JP4719574B2 - Planographic printing plate precursor - Google Patents

Description

  The present invention relates to a lithographic printing plate precursor, and more specifically, negative lithographic printing comprising a photosensitive layer containing a polymerizable composition comprising a polyurethane resin having an ethylenically unsaturated bond, capable of highly sensitive writing with a laser beam. Regarding the original edition.

  Conventionally, PS plates having a structure in which an oleophilic photosensitive resin layer is provided on a hydrophilic support are widely used as photosensitive lithographic printing plates, and the plate making method is usually mask exposure via a lithographic film. After (surface exposure), an unnecessary photosensitive resin layer was dissolved and removed to form an image portion and a non-image portion to obtain a desired printing plate.

  In recent years, digitization techniques that electronically process, store, and output image information using a computer have become widespread. Various new image output methods corresponding to such digitization techniques have come into practical use. As a result, computer-to-plate (CTP) technology that scans highly directional light such as laser light according to digitized image information and directly produces printing plates without going through a lithographic film is eagerly desired. Therefore, obtaining a lithographic printing plate precursor adapted to this is an important technical issue.

  As such a lithographic printing plate precursor capable of scanning exposure, an oleophilic photosensitive resin layer containing a photosensitive compound capable of generating active species such as radicals and Bronsted acid by laser exposure on a hydrophilic support (hereinafter referred to as “lithographic printing plate precursor”) , Which is also referred to as a photosensitive layer) has been proposed and is already on the market. This negative lithographic printing plate precursor is laser-scanned based on digital information to generate active species, which causes physical or chemical changes in the photosensitive layer to insolubilize it, followed by development processing to enable the lithographic printing plate Can be obtained. In particular, a photopolymerization type photosensitive layer containing a photopolymerization initiator excellent in photosensitive speed on a hydrophilic support, an addition-polymerizable ethylenically unsaturated compound, and a binder polymer soluble in an alkali developer, and necessary A lithographic printing plate precursor provided with an oxygen-blocking protective layer in accordance with the printing plate having desirable printing performance due to advantages such as excellent productivity, simple development processing, and good resolution and inking properties. It can be.

Also, in recent years, disposal of waste liquid discharged with alkali development processing has become a major concern for the entire industry due to consideration for the global environment, and alkali (eg, potassium hydroxide) that is the main component of the developer is becoming a major concern. Attention is focused on measures to reduce the burden of waste liquid disposal by development processing that does not rely on a strong alkaline developer having a pH of 10 or more (such as a mild development treatment with a solution of pH 2 to 10) containing a high concentration of such a substance (generally called a strong base). Gathered.
Accordingly, a planographic printing plate that expresses desirable printing performance not only in a strong alkali development process at pH 10 or higher but also in a mild development process with a solution having a pH of 2 to 10 has been strongly desired.

Conventionally, alkali-soluble polyurethane resin binders (for example, see Patent Documents 1 and 2) and alkali-soluble acrylic resin binders having an ethylenically unsaturated bond in the side chain (for example, Patent Document 3) for the purpose of increasing printing durability of printing plates. And 4) have been used.
In increasing the printing durability, the copolymer component of the polyurethane resin binder is changed (for example, see Patent Documents 5 and 6), or the unit structure containing ethylenically unsaturated bonds in the acrylic resin binder is changed. This is a common approach (see, for example, Patent Document 7).

  However, in the study of high printing durability in the above polyurethane resin binder, a trade-off with developability with time (substantially synonymous with raw storage) due to the high cohesion resulting from the urethane bond in the polyurethane structure, and the acrylic In the study of improving the printing durability by changing the unit structure containing the side chain ethylenically unsaturated bond in the resin binder, the development with time is caused by dark polymerization of the C = C double bond part of the side chain. There was a potential trade-off.

Furthermore, in a mild development system using a liquid having a pH of 2 to 10, since it is very low alkali with respect to a conventional strong alkali, the alkali solubility is insufficient, and as a result, there is a problem of smearing during printing due to poor development. Was holding.
Japanese Unexamined Patent Publication No. 63-11345 Japanese Patent Publication No. 7-120038 Japanese Examined Patent Publication No. 3-63740 Japanese Patent Laid-Open No. 10-10719 Japanese Patent Laid-Open No. 11-352691 JP 2001-125257 A JP 2002-229207 A

  The object of the present invention is that mild development processing at pH 2 to 10 or aqueous solution processing containing a water-soluble polymer is possible, and while maintaining good printing durability, very good raw storage stability (over time) It is an object of the present invention to provide a planographic printing plate precursor having a property that developability is not deteriorated due to non-image area stains, and a method for producing a planographic printing plate using the same.

The present invention is as follows.
(1) A planographic printing plate precursor having at least a photosensitive layer on a support is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then an automatic processor equipped with a rubbing member. In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of a developer having a pH of 2 to 10, the photosensitive layer is (A) 360 nm to 450 nm. Sensitizing dye that absorbs light of (B), (B) a polymerization initiator, (C) a polymerizable compound, and (D) a photosensitive composition containing a binder polymer, wherein (D) is ethylenically unsaturated. units and a hydrophilic group having a bond (excluding a carboxyl group) polyurethane resin having a unit having a (However, the following diisocyanate compounds (i) -1 and (i) -4 parallel The following diol compounds (ii) -1, (iii) -5 and (iv) The lithographic printing plate precursor, characterized in that a -5 excluding polyurethane resin synthesized from).
(2) After exposing the lithographic printing plate precursor having at least a photosensitive layer on the support using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, an automatic processor equipped with a rubbing member In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of an aqueous solution containing a water-soluble polymer, the photosensitive layer is (A) 360 nm to 450 nm. It is formed of a photosensitive composition containing a sensitizing dye that absorbs light, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer, wherein (D) is an ethylenically unsaturated bond. A lithographic printing plate precursor characterized by being a polyurethane resin having a unit having a unit and a unit having a hydrophilic group (excluding a carboxyl group).
(3) The unit having the ethylenically unsaturated bond is a unit having at least one of functional groups represented by the following general formulas (1) to (3): The lithographic printing plate precursor as described in (2).
In general formula (1), R ^{1 to} R ³ each independently represents a hydrogen atom or a monovalent organic group, X represents an oxygen atom, a sulfur atom or —N (R ¹² ) —, and R ¹² represents hydrogen. Represents an atom or a monovalent organic group.
In the general formula (2), R ^{4 to} R ⁸ each independently represents a hydrogen atom or a monovalent organic group, Y represents an oxygen atom, a sulfur atom or —N (R ¹² ) —, and R ¹² represents a general formula. It is synonymous with R < ¹² > of Formula (1).
In the general formula (3), R ⁹ represents a hydrogen atom or an alkyl group which may have a substituent, and R ¹⁰ and R ¹¹ are each independently a hydrogen atom, a halogen atom, an amino group, or a dialkylamino group. A carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an alkyl group which may have a substituent, an aryl group which may have a substituent, an alkoxy group which may have a substituent, Aryloxy group which may have a substituent, alkylamino group which may have a substituent, arylamino group which may have a substituent, alkylsulfonyl group which may have a substituent, substituent Z represents an oxygen atom, a sulfur atom, —N (R ¹³ ) — or a phenylene group which may have a substituent, and R ¹³ has a substituent. Represents a good alkyl group.
(4) The lithographic printing plate precursor as described in any one of (1) to (3) above, wherein the binder polymer is a polyurethane resin having a (meth) acryloyl group.
(5) The binder polymer is a reaction product of a diisocyanate compound and a diol compound, and at least one of the diol compounds is a compound represented by the following general formula (G). The lithographic printing plate precursor as described in any one of (4).
In general formula (G), R ^{1 to} R ³ each independently represent a hydrogen atom or a monovalent organic group, A represents a divalent organic residue, X represents an oxygen atom, a sulfur atom or N (R ¹² )-And R ¹² represents a hydrogen atom or a monovalent organic group.
(6) unit having a hydrophilic group, scan sulfone group, a sulfonic acid base, and characterized by a unit and / or polyether diol unit having at least one group selected from phosphate and phosphoric acid salt The lithographic printing plate precursor as described in any one of (1) to (5) above.
(7) The lithographic printing plate precursor as described in any one of (1) to (6) above, wherein the lithographic printing plate precursor has a protective layer on a photosensitive layer.
(8) The lithographic printing plate precursor as described in any one of (1) to (7) above, wherein part or all of the photosensitive layer component is encapsulated in microcapsules.
(9) The lithographic printing plate precursor as described in any one of (1) to (8) above, wherein the rubbing member is at least two rotating brush rolls.
(10) The lithographic printing plate precursor as described in any one of (1) to (9) above, wherein an image is recorded on an FM screen during the exposure.
(11) At least a photosensitive layer on the support, and the photosensitive layer (A) a sensitizing dye that absorbs light of 360 nm to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D ) A polyurethane resin formed of a photosensitive composition containing a binder polymer, wherein the (D) has a unit having a hydrophilic group (excluding a carboxyl group) and a unit having an ethylenically unsaturated bond ( However, lithographic printing which is a polyurethane resin synthesized from the following diisocyanate compounds (i) -1 and (i) -4 and the following diol compounds (ii) -1, (iii) -5 and (iv) -5) After exposing the plate precursor using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, the pH is set to 2 to 2 by an automatic processor equipped with a rubbing member. Presence of the developing solution 0, rubbed by rubbing the plate surface with a member, the planographic printing plate creation method of removing the photosensitive layer in the unexposed portion.
(12) At least a photosensitive layer on the support, and the photosensitive layer (A) a sensitizing dye that absorbs light of 360 nm to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D ) A polyurethane resin formed of a photosensitive composition containing a binder polymer, wherein (D) has a unit having a hydrophilic group (excluding a carboxyl group) and a unit having an ethylenically unsaturated bond. In the presence of an aqueous solution containing a water-soluble polymer, an lithographic printing plate precursor is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then subjected to an automatic processor equipped with a rubbing member. A method for preparing a lithographic printing plate, in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member.
The present invention relates to a lithographic printing plate precursor as described in (1) to (10) above and a method for preparing the lithographic printing plate as described in (11) to (12) above. In order to describe.
1. The lithographic printing plate precursor having at least a photosensitive layer on the support is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then the pH is adjusted by an automatic processor equipped with a rubbing member. In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of 2 to 10 developer, the photosensitive layer is (A) a light of 360 nm to 450 nm. A unit comprising a photosensitive composition containing a sensitizing dye to be absorbed, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer, wherein (D) has a hydrophilic group. A lithographic printing plate precursor characterized by comprising a polyurethane resin.
2. The lithographic printing plate precursor having at least a photosensitive layer on the support is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then the pH is adjusted by an automatic processor equipped with a rubbing member. In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of 2 to 10 developer, the photosensitive layer is (A) a light of 360 nm to 450 nm. It is formed by a photosensitive composition containing a sensitizing dye to be absorbed, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer, and (D) has an ethylenically unsaturated bond. A lithographic printing plate precursor comprising a polyurethane resin having a unit and a unit having a hydrophilic group.
3. A lithographic printing plate precursor having at least a photosensitive layer on a support is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then water-soluble by an automatic processor equipped with a rubbing member. In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of an aqueous solution containing a polymer, the photosensitive layer (A) absorbs light of 360 nm to 450 nm. Sensitizing dye, (B) a polymerization initiator, (C) a polymerizable compound and (D) a photosensitive composition containing a binder polymer, wherein (D) has an ethylenically unsaturated bond A lithographic printing plate precursor characterized by being a polyurethane resin having a unit having a hydrophilic group.
4). The lithographic printing plate precursor as described in 2 or 3 above, wherein the binder polymer is a polyurethane resin having a (meth) acryloyl group.
5. The binder polymer is a reaction product of a diisocyanate compound and a diol compound, and at least one of the diol compounds is a compound represented by the following general formula (G). The lithographic printing plate precursor described.

In general formula (G), R ^{1 to} R ³ each independently represents a hydrogen atom or a monovalent organic group, A represents a divalent organic residue, X represents an oxygen atom, a sulfur atom, or N ( R ¹² ) —, and R ¹² represents a hydrogen atom or a monovalent organic group.

6). The unit having the hydrophilic group is a unit having at least one acid group selected from a carboxyl group, a sulfone group and a phosphoric acid group or a salt group thereof and / or a polyether diol unit. The lithographic printing plate precursor as described in any one of -5.
7). The lithographic printing plate precursor as described in any one of 1 to 6 above, wherein the lithographic printing plate precursor has a protective layer on a photosensitive layer.
8). The lithographic printing plate precursor as described in any one of 1 to 7 above, wherein some or all of the photosensitive layer components are encapsulated in microcapsules.
9. The lithographic printing plate precursor as described in any one of 1 to 3 above, wherein the rubbing member is at least two rotating brush rolls.
10. 4. The lithographic printing plate precursor as described in any one of 1 to 3 above, wherein an image is recorded on an FM screen during the exposure.
11. The support has at least a photosensitive layer, and the photosensitive layer is (A) a sensitizing dye that absorbs light of 360 nm to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer. A lithographic printing plate precursor, which is a polyurethane resin having a unit having a hydrophilic group, is mounted with a light source having an oscillation wavelength in the range of 360 nm to 450 nm. A lithographic plate that removes the photosensitive layer in the non-exposed area by rubbing the plate surface with a rubbing member in the presence of a developer having a pH of 2 to 10 by an automatic processor equipped with a rubbing member after exposure using an exposure apparatus. How to make a print version.
12 The support has at least a photosensitive layer, and the photosensitive layer is (A) a sensitizing dye that absorbs light of 360 nm to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer. A lithographic printing plate precursor, which is a polyurethane resin having a unit having a hydrophilic group, is mounted with a light source having an oscillation wavelength in the range of 360 nm to 450 nm. Lithographic printing that removes the photosensitive layer in non-exposed areas by rubbing the plate surface with a rubbing member in the presence of an aqueous solution containing a water-soluble polymer by an automatic processor equipped with a rubbing member after exposure using an exposure apparatus How to create a version.

In order to maintain the film strength of the photosensitive layer and develop high printing durability, a polyurethane resin has been conventionally used in a strong alkali development system. Also in the present invention, a polyurethane resin is used for the mother skeleton, and as a result, it is considered that high printing durability is expressed by high hydrogen bondability of the urethane bond in the main chain.
On the other hand, in an extremely mild development system having a pH of 2 to 10 or an aqueous solution system containing a water-soluble polymer, the aggregation of the resin due to the hydrogen bond reduces the developability / removability of the unexposed portion of the photosensitive layer, and thus the raw storage stability. (Printing stains with time) It is normal to cause deterioration, but in the present invention, by introducing a unit having a hydrophilic group, the affinity with water or a water-soluble polymer as a solvent is increased. It is presumed that the raw shelf life has been improved.
Furthermore, as a preferred embodiment of the present application, an ethylenically unsaturated bond is introduced into the side chain, and this improves the crosslinking efficiency in exposure, thereby reducing development damage (in other words, reducing the film strength by reducing the crosslinkability). As a result, it is considered that the trade-off between printing durability and raw storage stability has been overcome.

  According to the present invention, a lithographic printing plate precursor capable of mild development processing having a pH of 2 to 10 or aqueous solution processing containing a water-soluble polymer, maintaining printing durability as much as possible and having very good raw storage stability. Can be provided.

