マテリアルズ・ジャパン社製）等が挙げられる。 Examples of commercially available silicone surfactants include BYK-354, BYK-300, BYK-302, BYK-306, BYK-307, BYK-310, BYK-313, BYK-315, BYK-320, BYK-322, BYK-323, BYK-325, BYK-330, BYK-331, BYK-333, BYK-342, BYK-345, BYK-346, BYK-347, BYK-348, BYK- 349, BYK-370, BYK-378, BYK-3455 (all manufactured by Big Chemie Japan Co., Ltd.), Surflon S-611 (manufactured by AGC Seimi Chemical Co., Ltd.), Tore Silicone DC3PA, Tore Silicone DC7PA, Tore Silicone SH11PA, Tore Silicone SH21PA , Torresi Corn SH28PA, Torre Silicone SH29PA, Torre Silicone SH30PA, Torre Silicone SH-190, Torre Silicone SH-193, Torre Silicone SZ-6032, Torre Silicone SF-8428, Torre Silicone DC-57, Tole Silicone DC-190 (all are Toray Silicone -Dow Corning Silicone Co., Ltd.), TSF-4440, TSF-4300, TSF-4445, TSF-4446, TSF-4460, TSF-4442 (all manufactured by Momentive Performance Materials Japan). .
また、上記界面活性剤としては、例えば、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンステアリルエーテル、ポリオキシエチレンオレイルエーテル等のポリオキシエチレンアルキルエーテル類や、ポリオキシエチレンｎ−オクチルフェニルエーテル、ポリオキシエチレンｎ−ノニルフェニルエーテル等のポリオキシエチレンアリールエーテル類や、ポリオキシエチレンジラウレート、ポリオキシエチレンジステアレート等のポリオキシエチレンジアルキルエステル類等を用いることもできる。 Examples of the surfactant include polyoxyethylene alkyl ethers such as polyoxyethylene lauryl ether, polyoxyethylene stearyl ether, polyoxyethylene oleyl ether, polyoxyethylene n-octylphenyl ether, and polyoxyethylene. Polyoxyethylene aryl ethers such as n-nonylphenyl ether and polyoxyethylene dialkyl esters such as polyoxyethylene dilaurate and polyoxyethylene distearate can also be used.
上記界面活性剤の含有量は、上記ポリイソブチレン骨格を有する樹脂１００重量部に対して、好ましい下限が０．０１重量部、好ましい上限が５重量部である。上記界面活性剤の含有量が０．０１重量部未満であると、塗布後の平坦性を向上させる効果が充分に発揮されないことがある。上記界面活性剤の含有量が５重量部を超えると、塗布後の平坦性が逆に損なわれたり、本発明の有機ＥＬ表示素子封止用樹脂組成物と被着体との接着性が低下したりすることがある。上記界面活性剤の含有量は、フッ素系界面活性剤では、より好ましい下限は０．０２重量部、より好ましい上限は１重量部である。また、シリコーン系界面活性剤では、より好ましい下限は０．１重量部、より好ましい上限は２重量部である。 The content of the surfactant is preferably 0.01 parts by weight and preferably 5 parts by weight with respect to 100 parts by weight of the resin having the polyisobutylene skeleton. If the content of the surfactant is less than 0.01 parts by weight, the effect of improving the flatness after coating may not be sufficiently exhibited. When the content of the surfactant exceeds 5 parts by weight, the flatness after coating is adversely affected, or the adhesion between the organic EL display element sealing resin composition of the present invention and the adherend is lowered. Sometimes. The content of the surfactant is more preferably 0.02 parts by weight and more preferably 1 part by weight for the fluorine-based surfactant. Moreover, in a silicone type surfactant, a more preferable minimum is 0.1 weight part and a more preferable upper limit is 2 weight part.
また、本発明の有機ＥＬ表示素子封止用樹脂組成物は、本発明の目的を阻害しない範囲で、必要に応じて、紫外線吸収剤、光安定剤、酸化防止剤等の公知の各種添加剤を含有してもよい。 Moreover, the resin composition for sealing an organic EL display device of the present invention is a known various additives such as an ultraviolet absorber, a light stabilizer, an antioxidant, and the like, as long as the object of the present invention is not impaired. It may contain.
