JP5552863B2 - High-strength hot-dip galvanized steel sheet and manufacturing method thereof - Google Patents

Description

  The present invention relates to a high-strength hot-dip galvanized steel sheet excellent in workability using a high-strength steel sheet containing Si and Mn as a base material and a method for producing the same.

  In recent years, in the fields of automobiles, home appliances, building materials and the like, surface-treated steel sheets imparted with rust resistance to raw steel sheets, particularly hot-dip galvanized steel sheets and galvannealed steel sheets have been widely used. In addition, from the viewpoint of improving the fuel efficiency of automobiles and improving the collision safety of automobiles, there is an increasing demand for reducing the thickness of the vehicle body by increasing the strength of the vehicle body material and reducing the weight of the vehicle body. Therefore, application of high-strength steel sheets to automobiles is being promoted.

  In general, a hot dip galvanized steel sheet uses a thin steel sheet obtained by hot rolling or cold rolling a slab as a base material, and the base steel sheet is used in an annealing furnace of a continuous hot dip galvanizing line (hereinafter referred to as CGL). Manufactured by recrystallization annealing and hot dip galvanizing. In the case of an alloyed hot-dip galvanized steel sheet, it is manufactured after further hot-dip galvanizing treatment.

  Here, there are DFF type (direct flame type), NOF type (non-oxidation type), all radiant tube type, etc. as the heating furnace type of CGL annealing furnace. The construction of CGLs equipped with an all-radiant tube type heating furnace is increasing for the reason that it is possible to produce high-quality plated steel sheets at low cost due to difficulty in carrying out the process. However, unlike the DFF type (direct flame type) and NOF type (non-oxidation type), the all-radiant tube type heating furnace does not have an oxidation step immediately before annealing, so a steel plate containing an easily oxidizable element such as Si or Mn. Is disadvantageous in terms of securing plating properties.

  As a method for producing a hot-dip galvanized steel sheet using a high-strength steel sheet containing a large amount of Si and Mn as a base material, Patent Document 1 and Patent Document 2 define a heating temperature in a reduction furnace by an expression expressed by a partial pressure of water vapor. A technique for internally oxidizing the surface layer of the railway by increasing the dew point is disclosed. However, since the area for controlling the dew point is premised on the entire inside of the furnace, it is difficult to control the dew point, and stable operation is difficult. In addition, in the manufacture of galvannealed steel sheets under unstable dew point control, variations in the distribution of internal oxides formed on the base steel sheet were observed, and wetting in the longitudinal and width directions of the steel sheet was observed. There is a concern that defects such as unevenness in properties and unevenness in alloying may occur.

In Patent Document 3, not only the oxidizing gases H ₂ O and O ₂ but also the CO ₂ concentration are simultaneously defined, so that the surface layer immediately before plating is internally oxidized to suppress external oxidation. A technique for improving the appearance is disclosed. However, similarly to Patent Documents 1 and 2, also in Patent Document 3, cracks are likely to occur during processing due to the presence of the internal oxide, and the plating peel resistance deteriorates. Moreover, deterioration of corrosion resistance is also recognized. Further, there is a concern that CO ₂ may cause problems such as in-furnace contamination, carburizing on the steel sheet surface, and mechanical characteristics changing.

  Furthermore, recently, the application of high-strength hot-dip galvanized steel sheets and high-strength alloyed hot-dip galvanized steel sheets to places where machining is severe has progressed, and the anti-plating resistance characteristics at the time of high processing have become important. Yes. Specifically, it is required to suppress plating peeling at the processed part when the plated steel sheet is bent at an angle of more than 90 ° and bent at an acute angle or when the steel sheet is processed by impact.

  In order to satisfy such characteristics, not only does a large amount of Si be added to the steel to ensure the desired steel sheet structure, but also the iron core directly under the plating layer, which may be the starting point of cracking during high processing. More advanced control of the structure and structure of the surface layer is required. However, such control is difficult with the prior art, and hot dip galvanization with excellent anti-plating properties at high processing using CGL with Si-containing high-strength steel plate as a base material with an all-radiant tube type heating furnace in the annealing furnace. A steel plate could not be produced.

JP 2004-323970 A JP 2004-315960 A JP 2006-233333 A

  The present invention has been made in view of such circumstances, and uses a steel sheet containing Si and Mn as a base material, and has a high-strength hot-dip galvanized steel sheet excellent in plating appearance, corrosion resistance, and plating peeling resistance during high processing, and It aims at providing the manufacturing method.