<Lithographic printing plate precursor>
The lithographic printing plate precursor of the present invention is obtained by exposing a lithographic printing plate precursor having at least a photosensitive layer on a support using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then rubbing member The photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of a developer having a pH of 2 to 10 or in the presence of an aqueous solution containing a water-soluble polymer. The photosensitive layer contains (A) a sensitizing dye that absorbs light of 360 to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer. It is formed of a composition, and the (D) is a polyurethane resin having a unit having a hydrophilic group.
The polyurethane resin preferably further has a unit having an ethylenically unsaturated bond.
Further, the lithographic printing plate precursor of the present invention, after exposing the lithographic printing plate precursor having at least a photosensitive layer on a support using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, Using an automatic processor equipped with a rubbing member, the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with the rubbing member in the presence of an aqueous solution containing a water-soluble polymer or in the presence of an aqueous solution containing a water-soluble polymer. The photosensitive layer contains (A) a sensitizing dye that absorbs light of 360 to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer. And (D) is a polyurethane resin having a unit having an ethylenically unsaturated bond and a unit having a hydrophilic group.

In the lithographic printing plate precursor according to the invention, an intermediate layer (undercoat layer) may be provided for the purpose of improving the adhesion and stain resistance between the photosensitive layer and the support. Further, a protective layer (also referred to as an overcoat layer) may be further provided on the photosensitive layer in order to perform exposure in the air. The protective layer prevents exposure of low molecular weight compounds such as oxygen and basic substances present in the atmosphere that hinder the image formation reaction caused by exposure in the photosensitive layer, and enables exposure in the atmosphere. To do.
Hereinafter, the elements constituting the lithographic printing plate precursor according to the invention will be described in detail.

(Photosensitive layer)
The photosensitive layer of the lithographic printing plate precursor according to the invention includes, as essential components, (A) a sensitizing dye that absorbs light of 360 to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a hydrophilic property. A polymerizable negative photosensitive layer formed of a photosensitive composition containing a polyurethane resin having a unit having a group and further containing a colorant and other optional components as required.
Control of the developing speed of the unexposed portion of the photosensitive layer and the penetration speed of the developer into the photosensitive layer after curing can be performed by a conventional method in addition to the method using the binder polymer. Addition of a hydrophilic compound is useful for improving the development speed, and means for adding a hydrophobic compound is useful for suppressing the penetration of the developer into the exposed area.

  Since the polymerizable negative photosensitive layer in the present invention is sensitive to light of 360 nm to 450 nm, it can be exposed to a blue laser useful for CTP. Such a sensitizing dye that absorbs light of 360 nm to 450 nm is in an electronically excited state with high sensitivity to blue laser irradiation (exposure), and the electron transfer, energy transfer, and the like related to the electronically excited state are present in the photosensitive layer. It acts on the coexisting polymerization initiator to cause a chemical change in the polymerization initiator to generate radicals. Then, the polymerizable compound causes a polymerization reaction by the generated radical, and the exposed portion is cured to become an image portion.

The lithographic printing plate precursor according to the invention is particularly suitable for plate making directly drawn with a blue laser beam having a wavelength of 360 nm to 450 nm, because the photosensitive layer contains a sensitizing dye that absorbs light of 360 nm to 450 nm. In addition, it can exhibit high image-forming properties as compared with conventional lithographic printing plate precursors.
Below, each component which comprises the photosensitive composition which forms the photosensitive layer of the lithographic printing plate precursor concerning this invention is demonstrated.

(A) Sensitizing dye that absorbs light of 360 nm to 450 nm The sensitizing dye that absorbs light of 360 nm to 450 nm used in the photosensitive composition used in the present invention has an absorption maximum in a wavelength range of 360 nm to 450 nm. It is preferable to have Examples of such a sensitizing dye include merocyanine dyes represented by the following general formula (I), benzopyrans and coumarins represented by the following general formula (II), and fragrances represented by the following general formula (III). And anthracenes represented by the following general formula (IV).

(In the formula, A represents an S atom or NR ₆ , R ₆ represents a monovalent non-metallic atomic group, Y represents a basic nucleus of the dye in cooperation with the adjacent A and the adjacent carbon atom. metallic atomic group, X1, X ₂ each independently represents a monovalent non-metallic atomic group, X _1, X ₂ may be bonded to form an acidic nucleus of the dye together.)

(In the formula, = Z represents a carbonyl group, a thiocarbonyl group, an imino group or an alkylidene group represented by the partial structural formula (I ′), and X ₁ and X ₂ have the same meanings as those in the general formula (II)). R _{7 to} R ₁₂ each independently represents a monovalent nonmetallic atomic group.)

(In the formula, Ar ₃ represents an aromatic group or a heteroaromatic group which may have a substituent, and R ₁₃ represents a monovalent non-metallic atomic group. More preferable R ₁₃ represents an aromatic group or It is a heteroaromatic group, and Ar ₃ and R ₁₃ may be bonded to each other to form a ring.)

(In the formula, X ₃ , X ₄ and R _{14 to} R ₂₁ each independently represent a monovalent non-metallic atomic group, and more preferable X ₃ and X ₄ are electron donating groups having a negative Hammett's substituent constant. .)

Preferred examples of the monovalent nonmetallic atomic group represented by X ₁ to X ₄ and R ₆ to R ₂₁ in the general formulas (I) to (IV) include a hydrogen atom, an alkyl group (for example, a methyl group, Ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, hexadecyl group, octadecyl group, eicosyl group, isopropyl group, isobutyl group , S-butyl group, t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group, 2-norbornyl group, chloromethyl group , Bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxymethyl group, methoxyethoxyethyl , Allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-
Cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, allyloxycarbonyl Butyl group, chlorophenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl-N- (sulfophenyl) Carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group, N-methyl- -(Phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobutyl group, tolylphosphonohexyl Group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonatooxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p-methylbenzyl group, cinnamyl group Allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc.), aryl group (for example, phenyl Group, biphenyl group, naphthyl group, tolyl group, xylyl group, mesityl , Cumenyl group, chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group , Methylaminophenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group, cyanophenyl group, sulfo Phenyl group, sulfonatophenyl group, phosphonophenyl group, phosphonatophenyl group, etc.), heteroaryl group (for example, thiophene, thiathrene, furan, pyran, Benzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indoyl, indazole, purine, quinolidine, isoquinoline, phthalazine, naphthyridine, quinazoline, sinoline , Pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthroline, phthalazine, phenazazine, phenoxazine, furazane, phenoxazine, etc.), alkenyl group (for example, vinyl group, 1-propenyl group, 1-butenyl group, cinnamyl group) 2-chloro-1-ethenyl group, etc.), alkynyl group (for example, ethynyl group, 1-propynyl group, 1-butynyl group, trimethylsilylethynyl group, etc.), halogen Child (-F, -Br, -Cl, -I), hydroxyl group, alkoxy group, aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group, N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyl group Oxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, arylsulfoxy group, acylthio group, acylamino group, N- Alkylacylamino group, N-arylacylamino group, ureido group, N'-al Killureido group, N ', N'-dialkylureido group, N'-arylureido group, N', N'-diarylureido group, N'-alkyl-N'-arylureido group, N-alkylureido group, N- Arylureido group, N′-alkyl-N-alkylureido group, N′-alkyl-N-arylureido group, N ′, N′-dialkyl-N-alkylureido group, N ′, N′-dialkyl-N— Arylureido group, N′-aryl-N-alkylureido group, N′-aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N— Arylureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl -N-Alkoki Sicarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, formyl group, acyl group, carboxyl group, alkoxy Carbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkyl Sulfinyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group, sulfo group (—SO ₃ H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N -Alkyl sul Inamoyl group, N, N-dialkylsulfinamoyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfane group Famoyl group, N, N-dialkylsulfamoyl group, N-arylsulfamoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (—PO ₃ H ₂ ) and its conjugate base group (hereinafter referred to as phosphonate group), dialkyl phosphono group (—PO ₃ (alkyl) ₂ ), diaryl phosphono group (—PO ₃ (aryl) ₂ ), alkylaryl phosphono group (-PO ₃ (alkyl) (aryl)), monoalkyl phosphono group (-PO ₃ H (alkyl)) and its conjugated base group (hereinafter referred to as alkyl phosphonophenyl group), Monoari Ruhosufono group (-PO ₃ H (aryl)) and its conjugated base group (hereinafter referred to as aryl phosphonophenyl group), phosphonooxy group (-OPO ₃ H ₂₎ and its conjugated base group (hereinafter, phosphonophenyl group Dialkyl phosphonooxy group (—OPO ₃ (alkyl) ₂ ), diaryl phosphonooxy group (—OPO ₃ (aryl) ₂ ), alkylaryl phosphonooxy group (—OPO ₃ (alkyl) (aryl)) ), A monoalkylphosphonooxy group (—OPO ₃ H (alkyl)) and its conjugate base group (hereinafter referred to as an alkylphosphonatooxy group), a monoarylphosphonooxy group (—OPO ₃ H (aryl)) and Examples thereof include conjugated base groups (hereinafter referred to as arylphosphonatooxy groups), cyano groups, nitro groups, etc. Among the above substituents, hydrogen atoms, alkyl groups, aryl groups, halogens, etc. Child, an alkoxy group, an acyl group are particularly preferred.

  Examples of the basic nucleus of the dye formed together with A adjacent to Y and the adjacent carbon atom in the general formula (I) include 5-, 6-, and 7-membered nitrogen-containing or sulfur-containing heterocycles. A 5- or 6-membered heterocyclic ring is preferable.

  Examples of nitrogen-containing heterocycles include, for example, the basic nucleus in merocyanine dyes described in LGBrooker et al., J. Am. Chem. Soc., 73, 5326-5358 (1951). Any of those known to be used can be suitably used. Specific examples include thiazoles (for example, thiazole, 4-methylthiazole, 4-phenylthiazole, 5-methylthiazole, 5-phenylthiazole, 4,5-dimethylthiazole, 4,5-diphenylthiazole, 4,5- Di (p-methoxyphenylthiazole), 4- (2-thienyl) thiazole, etc.), benzothiazoles (eg, benzothiazole, 4-chlorobenzothiazole, 5-chlorobenzothiazole, 6-chlorobenzothiazole, 7- Chlorobenzothiazole, 4-methylbenzothiazole, 5-methylbenzothiazole, 6-methylbenzothiazole, 5-bromobenzothiazole, 4-phenylbenzothiazole, 5-phenylbenzothiazole, 4-methoxybenzothiazole, 5-methoxybenzo Thiazole, 6-methoxybenzothia Sol, 5-iodobenzothiazole, 6-iodobenzothiazole, 4-ethoxybenzothiazole, 5-ethoxybenzothiazole, tetrahydrobenzothiazole, 5,6-dimethoxybenzothiazole, 5,6-dioxymethylenebenzothiazole, 5- Hydroxybenzothiazole, 6-hydroxybenzothiazole, 6-dimethylaminobenzothiazole, 5-ethoxycarbonylbenzothiazole, etc.), naphthothiazoles (for example, naphtho [1,2] thiazole, naphtho [2,1] thiazole, 5- Methoxynaphtho [2,1] thiazole, 5-ethoxynaphtho [2,1] thiazole, 8-methoxynaphtho [1,2] thiazole, 7-methoxynaphtho [1,2] thiazole, etc.), thianaphtheno-7 ′, 6 ', 4,5-thiazoles (eg 4'- Oxythianaphtheno-7 ′, 6 ′, 4,5-thiazole, etc.), oxazoles (eg, 4-methyloxazole, 5-methyloxazole, 4-phenyloxazole, 4,5-diphenyloxazole, 4-ethyloxazole, 4,5-dimethyloxazole, 5-phenyloxazole, etc.), benzoxazoles (benzoxazole, 5-chlorobenzoxazole, 5-methylbenzoxazole, 5-phenylbenzoxazole, 6-methylbenzoxazole, 5,6-dimethyl Benzoxazole, 4,6-dimethylbenzoxazole, 6-methoxybenzoxazole, 5-methoxybenzoxazole, 4-ethoxybenzoxazole, 5-chlorobenzoxazole, 6-methoxybenzoxazole, 5-hydroxybenzoxazole , 6-hydroxybenzoxazole, etc.), naphthoxazoles (eg, naphtho [1,2] oxazole, naphtho [2,1] oxazole, etc.), selenazoles (eg, 4-methylselenazole, 4-phenylselenazole, etc.) ), Benzoselenazoles (eg, benzoselenazole, 5-chlorobenzoselenazole, 5-methoxybenzoselenazole, 5-hydroxybenzoselenazole, tetrahydrobenzoselenazole, etc.), naphthoselenazoles (eg, naphtho [ 1,2] selenazole, naphtho [2,1] selenazole etc.), thiazolines (eg thiazoline, 4-methylthiazoline etc.), 2-quinolines (eg quinoline, 3-methylquinoline, 5-methylquinoline, 7 -Methylquinoline, 8-methylquinoline, 6-chloroquinoline, 4-chloroquinoline, 6-methoxyquinoline, 6-ethoxyquinoline, 6-hydroxyquinoline, 8-hydroxyquinoline, etc., 4-quinolines (for example, quinoline, 6-methoxyquinoline, 7-methylquinoline, 8-methylquinoline, etc.) ) 1-isoquinolines (eg, isoquinoline, 3,4-dihydroisoquinoline, etc.), 3-isoquinolines (eg, isoquinoline, etc.), benzimidazoles (eg, 1,3-diethylbenzimidazole, 1-ethyl- 3-phenylbenzimidazole, etc.), 3,3-dialkylindolenins (eg 3,3-dimethylindolenin, 3,3,5, -trimethylindolenine, 3,3,7, -trimethylindolenine, etc.) 2-pyridines (eg, pyridine, 5-methylpyridine, etc.), 4-pyridine (eg, pyridine, etc.) Etc.

Examples of the sulfur-containing heterocycle include a dithiol partial structure in dyes described in JP-A-3-296759.
Specific examples include benzodithiols (eg, benzodithiol, 5-t-butylbenzodithiol, 5-methylbenzodithiol, etc.), naphthodithiols (eg, naphtho [1,2] dithiol, naphtho [2,1] Dithiols, etc.), dithiols (for example, 4,5-dimethyldithiols, 4-phenyldithiols, 4-methoxycarbonyldithiols, 4,5-dimethoxycarbonylbenzodithiols, 4,5-ditrifluoromethyldithiols, 4 , 5-dicyanodithiol, 4-methoxycarbonylmethyldithiol, 4-carboxymethyldithiol, and the like.

  As mentioned above, for the sake of convenience, the description used in the description of the heterocyclic ring has conventionally used the name of the heterocyclic mother skeleton, but when forming the basic skeleton partial structure of the sensitizing dye, for example, in the case of the benzothiazole skeleton It is introduced in the form of an alkylidene-type substituent with one degree of unsaturation, such as a 3-substituted-2 (3H) -benzothiazolidene group.

  Of the sensitizing dyes as compounds having an absorption maximum in the wavelength range of 360 nm to 450 nm, a dye more preferable from the viewpoint of high sensitivity is a dye represented by the following general formula (V).

(In the general formula (V), A represents an aromatic ring or a hetero ring which may have a substituent, and X represents an oxygen atom, a sulfur atom or ═N (R ₃ ). R ₁ , R ₂ and R ₃ each independently represents a hydrogen atom or a monovalent nonmetallic atomic group, and A and R ₁ and R ₂ and R ₃ are bonded to each other to form an aliphatic or aromatic ring. May be.)

The general formula (V) will be described in more detail. R ₁ , R ₂ and R ₃ are each independently a hydrogen atom or a monovalent nonmetallic atomic group, preferably a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, substituted or non-substituted It represents a substituted aryl group, a substituted or unsubstituted heteroaryl group, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkylthio group, a hydroxyl group, or a halogen atom.