本発明の有機ＥＬ表示素子封止用樹脂組成物を製造する方法としては、例えば、上記ポリイソブチレン骨格を有する樹脂を溶解可能な溶剤に本発明にかかる層状複水酸化物を分散させた分散液と、上記ポリイソブチレン骨格を有する樹脂及び必要に応じて用いられる粘着付与樹脂等の他の成分（以下、「ポリイソブチレン骨格を有する樹脂等」ともいう）とを混合して、本発明にかかる層状複水酸化物を、上記ポリイソブチレン骨格を有する樹脂中に分散させる方法が好ましく用いられる。上記ポリイソブチレン骨格を有する樹脂等は、予め本発明にかかる層状複水酸化物を分散させる溶剤と同様の溶剤で溶解させた溶液として用いてもよい。ここで、透明性及びバリア性の観点から、本発明にかかる層状複水酸化物は、上記ポリイソブチレン骨格を有する樹脂中に高度に分散していることが好ましい。ここで、上記「高度に分散している」とは、電子顕微鏡で観察した際に、本発明にかかる層状複水酸化物の凝集がなく、層間剥離及び分散が確認できる状態のことを言う。 As a method for producing the resin composition for sealing an organic EL display device of the present invention, for example, a dispersion in which the layered double hydroxide according to the present invention is dispersed in a solvent capable of dissolving the resin having the polyisobutylene skeleton. And the above-mentioned resin having a polyisobutylene skeleton and other components such as a tackifier resin used as necessary (hereinafter also referred to as “resin having a polyisobutylene skeleton”) are mixed to form a layer according to the present invention A method of dispersing the double hydroxide in the resin having the polyisobutylene skeleton is preferably used. The above-mentioned resin having a polyisobutylene skeleton may be used as a solution previously dissolved in the same solvent as the solvent for dispersing the layered double hydroxide according to the present invention. Here, from the viewpoints of transparency and barrier properties, the layered double hydroxide according to the present invention is preferably highly dispersed in the resin having the polyisobutylene skeleton. Here, “highly dispersed” means a state in which delamination and dispersion can be confirmed without aggregation of the layered double hydroxide according to the present invention when observed with an electron microscope.
上記溶剤としては、例えば、ベンゼン、トルエン、キシレン等の芳香族類や、メタノール、エタノール、イソプロピルアルコール等のアルコール類や、Ｎ，Ｎ’−ジメチルホルムアミド、Ｎ，Ｎ’−ジメチルアセトアミド、Ｎ−メチル−２−ピロリドン等のアミド類や、γ−ブチロラクトン、γ−バレロラクトン、δ−バレロラクトン等のラクトン類や、エチレンカーボネート、プロピレンカーボネート等のカーボネート類や、モノグライム、ジグライム、トリグライム等のグライム類や、ジメチルスルホキシド等の非プロトン性極性溶媒類等が挙げられる。なかでも、Ｎ，Ｎ’−ジメチルホルムアミドが好ましい。 Examples of the solvent include aromatics such as benzene, toluene and xylene, alcohols such as methanol, ethanol and isopropyl alcohol, N, N′-dimethylformamide, N, N′-dimethylacetamide and N-methyl. Amides such as 2-pyrrolidone, lactones such as γ-butyrolactone, γ-valerolactone and δ-valerolactone, carbonates such as ethylene carbonate and propylene carbonate, and glymes such as monoglyme, diglyme and triglyme And aprotic polar solvents such as dimethyl sulfoxide. Of these, N, N′-dimethylformamide is preferable.
本発明にかかる層状複水酸化物を溶剤に分散させた分散液と上記ポリイソブチレン骨格を有する樹脂等とを混合する方法としては、例えば、ホモディスパー、ホモミキサー、万能ミキサー、プラネタリーミキサー、ニーダー、３本ロール等の混合機を用いる方法等が挙げられる。 Examples of the method for mixing the dispersion obtained by dispersing the layered double hydroxide according to the present invention in a solvent and the resin having the polyisobutylene skeleton include, for example, homodispers, homomixers, universal mixers, planetary mixers, kneaders. Examples include a method using a mixer such as a three roll.
本発明にかかる層状複水酸化物を溶剤に分散させた分散液と上記ポリイソブチレン骨格を有する樹脂等とを混合して本発明の有機ＥＬ表示素子封止用樹脂組成物を製造した場合、得られた有機ＥＬ表示素子封止用樹脂組成物を用いて有機ＥＬ表示素子を封止する際には、乾燥等により溶剤を除去する必要がある。
上記溶剤を除去する方法として、有機ＥＬ表示素子上に該溶剤を含む有機ＥＬ表示素子封止用樹脂組成物を直接塗布してから乾燥させる方法を用いると、有機ＥＬ表示素子が溶剤との接触や乾燥時の加熱により劣化する場合がある。
そのため、上記溶剤を除去する方法としては、溶剤を含む有機ＥＬ表示素子封止用樹脂組成物を、ガラスやガスバリアフィルムのような透明防湿性基材上に塗布してから乾燥させる方法が好ましく用いられる。乾燥させて上記溶剤を除去した後、有機ＥＬ表示素子封止用樹脂組成物を介して、有機発光材料層を有する積層体を形成した基板（以下、「有機ＥＬ表示素子基板」ともいう）と、透明防湿性基材とを貼り合わせ、有機ＥＬ表示素子封止用樹脂組成物を硬化させることにより有機ＥＬ表示素子の封止を行うことができる。
また、上記溶剤を除去する方法としては、離型処理を施したＰＥＴ（ポリエチレンテレフタレート）フィルムのような支持体上に、溶剤を含む有機ＥＬ表示素子封止用樹脂組成物を塗布してから乾燥させる方法も好ましく用いられる。乾燥させて上記溶剤を除去した後、上記支持体上に塗布し、乾燥させた有機ＥＬ表示素子封止用樹脂組成物を、有機ＥＬ表示素子基板上、又は、ガラス等の透明防湿性基材上にラミネートして転写した後、有機ＥＬ表示素子封止用樹脂組成物を介して有機ＥＬ表示素子基板と透明防湿性基材とを貼り合わせ、有機ＥＬ表示素子封止用樹脂組成物を硬化させることにより有機ＥＬ表示素子の封止を行うことができる。
When the dispersion liquid in which the layered double hydroxide according to the present invention is dispersed in a solvent is mixed with the resin having the polyisobutylene skeleton, the resin composition for sealing an organic EL display element of the present invention is obtained. When the organic EL display element is sealed using the obtained organic EL display element sealing resin composition, it is necessary to remove the solvent by drying or the like.