Conventionally, the inside of a steel plate has been actively oxidized for the purpose of improving the plating property. However, at the same time, corrosion resistance and workability deteriorate. Therefore, the present inventors have studied a method for solving the problem by a new method not confined to the conventional idea. As a result, by appropriately controlling the atmosphere and temperature of the annealing process, the formation of internal oxidation is suppressed in the surface layer of the steel sheet directly under the plating layer, and the excellent plating appearance, higher corrosion resistance and good resistance to high processing. It has been found that plating peelability can be obtained. Specifically, in the heating process, the temperature in the annealing furnace: 600 ° C. or more and A ° C. or less (A: 650 ≦ A ≦ 900) is set to a temperature increase rate of 7 ° C./s or more, and the dew point of the atmosphere is − Annealing and hot dip galvanizing are performed while controlling the temperature to be 40 ° C. or lower. Temperature of annealing furnace: 600 ° C. or higher and A ° C. or lower (A: 650 ≦ A ≦ 900) temperature increase rate: 7 ° C./s or more, selective surface oxidation of easily oxidizable elements (hereinafter referred to as surface) (Referred to as thickening). Further, by setting the temperature range of the annealing furnace temperature: 600 ° C. or more and A ° C. or less (A: 650 ≦ A ≦ 900) to the dew point of the atmosphere: −40 ° C. or less, the oxygen potential at the interface between the steel sheet and the atmosphere is lowered. Suppresses surface concentration without forming internal oxidation.
By controlling the temperature rise rate and dew point in the atmosphere in this way, internal oxidation is not formed, surface concentration is suppressed as much as possible, and high-strength melting with excellent plating appearance, corrosion resistance, and resistance to plating peeling during high processing A galvanized steel sheet will be obtained. In addition, having excellent plating appearance means having an appearance in which non-plating and alloying unevenness are not recognized.
And, the high-strength hot-dip galvanized steel sheet obtained by the above method is Fe, Si, Mn, Al, P, and B, in the steel sheet surface layer portion within 100 μm from the surface of the base steel sheet, immediately below the galvanized layer. The formation of one or more oxides selected from Nb, Ti, Cr, Mo, Cu, and Ni (excluding only Fe) is suppressed, and the total amount formed is 0.060 g / m ² or less per side. It is suppressed. Thereby, the plating appearance is excellent, the corrosion resistance is remarkably improved, the crack prevention at the bending process in the surface layer of the base metal is realized, and the plating peeling resistance at the high processing is excellent.

The present invention is based on the above findings, and features are as follows.
[1] By mass%, C: 0.01 to 0.18%, Si: 0.02 to 2.0%, Mn: 1.0 to 3.0%, Al: 0.001 to 1.0% , P: 0.005 to 0.060%, S ≦ 0.01%, with the balance being Fe and unavoidable impurities on the surface of the steel sheet, the plating adhesion amount per side is 20 to 120 g / m ² A method for producing a high-strength hot-dip galvanized steel sheet having a galvanized layer, and when the steel sheet is subjected to annealing and hot-dip galvanizing treatment in a continuous hot-dip galvanizing facility, in the heating process, the temperature in the annealing furnace: 600 ° C. or higher A high-strength hot-dip galvanized steel sheet characterized by having a temperature range of A ° C. or lower (A: 650 ≦ A ≦ 900) at a rate of temperature increase of 7 ° C./s or higher and an atmospheric dew point of −40 ° C. or lower. Production method.
[2] In the above [1], the steel sheet is in mass% as a component composition, and further B: 0.001 to 0.005%, Nb: 0.005 to 0.05%, Ti: 0.005. -0.05%, Cr: 0.001-1.0%, Mo: 0.05-1.0%, Cu: 0.05-1.0%, Ni: 0.05-1.0% A method for producing a high-strength hot-dip galvanized steel sheet, comprising one or more elements selected from the inside.
[3] In the above [1] or [2], after the hot dip galvanizing treatment, the steel plate is further heated to a temperature of 450 ° C. or higher and 600 ° C. or lower to perform alloying treatment, and the Fe content of the galvanized layer is set to 7 A method for producing a high-strength hot-dip galvanized steel sheet, characterized by being in the range of ˜15 mass%.
[4] Fe, Si, Mn, Al produced by the production method according to any one of [1] to [3], and formed in a steel plate surface layer portion within 100 μm from the surface of the underlying steel plate immediately below the galvanized layer. A high-strength hot-dip galvanized steel sheet, wherein the oxides of P, B, Nb, Ti, Cr, Mo, Cu, and Ni are 0.060 g / m ² or less per side.

  In the present invention, the high strength means that the tensile strength TS is 340 MPa or more. The high-strength hot-dip galvanized steel sheet of the present invention includes a plated steel sheet (hereinafter sometimes referred to as GI) that is not subjected to alloying after the hot-dip galvanizing process, and a plated steel sheet (hereinafter referred to as GA) that is subjected to the alloying process. In some cases).

  ADVANTAGE OF THE INVENTION According to this invention, the high intensity | strength hot-dip galvanized steel plate excellent in plating external appearance, corrosion resistance, and the plating peeling resistance at the time of high processing is obtained.

  Hereinafter, the present invention will be specifically described. In the following description, the content of each element of the steel component composition and the unit of the content of each element of the plating layer component composition are all “mass%”, and hereinafter, simply “%” unless otherwise specified. Show.