Preferable examples of R ₁ , R ₂ and R ₃ will be specifically described. Examples of preferable alkyl groups include linear, branched, and cyclic alkyl groups having 1 to 20 carbon atoms. Specific examples thereof include a methyl group, an ethyl group, a propyl group, Butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, hexadecyl, octadecyl, eicosyl, isopropyl, isobutyl, s-butyl, Examples thereof include a t-butyl group, an isopentyl group, a neopentyl group, a 1-methylbutyl group, an isohexyl group, a 2-ethylhexyl group, a 2-methylhexyl group, a cyclohexyl group, a cyclopentyl group, and a 2-norbornyl group. Of these, linear alkyl groups having 1 to 12 carbon atoms, branched alkyl groups having 3 to 12 carbon atoms, and cyclic alkyl groups having 5 to 10 carbon atoms are more preferable.

As the substituent of the substituted alkyl group, a monovalent nonmetallic atomic group excluding hydrogen is used, and preferred examples include halogen atoms (—F, —Br, —Cl, —I), hydroxyl groups, alkoxy groups, Aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, arylsulfoxy group, Ruthio group, acylamino group, N-alkylacylamino group, N-arylacylamino group, ureido group, N′-alkylureido group, N ′, N′-dialkylureido group, N′-arylureido group, N ′, N'-diarylureido group, N'-alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido group, N'-alkyl-N-aryl Ureido group, N ′, N′-dialkyl-N-alkylureido group, N ′, N′-dialkyl-N-arylureido group, N′-aryl-N-alkylureido group, N′-aryl-N-aryl Ureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-arylureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′- Alkyl-N'-aryl-N-ary Ureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl-N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N- Aryl-N-aryloxycarbonylamino group, formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkylsulfinyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group, sulfo group (—SO ₃ H) and its conjugate base group , Sulfonato Group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N-alkylsulfinamoyl group, N, N-dialkylsulfinamoyl group, N-arylsulfinamoyl group, N, N-diarylsulfina Moyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N-arylsulfamoyl group, N, N-diarylsulfur Famoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (—PO ₃ H ₂ ) and its conjugate base group (hereinafter referred to as phosphonate group), dialkyl phosphono group (—PO ₃ (alkyl)) _2), diaryl phosphono group (-PO ₃ (aryl) _2), alkyl aryl phosphono group _{(-PO 3 (alkyl) (aryl} )), monoalkyl Sufono group (-PO ₃ H (alkyl)) and its conjugated base group (hereinafter referred to as alkyl phosphonophenyl group), monoaryl phosphono group (-PO ₃ H (aryl)) and its conjugated base group (hereinafter, aryl Phosphonate group), phosphonooxy group (—OPO ₃ H ₂ ) and its conjugate base group (hereinafter referred to as phosphonateoxy group), dialkyl phosphonooxy group (—OPO ₃ (alkyl) ₂ ), diaryl Phosphonooxy group (—OPO ₃ (aryl) ₂ ), alkylaryl phosphonooxy group (—OPO ₃ (alkyl) (aryl)), monoalkyl phosphonooxy group (—OPO ₃ H (alkyl)) and conjugation thereof A base group (hereinafter referred to as an alkylphosphonatooxy group), a monoarylphosphonooxy group (—OPO ₃ H (aryl)) and a conjugated base group thereof (hereinafter referred to as an arylphosphonatooxy group), Examples include a cyano group, a nitro group, an aryl group, a heteroaryl group, an alkenyl group, and an alkynyl group.

  Specific examples of the alkyl group in these substituents include the above-described alkyl groups, and specific examples of the aryl group include a phenyl group, a biphenyl group, a naphthyl group, a tolyl group, a xylyl group, a mesityl group, and a cumenyl group. , Chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylamino Phenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group, Examples thereof include a cyanophenyl group, a sulfophenyl group, a sulfonatophenyl group, a phosphonophenyl group, and a phosphonatophenyl group.

As the preferred heteroaryl group as R ₁ , R ₂ and R ₃ , a monocyclic or polycyclic aromatic ring containing at least one of nitrogen, oxygen and sulfur atoms is used, and examples of particularly preferred heteroaryl groups are as follows. Is, for example, thiophene, thiathrene, furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indolizine, indazole, indazole, Purine, quinolidine, isoquinoline, phthalazine, naphthyridine, quinazoline, sinoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthrolin, phthalazine, phenalazine, phenoxazine, flaza And phenoxazine and the like, and these may be further benzo-fused or may have a substituent.

Examples of preferable alkenyl groups as R ₁ , R ₂ and R ₃ include vinyl group, 1-propenyl group, 1-butenyl group, cinnamyl group, 2-chloro-1-ethenyl group and the like, and alkynyl Examples of the group include ethynyl group, 1-propynyl group, 1-butynyl group, trimethylsilylethynyl group and the like. Examples of G1 in the acyl group (G1CO-) include hydrogen and the above alkyl groups and aryl groups. Of these substituents, halogen atoms (—F, —Br, —Cl, —I), alkoxy groups, aryloxy groups, alkylthio groups, arylthio groups, N-alkylamino groups, N, N— Dialkylamino group, acyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, acylamino group, formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, sulfo group, sulfonate group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group Group, N-arylsulfamoyl group, N-alkyl-N -Arylsulfamoyl group, phosphono group, phosphonate group, dialkyl phosphono group, diaryl phosphono group, monoalkyl phosphono group, alkyl phosphonate group, monoaryl phosphono group, aryl phosphonate group, phosphonooxy group, A phosphonatooxy group, an aryl group, and an alkenyl group are mentioned.

  On the other hand, examples of the alkylene group in the substituted alkyl group include divalent organic residues obtained by removing any one of the hydrogen atoms on the alkyl group having 1 to 20 carbon atoms. Can include linear alkylene groups having 1 to 12 carbon atoms, branched chains having 3 to 12 carbon atoms, and cyclic alkylene groups having 5 to 10 carbon atoms.

Specific examples of preferable substituted alkyl groups as R ₁ , R ₂ and R ₃ obtained by combining the substituent with an alkylene group include chloromethyl group, bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxy Methyl group, methoxyethoxyethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N -Cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl Group, allyloxycarbonylbutyl group, chlorophenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl- N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobutyl Group, tolylphosphono Xyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonatoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p-methylbenzyl group, cinnamyl Group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, and the like.

Specific examples of preferred aryl groups as R ₁ , R ₂ and R ₃ include those in which 1 to 3 benzene rings form a condensed ring, and those in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Specific examples include a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, and a fluorenyl group, and among these, a phenyl group and a naphthyl group are more preferable. .

Specific examples of preferred substituted aryl groups as R ₁ , R _2, and R ₃ include those having a monovalent non-metallic atomic group excluding hydrogen as a substituent on the ring-forming carbon atom of the aforementioned aryl group. . Examples of preferred substituents include the aforementioned alkyl groups, substituted alkyl groups, and those previously shown as substituents in the substituted alkyl group. Preferred examples of such a substituted aryl group include biphenyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, fluorophenyl group, chloromethylphenyl group, trifluoromethylphenyl group. Hydroxyphenyl group, methoxyphenyl group, methoxyethoxyphenyl group, allyloxyphenyl group, phenoxyphenyl group, methylthiophenyl group, tolylthiophenyl group, ethylaminophenyl group, diethylaminophenyl group, morpholinophenyl group, acetyloxyphenyl group, Benzoyloxyphenyl group, N-cyclohexylcarbamoyloxyphenyl group, N-phenylcarbamoyloxyphenyl group, acetylaminophenyl group, N-methylbenzoylaminophenyl group, carboxy Enyl group, methoxycarbonylphenyl group, allyloxycarbonylphenyl group, chlorophenoxycarbonylphenyl group, carbamoylphenyl group, N-methylcarbamoylphenyl group, N, N-dipropylcarbamoylphenyl group, N- (methoxyphenyl) carbamoylphenyl group N-methyl-N-sulfophenyl) carbamoylphenyl group, sulfophenyl group, sulfonatophenyl group, sulfamoylphenyl group, N-ethylsulfamoylphenyl group, N, N-dipropylsulfamoylphenyl group, N -Tolylsulfamoylphenyl group, N-methyl-N- (phosphonophenyl) sulfamoylphenyl group, phosphonophenyl group, phosphonatophenyl group, diethylphosphonophenyl group, diphenylphosphonophenyl group, methylphosphine Ionophenyl group, methylphosphonatophenyl group, tolylphosphonophenyl group, tolylphosphonatophenyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallylphenyl group, 2-methylpropenylphenyl group, 2 -Propynylphenyl group, 2-butynylphenyl group, 3-butynylphenyl group, and the like.

Next, A in the general formula (V) will be described. A represents an aromatic ring or a heterocyclic ring which may have a substituent. Specific examples of the aromatic ring or heterocyclic ring which may have a substituent include R ₁ and R in the general formula (V) similar to those described in ₂ and R ₃ can be exemplified.

  The sensitizing dye represented by the general formula (V) is a condensation of an acidic nucleus as shown above or an acidic nucleus having an active methylene group with a substituted or unsubstituted aromatic ring or heterocyclic ring. Although obtained by reaction, these can be synthesized with reference to JP-B-59-28329.

  Preferred specific examples (D1) to (D41) of the compound represented by the general formula (V) are shown below. In addition, an isomer with a double bond connecting an acidic nucleus and a basic nucleus is not limited to either isomer.

  The sensitizing dye that absorbs light of 360 nm to 450 nm is preferably used in the range of 1.0 to 10.0% by mass in the total components of the photosensitive composition. More preferably, it is the range of 1.5-5.0 mass%.

(B) Polymerization initiator The polymerization initiator used in the present invention is a compound that generates radicals by light or thermal energy and initiates and accelerates the polymerization of a compound having a polymerizable unsaturated group. As such a radical generator, a known polymerization initiator or a compound having a bond having a small bond dissociation energy can be appropriately selected and used.

  Examples of the compounds that generate radicals include organic halogen compounds, carbonyl compounds, organic peroxides, azo polymerization initiators, azide compounds, metallocene compounds, hexaarylbiimidazole compounds, organic boron compounds, disulfone compounds, and oximes. Examples thereof include ester compounds and onium salt compounds.

  Specific examples of the organic halogen compound include Wakabayashi et al., “Bull Chem. Soc Japan” 42, 2924 (1969), US Pat. No. 3,905,815, Japanese Patent Publication No. 46-4605, JP 48-36281, JP 53-133428, JP 55-3070, JP 60-239736, JP 61-169835, JP 61-169837, JP 62- 58241, JP-A 62-212401, JP-A 63-70243, JP-A 63-298339, P. The compound as described in Hutt, "Journal of Heterocyclic Chemistry", 1 (No. 3) (1970) is mentioned. Of these, oxazole compounds and S-triazine compounds substituted with a trihalomethyl group are preferred.

  More preferable examples include s-triazine derivatives in which at least one mono, di, or trihalogen-substituted methyl group is bonded to the s-triazine ring, and oxadiazole derivatives in which the oxadiazole ring is bonded. Specifically, for example, 2,4,6-tris (monochloromethyl) -s-triazine, 2,4,6-tris (dichloromethyl) -s-triazine, 2,4,6-tris (trichloromethyl) -S-triazine, 2-methyl-4,6-bis (trichloromethyl) -s-triazine, 2-n-propyl-4,6-bis (trichloromethyl) -s-triazine, 2- (α, α, β-trichloroethyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (3,4-epoxyphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- [1- (P-methoxyphenyl) -2,4-butadienyl] -4,6-bis (trichloromethyl) -s-triazine, 2-styryl-4,6-bis (trichloromethyl) -s-triazine, 2- ( -Methoxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2- (pi-propyloxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p- Tolyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (4-methoxynaphthyl) -4,6-bis (trichloromethyl) -s-triazine, 2-phenylthio-4,6-bis ( Trichloromethyl) -s-triazine, 2-benzylthio-4,6-bis (trichloromethyl) -s-triazine, 2,4,6-tris (dibromomethyl) -s-triazine, 2,4,6-tris ( Tribromomethyl) -s-triazine, 2-methyl-4,6-bis (tribromomethyl) -s-triazine, 2-methoxy-4,6-bis (tribromomethyl) Etc. -s- triazine and the following compounds.

  Examples of the carbonyl compound include benzophenone, Michler ketone, 2-methylbenzophenone, 3-methylbenzophenone, 4-methylbenzophenone, 2-chlorobenzophenone, 4-bromobenzophenone, 2-carboxybenzophenone and other benzophenone derivatives, 2,2-dimethoxy- 2-phenylacetophenone, 2,2-diethoxyacetophenone, 1-hydroxycyclohexyl phenyl ketone, α-hydroxy-2-methylphenylpropanone, 1-hydroxy-1-methylethyl- (p-isopropylphenyl) ketone, 1- Hydroxy-1- (p-dodecylphenyl) ketone, 2-methyl- (4 ′-(methylthio) phenyl) -2-morpholino-1-propanone, 1,1,1-trichloromethyl- (p-butylphenyl) Acetophenone derivatives such as ketones, thioxanthone derivatives such as thioxanthone, 2-ethylthioxanthone, 2-isopropylthioxanthone, 2-chlorothioxanthone, 2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2,4-diisopropylthioxanthone, p- Examples thereof include benzoic acid ester derivatives such as ethyl dimethylaminobenzoate and ethyl p-diethylaminobenzoate.

  As the azo compound, for example, an azo compound described in JP-A-8-108621 can be used.

  Examples of the organic peroxide include trimethylcyclohexanone peroxide, acetylacetone peroxide, 1,1-bis (tert-butylperoxy) -3,3,5-trimethylcyclohexane, 1,1-bis (tert-butyl). Peroxy) cyclohexane, 2,2-bis (tert-butylperoxy) butane, tert-butyl hydroperoxide, cumene hydroperoxide, diisopropylbenzene hydroperoxide, 2,5-dimethylhexane-2,5-dihydro Peroxide, 1,1,3,3-tetramethylbutyl hydroperoxide, tert-butylcumyl peroxide, dicumyl peroxide, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane, 2, -Oxanoyl peroxide, succinic peroxide, benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, diisopropyl peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, di-2-ethoxyethyl peroxydicarbonate , Dimethoxyisopropyl peroxycarbonate, di (3-methyl-3-methoxybutyl) peroxydicarbonate, tert-butyl peroxyacetate, tert-butyl peroxypivalate, tert-butyl peroxyneodecanoate, tert- Butyl peroxyoctanoate, tert-butyl peroxylaurate, tersyl carbonate, 3,3 ′, 4,4′-tetra- (t-butylperoxycarbonyl) benzophenone, 3,3 ′, 4,4 ′ − Tra- (t-hexylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra- (p-isopropylcumylperoxycarbonyl) benzophenone, carbonyldi (t-butylperoxydihydrogen diphthalate), carbonyl And di (t-hexylperoxydihydrogen diphthalate).

  Examples of the metallocene compound include JP-A-59-152396, JP-A-61-151197, JP-A-63-41484, JP-A-2-249, JP-A-2-4705, Various titanocene compounds described in JP-A-5-83588, such as di-cyclopentadienyl-Ti-bis-phenyl, di-cyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, Di-cyclopentadienyl-Ti-bis-2,4-di-fluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,4,6-trifluorophen-1-yl, di- -Cyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,3,4,5,6-penta Fluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,4,6-trifluoropheny -1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,4 , 5,6-pentafluorophen-1-yl, bis (cyclopentadienyl) -bis (2,6-difluoro-3- (pyr-1-yl) phenyl) titanium, JP-A-1-304453, Examples thereof include iron-arene complexes described in JP-A-1-152109.