As a method for removing the solvent, when a method in which an organic EL display element sealing resin composition containing the solvent is directly applied on the organic EL display element and then dried is used, the organic EL display element comes into contact with the solvent. And may deteriorate due to heating during drying.
Therefore, as a method for removing the solvent, a method in which an organic EL display element sealing resin composition containing a solvent is applied on a transparent moisture-proof substrate such as glass or a gas barrier film and then dried is preferably used. It is done. A substrate (hereinafter also referred to as “organic EL display element substrate”) on which a laminate having an organic light emitting material layer is formed via an organic EL display element sealing resin composition after drying and removing the solvent. The organic EL display element can be sealed by bonding the transparent moisture-proof substrate and curing the organic EL display element sealing resin composition.
In addition, as a method for removing the solvent, a resin composition for sealing an organic EL display element containing a solvent is applied on a support such as a PET (polyethylene terephthalate) film which has been subjected to a release treatment, and then dried. The method of making it also preferably used. After removing the solvent by drying, the resin composition for sealing an organic EL display element coated on the support and dried is applied to an organic EL display element substrate or a transparent moisture-proof substrate such as glass. After laminating and transferring, the organic EL display element substrate and the transparent moisture-proof substrate are bonded together via the organic EL display element sealing resin composition, and the organic EL display element sealing resin composition is cured. By doing so, the organic EL display element can be sealed.
溶剤を含む有機ＥＬ表示素子封止用樹脂組成物を乾燥させる方法としては、例えば、熱風、赤外線、遠赤外線、輻射、電気ヒーター等により加熱乾燥を行う方法や、減圧下において乾燥を行う方法等が挙げられる。溶剤を含む有機ＥＬ表示素子封止用樹脂組成物を乾燥させる際、有機ＥＬ表示素子の劣化を防止する観点から、１２０℃以下で乾燥を行うことが好ましく、１００℃以下で乾燥を行うことがより好ましい。 As a method of drying the organic EL display element sealing resin composition containing a solvent, for example, a method of heating and drying with hot air, infrared rays, far infrared rays, radiation, an electric heater or the like, a method of drying under reduced pressure, etc. Is mentioned. When drying the organic EL display element sealing resin composition containing a solvent, from the viewpoint of preventing deterioration of the organic EL display element, drying is preferably performed at 120 ° C. or lower, and drying is performed at 100 ° C. or lower. More preferred.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、厚さ２０μｍに成形した時、波長４００〜８００ｎｍの可視光透過率が８５％以上であることが好ましい。上記可視光透過率が８５％未満であると、透明性に劣り、トップエミッション型の有機ＥＬ表示素子に適用できなくなることがある。上記可視光透過率のより好ましい下限は９０％である。
なお、上記可視光透過率は、有機ＥＬ表示素子封止用樹脂組成物厚さ２０μｍに成形し、厚さ０．７ｍｍの無アルカリガラス上に貼り付けて得られる積層体について、分光光度計を用いて測定できる。
When the resin composition for sealing an organic EL display element of the present invention is molded to a thickness of 20 μm, the visible light transmittance at a wavelength of 400 to 800 nm is preferably 85% or more. If the visible light transmittance is less than 85%, the transparency may be inferior, and it may not be applicable to a top emission type organic EL display element. A more preferable lower limit of the visible light transmittance is 90%.
The visible light transmittance is obtained by molding a spectrophotometer for a laminate obtained by molding the resin composition for sealing an organic EL display element to a thickness of 20 μm and affixing it on an alkali-free glass having a thickness of 0.7 mm. Can be measured.