First, an annealing atmosphere condition that determines the structure of the surface of the underlying steel sheet immediately below the plating layer, which is the most important requirement in the present invention, will be described.
In high-strength hot-dip galvanized steel sheets with a large amount of Si and Mn added to the steel, in order to satisfy corrosion resistance and anti-plating resistance during high processing, it may be the starting point for corrosion and cracking during high processing. Therefore, it is required to minimize internal oxidation of the surface layer of the railway just below the plating layer.

  Although it is possible to improve the plateability by promoting the internal oxidation of Si and Mn, this leads to deterioration of corrosion resistance and workability. For this reason, it is necessary to improve corrosion resistance and workability by suppressing internal oxidation while maintaining good plating properties, other than a method of promoting internal oxidation of Si or Mn. As a result of the examination, in the present invention, in order to suppress non-plating defects, first, the amount of surface concentrate formed is suppressed as much as possible by increasing the heating rate in the heating process. However, since it is difficult to completely suppress surface enrichment by itself, the oxygen potential is lowered by controlling the dew point in the annealing process, and the activity in the surface layer part of the easily oxidizable elements such as Si and Mn is reduced. Let And the external oxidation of these elements is suppressed and, as a result, the platability is improved. And the internal oxidation formed in a surface iron surface layer part is also suppressed, and corrosion resistance and high workability will be improved.

Such an effect is obtained when annealing and hot dip galvanizing treatment are performed in a continuous hot dip galvanizing facility, and in the heating process, the temperature in the annealing furnace is 600 ° C. or higher and A ° C. or lower (A: 650 ≦ A ≦ 900). Is controlled so that the temperature rising rate is 7 ° C./s or more and the dew point of the atmosphere is −40 ° C. or less. By controlling the temperature in the annealing furnace: 600 ° C. or more and A ° C. or less (A: 650 ≦ A ≦ 900) so that the temperature rising rate is 7 ° C./s or more, the amount of surface concentrate produced is suppressed as much as possible. To do. Furthermore, for the surface concentrate formed without being suppressed in the heating process, the dew point of the atmosphere is −40 ° C. in the temperature range of the annealing furnace temperature: 600 ° C. to A ° C. (A: 650 ≦ A ≦ 900). By controlling to be as follows, the oxygen potential at the interface between the steel plate and the atmosphere is lowered, and selective surface diffusion and oxidation of Si, Mn, etc. without forming internal oxidation (hereinafter referred to as surface concentration) Suppress. And higher corrosion resistance without unplating and good plating peeling resistance at the time of high processing will be obtained.
The reason why the temperature range for controlling the heating rate and the dew point is 600 ° C. or higher is as follows. In the temperature range below 600 ° C., surface enrichment and internal oxidation to such an extent that non-plating occurs, corrosion resistance deteriorates, plating peel resistance deteriorates, etc. do not occur. Therefore, the temperature is set to 600 ° C. or higher, which is a temperature range in which the effect of the present invention is exhibited.
The reason why the temperature range is set to A ° C. or lower (A: 650 ≦ A ≦ 900) is as follows. First, in the temperature range below 650 ° C., the time for controlling the temperature increase rate to 7 ° C./s or more is short, and the effect of the present invention is small. Even if the dew point is lowered to −40 ° C. or lower, the effect of suppressing surface concentration is not sufficient. For this reason, A shall be 650 degreeC or more. Moreover, when it exceeds 900 degreeC, there is no problem in the effect of this invention, but it becomes disadvantageous from a viewpoint of deterioration by the oxidation of the equipment (roll etc.) in an annealing furnace, and a cost increase. Therefore, it shall be 900 degrees C or less.
The reason why the rate of temperature rise is 7 ° C./s or more and the dew point is −40 ° C. or less is as follows. The effect of suppressing surface concentration begins to be recognized when the rate of temperature rise is 7 ° C./s or more and the dew point is −40 ° C. or less. The upper limit of the rate of temperature rise is not particularly set, but if it is 500 ° C./s or more, the effect is saturated and disadvantageous in terms of cost. Moreover, although the minimum of a dew point is not provided, since an effect will be saturated and it will become disadvantageous in cost at -80 degrees C or less, -80 degrees C or more is desirable.

  It is possible to set the heating rate to 7 ° C./s or more, for example, by placing the induction heater in an annealing furnace in which the steel plate temperature is 600 ° C. or more and A ° C. or less.

Next, the steel component composition of the high-strength hot-dip galvanized steel sheet that is the subject of the present invention will be described.
C: 0.01 to 0.18%
C improves workability by forming martensite or the like as a steel structure. For that purpose, 0.01% or more is necessary. On the other hand, if it exceeds 0.18%, the weldability deteriorates. Therefore, the C content is 0.01% or more and 0.18% or less.