  Examples of the hexaarylbiimidazole compound include the specification of JP-B-6-29285, U.S. Pat. Nos. 3,479,185, 4,311,783, and 4,622,286. And, specifically, 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-bromophenyl) )) 4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o, p-dichlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2 ′ -Bis (o-chlorophenyl) -4,4 ', 5,5'-tetra (m-methoxyphenyl) biidazole, 2,2'-bis (o, o'-dichlorophenyl) -4,4', 5,5 '-Tetraphenylbiimidazole, 2, 2' Bis (o-nitrophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-methylphenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole 2,2′-bis (o-trifluorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole and the like.

  Examples of the organoboron compound include JP-A-62-143044, JP-A-62-1050242, JP-A-9-188585, JP-A-9-188686, JP-A-9-188710, JP-A 2000-. No. 131837, Japanese Patent Application Laid-Open No. 2002-107916, Japanese Patent No. 2764769, Japanese Patent Application Laid-Open No. 2002-116539, and Kunz, Martin “Rad Tech '98. Proceeding April 19-22, 1998, Chicago”, etc. Organoborates described in JP-A-6-157623, JP-A-6-175564, JP-A-6-175561, and organic boron oxosulfonium complexes, JP-A-6-175554 No. 6, JP-A-6-17555 Organoboron iodonium complexes described in JP-A-9-188710, organoboron phosphonium complexes described in JP-A-9-188710, JP-A-6-348011, JP-A-7-128785, JP-A-7-140589, Examples thereof include organoboron transition metal coordination complexes such as Kaihei 7-306527 and JP-A-7-292014.

  Examples of the disulfone compound include compounds described in JP-A Nos. 61-166544 and 2003-328465.

  Examples of the oxime ester compound include JCS Perkin II (1979) 1653-1660), JCSPerkin II (1979) 156-162, Journal of Photopolymer Science and Technology (1995) 202-232, and JP-A 2000-66385. And compounds described in JP 2000-80068 A. Specific examples include compounds represented by the following structural formula.

  Examples of the onium salt compound include S.I. I. Schlesinger, Photogr. Sci. Eng. , 18, 387 (1974), T.A. S. Diazonium salts described in Bal et al, Polymer, 21, 423 (1980), ammonium salts described in US Pat. No. 4,069,055, JP-A-4-365049, etc., US Pat. No. 4,069 , 055, 4,069,056, phosphonium salts described in European Patent Nos. 104,143, US Pat. Nos. 339,049, 410,201, JP -150848, JP-A-2-296514, iodonium salts, European Patent Nos. 370,693, 390,214, 233,567, 297,443, and 297 442, U.S. Pat. Nos. 4,933,377, 161,811, 410,201, 339,049, 4,760,013 No. 4,734,444, No. 2,833,827, German Patent No. 2,904,626, No. 3,604,580, No. 3,604,581 Or a sulfonium salt described in J. V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 17, 1047 (1979), a selenonium salt described in C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988), and onium salts such as arsonium salts.

In the present invention, these onium salts function not as acid generators but as ionic radical polymerization initiators.
The onium salt suitably used in the present invention is an onium salt represented by the following general formulas (RI-I) to (RI-III).

In the formula (RI-I), Ar ₁₁ represents an aryl group having 20 or less carbon atoms which may have 1 to 6 substituents, and preferred substituents include an alkyl group having 1 to 12 carbon atoms and a carbon number. 1-12 alkenyl group, C1-C12 alkynyl group, C1-C12 aryl group, C1-C12 alkoxy group, C1-C12 aryloxy group, halogen atom, C1-C1 12 alkylamino groups, C1-C12 dialkylamino groups, C1-C12 alkylamide groups or arylamide groups, carbonyl groups, carboxyl groups, cyano groups, sulfonyl groups, C1-C12 thioalkyl groups And a thioaryl group having 1 to 12 carbon atoms. Z ₁₁ ^- represents a monovalent anion, specifically a halogen ion, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, thiosulfonate ion, a sulfate ion Can be mentioned. Among these, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion and sulfinate ion are preferable from the viewpoint of stability.

In the formula (RI-II), Ar ₂₁ and Ar ₂₂ each independently represent an aryl group having 20 or less carbon atoms which may have 1 to 6 substituents, and preferred substituents include 1 to 1 carbon atoms. 12 alkyl groups, an alkenyl group having 1 to 12 carbon atoms, an alkynyl group having 1 to 12 carbon atoms, an aryl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 1 to 12 carbon atoms, Halogen atom, C1-C12 alkylamino group, C1-C12 dialkylamino group, C1-C12 alkylamide group or arylamide group, carbonyl group, carboxyl group, cyano group, sulfonyl group, carbon Examples thereof include a thioalkyl group having 1 to 12 carbon atoms and a thioaryl group having 1 to 12 carbon atoms. Z ₂₁ ^- represents a monovalent anion. Specific examples include halogen ions, perchlorate ions, hexafluorophosphate ions, tetrafluoroborate ions, sulfonate ions, sulfinate ions, thiosulfonate ions, and sulfate ions. Among these, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, and carboxylate ion are preferable from the viewpoint of stability and reactivity.

In the formula (RI-III), R ₃₁ , R ₃₂ and R ₃₃ are each independently an aryl group, alkyl group, alkenyl group or alkynyl having 20 or less carbon atoms, which may have 1 to 6 substituents. Represents a group. Among them, an aryl group is preferable from the viewpoint of reactivity and stability. Examples of the substituent include an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 1 to 12 carbon atoms, an alkynyl group having 1 to 12 carbon atoms, an aryl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, Aryloxy group having 1 to 12 carbon atoms, halogen atom, alkylamino group having 1 to 12 carbon atoms, dialkylamino group having 1 to 12 carbon atoms, alkylamide group or arylamide group having 1 to 12 carbon atoms, carbonyl group, carboxyl Group, a cyano group, a sulfonyl group, a thioalkyl group having 1 to 12 carbon atoms, and a thioaryl group having 1 to 12 carbon atoms. Z ₃₁ ^- represents a monovalent anion. Specific examples include halogen ions, perchlorate ions, hexafluorophosphate ions, tetrafluoroborate ions, sulfonate ions, sulfinate ions, thiosulfonate ions, and sulfate ions. Among these, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, and carboxylate ion are preferable from the viewpoints of stability and reactivity. More preferred are the carboxylate ions described in JP-A No. 2001-343742, and particularly preferred are the carboxylate ions described in JP-A No. 2002-148790.

  The polymerization initiator is not limited to the above, but a triazine-based initiator, an organic halogen compound, an oxime ester compound, a diazonium salt, an iodonium salt, and a sulfonium salt are more preferable from the viewpoints of reactivity and stability.

  These polymerization initiators may be used alone or in combination of two or more. Moreover, these polymerization initiators may be added to the same layer as other components, or another layer may be provided and added thereto. These polymerization initiators are preferably from 0.1 to 50% by mass, more preferably from 0.5 to 30% by mass, particularly preferably from 0.8 to 20% by mass, based on the total solid content constituting the photosensitive layer. Can be added.

(C) Polymerizable compound The polymerizable compound used in the photosensitive layer in the invention is an addition polymerizable compound having at least one ethylenically unsaturated double bond, and preferably has at least one terminal ethylenically unsaturated bond, preferably It is selected from compounds having two or more. Such a compound group is widely known in the industrial field, and can be used without any particular limitation in the present invention. These have chemical forms such as monomers, prepolymers, i.e. dimers, trimers and oligomers, or mixtures thereof and copolymers thereof. Examples of monomers and copolymers thereof include unsaturated carboxylic acids (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.), and esters and amides thereof. In this case, an ester of an unsaturated carboxylic acid and an aliphatic polyhydric alcohol compound, or an amide of an unsaturated carboxylic acid and an aliphatic polyvalent amine compound is used. In addition, an addition reaction product of an unsaturated carboxylic acid ester or amide having a nucleophilic substituent such as a hydroxyl group, amino group or mercapto group with a monofunctional or polyfunctional isocyanate or epoxy, and a monofunctional or polyfunctional compound. A dehydration condensation reaction product with a functional carboxylic acid is also preferably used. Further, an addition reaction product of an unsaturated carboxylic acid ester or amide having an electrophilic substituent such as an epoxy group or an epoxy group with a monofunctional or polyfunctional alcohol, amine or thiol, a halogen group or Also suitable are substitution reaction products of unsaturated carboxylic acid esters or amides having a leaving substituent such as a tosyloxy group with monofunctional or polyfunctional alcohols, amines or thiols. As another example, it is also possible to use a group of compounds substituted with unsaturated phosphonic acid, styrene, vinyl ether or the like instead of the unsaturated carboxylic acid.

  Specific examples of monomers of esters of aliphatic polyhydric alcohol compounds and unsaturated carboxylic acids include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol diacrylate , Tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate , Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, isocyanuric acid ethylene oxide (EO) Examples include modified triacrylates and polyester acrylate oligomers.

  Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [p- (3-methacryloxy- 2-hydroxypro ) Phenyl] dimethyl methane, bis - [p- (methacryloxyethoxy) phenyl] dimethyl methane.

  Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,3-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate. Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate. Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate.

  Examples of other esters include aliphatic alcohol esters described in JP-B-51-47334 and JP-A-57-196231, JP-A-59-5240, JP-A-59- Those having an aromatic skeleton described in JP-A No. 5241 and JP-A-2-226149 and those containing an amino group described in JP-A-1-165613 are also preferably used. Furthermore, the ester monomers described above can also be used as a mixture.

  Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylene bisacrylamide, xylylene bismethacrylamide and the like. Examples of other preferable amide monomers include those having a cyclohexylene structure described in JP-B No. 54-21726.

  Further, urethane-based addition polymerizable compounds produced by using an addition reaction of isocyanate and hydroxyl group are also suitable. Specific examples thereof include, for example, one molecule described in JP-B-48-41708. A vinylurethane compound containing two or more polymerizable vinyl groups in one molecule obtained by adding a vinyl monomer containing a hydroxyl group represented by the following general formula (A) to a polyisocyanate compound having two or more isocyanate groups Etc.

_{CH 2 = C (R 4)} COOCH 2 CH (R 5) OH (A)
(However, R ₄ and R ₅ represent H or CH _3. )

  Also, urethane acrylates such as those described in JP-A-51-37193, JP-B-2-32293, JP-B-2-16765, JP-B-58-49860, JP-B-56- Urethane compounds having an ethylene oxide skeleton described in Japanese Patent No. 17654, Japanese Patent Publication No. 62-39417, and Japanese Patent Publication No. 62-39418 are also suitable. Furthermore, addition polymerizable compounds having an amino structure or a sulfide structure in the molecule described in JP-A-63-277653, JP-A-63-260909, and JP-A-1-105238 are used. Depending on the case, it is possible to obtain a photopolymerizable composition excellent in the photosensitive speed.

  Other examples include polyester acrylates, epoxy resins and (meth) acrylic acid as described in JP-A-48-64183, JP-B-49-43191, JP-B-52-30490, and JP-A-52-30490. Mention may be made of polyfunctional acrylates and methacrylates such as reacted epoxy acrylates. In addition, specific unsaturated compounds described in JP-B-46-43946, JP-B-1-40337, JP-B-1-40336, and vinylphosphonic acid-based compounds described in JP-A-2-25493 are also included. Can be mentioned. In some cases, a structure containing a perfluoroalkyl group described in JP-A-61-22048 is preferably used. Furthermore, Journal of Japan Adhesion Association vol. 20, no. 7, pages 300 to 308 (1984), which are introduced as photocurable monomers and oligomers, can also be used.

About these polymerizable compounds, the details of usage such as the structure, single use or combination, addition amount, etc. can be arbitrarily set according to the performance design of the final lithographic printing plate precursor. For example, it is selected from the following viewpoints.
From the viewpoint of sensitivity, a structure having a large unsaturated group content per molecule is preferable, and in many cases, a bifunctional or higher functionality is preferable. Further, in order to increase the strength of the image area, that is, the cured film, those having three or more functionalities are preferable. Further, different functional numbers and different polymerizable groups (for example, acrylic acid ester, methacrylic acid ester, styrenic compound, vinyl ether type). A method of adjusting both sensitivity and strength by using a compound) is also effective.
In addition, the compatibility and dispersibility with other components in the photosensitive layer (for example, binder polymer, polymerization initiator, colorant, etc.), the selection and use method of the polymerizable compound is an important factor. In some cases, the compatibility can be improved by using a low-purity compound or by using two or more kinds in combination. In addition, a specific structure may be selected for the purpose of improving adhesion to a support or a protective layer described later.

  The polymerizable compound is preferably used in the range of 5 to 80% by mass, more preferably 25 to 75% by mass, based on the total solid content of the photosensitive layer. These may be used alone or in combination of two or more. In addition, the usage of the polymerizable compound can be arbitrarily selected from the viewpoint of polymerization inhibition with respect to oxygen, resolution, fogging, refractive index change, surface adhesiveness, etc. The layer construction and coating method such as undercoating and overcoating can also be carried out.

(D) Polyurethane resin having a unit having a hydrophilic group
The photosensitive layer of the lithographic printing plate precursor according to the invention contains a polyurethane resin having a unit having a hydrophilic group as an essential component. Examples of the unit having a hydrophilic group include an organic group comprising at least one of an acid group, an ether bond, an amide bond, a urea bond, an ester bond, a urethane bond, a biuret bond, and an allophanate bond. More preferred are an organic group having an acid group and a polyether unit. Examples of the acid group include acid groups such as a carboxyl group, a sulfone group, and a phosphoric acid group. The polyether unit is a residue derived from polyether diol which is one of diol components which are raw materials for synthesizing a polyurethane resin described later. Here, the acid group may be a salt such as an alkali metal salt or an ammonium salt.
A more preferred unit having a hydrophilic group is an organic group having an acid group or a salt thereof, and particularly preferred is an organic group containing a sulfonic acid or a sulfonate.

  When the hydrophilic group of the present invention is an acid group, the content in the binder polymer is preferably 0.1 to 50 mol% with respect to the total molar amount of the structural unit, from the viewpoint of developability, From the viewpoint of achieving both printing durability and raw storage stability, 0.5 to 30 mol% is more preferable, and 1.0 to 20 mol% is most preferable.

  That is, it is preferable that 0.001 to 20 g of the binder polymer that can be used in the present invention can be dissolved in 100 g of the developer according to claims 1 and 2, and 0 in terms of both printing durability and raw storage stability. It is more preferable that 0.005 to 10 g can be dissolved, and it is particularly preferable that 0.01 to 5 g can be dissolved. Furthermore, it is preferable that 0.001 to 30 g can be dissolved in 100 g of the aqueous solution according to claim 3, and 0.005 to 20 g can be more preferably dissolved from the viewpoint of both printing durability and raw storage stability. It is particularly preferable that 10 g can be dissolved.

  By having a unit having the above hydrophilic group, the affinity for water and hydrophilic polymer is increased, and the raw storage stability can be improved.

  The polyurethane resin having a unit having a hydrophilic group used in the present invention preferably further has a unit having an ethylenically unsaturated bond. The polyurethane resin having a unit having an ethylenically unsaturated bond preferably has at least one of functional groups represented by the following general formulas (1) to (3) in the side chain of the resin. First, the functional groups represented by the following general formulas (1) to (3) will be described.

In the general formula (1), R ^{1 to} R ³ each independently represents a hydrogen atom or a monovalent organic group, and R ¹ is preferably a hydrogen atom or an alkyl which may have a substituent. A hydrogen atom and a methyl group are preferable because of high radical reactivity. R ² and R ³ are each independently a hydrogen atom, a halogen atom, an amino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an optionally substituted alkyl group, or a substituted group. An aryl group that may have a group, an alkoxy group that may have a substituent, an aryloxy group that may have a substituent, an alkylamino group that may have a substituent, and a substituent An arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, a substituent An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

X represents an oxygen atom, a sulfur atom, or N (R ¹² ) —, and R ¹² represents a hydrogen atom or a monovalent organic group. Here, examples of R ¹² include an alkyl group which may have a substituent, and among them, a hydrogen atom, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

  Here, examples of the substituent that can be introduced include an alkyl group, an alkenyl group, an alkynyl group, an aryl group, an alkoxy group, an aryloxy group, a halogen atom, an amino group, an alkylamino group, an arylamino group, a carboxyl group, an alkoxycarbonyl group, A sulfo group, a nitro group, a cyano group, an amide group, an alkylsulfonyl group, an arylsulfonyl group and the like can be mentioned.