本発明の有機ＥＬ表示素子封止用樹脂組成物は、厚さ２０μｍに成形した時、ヘイズが２％以下であることが好ましい。上記ヘイズが２％を超えると、透明性に劣り、トップエミッション型の有機ＥＬ表示素子に適用できなくなることがある。上記ヘイズのより好ましい上限は１％である。
なお、上記ヘイズは、有機ＥＬ表示素子封止用樹脂組成物厚さ２０μｍに成形し、厚さ０．７ｍｍの無アルカリガラス上に貼り付けて得られる積層体について、ヘイズメーターを用いて測定できる。
The organic EL display element sealing resin composition of the present invention preferably has a haze of 2% or less when molded to a thickness of 20 μm. When the haze exceeds 2%, the transparency is inferior, and it may not be applicable to a top emission type organic EL display element. A more preferable upper limit of the haze is 1%.
In addition, the said haze can be measured using a haze meter about the laminated body obtained by shape | molding the resin composition for organic EL display element sealing to 20 micrometers in thickness, and affixing on the non-alkali glass of thickness 0.7mm. .
本発明の有機ＥＬ表示素子封止用樹脂組成物をシート状に成形してなる有機ＥＬ表示素子封止用樹脂シートもまた、本発明の１つである。 An organic EL display element sealing resin sheet obtained by molding the organic EL display element sealing resin composition of the present invention into a sheet form is also one aspect of the present invention.
本発明の有機ＥＬ表示素子封止用樹脂組成物をシート状に成形する方法としては、比較的低温で均一な膜厚のシートを形成することができることから、溶液塗布法が好ましい。具体的には例えば、溶剤を含有する本発明の有機ＥＬ表示素子封止用樹脂組成物溶液を、離型処理を施したＰＥＴ（ポリエチレンテレフタレート）等のフィルム（以下、「離型フィルム」ともいう）上に所定の厚みに塗布し、溶剤を乾燥することによりフィルムを得る方法が好適に用いられる。 As a method for forming the organic EL display element sealing resin composition of the present invention into a sheet shape, a solution coating method is preferable because a sheet having a uniform film thickness can be formed at a relatively low temperature. Specifically, for example, the resin composition solution for sealing an organic EL display element of the present invention containing a solvent is a film (hereinafter referred to as “release film”) such as PET (polyethylene terephthalate) subjected to a release treatment. The method of obtaining a film by applying the film to a predetermined thickness and drying the solvent is preferably used.
溶剤を含有する本発明の有機ＥＬ表示素子封止用樹脂組成物溶液を離型フィルム上に塗布する方法としては、例えば、ロールコート、スリットコート、コンマコート、グラビアコート、キスコート、ダイコート、リップコート、ブレードコート、バーコート等の公知の方法を用いることができる。 Examples of the method of applying the resin composition solution for sealing an organic EL display element of the present invention containing a solvent on a release film include a roll coat, a slit coat, a comma coat, a gravure coat, a kiss coat, a die coat, and a lip coat. Well-known methods such as blade coating and bar coating can be used.
本発明の有機ＥＬ表示素子封止用樹脂組成物及び／又は本発明の有機ＥＬ表示素子封止用樹脂シートを用いて製造される有機ＥＬ表示素子もまた、本発明の１つである。
本発明の有機ＥＬ表示素子を製造する方法としては、例えば、離型フィルム上に形成した本発明の有機ＥＬ表示素子封止用樹脂シートを、ロール貼り合わせにより有機ＥＬ表示素子基板上に熱ラミネートし、離型フィルムを剥離した後に、極薄ガラスやガスバリア性を有するプラスチックシートを、本発明の有機ＥＬ表示素子封止用樹脂シートを介して有機ＥＬ表示素子基板の有機発光材料層を有する積層体上に積層して有機ＥＬ表示素子の封止を行う方法や、離型フィルム上に形成した本発明の有機ＥＬ表示素子封止用樹脂シートを、ロール貼り合わせによりガラスやガスバリア性を有するプラスチックシート上に熱ラミネートし、離型フィルムを剥離した後に、更に本発明の有機ＥＬ表示素子封止用樹脂シートを介して有機発光材料層を有する積層体を形成した基板に積層して有機ＥＬ表示素子の封止を行う方法等が挙げられる。
The organic EL display element manufactured using the organic EL display element sealing resin composition of the present invention and / or the organic EL display element sealing resin sheet of the present invention is also one aspect of the present invention.
As a method for producing the organic EL display element of the present invention, for example, the organic EL display element sealing resin sheet of the present invention formed on a release film is thermally laminated on the organic EL display element substrate by roll bonding. Then, after the release film is peeled off, the plastic sheet having ultrathin glass or gas barrier property is laminated with the organic light emitting material layer of the organic EL display element substrate through the organic EL display element sealing resin sheet of the present invention. A method of sealing an organic EL display element by laminating on a body, or a resin having a glass or gas barrier property by laminating the organic EL display element sealing resin sheet of the present invention formed on a release film. After heat laminating on the sheet and peeling off the release film, an organic light emitting material layer is further formed through the resin sheet for sealing an organic EL display element of the present invention. A method in which by laminating the substrate formed with the laminate performs sealing of organic EL display element and the like.