Si: 0.02 to 2.0%
Si is an element effective for strengthening steel to obtain a good material, and 0.02% or more is necessary to obtain the intended strength of the present invention. If Si is less than 0.02%, the strength within the scope of application of the present invention cannot be obtained, and there is no particular problem with respect to resistance to plating peeling during high processing. On the other hand, if it exceeds 2.0%, it becomes difficult to improve the plating peel resistance at the time of high processing. Therefore, the Si content is 0.02% or more and 2.0% or less.

Mn: 1.0-3.0%
Mn is an element effective for increasing the strength of steel. In order to ensure mechanical properties and strength, it is necessary to contain 1.0% or more. On the other hand, if it exceeds 3.0%, it becomes difficult to ensure weldability and plating adhesion, and to ensure a balance between strength and ductility. Therefore, the Mn content is 1.0% or more and 3.0% or less.

Al: 0.001 to 1.0%
Al is added for the purpose of deoxidizing molten steel, but if the content is less than 0.001%, the purpose is not achieved. The effect of deoxidation of molten steel is obtained at 0.001% or more. On the other hand, if it exceeds 1.0%, the cost increases. Therefore, the Al content is 0.001% or more and 1.0% or less.

P: 0.005 to 0.060% or less P is one of the elements inevitably contained, and in order to make it less than 0.005%, there is a concern about an increase in cost, so 0.005% or more And On the other hand, if P exceeds 0.060%, weldability deteriorates. Furthermore, the surface quality deteriorates. Further, when the alloying treatment is not performed, the plating adhesion is deteriorated, and when the alloying treatment is performed, the alloying treatment temperature cannot be increased unless the alloying treatment temperature is increased. Also, if the alloying temperature is raised to achieve the desired degree of alloying, the ductility deteriorates and at the same time the adhesion of the alloyed plating film deteriorates, so the desired degree of alloying, good ductility, and alloyed plating film Cannot be achieved. Therefore, the P content is 0.005% or more and 0.060% or less.

S ≦ 0.01%
S is one of the elements inevitably contained. The lower limit is not specified, but if it is contained in a large amount, the weldability deteriorates, so the content is made 0.01% or less.

In order to control the balance between strength and ductility, B: 0.001 to 0.005%, Nb: 0.005 to 0.05%, Ti: 0.005 to 0.05%, Cr: 0.001 One or more elements selected from -1.0%, Mo: 0.05-1.0%, Cu: 0.05-1.0%, Ni: 0.05-1.0% are required. It may be added depending on.
The reason for limiting the appropriate addition amount in the case of adding these elements is as follows.

B: 0.001 to 0.005%
When B is less than 0.001%, it is difficult to obtain an effect of promoting quenching. On the other hand, if it exceeds 0.005%, the plating adhesion deteriorates. Therefore, when it contains, B amount shall be 0.001% or more and 0.005% or less.

Nb: 0.005 to 0.05%
If Nb is less than 0.005%, it is difficult to obtain the effect of adjusting the strength and the effect of improving the plating adhesion at the time of composite addition with Mo. On the other hand, if it exceeds 0.05%, the cost increases. Therefore, when it contains, Nb amount shall be 0.005% or more and 0.05% or less.

Ti: 0.005 to 0.05%
If Ti is less than 0.005%, the effect of adjusting the strength is difficult to obtain. On the other hand, if it exceeds 0.05%, the plating adhesion deteriorates. Therefore, when it contains, Ti amount shall be 0.005% or more and 0.05% or less.

Cr: 0.001 to 1.0%
When Cr is less than 0.001%, it is difficult to obtain a hardenability effect. On the other hand, if it exceeds 1.0%, the surface of Cr is concentrated, so that the plating adhesion and weldability deteriorate. Therefore, when it contains, Cr amount shall be 0.001% or more and 1.0% or less.

Mo: 0.05-1.0%
If Mo is less than 0.05%, it is difficult to obtain the effect of adjusting the strength and the effect of improving the plating adhesion at the time of composite addition with Nb, Ni or Cu. On the other hand, if it exceeds 1.0%, cost increases. Therefore, when contained, the Mo content is 0.05% or more and 1.0% or less.

Cu: 0.05 to 1.0%
If Cu is less than 0.05%, it is difficult to obtain the effect of promoting the formation of the residual γ phase and the effect of improving the plating adhesion when combined with Ni or Mo. On the other hand, if it exceeds 1.0%, cost increases. Therefore, when contained, the Cu content is 0.05% or more and 1.0% or less.

Ni: 0.05-1.0%
When Ni is less than 0.05%, it is difficult to obtain the effect of promoting the formation of the residual γ phase and the effect of improving the plating adhesion when Cu and Mo are added together. On the other hand, if it exceeds 1.0%, cost increases. Therefore, when it contains, Ni amount shall be 0.05% or more and 1.0% or less.

  The balance other than the above is Fe and inevitable impurities.

  Next, the manufacturing method of the high-strength hot-dip galvanized steel sheet of the present invention and the reason for limitation will be described.