In the general formula (2), R ^{4 to} R ⁸ each independently represents a hydrogen atom or a monovalent organic group, and R ^{4 to} R ⁸ are preferably a hydrogen atom, a halogen atom, an amino group, or a dialkyl. Amino group, carboxyl group, alkoxycarbonyl group, sulfo group, nitro group, cyano group, alkyl group which may have a substituent, aryl group which may have a substituent, alkoxy which may have a substituent A group, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, an arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, Examples include an arylsulfonyl group which may have a substituent. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, an alkyl group which may have a substituent, and an aryl which may have a substituent The ru group is preferred.

Examples of the substituent that can be introduced are the same as those in the general formula (1). Y represents an oxygen atom, a sulfur atom, or N (R ¹² ) —. R ¹² has the same meaning as R ¹² in general formula (1), and preferred examples are also the same.

In the general formula (3), R ⁹ is preferably a hydrogen atom or an alkyl group which may have a substituent. Among them, a hydrogen atom or a methyl group has high radical reactivity. To preferred. R ¹⁰ and R ¹¹ are each independently a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, or an alkyl group which may have a substituent. An aryl group which may have a substituent, an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, a substituent An arylamino group which may have, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, etc. are mentioned, among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

Here, examples of the substituent that can be introduced are the same as those in the general formula (1). Further, Z is an oxygen atom, a sulfur atom, -N (R ¹³⁾ -, or a phenylene group which may have a substituent. Examples of R ¹³ include an alkyl group which may have a substituent. Among them, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

  Next, the basic skeleton of the polyurethane resin according to the present invention will be described. The polyurethane resin according to the present invention is represented by a reaction product of at least one diisocyanate compound represented by the following general formula (4) and at least one diol compound represented by the general formula (5). A polyurethane resin having a structural unit as a basic skeleton.

OCN-X ⁰ -NCO (4)
HO-Y ⁰ -OH (5)

In general formulas (4) and (5), X ⁰ and Y ⁰ each independently represent a divalent organic residue. At least one of X ⁰ and Y ⁰ is preferably a unit having a hydrophilic group. Further, from the viewpoint of synthesis, Y ⁰ is more preferably a unit having a hydrophilic group.

  At least one of the diisocyanate compound represented by the general formula (4) and the diol compound represented by the general formula (5) is at least one of the groups represented by the general formulas (1) to (3). If it has one, groups represented by the above general formulas (1) to (3) are introduced into the side chain as a reaction product of the diisocyanate compound and the diol compound.

By using the compounds represented by the general formula (4) and the general formula (5), a polyurethane resin having a unit having a hydrophilic group and a polyurethane resin further having a unit having an ethylenically unsaturated bond Is generated. According to such a method, the polyurethane resin according to the present invention (hereinafter also referred to as a specific polyurethane resin) can be easily obtained, rather than replacing and introducing a desired hydrophilic group or ethylenically unsaturated bond after the reaction of the polyurethane resin. Can be manufactured.

1) Diisocyanate compound The diisocyanate compound represented by the above general formula (4) is obtained, for example, by subjecting a triisocyanate compound to 1 equivalent of a monofunctional alcohol or monofunctional amine compound having an unsaturated group. There are products that are produced.
Examples of the triisocyanate compound include those shown below, but are not limited thereto.

  Examples of the monofunctional alcohol or monofunctional amine compound having an unsaturated group include those shown below, but are not limited thereto.

  Here, as a method for introducing an unsaturated group into the side chain of the polyurethane resin, a method using a diisocyanate compound containing an unsaturated group in the side chain as a raw material for producing the polyurethane resin is suitable. Examples of a diisocyanate compound obtained by addition reaction of a triisocyanate compound with one equivalent of a monofunctional alcohol having a unsaturated group or a monofunctional amine compound having an unsaturated group in the side chain include, for example, Although the following are mentioned, it is not limited to this.

  The specific polyurethane resin used in the present invention contains, for example, the above-described ethylenically unsaturated bond from the viewpoint of improving compatibility with other components in the polymerizable composition and improving storage stability. Diisocyanate compounds other than diisocyanate compounds can be copolymerized.

  Examples of the diisocyanate compound to be copolymerized include the following. Preferred is a diisocyanate compound represented by the following general formula (6).

OCN-L ¹ -NCO (6)

In General Formula (6), L ¹ represents a divalent aliphatic or aromatic hydrocarbon group which may have a substituent. If necessary, L ¹ may have another functional group that does not react with an isocyanate group, such as an ester, urethane, amide, or ureido group.

Specific examples of the diisocyanate compound represented by the general formula (6) include those shown below.
That is, 2,4-tolylene diisocyanate, dimer of 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, p-xylylene diisocyanate, m-xylylene diisocyanate, 4,4′-diphenylmethane diisocyanate Aromatic diisocyanate compounds such as 1,5-naphthylene diisocyanate, 3,3′-dimethylbiphenyl-4,4′-diisocyanate;
Aliphatic diisocyanate compounds such as hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, dimer acid diisocyanate and the like;
Alicyclic diisocyanate compounds such as isophorone diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2,4 (or 2,6) diisocyanate, 1,3- (isocyanatomethyl) cyclohexane;
And a diisocyanate compound which is a reaction product of a diol and a diisocyanate such as an adduct of 1 mol of 1,3-butylene glycol and 2 mol of tolylene diisocyanate.

2) Diol Compound As the diol compound represented by the general formula (5), a polyether diol compound, a polyester diol compound, a polycarbonate diol compound, and the like are widely used.

  Here, as a method for introducing an ethylenically unsaturated bond into the side chain of the polyurethane resin, in addition to the above-described method, a diol compound containing an ethylenically unsaturated bond in the side chain is used as a raw material for producing the polyurethane resin. A method is also suitable. Such a diol compound may be a commercially available one such as trimethylolpropane monoallyl ether, or a carboxylic acid containing a halogenated diol compound, a triol compound, an aminodiol compound, and an ethylenically unsaturated bond. , An acid chloride, an isocyanate, an alcohol, an amine, a thiol, or a compound easily produced by a reaction with an alkyl halide compound. Specific examples of these compounds include, but are not limited to, the compounds shown below.

  Further, as a more preferable binder resin in the present invention, the polyurethane resin was obtained by using a diol compound represented by the following general formula (G) as at least one diol compound having an ethylenically unsaturated bond group in the synthesis of polyurethane. Mention may be made of polyurethane resins.

In the general formula (G), R ^{1 to} R ³ each independently represents a hydrogen atom or a monovalent organic group, A represents a divalent organic residue, X represents an oxygen atom, a sulfur atom, or N (R ¹²⁾ - represents, R ¹² represents a hydrogen atom or a monovalent organic group.
Incidentally, R ¹ to R ³ and X in the general formula (G) has the same meaning as R ¹ to R ³ and X in the general formula (1), preferred embodiments versa.
By using a polyurethane resin derived from such a diol compound, it is considered that the coating strength of the layer can be improved by suppressing the excessive molecular motion of the polymer main chain caused by the secondary alcohol having a large steric hindrance. It is done.
Hereinafter, specific examples of the diol compound represented by the general formula (G) which are suitably used for the synthesis of the specific polyurethane resin will be shown.

The specific polyurethane resin used in the present invention contains, for example, the above-described ethylenically unsaturated bond from the viewpoint of improving compatibility with other components in the polymerizable composition and improving storage stability. A diol compound other than the diol compound can be copolymerized.
Examples of such diol compounds include the polyether diol compounds, polyester diol compounds, and polycarbonate diol compounds described above.

  Examples of the polyether diol compound include compounds represented by the following formulas (7), (8), (9), (10), and (11), and random copolymerization of ethylene oxide and propylene oxide having a hydroxyl group at the terminal. Coalescence is mentioned.

In formulas (7) to (11), R ¹⁴ represents a hydrogen atom or a methyl group, and X ¹ represents the following group. Moreover, a, b, c, d, e, f, and g each represent an integer of 2 or more, and preferably an integer of 2 to 100.

Specific examples of the polyether diol compound represented by the above formulas (7) and (8) include the following.
That is, diethylene glycol, triethylene glycol, tetraethylene glycol, pentaethylene glycol, hexaethylene glycol, heptaethylene glycol, octaethylene glycol, di-1,2-propylene glycol, tri-1,2-propylene glycol, tetra-1, 2-propylene glycol, hexa-1,2-propylene glycol, di-1,3-propylene glycol, tri-1,3-propylene glycol, tetra-1,3-propylene glycol, di-1,3-butylene glycol, Tri-1,3-butylene glycol, hexa-1,3-butylene glycol, polyethylene glycol having a weight average molecular weight of 1000, polyethylene glycol having a weight average molecular weight of 1500, poly having a weight average molecular weight of 2000 Tylene glycol, polyethylene glycol with a weight average molecular weight of 3000, polyethylene glycol with a weight average molecular weight of 7500, polypropylene glycol with a weight average molecular weight of 400, polypropylene glycol with a weight average molecular weight of 700, polypropylene glycol with a weight average molecular weight of 1000, polypropylene glycol with a weight average molecular weight of 2000 , Polypropylene glycol having a weight average molecular weight of 3000, polypropylene glycol having a weight average molecular weight of 4000, and the like.

Specific examples of the polyether diol compound represented by the formula (9) include those shown below.
That is, Sanyo Chemical Industries, Ltd. (trade name) PTMG650, PTMG1000, PTMG2000, PTMG3000, and the like.

Specific examples of the polyether diol compound represented by the formula (10) include those shown below.
That is, Sanyo Chemical Industries, Ltd. (trade name) New Pole PE-61, New Pole PE-62, New Pole PE-64, New Pole PE-68, New Pole PE-71, New Pole PE-74, New Pole PE-75, New Pole PE-78, New Pole PE-108, New Pole PE-128, New Pole PE-61, and the like.

Specific examples of the polyether diol compound represented by the formula (11) include those shown below.
That is, Sanyo Chemical Industries, Ltd. (trade name) New Pole BPE-20, New Pole BPE-20F, New Pole BPE-20NK, New Pole BPE-20T, New Pole BPE-20G, New Pole BPE-40, New Pole BPE-60, New Pole BPE-100, New Pole BPE-180, New Pole BPE-2P, New Pole BPE-23P, New Pole BPE-3P, New Pole BPE-5P, and the like.

Specific examples of the random copolymer of ethylene oxide and propylene oxide having a hydroxyl group at the terminal include the following.
That is, Sanyo Chemical Industries, Ltd. (trade name) New Pole 50HB-100, New Pole 50HB-260, New Pole 50HB-400, New Pole 50HB-660, New Pole 50HB-2000, New Pole 50HB-5100, etc. It is.

  Examples of the polyester diol compound include compounds represented by formulas (12) and (13).

In formulas (12) and (13), L ² , L ³ and L ⁴ may be the same or different and each represents a divalent aliphatic or aromatic hydrocarbon group, and L ⁵ represents a divalent aliphatic carbonization. Represents a hydrogen group. Preferably, L ^{2 to} L ⁴ each represent an alkylene group, an alkenylene group, an alkynylene group, or an arylene group, and L ⁵ represents an alkylene group. In addition, other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom may be present in L ^{2 to} L ⁵ . n1 and n2 are each an integer of 2 or more, preferably an integer of 2 to 100.
As the polycarbonate diol compound, there is a compound represented by the formula (14).

In the formula (14), L ⁶ may be the same or different and each represents a divalent aliphatic or aromatic hydrocarbon group. Preferably, L ⁶ represents an alkylene group, an alkenylene group, an alkynylene group or an arylene group. In addition, other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom may be present in L ⁶ . n3 is an integer of 2 or more, and preferably represents an integer of 2 to 100.

  Specific examples of the diol compound represented by the above formula (12), (13) or (14) include (Exemplary Compound No. 1) to (Exemplary Compound No. 18) shown below. N in the specific examples represents an integer of 2 or more.

  Moreover, in the synthesis | combination of specific polyurethane resin, the diol compound which has a substituent which does not react with an isocyanate group other than the said diol compound can also be used together. Examples of such diol compounds include those shown below.

^{HO-L 7 -O-CO-} L 8 -CO-O-L 7 -OH (15)
^{HO-L 8 -CO-O-} L 7 -OH (16)

In the formulas (15) and (16), L ⁷ and L ⁸ may be the same or different, and each may have a substituent (for example, an alkyl group, an aralkyl group, an aryl group, an alkoxy group, an aryloxy group, —F, — And a divalent aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group, which may have a halogen atom such as Cl, -Br, and -I. If necessary, L ⁷ and L ⁸ may have another functional group that does not react with an isocyanate group, such as a carbonyl group, an ester group, a urethane group, an amide group, or a ureido group. Note that L ⁷ and L ⁸ may form a ring.

  A diol compound having an acid group can be used for the synthesis of the specific polyurethane resin having a unit having an acid group such as a carboxyl group, a sulfone group, or a phosphoric acid group. Examples of the diol compound having a carboxyl group include those represented by the following formulas (17) to (19).

In the formulas (17) to (19), R ¹⁵ is a hydrogen atom, a substituent (for example, a halogen atom such as a cyano group, a nitro group, —F, —Cl, —Br, —I, etc.), —CONH ₂ , —COOR ^16. , -OR ¹⁶ ,
Each group includes —NHCONHR ¹⁶ , —NHCOOR ¹⁶ , —NHCOR ¹⁶ , —OCONHR ¹⁶ (wherein R ¹⁶ represents an alkyl group having 1 to 10 carbon atoms and an aralkyl group having 7 to 15 carbon atoms). . Represents an alkyl group, an aralkyl group, an aryl group, an alkoxy group or an aryloxy group, which may have a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, or an aryl group having 6 to 15 carbon atoms. To express. L ⁹ , L ¹⁰ and L ¹¹ may be the same or different from each other, and may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy and halogeno groups are preferred). Represents a divalent aliphatic or aromatic hydrocarbon group, preferably an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 15 carbon atoms, more preferably an alkylene group having 1 to 8 carbon atoms. . If necessary, L ^{9 to} L ¹¹ may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, ureido, and ether groups. A ring may be formed by 2 or 3 of R ¹⁵ , L ⁷ , L ⁸ and L ⁹ .
Ar represents a trivalent aromatic hydrocarbon group which may have a substituent, and preferably represents an aromatic group having 6 to 15 carbon atoms.

Specific examples of the diol compound having a carboxyl group represented by the above formulas (17) to (19) include those shown below.
3,5-dihydroxybenzoic acid, 2,2-bis (hydroxymethyl) propionic acid, 2,2-bis (2-hydroxyethyl) propionic acid, 2,2-bis (3-hydroxypropyl) propionic acid, Bis (hydroxymethyl) acetic acid, bis (4-hydroxyphenyl) acetic acid, 2,2-bis (hydroxymethyl) butyric acid, 4,4-bis (4-hydroxyphenyl) pentanoic acid, tartaric acid, N, N-dihydroxyethylglycine N, N-bis (2-hydroxyethyl) -3-carboxy-propionamide and the like.

  For the synthesis of a specific polyurethane resin having a carboxyl group, in addition to the diol, a compound obtained by ring-opening a tetracarboxylic dianhydride represented by the following formulas (20) to (22) with a diol compound is used. It can also be used together.