有機ＥＬ表示素子の損傷や劣化を防ぐ観点から、本発明の有機ＥＬ表示素子の製造は、５０〜１００℃程度の温度範囲で行うことが好ましい。そのため、本発明の有機ＥＬ表示素子封止用樹脂シートは、この温度領域で流動性を発現する溶融粘度を有することが好ましい。 From the viewpoint of preventing damage and deterioration of the organic EL display element, the organic EL display element of the present invention is preferably produced in a temperature range of about 50 to 100 ° C. Therefore, the resin sheet for sealing an organic EL display element of the present invention preferably has a melt viscosity that exhibits fluidity in this temperature range.
本発明の有機ＥＬ表示素子封止用樹脂組成物及び本発明の有機ＥＬ表示素子封止用樹脂シートは、反応性をもたないシート状粘着剤やシート状の熱可塑性樹脂等の従来の封止材料と比較して、耐熱性やバリア性に優れるものとなる。
また、本発明の有機ＥＬ表示素子封止用樹脂シートは、着色がなく透明性に優れるため、発光の取り出し効率に優れるトップエミッション型の有機ＥＬ表示素子に適用できる。
更に、本発明の有機ＥＬ表示素子は、本発明の有機ＥＬ表示素子封止用樹脂組成物及び／又は有機ＥＬ表示素子封止用樹脂シートを用いて、有機発光材料層を有する積層体が形成されたガラス又はフィルムと、対向するガラス又はフィルムとの間隙を封止することにより、水分の浸入を抑制してダークスポットの発生や該ダークスポットの成長による表示の劣化を抑制することができ、寿命や信頼性に優れるものとなる。
The resin composition for encapsulating an organic EL display element of the present invention and the resin sheet for encapsulating an organic EL display element of the present invention are a conventional seal such as a sheet-like pressure-sensitive adhesive or a sheet-like thermoplastic resin having no reactivity. Compared to a stopping material, it has excellent heat resistance and barrier properties.
Moreover, since the organic EL display element sealing resin sheet of the present invention is not colored and excellent in transparency, it can be applied to a top emission type organic EL display element excellent in emission extraction efficiency.
Furthermore, the organic EL display element of the present invention is formed of a laminate having an organic light emitting material layer using the organic EL display element sealing resin composition and / or the organic EL display element sealing resin sheet of the present invention. By sealing the gap between the glass or film made and the opposing glass or film, it is possible to suppress the ingress of moisture and suppress the deterioration of display due to the generation of dark spots and the growth of the dark spots, It will be excellent in life and reliability.
本発明によれば、透明性及びバリア性に優れる有機エレクトロルミネッセンス表示素子封止用樹脂組成物を提供することができる。また、本発明によれば、該有機エレクトロルミネッセンス表示素子封止用樹脂組成物を用いてなる有機エレクトロルミネッセンス表示素子封止用樹脂シート及び有機エレクトロルミネッセンス表示素子を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the resin composition for organic electroluminescent display element sealing excellent in transparency and barrier property can be provided. Moreover, according to this invention, the organic electroluminescent display element sealing resin sheet and organic electroluminescent display element which use this organic electroluminescent display element sealing resin composition can be provided.
以下に実施例を掲げて本発明を更に詳しく説明するが、本発明はこれら実施例のみに限定されない。 Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.
ステアリン酸処理層状複水酸化物として、下記の市販品を使用した。
（ステアリン酸処理層状複水酸化物Ａ）
合成ハイドロタルサイトＭｇ４．５Ａｌ２（ＯＨ）１３ＣＯ３・３．５Ｈ２Ｏ（堺化学社製、「ＳＴＡＢＩＡＣＥ ＨＴ−Ｐ」）、平均粒子径０．４５μｍ
（ステアリン酸処理層状複水酸化物Ｂ）
合成ハイドロタルサイトＭｇ４Ａｌ２（ＯＨ）１２ＣＯ３・３Ｈ２Ｏ（堺化学社製、「ＳＴＡＢＩＡＣＥ ＨＴ−１」）、平均粒子径０．５８μｍ
（ステアリン酸処理層状複水酸化物Ｃ）
合成ハイドロタルサイトＭｇ３．５Ｚｎ０．５Ａｌ２（ＯＨ）１２ＣＯ３・３Ｈ２Ｏ（堺化学社製、「ＳＴＡＢＩＡＣＥ ＨＴ−７」）、平均粒子径０．６３μｍ
The following commercially available products were used as the stearic acid-treated layered double hydroxide.