  The steel having the above chemical components is hot-rolled and then cold-rolled to obtain a steel plate, and then subjected to annealing and hot-dip galvanizing treatment in a continuous hot-dip galvanizing facility. At this time, in the present invention, in the heating process, the temperature range of the annealing furnace temperature: 600 ° C. or more and A ° C. or less (A: 650 ≦ A ≦ 900) is set to a temperature rising rate: 7 ° C./s or more, and Atmospheric dew point: -40 ° C or lower. This is the most important requirement in the present invention.

Hot rolling Usually, it can be performed on the conditions performed.

It is preferable to perform a pickling treatment after hot pickling. The black scale formed on the surface in the pickling process is removed, and then cold-rolled. The pickling conditions are not particularly limited.

Cold rolling is preferably performed at a rolling reduction of 40% to 80%. If the rolling reduction is less than 40%, the recrystallization temperature is lowered, and the mechanical characteristics are likely to deteriorate. On the other hand, when the rolling reduction exceeds 80%, the steel sheet is a high-strength steel plate, so that not only the rolling cost is increased, but also the surface concentration during annealing is increased, so that the plating characteristics are deteriorated.

The cold-rolled steel sheet is annealed and then hot dip galvanized.
In the annealing furnace, a heating process is performed in which the steel sheet is heated to a predetermined temperature in a preceding heating zone, and a soaking process is performed in which the temperature is maintained at a predetermined temperature for a predetermined time in a subsequent soaking zone.
And as mentioned above, the temperature range of annealing furnace temperature: 600 degreeC or more and A degrees C or less (A: 650 <= A <= 900) shall be temperature rising rate: 7 degree-C / s or more, and the dew point of atmosphere: -40 Annealing and hot dip galvanizing are performed while controlling the temperature to be equal to or lower. Since the normal dew point is higher than −40 ° C., the dew point is set to −40 ° C. or lower by absorbing and removing moisture in the furnace with an absorbent.

  Note that the dew point in the annealing furnace atmosphere other than the region of 600 ° C. or more and A ° C. or less may be higher than −40 ° C. It may be -40 ° C to -10 ° C which is a normal operation condition.

If the hydrogen concentration in the annealing furnace atmosphere is less than 1 vol%, the activation effect by reduction cannot be obtained, and the plating peel resistance deteriorates. The upper limit is not particularly specified, but if it exceeds 50 vol%, the cost increases and the effect is saturated. Therefore, the hydrogen concentration is preferably 1 vol% or more and 50 vol% or less. In addition, the gas component in an annealing furnace consists of nitrogen and an unavoidable impurity gas other than hydrogen. Other gas components may be included as long as the effects of the present invention are not impaired.
The hot dip galvanizing treatment can be performed by a conventional method.

Next, an alloying treatment is performed as necessary.
When the alloying treatment is performed subsequent to the hot dip galvanizing treatment, the hot dip galvanizing treatment is performed, and then the steel plate is heated to 450 ° C. or more and 600 ° C. or less to perform the alloying treatment, and the Fe content of the plating layer is 7 to 15 % Is preferable. If it is less than 7%, uneven alloying occurs and flaking properties deteriorate. On the other hand, if it exceeds 15%, the plating peel resistance deteriorates.

As described above, the high-strength hot-dip galvanized steel sheet of the present invention is obtained. The high-strength hot-dip galvanized steel sheet of the present invention has a galvanized layer having a plating adhesion amount of 20 to 120 g / m ^{2 on} one surface of the steel sheet. If it is less than 20 g / m ² , it becomes difficult to ensure corrosion resistance. On the other hand, when it exceeds 120 g / m ² , the plating peel resistance deteriorates.
And it has the characteristic in the structure of the base steel plate surface just under a plating layer as follows.
In the steel plate surface layer portion within 100 μm from the surface of the underlying steel plate immediately below the galvanized layer, it is selected from Fe, Si, Mn, Al, P, and further B, Nb, Ti, Cr, Mo, Cu, and Ni. The formation of one or more oxides is suppressed to 0.060 g / m ² or less per side in total.
In hot-dip galvanized steel sheets with Si and a large amount of Mn added to the steel, in order to satisfy the corrosion resistance and anti-plating resistance during high processing, there is a possibility of starting from corrosion and cracking during high processing. It is required to minimize the internal oxidation of the surface layer of the ground metal directly below a certain plating layer. Therefore, in the present invention, first, the activity in the surface layer portion of the iron base such as Si or Mn, which is an easily oxidizable element, is reduced by lowering the oxygen potential in the annealing process in order to ensure the plating property. And the external oxidation of these elements is suppressed and, as a result, the platability is improved. Furthermore, internal oxidation formed in the surface layer portion of the ground iron is also suppressed, and corrosion resistance and high workability are improved. Such effects are at least selected from Fe, Si, Mn, Al, P, and further B, Nb, Ti, Cr, Mo, Cu, Ni on the steel sheet surface layer portion within 100 μm from the surface of the base steel plate. It is recognized by suppressing the formation amount of one or more oxides to 0.060 g / m ² or less in total. When the total oxide formation amount (hereinafter referred to as internal oxidation amount) exceeds 0.060 g / m ² , the corrosion resistance and the high workability deteriorate. Even if the internal oxidation amount is suppressed to less than 0.0001 g / m ² , the corrosion resistance and the high workability improvement effect are saturated, so the lower limit of the internal oxidation amount is preferably 0.0001 g / m ² .