In formulas (20) to (22), L ¹² may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy, halogeno, ester, or amide groups are preferred). Represents an aliphatic or aromatic hydrocarbon group, —CO—, —SO—, —SO ₂ —, —O— or —S—, preferably a single bond and a divalent aliphatic group having 1 to 15 carbon atoms. It represents a hydrocarbon group, —CO—, —SO ₂ —, —O— or —S—. R ¹⁷ and R ¹⁸ may be the same or different and each represents a hydrogen atom, an alkyl group, an aralkyl group, an aryl group, an alkoxy group, or a halogeno group, preferably a hydrogen atom or an alkyl having 1 to 8 carbon atoms. Group, an aryl group having 6 to 15 carbon atoms, an alkoxy group having 1 to 8 carbon atoms or a halogeno group. Two of L ¹² , R ¹⁷ and R ¹⁸ may be bonded to form a ring.

R ¹⁹ and R ²⁰ may be the same or different and each represents a hydrogen atom, an alkyl group, an aralkyl group, an aryl group or a halogeno group, preferably a hydrogen atom, an alkyl having 1 to 8 carbon atoms, or a carbon number of 6 Represents ~ 15 aryl groups. Two of L ¹² , R ¹⁹ and R ²⁰ may be bonded to form a ring. L ¹³ and L ¹⁴ may be the same or different and each represents a single bond, a double bond or a divalent aliphatic hydrocarbon group, preferably a single bond, a double bond or a methylene group. A represents a mononuclear or polynuclear aromatic ring. Preferably, it represents an aromatic ring having 6 to 18 carbon atoms.

Specific examples of the compound represented by the above formula (20), (21) or (22) include those shown below.
That is, pyromellitic dianhydride, 3,3 ′, 4,4′-benzophenone tetracarboxylic dianhydride, 3,3 ′, 4,4′-diphenyltetracarboxylic dianhydride, 2, 3,6,7-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 4,4′-sulfonyldiphthalic dianhydride, 2,2-bis (3 , 4-Dicarboxyphenyl) propane dianhydride, bis (3,4-dicarboxyphenyl) ether dianhydride, 4,4 ′-[3,3 ′-(alkylphosphoryldiphenylene) -bis (iminocarbonyl) Aromatic tetracarboxylic dianhydrides such as diphthalic dianhydride, adducts of hydroquinone diacetate and trimetic anhydride, diacetyldiamine and trimetic anhydride; 5- (2,5-dioxote Trahydrofuryl) -3-methyl-3-cyclohexsi-1,2-dicarboxylic anhydride (Dainippon Ink Chemical Co., Ltd., Epicron B-4400), 1,2,3,4-cyclopentanetetra Alicyclic tetracarboxylic dianhydrides such as carboxylic dianhydride, 1,2,4,5-cyclohexanetetracarboxylic dianhydride, tetrahydrofuran tetracarboxylic dianhydride; 1,2,3,4-butane Aliphatic tetracarboxylic dianhydrides such as tetracarboxylic dianhydride and 1,2,4,5-pentanetetracarboxylic dianhydride are listed.

Examples of a method for introducing a compound obtained by ring-opening these tetracarboxylic dianhydrides with a diol compound into a polyurethane resin include the following methods.
a) A method of reacting an alcohol-terminated compound obtained by ring-opening tetracarboxylic dianhydride with a diol compound and a diisocyanate compound.
b) A method of reacting an alcohol-terminated urethane compound obtained by reacting a diisocyanate compound under an excess of a diol compound with tetracarboxylic dianhydride.

Specific examples of the diol compound used for the ring-opening reaction include those shown below.
That is, ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, dipropylene glycol, polyethylene glycol, polypropylene glycol, neopentyl glycol, 1,3-butylene glycol, 1,6-hexanediol, 2-butene- 1,4-diol, 2,2,4-trimethyl-1,3-pentanediol, 1,4-bis-β-hydroxyethoxycyclohexane, cyclohexanedimethanol, tricyclodecane dimethanol, hydrogenated bisphenol A, hydrogenated Bisphenol F, bisphenol A ethylene oxide adduct, bisphenol A propylene oxide adduct, bisphenol F ethylene oxide adduct, bisphenol F pro Renoxide adduct, hydrogenated bisphenol A ethylene oxide adduct, hydrogenated bisphenol A propylene oxide adduct, hydroquinone dihydroxyethyl ether, p-xylylene glycol, dihydroxyethyl sulfone, bis (2-hydroxyethyl) -2, Examples include 4-tolylene dicarbamate, 2,4-tolylene-bis (2-hydroxyethylcarbamide), bis (2-hydroxyethyl) -m-xylylenedicarbamate, and bis (2-hydroxyethyl) isophthalate.

  Examples of the diol having a sulfone group include the following diols, but are not limited thereto.

  Examples of the diol having a phosphoric acid group include, but are not limited to, the following diols.

The specific polyurethane resin that can be used in the present invention is synthesized by adding the above-mentioned diisocyanate compound and diol compound to an aprotic solvent and adding a known catalyst having an activity corresponding to the respective reactivity, and heating. The molar ratio (M _a : M _b ) of the diisocyanate and diol compound used in the synthesis is preferably 1: 1 to 1.2: 1, and the molecular weight or viscosity is desired by treating with alcohols or amines. The product having the physical properties is finally synthesized in a form in which no isocyanate group remains.

  Moreover, what has an ethylenically unsaturated bond in a polymer terminal and / or a polymer principal chain is also used suitably for the specific polyurethane resin which concerns on this invention.

  As a method for introducing an unsaturated group into the polymer terminal, there are the following methods. That is, in the step of treating with the residual isocyanate group at the polymer end and the alcohols or amines in the above-mentioned polyurethane resin synthesis step, an alcohol or amine having an unsaturated group may be used. Specific examples of such a compound include the same compounds as those exemplified above as the monofunctional alcohol or monofunctional amine compound having an unsaturated group.

As a method for introducing an unsaturated group into a polymer main chain, there is a method of using a diol compound having an unsaturated group in the main chain direction for the synthesis of a polyurethane resin. Specific examples of the diol compound having an unsaturated group in the main chain direction include the following compounds.
That is, cis-2-butene-1,4-diol, trans-2-butene-1,4-diol, polybutadiene diol, and the like.

  The ethylenically unsaturated bond is preferably introduced into the polymer side chain rather than the polymer end from the viewpoint that the introduction amount can be easily controlled and the introduction amount can be increased, and the crosslinking reaction efficiency is improved.

  The ethylenically unsaturated bond group to be introduced is preferably a methacryloyl group, an acryloyl group or a styryl group, more preferably a methacryloyl group or an acryloyl group, from the viewpoint of forming a crosslinked cured film. From the viewpoint of coexistence of the formability of the crosslinked cured film and the raw storage stability, a methacryloyl group is more preferable.

  As an introduction amount of the ethylenically unsaturated bond contained in the specific polyurethane resin according to the present invention, in terms of equivalent, 0.3 meq / g or more of an ethylenically unsaturated bond group in the side chain, and further 0.35 to It is preferable to contain 1.50 meq / g. That is, a polyurethane resin containing 0.35 to 1.50 meq / g of methacryloyl group in the side chain is most preferable.

  The molecular weight of the specific polyurethane resin according to the present invention is preferably 10,000 or more in terms of weight average molecular weight, and more preferably in the range of 40,000 to 200,000. In particular, when the polymerizable composition of the present invention is used for the recording layer of a lithographic printing plate precursor, the weight average molecular weight is excellent in the strength of the image area within this range, and the developability of the non-image area by the alkaline developer is improved. Excellent.

  Although the specific example of the specific polyurethane resin used for this invention below is shown in Table 1-Table 11, it is not limited to these.

  The polyurethane resin having a unit having a hydrophilic group in the present application preferably has a unit having an ethylenically unsaturated bond. A more preferred embodiment includes a polyurethane resin having a unit in which the hydrophilic group is a sulfone group (or a salt thereof) and a unit having an ethylenically unsaturated bond. A particularly preferred embodiment includes a polyurethane resin having a unit in which the hydrophilic group is a sulfone group (or a salt thereof) and a unit from the diol compound represented by the general formula (G).

  An alkali-soluble polymer containing a polyurethane resin having a structure different from that of the specific polyurethane resin can be used in combination with the specific polyurethane resin of the present invention. For example, the specific polyurethane resin can be used in combination with a polyurethane resin containing an aromatic group in the main chain and / or side chain.

(Co-sensitizer)
The sensitivity of the photosensitive layer can be further improved by using certain additives. Such a compound is referred to as a co-sensitizer in the present invention. These mechanisms of action are not clear, but many are thought to be based on the following chemical processes. That is, a photoreaction initiated by light absorption of the above-described photopolymerization initiation system, and various intermediate active species (radicals, peroxides, oxidizing agents, reducing agents, etc.) generated in the course of the subsequent addition polymerization reaction, It is presumed that the co-sensitizer reacts to generate a new active radical. These can be broadly divided into (a) those that can be reduced to generate active radicals, (b) those that can be oxidized to generate active radicals, and (c) radicals that are more active by reacting with less active radicals. Can be classified into those that act as chain transfer agents, but there is often no generality as to which of these individual compounds belong.

(A) Compound that is reduced to produce an active radical Compound having a carbon-halogen bond: It is considered that the carbon-halogen bond is reductively cleaved to generate an active radical. Specifically, for example, trihalomethyl-s-triazines and trihalomethyloxadiazoles can be preferably used.
Compound having nitrogen-nitrogen bond: It is considered that the nitrogen-nitrogen bond is reductively cleaved to generate an active radical. Specifically, hexaarylbiimidazoles and the like are preferably used.
Compound having oxygen-oxygen bond: It is considered that the oxygen-oxygen bond is reductively cleaved to generate an active radical. Specifically, for example, organic peroxides are preferably used.
Onium compounds: It is considered that carbon-hetero bonds and oxygen-nitrogen bonds are reductively cleaved to generate active radicals. Specifically, for example, diaryliodonium salts, triarylsulfonium salts, N-alkoxypyridinium (azinium) salts and the like are preferably used.
Ferrocene and iron arene complexes: An active radical can be reductively generated.

(B) Compound which is oxidized to generate an active radical Alkylate complex: It is considered that a carbon-hetero bond is oxidatively cleaved to generate an active radical. Specifically, for example, triarylalkyl borates are preferably used.
Alkylamine compound: It is considered that the C—X bond on carbon adjacent to nitrogen is cleaved by oxidation to generate an active radical. X is preferably a hydrogen atom, a carboxyl group, a trimethylsilyl group, a benzyl group or the like. Specific examples include ethanolamines, N-phenylglycines, N-trimethylsilylmethylanilines, and the like.
Sulfur-containing and tin-containing compounds: Compounds in which the nitrogen atoms of the above-described amines are replaced with sulfur atoms and tin atoms can generate active radicals by the same action. Further, a compound having an SS bond is also known to be sensitized by SS cleavage.

α-Substituted methylcarbonyl compound: An active radical can be generated by oxidative cleavage of the carbonyl-α carbon bond. Moreover, what converted carbonyl into the oxime ether also shows the same effect | action. Specifically, 2-alkyl-1- [4- (alkylthio) phenyl] -2-morpholinopronone-1 and these and a hydroxylamine were reacted, and then N—OH was etherified. Examples include oxime ethers.
Sulfinic acid salts: An active radical can be reductively generated. Specific examples include sodium arylsulfinate.

  (C) Compounds that react with radicals to convert to highly active radicals or act as chain transfer agents Compounds that react with radicals to convert to highly active radicals or act as chain transfer agents include, for example, SH, PH in the molecule , SiH, and GeH are used. These can donate hydrogen to low-activity radical species to generate radicals, or can be oxidized and then deprotonated to generate radicals. Specifically, 2-mercaptobenzimidazoles etc. are mentioned, for example.

  Many more specific examples of these co-sensitizers are described, for example, in JP-A-9-236913 as additives for the purpose of improving sensitivity. Some examples are shown below, but the present invention is not limited thereto.

  These co-sensitizers can also be subjected to various chemical modifications for improving the characteristics of the photosensitive layer of the lithographic printing plate precursor as in the case of the sensitizing dye. For example, bonds with sensitizing dyes, titanocene, addition polymerizable unsaturated compounds and other radical generating parts, introduction of hydrophilic sites, improved compatibility, introduction of substituents for suppressing crystal precipitation, substituents for improving adhesion Methods such as introduction and polymerization can be used. These co-sensitizers can be used alone or in combination of two or more. The amount used is 0.05 to 100 parts by mass, preferably 1 to 80 parts by mass, and more preferably 3 to 50 parts by mass with respect to 100 parts by mass of the compound having an ethylenically unsaturated double bond.

(Microcapsule)
In the present invention, as a method for causing the photosensitive layer to contain the above-described photosensitive layer constituents and other constituents described later, for example, as described in JP-A Nos. 2001-277740 and 2001-277742, A part of the components can be encapsulated in microcapsules and added to the photosensitive layer. In that case, each component can be contained in any ratio in and out of the microcapsule.

  As a method for microencapsulating the photosensitive layer constituent components, known methods can be applied. For example, as a method for producing microcapsules, a method using coacervation found in U.S. Pat. Nos. 2,800,547 and 2,800,498, U.S. Pat. No. 3,287,154, JP-B-38-19574, 42-446 by the interfacial polymerization method, US Pat. No. 3,418,250, US Pat. No. 3,660,304 by polymer precipitation method, US Pat. No. 3,796,669, isocyanate polyol A method using a wall material, a method using an isocyanate wall material found in US Pat. No. 3,914,511, and a urea-formaldehyde system found in US Pat. Nos. 4,001,140, 4,087,376 and 4,089,802. Or urea formaldehyde-resorcino A method using a wall forming material, a method using a wall material such as melamine-formaldehyde resin and hydroxycellulose, as shown in US Pat. No. 4,025,445, and Japanese Patent Publication Nos. 36-9163 and 51-9079. In situ method using monomer polymerization, spray drying method found in British Patent No. 930422, US Pat. No. 3,111,407, electrolytic dispersion cooling method seen in British Patent Nos. 952807 and 967074, etc. However, it is not limited to these.

  A preferable microcapsule wall used in the present invention has a three-dimensional cross-linking and has a property of swelling with a solvent. From such a viewpoint, the wall material of the microcapsule is preferably polyurea, polyurethane, polyester, polycarbonate, polyamide, and a mixture thereof, and particularly preferably polyurea and polyurethane. Moreover, you may introduce | transduce into the microcapsule wall the compound which has crosslinkable functional groups, such as an ethylenically unsaturated bond which can be introduce | transduced into said water-insoluble polymer.

  The average particle size of the microcapsules is preferably 0.01 to 3.0 μm. 0.05-2.0 micrometers is further more preferable, and 0.10-1.0 micrometer is especially preferable. Within this range, good resolution and stability over time can be obtained.

(Other photosensitive layer components)
The photosensitive layer of the present invention can further contain various additives as required. These will be described below.

(Surfactant)
In the present invention, it is preferable to use a surfactant in the photosensitive layer in order to promote developability and improve the coated surface state. Examples of the surfactant include nonionic surfactants, anionic surfactants, cationic surfactants, amphoteric surfactants, and fluorosurfactants. Surfactant may be used independently and may be used in combination of 2 or more type.

  The nonionic surfactant used for this invention is not specifically limited, A conventionally well-known thing can be used. For example, polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, glycerin fatty acid partial esters, sorbitan fatty acid partial esters, pentaerythritol Fatty acid partial esters, propylene glycol mono fatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, polyglycerin fatty acid partial esters, Polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acid diethanolamides, N N- bis-2-hydroxyalkylamines, polyoxyethylene alkylamines, triethanolamine fatty acid ester, trialkylamine oxide, polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol.