(Stearic acid-treated layered double hydroxide A)
Synthetic hydrotalcite Mg 4.5 Al 2 (OH) 13 CO 3 · 3.5H 2 O ( manufactured by Sakai Chemical Industry Co., Ltd., "STABIACE HT-P"), the average particle diameter of 0.45μm
(Stearic acid-treated layered double hydroxide B)
Synthetic hydrotalcite Mg 4 Al 2 (OH) 12 CO 3 3H 2 O (manufactured by Sakai Chemical Co., Ltd., “STABIACE HT-1”), average particle size 0.58 μm
(Stearic acid-treated layered double hydroxide C)
Synthetic hydrotalcite Mg 3.5 Zn 0.5 Al 2 (OH) 12 CO 3 .3H 2 O (manufactured by Sakai Chemical Co., Ltd., “STABIACE HT-7”), average particle size 0.63 μm
（実施例１）
（１）層状複水酸化物分散液の調製
５００ｍＬ容の容器に、層状複水酸化物として、ステアリン酸処理層状複水酸化物Ａ１００重量部、及び、トルエン４００重量部を加え、超音波洗浄器で４０ｋＨｚの振動数の超音波を照射しながら同時にディスパーにより２５００ｒｐｍの回転数で２０分間撹拌し、ステアリン酸処理層状複水酸化物Ａを２０重量％含有するトルエン分散液を調製した。
Example 1
(1) Preparation of layered double hydroxide dispersion To a 500 mL container, 100 parts by weight of stearic acid-treated layered double hydroxide A and 400 parts by weight of toluene are added as a layered double hydroxide, and an ultrasonic cleaner. The mixture was stirred for 20 minutes at a rotational speed of 2500 rpm with a disper while irradiating ultrasonic waves with a frequency of 40 kHz, to prepare a toluene dispersion containing 20% by weight of stearic acid-treated layered double hydroxide A.
（２）有機ＥＬ表示素子封止用樹脂組成物溶液の調製
５００ｍＬ容の容器に、ポリイソブチレン骨格を有する樹脂として、重量平均分子量３４万のポリイソブチレン樹脂（ＢＡＳＦ社製、「Ｏｐｐａｎｏｌ Ｂ５０ＳＦ」）９０重量部、粘着付与樹脂として脂環族飽和炭化水素樹脂（荒川化学社製、「アルコン Ｐ−９０」、軟化点９０℃）１０重量部、及び、トルエン４００重量部を加えて撹拌、溶解し、ポリイソブチレン樹脂を含有するトルエン溶液を調製した。
そこに、「（１）層状複水酸化物分散液の調製」で調製した層状複水酸化物分散液２００重量部、及び、シランカップリング剤として３−グリシドキシプロピルトリメトキシシラン（信越化学工業社製、「ＫＢＭ−４０３」）１．０重量部を加え、自転公転型撹拌混合機（シンキー社製、「あわとり練太郎 ＡＲＥ−３１０型」）により、撹拌速度２０００ｒｐｍで２分間の撹拌混合と脱泡とを行い、均一な有機ＥＬ表示素子封止用樹脂組成物溶液を得た。
(2) Preparation of Organic EL Display Element Sealing Resin Composition Solution In a 500 mL container, a polyisobutylene resin having a weight average molecular weight of 340,000 (manufactured by BASF, “Opanol B50SF”) 90 is used as a resin having a polyisobutylene skeleton. 10 parts by weight of an alicyclic saturated hydrocarbon resin (manufactured by Arakawa Chemical Co., Ltd., “Arcon P-90”, softening point 90 ° C.) and 400 parts by weight of toluene as a tackifying resin and stirred and dissolved A toluene solution containing a polyisobutylene resin was prepared.
There, 200 parts by weight of the layered double hydroxide dispersion prepared in “(1) Preparation of layered double hydroxide dispersion” and 3-glycidoxypropyltrimethoxysilane (Shin-Etsu Chemical) as the silane coupling agent (KBM-403, manufactured by Kogyo Co., Ltd.) was added in an amount of 1.0 part by weight, and the mixture was stirred for 2 minutes at a rotation speed of 2000 rpm using a rotation / revolution type stirring mixer (Shinky Corporation, “Awatori Nertaro ARE-310 type”). Mixing and defoaming were performed to obtain a uniform resin composition solution for sealing an organic EL display element.
（３）有機ＥＬ表示素子封止用樹脂シートの作製
「（２）有機ＥＬ表示素子封止用樹脂組成物溶液の調製」で得られた有機ＥＬ表示素子封止用樹脂組成物溶液を、離型処理を施したＰＥＴフィルム（ＰＥＴ離型フィルム）上に、乾燥後の厚みが所望の膜厚（２０μｍ）となるようにアプリケーターを調整して塗布し、オーブン中で１００℃にて１５分間乾燥してＰＥＴフィルム上に積層された有機ＥＬ表示素子封止用樹脂シートを得た。
(3) Preparation of Resin Sheet for Sealing Organic EL Display Element The resin composition solution for sealing an organic EL display element obtained in “(2) Preparation of resin composition solution for sealing an organic EL display element” is separated. On the PET film (PET release film) that has been subjected to mold treatment, the applicator is adjusted and applied so that the thickness after drying becomes the desired film thickness (20 μm), and dried in an oven at 100 ° C. for 15 minutes. Thus, an organic EL display element sealing resin sheet laminated on the PET film was obtained.