  Furthermore, in addition to the above, in the present invention, in order to improve the plating peel resistance, the base iron structure on which the Si and Mn-based composite oxide grows is preferably a soft and rich workability ferrite phase.

  Hereinafter, the present invention will be specifically described based on examples.

  The hot-rolled steel sheet having the steel composition shown in Table 1 was pickled and the black scale removed, and then cold-rolled under the conditions shown in Table 2 to obtain a cold-rolled steel sheet having a thickness of 1.0 mm.

  Next, the cold-rolled steel sheet obtained above was charged into a CGL equipped with an all-radiant tube type heating furnace in an annealing furnace. In CGL, as shown in Table 2, after controlling the heating rate and dew point in the temperature range of 600 ° C. or higher and A ° C. or lower (A: 650 ≦ A ≦ 900), annealing is performed, and then Al content at 460 ° C. is contained. Hot dip galvanizing treatment was performed in a Zn bath. The dew point of the atmosphere in the annealing furnace other than the region of 600 ° C. to A ° C. was basically −35 ° C. In the heating furnace, heating by an all radiant tube and heating by an induction heater were used in combination, and the temperature rising rate was set to 7 ° C./s.

The gas components in the atmosphere consisted of nitrogen, hydrogen, and inevitable impurity gases, and the dew point of −40 ° C. or lower was controlled by absorbing and removing moisture in the atmosphere. The hydrogen concentration in the atmosphere was basically 10 vol%.
In addition, GA used a 0.14% Al-containing Zn bath, and GI used a 0.18% Al-containing Zn bath. The adhesion amount was adjusted by gas wiping, and GA was alloyed.

  The hot-dip galvanized steel sheets (GA and GI) obtained as described above were examined for appearance (plating appearance), corrosion resistance, plating peeling resistance during high processing, and workability. Moreover, the quantity (internal oxidation amount) of the oxide which exists in the surface steel plate surface layer part to 100 micrometers directly under a plating layer was measured. The measurement method and evaluation criteria are shown below.

<Appearance>
Appearance was judged as good appearance (symbol ◯) when there was no appearance defect such as non-plating or alloying unevenness, and when it was present, it was judged as poor appearance (symbol x).

<Corrosion resistance>
A salt spray test based on JIS Z 2371 (2000) was conducted for three days on an alloyed hot-dip galvanized steel sheet with dimensions of 70 mm x 150 mm, and the corrosion product was treated with chromic acid (concentration 200 g / L, 80 ° C) for 1 minute. After washing and removing, the plating corrosion weight loss (g / m ² · day) before and after the test per one side was measured by a weight method and evaluated according to the following criteria.
○ (Good): Less than 20g / m ² · day × (Poor): 20g / m ² · Day or more

<Plating resistance>
With regard to the resistance to plating peeling at the time of high processing, in GA, it is required to suppress plating peeling at the bent portion when bent at an acute angle exceeding 90 °. In this example, the cellophane tape was pressed against the processed portion bent by 120 ° to transfer the peeled material to the cellophane tape, and the amount of the peeled material on the cellophane tape was determined by the fluorescent X-ray method as the Zn count number. At this time, the mask diameter is 30 mm, the fluorescent X-ray acceleration voltage is 50 kV, the acceleration current is 50 mA, and the measurement time is 20 seconds. In light of the following criteria, those with ranks 1 and 2 were evaluated to have good plating peel resistance (symbol ◯), and those with three or more were evaluated to have poor plating peel resistance (symbol x).
Fluorescent X-ray Zn count number Rank 0 to less than 500: 1 (good)
500 or more and less than 1000: 2
1000 or more and less than −2000: 3
2000 or more and less than −3000: 4
3000 or more: 5 (poor)
In GI, resistance to plating peeling during an impact test is required. A ball impact test was performed, the processed part was peeled off with tape, and the presence or absence of peeling of the plating layer was visually determined. Ball impact conditions are a ball weight of 1000 g and a drop height of 100 cm.
○: Plating layer is not peeled ×: Plating layer is peeled

<Processability>
For workability, JIS No. 5 tensile test specimens were taken from the sample in the 90 ° direction with respect to the rolling direction, and subjected to a tensile test at a constant crosshead speed of 10 mm / min in accordance with the provisions of JIS Z 2241. / MPa) and elongation (El%) were measured, and when TS was less than 650 MPa, TS × El ≧ 22000 was judged good, and TS × El <22000 was judged poor. When TS was 650 MPa or more and 900 MPa, TS × El ≧ 20000 was judged good, and TS × El <20000 was judged poor. When TS was 900 MPa or more, TS × El ≧ 18000 was judged good, and TS × El <18000 was judged poor.