The anionic surfactant used in the present invention is not particularly limited, and conventionally known anionic surfactants can be used. For example, fatty acid salts, abietic acid salts, hydroxyalkane sulfonates, alkane sulfonates, dialkyl sulfosuccinate esters, linear alkyl benzene sulfonates, branched alkyl benzene sulfonates, alkyl naphthalene sulfonates, alkyl phenoxy poly Oxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium salt, N-alkyl sulfosuccinic acid monoamide disodium salt, petroleum sulfonates, sulfated beef oil, fatty acid alkyl esters Sulfates, alkyl sulfates, polyoxyethylene alkyl ether sulfates, fatty acid monoglyceride sulfates, polyoxyethylene alcohol Ruphenyl ether sulfates, polyoxyethylene styryl phenyl ether sulfates, alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl phenyl ether phosphates, styrene / maleic anhydride Examples thereof include partial saponification products of polymers, partial saponification products of olefin / maleic anhydride copolymers, and naphthalene sulfonate formalin condensates.

The cationic surfactant used in the present invention is not particularly limited, and conventionally known cationic surfactants can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.
The amphoteric surfactant used in the present invention is not particularly limited, and conventionally known amphoteric surfactants can be used. Examples thereof include carboxybetaines, aminocarboxylic acids, sulfobetaines, aminosulfuric esters, and imidazolines.

  Of the above surfactants, the term “polyoxyethylene” can be read as “polyoxyalkylene” such as polyoxymethylene, polyoxypropylene, polyoxybutylene, etc. These surfactants can also be used.

  More preferable surfactants include fluorine-based surfactants containing a perfluoroalkyl group in the molecule. Examples of such fluorosurfactants include anionic types such as perfluoroalkyl carboxylates, perfluoroalkyl sulfonates, and perfluoroalkyl phosphates; amphoteric types such as perfluoroalkyl betaines; Cation type such as trimethylammonium salt; perfluoroalkylamine oxide, perfluoroalkylethylene oxide adduct, oligomer containing perfluoroalkyl group and hydrophilic group, oligomer containing perfluoroalkyl group and lipophilic group, perfluoroalkyl Nonionic types such as an oligomer containing a group, a hydrophilic group and a lipophilic group, and a urethane containing a perfluoroalkyl group and a lipophilic group. Also preferred are the fluorosurfactants described in JP-A-62-170950, JP-A-62-226143 and JP-A-60-168144.

Surfactant can be used individually or in combination of 2 or more types.
The content of the surfactant is preferably 0.001 to 10% by mass and more preferably 0.01 to 7% by mass with respect to the total solid content of the photosensitive layer.

(Hydrophilic polymer)
In the present invention, a hydrophilic polymer can be contained in order to improve the developability and the dispersion stability of the microcapsules.
Examples of the hydrophilic polymer include hydroxy group, carboxyl group, carboxylate group, hydroxyethyl group, polyoxyethyl group, hydroxypropyl group, polyoxypropyl group, amino group, aminoethyl group, aminopropyl group, ammonium group, Preferred are those having a hydrophilic group such as an amide group, carboxymethyl group, sulfonic acid group, and phosphoric acid group.

Specific examples include gum arabic, casein, gelatin, starch derivatives, carboxymethylcellulose and its sodium salt, cellulose acetate, sodium alginate, vinyl acetate-maleic acid copolymers, styrene-maleic acid copolymers, polyacrylic acids and their salts, Polymethacrylic acids and their salts, homopolymers and copolymers of hydroxyethyl methacrylate, homopolymers and copolymers of hydroxyethyl acrylate, homopolymers and copolymers of hydroxypropyl methacrylate, homopolymers and copolymers of hydroxypropyl acrylate, homopolymers of hydroxybutyl methacrylate Polymers and copolymers, homopolymers and copolymers of hydroxybutyl acrylate Polyethylene glycols, hydroxypropylene polymers, polyvinyl alcohols, hydrolyzed polyvinyl acetate, polyvinyl formal, polyvinyl butyral, polyvinyl pyrrolidone, acrylamide homopolymers and copolymers having a hydrolysis degree of 60 mol% or more, preferably 80 mol% or more , Homopolymers and polymers of methacrylamide, homopolymers and copolymers of N-methylolacrylamide, polyvinylpyrrolidone, alcohol-soluble nylon, polyether of 2,2-bis- (4-hydroxyphenyl) -propane and epichlorohydrin, etc. Is mentioned.

The hydrophilic polymer preferably has a weight average molecular weight of 5000 or more, more preferably 10,000 to 300,000. The hydrophilic polymer may be any of a random polymer, a block polymer, a graft polymer, and the like.
The content of the hydrophilic polymer in the photosensitive layer is preferably 20% by mass or less, more preferably 10% by mass or less, based on the total solid content of the photosensitive layer.

(Coloring agent)
In the present invention, a dye having a large absorption in the visible light region can be used as an image colorant. Specifically, Oil Yellow # 101, Oil Yellow # 103, Oil Pink # 312, Oil Green BG, Oil Blue BOS, Oil Blue # 603, Oil Black BY, Oil Black BS, Oil Black T-505 (orientated chemistry) Kogyo Co., Ltd.), Victoria Pure Blue, Crystal Violet (CI42555), Methyl Violet (CI42535), Ethyl Violet, Rhodamine B (CI145170B), Malachite Green (CI42000), Methylene Blue (CI522015), etc. And dyes described in Japanese Patent No. 293247. Also, pigments such as phthalocyanine pigments, azo pigments, carbon black, titanium oxide, etc. can be suitably used.

  These colorants are preferably added since it is easy to distinguish an image area from a non-image area after image formation. The amount added is preferably 0.01 to 10% by mass relative to the total solid content of the image recording material.

(Bake-out agent)
In the photosensitive layer of the present invention, a compound that changes color by an acid or a radical can be added in order to produce a printout image. As such a compound, various dyes such as diphenylmethane, triphenylmethane, thiazine, oxazine, xanthene, anthraquinone, iminoquinone, azo, and azomethine are effectively used.

  Specific examples include brilliant green, ethyl violet, methyl green, crystal violet, basic fuchsin, methyl violet 2B, quinaldine red, rose bengal, methanyl yellow, thymol sulfophthalein, xylenol blue, methyl orange, paramethyl red, Congo Fred, Benzopurpurin 4B, α-Naphthyl Red, Nile Blue 2B, Nile Blue A, Methyl Violet, Malachide Green, Parafuchsin, Victoria Pure Blue BOH [manufactured by Hodogaya Chemical Co., Ltd.], Oil Blue # 603 [Orient Chemical Kogyo Co., Ltd.], Oil Pink # 312 [Orient Chemical Co., Ltd.], Oil Red 5B [Orient Chemical Co., Ltd.], Oil Scarlet # 308 [Orient Gaku Kogyo Co., Ltd.], Oil Red OG [Orient Chemical Co., Ltd.], Oil Red RR [Orient Chemical Co., Ltd.], Oil Green # 502 [Orient Chemical Co., Ltd.], Spiron Red BEH Special [made by Hodogaya Chemical Co., Ltd.], m-cresol purple, cresol red, rhodamine B, rhodamine 6G, sulforhodamine B, auramine, 4-p-diethylaminophenyliminonaphthoquinone, 2-carboxyanilino-4-p- Diethylaminophenyliminonaphthoquinone, 2-carboxystearylamino-4-pN, N-bis (hydroxyethyl) amino-phenyliminonaphthoquinone, 1-phenyl-3-methyl-4-p-diethylaminophenylimino-5-pyrazolone, 1-β-naphthyl-4- - dyes and p of diethylamino phenyl imino-5-pyrazolone, p ', p "- hexamethyl triamnotriphenylmethane (leuco crystal violet), and a leuco dye such as Pergascript Blue SRB (manufactured by Ciba-Geigy).

  In addition to the above, a leuco dye known as a material for thermal paper or pressure-sensitive paper is also suitable. Specific examples include crystal violet lactone, malachite green lactone, benzoylleucomethylene blue, 2- (N-phenyl-N-methylamino) -6- (Np-tolyl-N-ethyl) amino-fluorane, 2-anilino. -3-methyl-6- (N-ethyl-p-toluidino) fluorane, 3,6-dimethoxyfluorane, 3- (N, N-diethylamino) -5-methyl-7- (N, N-dibenzylamino) ) -Fluorane, 3- (N-cyclohexyl-N-methylamino) -6-methyl-7-anilinofluorane, 3- (N, N-diethylamino) -6-methyl-7-anilinofluorane, 3 -(N, N-diethylamino) -6-methyl-7-xylidinofluorane, 3- (N, N-diethylamino) -6-methyl-7-chloro Fluorane, 3- (N, N-diethylamino) -6-methoxy-7-aminofluorane, 3- (N, N-diethylamino) -7- (4-chloroanilino) fluorane, 3- (N, N-diethylamino) -7-chlorofluorane, 3- (N, N-diethylamino) -7-benzylaminofluorane, 3- (N, N-diethylamino) -7,8-benzofluorane, 3- (N, N-dibutyl) Amino) -6-methyl-7-anilinofluorane, 3- (N, N-dibutylamino) -6-methyl-7-xylidinofluorane, 3-piperidino-6-methyl-7-anilinofluorane 3-pyrrolidino-6-methyl-7-anilinofluorane, 3,3-bis (1-ethyl-2-methylindol-3-yl) phthalide, 3,3-bis (1-n-butyl- -Methylindol-3-yl) phthalide, 3,3-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide, 3- (4-diethylamino-2-ethoxyphenyl) -3- (1-ethyl- 2-methylindol-3-yl) -4-zaphthalide, 3- (4-diethylaminophenyl) -3- (1-ethyl-2-methylindol-3-yl) phthalide, and the like.

  A suitable addition amount of the dye that changes color by acid or radical is 0.01 to 15% by mass relative to the solid content of the photosensitive layer.

(Polymerization inhibitor)
It is preferable to add a small amount of a thermal polymerization inhibitor to the photosensitive layer of the present invention in order to prevent unnecessary thermal polymerization of the radical polymerizable compound during the production or storage of the photosensitive layer.
Examples of the thermal polymerization inhibitor include hydroquinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4'-thiobis (3-methyl-6-t- (Butylphenol), 2,2'-methylenebis (4-methyl-6-tert-butylphenol), N-nitroso-N-phenylhydroxylamine aluminum salt are preferred.
The addition amount of the thermal polymerization inhibitor is preferably about 0.01 to about 5% by mass with respect to the total solid content of the photosensitive layer.

(Higher fatty acid derivatives, etc.)
In order to prevent polymerization inhibition by oxygen, a higher fatty acid derivative such as behenic acid or behenamide is added to the photosensitive layer of the present invention so that it is unevenly distributed on the surface of the photosensitive layer during the drying process after coating. May be. The amount of the higher fatty acid derivative added is preferably from about 0.1 to about 10% by weight based on the total solid content of the photosensitive layer.

(Plasticizer)
The photosensitive layer of the present invention may contain a plasticizer. Examples of the plasticizer include phthalates such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, diisobutyl phthalate, dioctyl phthalate, octyl capryl phthalate, dicyclohexyl phthalate, ditridecyl phthalate, butyl benzyl phthalate, diisodecyl phthalate, diallyl phthalate; Glycol esters such as glycol phthalate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, butyl phthalyl butyl glycolate, triethylene glycol dicaprylate; Phosphate esters such as tricresyl phosphate and triphenyl phosphate Diisobutyl adipate, dioctyl adipate, dimethyl sebacate, dibutyl sebacate, dioct Ruazereto, aliphatic dibasic acid esters such as dibutyl maleate; polyglycidyl methacrylate, triethyl citrate, glycerin triacetyl ester, butyl laurate in. The plasticizer content is preferably about 30% by mass or less based on the total solid content of the photosensitive layer.

(Inorganic fine particles)
The photosensitive layer of the present invention may contain inorganic fine particles in order to improve the strength of the cured film in the image area. As the inorganic fine particles, for example, silica, alumina, magnesium oxide, titanium oxide, magnesium carbonate, calcium alginate or a mixture thereof can be preferably mentioned. Even if they are not photothermally convertible, they can be used for strengthening the film, enhancing interfacial adhesion by surface roughening, and the like. The inorganic fine particles preferably have an average particle size of 5 nm to 10 μm, and more preferably 0.5 to 3 μm. Within the above range, it is possible to form a non-image portion having excellent hydrophilicity, which is stably dispersed in the photosensitive layer, sufficiently retains the film strength of the photosensitive layer, and hardly causes stains during printing.
The inorganic fine particles as described above can be easily obtained as a commercial product such as a colloidal silica dispersion.
The content of the inorganic fine particles is preferably 20% by mass or less, and more preferably 10% by mass or less, based on the total solid content of the photosensitive layer.

(Low molecular hydrophilic compound)
The photosensitive layer of the present invention can contain a hydrophilic low molecular weight compound for improving developability. Examples of hydrophilic low molecular weight compounds include water-soluble organic compounds such as glycols such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, and tripropylene glycol, and ether or ester derivatives thereof, glycerin, Polyhydroxys such as pentaerythritol, organic amines such as triethanolamine and diethanolamine monoethanolamine and salts thereof, organic sulfonic acids such as toluenesulfonic acid and benzenesulfonic acid and salts thereof, organic phosphonic acids such as phenylphosphonic acid and the like Organic carboxylic acids such as salts, tartaric acid, oxalic acid, citric acid, malic acid, lactic acid, gluconic acid, amino acids and their salts, and organic quaternary amines such as tetraethylamine hydrochloride Salt, and the like.

  In addition to the above, the photosensitive layer of the present invention can contain, for example, a cosensitizer.

(Formation of photosensitive layer)
The photosensitive layer of the present invention is formed by preparing or applying a coating solution by dispersing or dissolving the necessary components described above in a solvent. Solvents used here include ethylene dichloride, cyclohexanone, methyl ethyl ketone, methanol, ethanol, propanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, 2-methoxyethyl acetate, 1-methoxy-2-propyl acetate, dimethoxy Examples include ethane, methyl lactate, ethyl lactate, N, N-dimethylacetamide, N, N-dimethylformamide, tetramethylurea, N-methylpyrrolidone, dimethyl sulfoxide, sulfolane, γ-butyllactone, toluene, water, and the like. However, the present invention is not limited to this. These solvents are used alone or in combination. The solid content concentration of the coating solution is preferably 1 to 50% by mass.
The photosensitive layer of the present invention can be formed by preparing a plurality of coating solutions in which the same or different components are dispersed or dissolved in the same or different solvents, and repeatedly applying and drying a plurality of times.

The coating, the photosensitive layer coating amount on the support obtained after drying (solid content) may be varied according to the intended purpose, generally 0.3 to 3.0 g / m ² is preferred. Within this range, good sensitivity and good film properties of the photosensitive layer can be obtained.
Various methods can be used as a coating method. Examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.