（実施例２〜２２、比較例１）
用いた材料及び配合量を表１〜３に示したものとしたこと以外は、実施例１と同様にして有機ＥＬ表示素子封止用樹脂組成物溶液及び有機ＥＬ表示素子封止用樹脂シートを作製した。
(Examples 2 to 22, Comparative Example 1)
A resin composition solution for sealing an organic EL display element and a resin sheet for sealing an organic EL display element were prepared in the same manner as in Example 1 except that the used materials and blending amounts were those shown in Tables 1 to 3. Produced.
＜評価＞
実施例及び比較例で得られた各有機ＥＬ表示素子封止用樹脂シートについて、以下の評価を行った。結果を表１〜３に示した。
<Evaluation>
The following evaluation was performed about the resin sheet for sealing each organic EL display element obtained by the Example and the comparative example. The results are shown in Tables 1-3.
（１）バリア性
実施例及び比較例で得られた各有機ＥＬ表示素子封止用樹脂シートについて、ＪＩＳ Ｚ ０２０８のカップ法に準拠し、試験温度６０℃、試験湿度９０％の条件にて透湿度測定を行った。
透湿度が１６ｇ／ｍ２／２４ｈ以下であった場合を「○」、１６ｇ／ｍ２／２４ｈを超えた場合を「×」としてバリア性を評価した。
なお、実施例及び比較例で得られた各有機ＥＬ表示素子封止用樹脂シート（厚さ２０μｍ）は非常に柔軟であり、単独膜で測定カップに設置することが困難であったため、ＰＥＴ離型フィルム上に作製した各有機ＥＬ表示素子封止用樹脂シートをろ紙上に転写し、該ろ紙を支持体として測定カップに設置して透湿度測定を行った。また、透湿度は、厚みを１００μｍとした場合の値として換算した。
(1) Barrier properties Each of the organic EL display element sealing resin sheets obtained in Examples and Comparative Examples is transparent under the conditions of a test temperature of 60 ° C. and a test humidity of 90% in accordance with the cup method of JIS Z 0208. Humidity measurement was performed.
Moisture permeability and rated the barrier property when was less than 16g / m 2 / 24h as "○", the case where it exceeds 16g / m 2 / 24h "×".
In addition, since each organic EL display element sealing resin sheet (thickness 20 μm) obtained in Examples and Comparative Examples is very flexible and difficult to install in a measuring cup as a single film, Each resin sheet for sealing an organic EL display element produced on the mold film was transferred onto a filter paper, and the moisture permeability was measured by placing the filter paper as a support in a measuring cup. Further, the moisture permeability was converted as a value when the thickness was 100 μm.
（２）透明性
実施例及び比較例で得られた各有機ＥＬ表示素子封止用樹脂シート（厚さ２０μｍ）を、幅２５ｍｍ、長さ５０ｍｍ、厚さ０．７ｍｍの無アルカリガラス基板にロールラミネートして転写し、試験片を得た。得られた試験片について、分光光度計にて４００〜８００ｎｍの波長における可視光透過率を測定した。また、可視光透過率を測定した上記試験片について、へイズメーターを用いてヘイズ（曇価）の測定を行った。
透過率は、８５％以上であった場合を「○」、８５％未満であった場合を「×」とし、ヘイズは、２％以下であった場合を「○」、２％を超えた場合を「×」として透明性を評価した。
(2) Transparency Each organic EL display element sealing resin sheet (thickness 20 μm) obtained in the transparent examples and comparative examples is rolled onto a non-alkali glass substrate having a width of 25 mm, a length of 50 mm, and a thickness of 0.7 mm. Lamination and transfer were performed to obtain a test piece. About the obtained test piece, the visible light transmittance in the wavelength of 400-800 nm was measured with the spectrophotometer. Moreover, about the said test piece which measured the visible light transmittance | permeability, the haze (cloudiness value) was measured using the haze meter.
When the transmittance is 85% or more, “○”, when it is less than 85%, “X”, and when the haze is 2% or less, “○”, when it exceeds 2% The transparency was evaluated with “×”.
（３）接着性
実施例及び比較例で得られた各有機ＥＬ表示素子封止用樹脂シート（厚さ２０μｍ）を、幅２５ｍｍ、長さ３００ｍｍの大きさに切り出した。切り出したシートを無アルカリガラスの清浄面に２ｋｇの重さのローラーを１往復して貼付け、温度２３℃、湿度５０％の環境下で２４時間の静置した後、引張り試験機（オリエンテック社製、「テンシロン」）を用い、剥離角１８０°、剥離速度１００ｍｍ／分の条件にて剥離強度を測定した。
剥離強度が８Ｎ／２５ｍｍ以上であった場合を「○」、剥離強度が８Ｎ／２５ｍｍ未満であった場合を「△」、無アルカリガラスへの接着ができなかった場合を「×」として接着性を評価した。
(3) Adhesiveness Each resin sheet for sealing an organic EL display element (thickness 20 μm) obtained in Examples and Comparative Examples was cut into a size of 25 mm in width and 300 mm in length. The cut sheet was attached to a clean surface of alkali-free glass by reciprocating a 2 kg weight roller and left standing in an environment of temperature 23 ° C. and humidity 50% for 24 hours, and then a tensile tester (Orientec) Manufactured by “Tensilon”), and the peel strength was measured under the conditions of a peel angle of 180 ° and a peel speed of 100 mm / min.