<Internal oxidation amount in the region of 100 μm directly under the plating layer>
The amount of internal oxidation was measured by “impulse furnace melting-infrared absorption method”. However, since it is necessary to subtract the amount of oxygen contained in the material (that is, the high-strength steel plate before annealing), in the present invention, the surface layer portions on both surfaces of the high-strength steel plate after continuous annealing are polished by 100 μm or more in the steel. Measure the oxygen concentration, set the measured value as the amount of oxygen OH contained in the material, measure the oxygen concentration in the steel in the entire thickness direction of the high-strength steel sheet after continuous annealing, and measure the measured value internally. The subsequent oxygen amount OI was used. The difference between OI and OH (= OI-OH) is calculated using the oxygen amount OI after internal oxidation of the high-strength steel plate thus obtained and the oxygen amount OH contained in the material, and further, single-sided unit area (i.e. 1 m ²⁾ value converted into the amount per (g / m ²⁾ as an internal oxide amount.

  The results obtained as described above are shown in Table 2 together with the production conditions.

As is apparent from Table 2, GI and GA (examples of the present invention) produced by the method of the present invention are high-strength steel sheets containing a large amount of oxidizable elements such as Si and Mn. Excellent in workability and anti-plating resistance during high processing, and good plating appearance.
On the other hand, in the comparative example, any one or more of plating appearance, corrosion resistance, workability, and plating peeling resistance during high processing is inferior.

  The hot-rolled steel sheet having the steel composition shown in Table 3 was pickled and the black scale was removed, and then cold-rolled under the conditions shown in Table 4 to obtain a cold-rolled steel sheet having a thickness of 1.0 mm.

  Next, the cold-rolled steel sheet obtained above was charged into a CGL equipped with an all-radiant tube type heating furnace in an annealing furnace. In CGL, as shown in Table 4, after controlling the heating rate and dew point in the temperature range of 600 ° C. or higher and A ° C. or lower (A: 650 ≦ A ≦ 900), annealing is performed, and then Al content at 460 ° C. is contained. Hot dip galvanizing treatment was performed in a Zn bath. The dew point of the atmosphere in the annealing furnace other than the region of 600 ° C. to A ° C. was basically −35 ° C. In the heating furnace, heating by an all radiant tube and heating by an induction heater were used in combination, and the temperature rising rate was set to 7 ° C./s.

  The gas components in the atmosphere consisted of nitrogen, hydrogen, and inevitable impurity gases, and the dew point of −40 ° C. or lower was controlled by absorbing and removing moisture in the atmosphere. The hydrogen concentration in the atmosphere was basically 10 vol%.

  In addition, GA used a 0.14% Al-containing Zn bath, and GI used a 0.18% Al-containing Zn bath. The adhesion amount was adjusted by gas wiping, and GA was alloyed.

  The hot-dip galvanized steel sheets (GA and GI) obtained as described above were examined for appearance (plating appearance), corrosion resistance, plating peeling resistance during high processing, and workability. Moreover, the quantity (internal oxidation amount) of the oxide which exists in the surface steel plate surface layer part to 100 micrometers directly under a plating layer was measured. The measurement method and evaluation criteria are shown below.

<Appearance>
Appearance was judged as good appearance (symbol ◯) when there was no appearance defect such as non-plating or alloying unevenness, and when it was present, it was judged as poor appearance (symbol x).

<Corrosion resistance>
A salt spray test based on JIS Z 2371 (2000) was conducted for three days on an alloyed hot-dip galvanized steel sheet with dimensions of 70 mm x 150 mm, and the corrosion product was treated with chromic acid (concentration 200 g / L, 80 ° C) for 1 minute. After washing and removing, the plating corrosion weight loss (g / m ² · day) before and after the test per one side was measured by a weight method and evaluated according to the following criteria.
○ (Good): Less than 20g / m ² · day × (Poor): 20g / m ² · Day or more

<Plating resistance>
With regard to the resistance to plating peeling at the time of high processing, in GA, it is required to suppress plating peeling at the bent portion when bent at an acute angle exceeding 90 °. In this example, the cellophane tape was pressed against the processed portion bent by 120 ° to transfer the peeled material to the cellophane tape, and the amount of the peeled material on the cellophane tape was determined by the fluorescent X-ray method as the Zn count number. At this time, the mask diameter is 30 mm, the fluorescent X-ray acceleration voltage is 50 kV, the acceleration current is 50 mA, and the measurement time is 20 seconds. In light of the following criteria, those with ranks 1 and 2 were evaluated to have good plating peel resistance (symbol ◯), and those with three or more were evaluated to have poor plating peel resistance (symbol x).
Fluorescent X-ray Zn count number Rank 0 to less than 500: 1 (good)
500 or more and less than 1000: 2
1000 or more and less than −2000: 3
2000 or more and less than −3000: 4
3000 or more: 5 (poor)
In GI, resistance to plating peeling during an impact test is required. A ball impact test was performed, the processed part was peeled off with tape, and the presence or absence of peeling of the plating layer was visually determined. Ball impact conditions are a ball weight of 1000 g and a drop height of 100 cm.
○: Plating layer is not peeled ×: Plating layer is peeled