When the peel strength is 8 N / 25 mm or more, “◯”, when the peel strength is less than 8 N / 25 mm, “△”, and when the adhesion to the non-alkali glass is not possible, “X” Evaluated.
（４）有機ＥＬ表示素子の発光状態
スパッタリングにより厚さ１０００ÅのＩＴＯ透明電極を成膜した無アルカリガラス基板を透明支持基板とし、真空蒸着により、Ｎ，Ｎ’−ジ（１−ナフチル）−Ｎ，Ｎ’−ジフェニルベンジジン（α−ＮＰＤ）を蒸着速度１５Å／ｓで基板に堆積させ、膜厚６００Åの正孔輸送層を成膜した。次に、トリス（８−ヒドロキシキノリラ）アルミニウム（Ａｌｑ３）を１５Å／ｓの蒸着速度で膜厚６００Åに堆積し、発光層を形成した。その後、この基板を別の真空蒸着装置に移し、フッ化リチウムを０．２Å／ｓの蒸着速度で５Å成膜した後、アルミニウムを２０Å／ｓの速度で１０００Å成膜し、有機発光材料層を有する積層体を得た。
この積層体を形成した基板上に、実施例及び比較例で得られた各有機ＥＬ表示素子封止用樹脂シート（厚さ２０μｍ）を８０℃にてロールラミネートして転写した。更に、転写した有機ＥＬ表示素子封止用樹脂シートの上にガラス基板を重ね、真空ラミネータを用いて８０℃にて加熱圧着させ、有機ＥＬ表示素子を得た。
得られた有機ＥＬ表示素子を温度６０℃、湿度９０％の条件下にて１００時間暴露した後、１０Ｖの電圧を印加し素子の発光状態（発光及びダークスポットの有無）を目視で観察した。ダークスポットがなく、均一に発光した場合を「○」、発光はしたものの、ダークスポットがあった場合を「△」、全く発光しなかった場合を「×」として評価した。
(4) Light emitting state of organic EL display element A non-alkali glass substrate on which an ITO transparent electrode having a thickness of 1000 mm is formed by sputtering is used as a transparent support substrate, and N, N′-di (1-naphthyl) -N is formed by vacuum deposition. , N′-diphenylbenzidine (α-NPD) was deposited on the substrate at a deposition rate of 15 Å / s to form a 600 Å hole transport layer. Next, tris (8-hydroxyquinola) aluminum (Alq 3 ) was deposited at a film thickness of 600 Å at a vapor deposition rate of 15 Å / s to form a light emitting layer. After that, this substrate is transferred to another vacuum vapor deposition apparatus, and 5 μm of lithium fluoride is deposited at a deposition rate of 0.2 Å / s, and then 1000 μm of aluminum is deposited at a rate of 20 Å / s, and an organic light emitting material layer is formed. The laminated body which has was obtained.
Each organic EL display element sealing resin sheet (thickness: 20 μm) obtained in Examples and Comparative Examples was roll laminated at 80 ° C. and transferred onto the substrate on which this laminate was formed. Furthermore, a glass substrate was overlaid on the transferred resin sheet for sealing an organic EL display element, and heat-pressed at 80 ° C. using a vacuum laminator to obtain an organic EL display element.
The obtained organic EL display device was exposed for 100 hours under the conditions of a temperature of 60 ° C. and a humidity of 90%, and then a voltage of 10 V was applied to visually observe the light emitting state of the device (the presence or absence of light emission and dark spots). Evaluation was made with “◯” when there was no dark spot and light was emitted uniformly, “Δ” when light was emitted but there was a dark spot, and “X” when no light was emitted.
本発明によれば、透明性及びバリア性に優れる有機エレクトロルミネッセンス表示素子封止用樹脂組成物を提供することができる。また、本発明によれば、該有機エレクトロルミネッセンス表示素子封止用樹脂組成物を用いてなる有機エレクトロルミネッセンス表示素子封止用樹脂シート及び有機エレクトロルミネッセンス表示素子を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the resin composition for organic electroluminescent display element sealing excellent in transparency and barrier property can be provided. Moreover, according to this invention, the organic electroluminescent display element sealing resin sheet and organic electroluminescent display element which use this organic electroluminescent display element sealing resin composition can be provided.
Claims (7)