<Processability>
For workability, JIS No. 5 tensile test specimens were taken from the sample in the 90 ° direction with respect to the rolling direction, and subjected to a tensile test at a constant crosshead speed of 10 mm / min in accordance with the provisions of JIS Z 2241. / MPa) and elongation (El%) were measured, and when TS was less than 650 MPa, TS × El ≧ 22000 was judged good, and TS × El <22000 was judged poor. When TS was 650 MPa or more and 900 MPa, TS × El ≧ 20000 was judged good, and TS × El <20000 was judged poor. When TS was 900 MPa or more, TS × El ≧ 18000 was judged good, and TS × El <18000 was judged poor.

<Internal oxidation amount in the region of 100 μm directly under the plating layer>
The amount of internal oxidation was measured by “impulse furnace melting-infrared absorption method”. However, since it is necessary to subtract the amount of oxygen contained in the material (that is, the high-strength steel plate before annealing), in the present invention, the surface layer portions on both surfaces of the high-strength steel plate after continuous annealing are polished by 100 μm or more in the steel. Measure the oxygen concentration, set the measured value as the amount of oxygen OH contained in the material, measure the oxygen concentration in the steel in the entire thickness direction of the high-strength steel sheet after continuous annealing, and measure the measured value internally. The subsequent oxygen amount OI was used. The difference between OI and OH (= OI-OH) is calculated using the oxygen amount OI after internal oxidation of the high-strength steel plate thus obtained and the oxygen amount OH contained in the material, and further, single-sided unit area (i.e. 1 m ²⁾ value converted into the amount per (g / m ²⁾ as an internal oxide amount.

  The results obtained above are shown in Table 4 together with the production conditions.

As is apparent from Table 4, GI and GA (examples of the present invention) produced by the method of the present invention are high-strength steel sheets containing a large amount of oxidizable elements such as Si and Mn. Excellent in workability and anti-plating resistance during high processing, and good plating appearance.
On the other hand, in the comparative example, any one or more of plating appearance, corrosion resistance, workability, and plating peeling resistance during high processing is inferior.

  The high-strength hot-dip galvanized steel sheet according to the present invention is excellent in plating appearance, corrosion resistance, workability, and anti-plating resistance during high processing, and is used as a surface-treated steel sheet for reducing the weight and strength of an automobile body. be able to. In addition to automobiles, the steel sheet can be applied in a wide range of fields such as home appliances and building materials as a surface-treated steel sheet provided with rust prevention properties.

Claims (4)

In mass%, C: 0.01 to 0.18%, Si: 0.02 to 2.0%, Mn: 1.0 to 3.0%, Al: 0.001 to 1.0%, P: A galvanized layer containing 0.005 to 0.060%, S ≦ 0.01%, the balance being Fe and unavoidable impurities on the surface of the steel sheet, and the coating amount per one side being 20 to 120 g / m ² Is a method for producing a high-strength hot-dip galvanized steel sheet, and when the steel sheet is subjected to annealing and hot-dip galvanizing treatment in a continuous hot-dip galvanizing equipment, Production of a high-strength hot-dip galvanized steel sheet characterized by controlling only the temperature range of (A: 650 ≦ A ≦ 900) to a heating rate of 7 ° C./s or more and an atmospheric dew point of −40 ° C. or less. Method.   The steel sheet is in mass% as a component composition, and B: 0.001 to 0.005%, Nb: 0.005 to 0.05%, Ti: 0.005 to 0.05%, Cr: 0 One or more elements selected from 0.001 to 1.0%, Mo: 0.05 to 1.0%, Cu: 0.05 to 1.0%, Ni: 0.05 to 1.0% The manufacturing method of the high intensity | strength hot-dip galvanized steel plate of Claim 1 characterized by the above-mentioned.   After the hot dip galvanizing treatment, the steel plate is further heated to a temperature of 450 ° C. or higher and 600 ° C. or lower to perform alloying treatment, and the Fe content of the galvanized layer is set in the range of 7 to 15% by mass. The manufacturing method of the high intensity | strength hot-dip galvanized steel plate of Claim 1 or 2. Fe, Si, Mn, Al, P, B, Nb, produced by the production method according to any one of claims 1 to 3 and formed on a steel sheet surface layer portion within 100 μm from the surface of the underlying steel sheet immediately below the galvanized layer. A high-strength hot-dip galvanized steel sheet, wherein at least one oxide selected from Ti, Cr, Mo, Cu, and Ni is 0.060 g / m ² or less per side.