[Protective layer]
The lithographic printing plate precursor according to the invention is preferably provided with a protective layer (oxygen blocking layer) on the photosensitive layer in order to block diffusion and penetration of oxygen that hinders the polymerization reaction during exposure. The protective layer used in the present invention preferably has an oxygen permeability A at 25 ° C. and 1 atm of 1.0 ≦ A ≦ 20 (mL / m ² · day). When the oxygen permeability A is extremely low at less than 1.0 (mL / m ² · day), unnecessary polymerization reaction occurs at the time of production and raw storage, and unnecessary fogging and image streaking occur during image exposure. The problem that fatness arises arises. Conversely, when the oxygen permeability A exceeds 20 (mL / m ² · day) and is too high, the sensitivity is lowered. The oxygen permeability A is more preferably in the range of 1.5 ≦ A ≦ 12 (mL / m ² · day), further preferably 2.0 ≦ A ≦ 10.0 (mL / m ² · day). In addition to the oxygen permeability described above, the properties desired for the protective layer further do not substantially inhibit the transmission of light used for exposure, have excellent adhesion to the photosensitive layer, and are easy in the development process after exposure. It is desirable that it can be removed. The device concerning such a protective layer has been conventionally made, and is described in detail in US Pat. No. 3,458,311 and JP-B-55-49729.

  As a material that can be used for the protective layer, for example, a water-soluble polymer compound having relatively excellent crystallinity is preferably used. Specifically, polyvinyl alcohol, vinyl alcohol / vinyl phthalate copolymer, vinyl acetate / vinyl are used. Examples include water-soluble polymers such as alcohol / vinyl phthalate copolymer, vinyl acetate / crotonic acid copolymer, polyvinyl pyrrolidone, acidic celluloses, gelatin, gum arabic, polyacrylic acid, and polyacrylamide. Or they can be mixed. Of these, the use of polyvinyl alcohol as the main component gives the best results in terms of basic properties such as oxygen barrier properties and development removability.

  The polyvinyl alcohol used for the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains an unsubstituted vinyl alcohol unit for having necessary oxygen barrier properties and water solubility. Similarly, some of them may have other copolymer components. Specific examples of polyvinyl alcohol include those having a hydrolysis rate of 71 to 100 mol% and a polymerization repeating unit in the range of 300 to 2400. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405, PVA- 420, PVA-613, L-8 and the like, and these can be used alone or in combination. In a preferred embodiment, the content of polyvinyl alcohol in the protective layer is 20 to 95% by mass, and more preferably 30 to 90% by mass.

  Moreover, well-known modified polyvinyl alcohol can also be used preferably. For example, various hydrophilic modification sites such as anion modification sites modified with anions such as carboxyl groups and sulfo groups, cation modification sites modified with cations such as amino groups and ammonium groups, silanol modification sites, and thiol modification sites are randomly selected. Polyvinyl alcohol having various degrees of polymerization, the anion-modified site, the cation-modified site, the silanol-modified site, the thiol-modified site, the alkoxyl-modified site, the sulfide-modified site, and the ester modification of vinyl alcohol and various organic acids. Examples thereof include polyvinyl alcohol having various polymerization degrees having various modified sites such as a site, an ester-modified site of the anion-modified site and alcohols, an epoxy-modified site, and the like.

  As a component used by mixing with polyvinyl alcohol, polyvinyl pyrrolidone or a modified product thereof is preferable from the viewpoint of oxygen barrier properties and development removability, and the content in the protective layer is 3.5 to 80% by mass, preferably 10 to 60%. It is 15 mass%, More preferably, it is 15-30 mass%.

  Components of the protective layer (selection of PVA, use of additives), coating amount, and the like are selected in consideration of fogging, adhesion, and scratch resistance in addition to oxygen barrier properties and development removability. In general, the higher the hydrolysis rate of the PVA used (the higher the content of the unsubstituted vinyl alcohol unit in the protective layer), the thicker the film thickness, the higher the oxygen barrier property, which is advantageous in terms of sensitivity. The molecular weight of the (co) polymer such as polyvinyl alcohol (PVA) can be in the range of 2000 to 10 million, preferably in the range of 20,000 to 3 million.

  As another composition of the protective layer, glycerin, dipropylene glycol and the like can be added in an amount corresponding to several mass% with respect to the (co) polymer to provide flexibility. Anionic surfactants such as sodium acid salts; amphoteric surfactants such as alkylaminocarboxylates and alkylaminodicarboxylates; nonionic surfactants such as polyoxyethylene alkylphenyl ethers to the (co) polymer Mass% can be added.

  In addition, adhesion to the image area and scratch resistance are extremely important in handling the plate. That is, when a hydrophilic layer made of a water-soluble polymer is laminated on an oleophilic photosensitive layer, film peeling due to insufficient adhesion tends to occur, and the peeled part causes defects such as poor film hardening due to inhibition of oxygen polymerization. On the other hand, various proposals have been made to improve the adhesion between these two layers. For example, in U.S. Patent Application No. 292,501 and U.S. Patent Application No. 44,563, an acrylic emulsion or a water-insoluble vinyl pyrrolidone-vinyl acetate copolymer is contained in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesiveness can be obtained by mixing 20 to 60% by mass and laminating on a photosensitive layer. Any of these known techniques can be applied to the protective layer in the present invention. Such a coating method for the protective layer is described in detail in, for example, US Pat. No. 3,458,311 and Japanese Patent Publication No. 55-49729.

Furthermore, the protective layer in the lithographic printing plate precursor according to the invention preferably contains an inorganic stratiform compound for the purpose of improving oxygen barrier properties and photosensitive layer surface protection.
Here, the inorganic layered compound is a particle having a thin plate-like shape. For example, the following general formula A (B, C) _2-5 D ₄ O ₁₀ (OH, F, O) ₂
[However, A is any one of K, Na, and Ca, B and C are any of Fe (II), Fe (III), Mn, Al, Mg, and V, and D is Si or Al. And mica groups such as natural mica and synthetic mica, talc, teniolite, montmorillonite, saponite, hectorite, zirconium phosphate and the like represented by the formula 3MgO.4SiO.H ₂ O.

In the mica group, examples of natural mica include muscovite, soda mica, phlogopite, biotite and sericite. Further, as the synthetic mica, non-swelling mica such as fluorine phlogopite mica ₃ (AlSi ₃ O ₁₀ ) F ₂ , potassium tetrasilicon mica KMg _2.5 Si ₄ O ₁₀ ) F ₂ , and Na tetrasilicic mica NaMg _2.5 ( _{Si 4 O 10) F 2,} Na or Li teniolite _{(Na, Li) Mg 2 Li} (Si 4 O 10) F 2, montmorillonite based Na or Li hectorite _{(Na, Li) 1/8 Mg 2} /5 Li Examples thereof include swelling mica such as _1/8 (Si ₄ O ₁₀ ) F ₂ . Synthetic smectite is also useful.

In the present invention, among the inorganic layered compounds, fluorine-based swellable mica, which is a synthetic inorganic layered compound, is particularly useful. That is, this swellable synthetic mica and swellable viscosity minerals such as montmorillonite, saponite, hectorite, bentonite, etc. have a laminated structure composed of unit crystal lattice layers with a thickness of about 10 to 15 mm, Atomic substitution is significantly greater than other viscous minerals. As a result, the lattice layer is deficient in positive charges, and cations such as Na ⁺ , Ca ²⁺ and Mg ²⁺ are adsorbed between the layers in order to compensate for this. The cations present between these layers are called exchangeable cations and exchange with various cations. In particular, when the cation between the layers is Li ⁺ or Na ⁺ , since the ionic radius is small, the bond between the layered crystal lattices is weak, and the layer swells greatly with water. If shear is applied in this state, it will easily cleave and form a stable sol in water. Bentonite and swellable synthetic mica have this tendency and are useful in the present invention, and swellable synthetic mica is particularly preferably used.

  As the shape of the inorganic layered compound used in the present invention, from the viewpoint of diffusion control, the smaller the thickness, the better. The plane size is as long as it does not hinder the smoothness of the coated surface or the transmittance of actinic rays. Larger is better. Accordingly, the aspect ratio is 20 or more, preferably 100 or more, particularly preferably 200 or more. The aspect ratio is the ratio of the thickness to the major axis of the particle, and can be measured, for example, from a projected view of the particle by a micrograph. The larger the aspect ratio, the greater the effect that can be obtained.

  As for the particle diameter of the inorganic stratiform compound used in the present invention, the average major axis is 0.3 to 20 μm, preferably 0.5 to 10 μm, particularly preferably 1 to 5 μm. The average thickness of the particles is 0.1 μm or less, preferably 0.05 μm or less, particularly preferably 0.01 μm or less. For example, among inorganic layered compounds, the size of the swellable synthetic mica that is a representative compound is about 1 to 50 nm in thickness and about 1 to 20 μm in surface size.

  When the inorganic layered compound particles having such a large aspect ratio are contained in the protective layer, the coating film strength is improved, and the permeation of oxygen and moisture can be effectively prevented. Deterioration is prevented, and even when stored for a long time under high-humidity conditions, the storage stability of the planographic printing plate precursor does not deteriorate due to changes in humidity, and the storage stability is excellent.

  It is preferable that content of the inorganic stratiform compound in a protective layer is 5/1-1/100 by mass ratio with respect to the quantity of the binder used for a protective layer. Even when a plurality of types of inorganic layered compounds are used in combination, the total amount of these inorganic layered compounds is preferably the above-described mass ratio.

  Next, an example of a general dispersion method of the inorganic stratiform compound used for the protective layer will be described. First, 5 to 10 parts by mass of the swellable layered compound mentioned above as a preferred inorganic layered compound is added to 100 parts by mass of water, and the mixture is thoroughly swelled and swollen, and then dispersed by a disperser. Examples of the disperser used here include various mills that disperse mechanically by applying a direct force, a high-speed stirring disperser having a large shearing force, and a disperser that provides high-intensity ultrasonic energy. Specifically, ball mill, sand grinder mill, visco mill, colloid mill, homogenizer, tisol bar, polytron, homomixer, homo blender, ketdy mill, jet agitator, capillary emulsifier, liquid siren, electrostrictive ultrasonic generator, An emulsifying device having a Paulman whistle can be used. A dispersion of 5 to 10% by mass of the inorganic stratiform compound dispersed by the above method is highly viscous or gelled and has very good storage stability. When preparing a protective layer coating solution using this dispersion, it is preferably prepared by diluting with water and stirring sufficiently, and then blending with a binder solution.

  In addition to the inorganic layered compound, known additives such as a surfactant for improving coatability and a water-soluble plasticizer for improving film properties can be added to the protective layer coating solution. Examples of the water-soluble plasticizer include propionamide, cyclohexanediol, glycerin, sorbitol and the like. A water-soluble (meth) acrylic polymer can also be added. Furthermore, known additives for improving the adhesion to the photosensitive layer and the temporal stability of the coating solution may be added to the coating solution.

  The protective layer coating solution thus prepared is applied onto the photosensitive layer provided on the support and dried to form a protective layer. The coating solvent can be appropriately selected in relation to the binder, but when a water-soluble polymer is used, it is preferable to use distilled water or purified water. The method for applying the protective layer is not particularly limited, and a known method such as the method described in US Pat. No. 3,458,311 or Japanese Patent Publication No. 55-49729 can be applied. . Specific examples of the protective layer include blade coating, air knife coating, gravure coating, roll coating coating, spray coating, dip coating, and bar coating.

The coating amount of the protective layer is preferably in the range of 0.05 to 10 g / m ^{2 in} terms of the coating amount after drying. When the inorganic layered compound is contained, 0.1 to 0.5 g / The range of m ² is more preferable, and when the inorganic layered compound is not contained, the range of 0.5 to 5 g / m ² is more preferable.

[Support]
The support used in the lithographic printing plate precursor according to the invention is not particularly limited as long as it is a dimensionally stable plate-like hydrophilic support. For example, paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum, zinc, copper, etc.), plastic film (eg, cellulose diacetate, cellulose triacetate, cellulose propionate) Cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), and paper or plastic films on which the above-mentioned metals are laminated or deposited. Preferable supports include a polyester film and an aluminum plate. Among these, an aluminum plate that has good dimensional stability and is relatively inexpensive is preferable.

  The aluminum plate is a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of different elements, or a plastic laminated on a thin film of aluminum or an aluminum alloy. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is preferably 10% by mass or less. In the present invention, a pure aluminum plate is preferable, but completely pure aluminum is difficult to manufacture in terms of refining technology, and therefore may contain a slightly different element. The composition of the aluminum plate is not specified, and a publicly known material can be used as appropriate.

  The thickness of the support is preferably from 0.1 to 0.6 mm, more preferably from 0.15 to 0.4 mm, and even more preferably from 0.2 to 0.3 mm.

  Prior to using the aluminum plate, it is preferable to perform a surface treatment such as roughening treatment or anodizing treatment. By the surface treatment, it becomes easy to improve hydrophilicity and secure adhesion between the photosensitive layer and the support. Prior to roughening the aluminum plate, a degreasing treatment with a surfactant, an organic solvent, an alkaline aqueous solution or the like for removing rolling oil on the surface is performed as desired.

The surface roughening treatment of the aluminum plate is performed by various methods. For example, mechanical surface roughening treatment, electrochemical surface roughening treatment (surface roughening treatment for dissolving the surface electrochemically), chemical treatment, etc. Surface roughening treatment (roughening treatment that chemically selectively dissolves the surface).
As a method for the mechanical surface roughening treatment, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used.
Examples of the electrochemical surface roughening treatment include a method in which an alternating current or a direct current is used in an electrolytic solution containing an acid such as hydrochloric acid or nitric acid. Another example is a method using a mixed acid as described in JP-A-54-63902.

  The surface-roughened aluminum plate is subjected to an alkali etching treatment using an aqueous solution of potassium hydroxide, sodium hydroxide or the like, if necessary, further neutralized, and if desired, wear resistant. In order to increase the anodic oxidation treatment.

As the electrolyte used for the anodizing treatment of the aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, hydrochloric acid, oxalic acid, chromic acid or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.
The conditions for anodizing treatment vary depending on the electrolyte used, and thus cannot be specified in general. d m ² , voltage 1 to 100 V, and electrolysis time 10 seconds to 5 minutes are preferable. The amount of the anodized film formed is preferably from 1.0 to 5.0 g / m ^2, and more preferably 1.5 to 4.0 g / m ^2. Within this range, good printing durability and good scratch resistance of the non-image area of the lithographic printing plate can be obtained.

  As the support used in the present invention, the substrate having the above-mentioned surface treatment and having an anodized film may be used as it is, but for further improvement in adhesion to the upper layer, hydrophilicity, resistance to contamination, heat insulation and the like. If necessary, it contains a micropore enlargement treatment, a micropore sealing treatment, and a hydrophilic compound described in Japanese Patent Application Laid-Open Nos. 2001-253181 and 2001-322365. A surface hydrophilization treatment immersed in an aqueous solution can be selected as appropriate. Of course, these enlargement processing and sealing processing are not limited to those described above, and any conventionally known method can be performed.

Sealing treatment includes vapor sealing, single treatment with zirconic fluoride, treatment with an aqueous solution containing an inorganic fluorine compound such as treatment with sodium fluoride, vapor sealing with addition of lithium chloride, sealing with hot water. Hole processing is also possible.
Of these, sealing treatment with an aqueous solution containing an inorganic fluorine compound, sealing treatment with water vapor, and sealing treatment with hot water are preferable.

  The hydrophilization treatment is described in the specifications of US Pat. Nos. 2,714,066, 3,181,461, 3,280,734, and 3,902,734. There are such alkali metal silicate methods. In this method, the support is immersed in an aqueous solution such as sodium silicate or electrolytically treated. In addition, the treatment with potassium zirconate fluoride described in JP-B 36-22063, U.S. Pat. Nos. 3,276,868, 4,153,461 and 4,689, And a method of treating with polyvinylphosphonic acid as described in the specification of No. 272.

  When using a support with insufficient surface hydrophilicity such as a polyester film as the support of the present invention, it is desirable to apply a hydrophilic layer to make the surface hydrophilic. As the hydrophilic layer, at least one element selected from beryllium, magnesium, aluminum, silicon, titanium, boron, germanium, tin, zirconium, iron, vanadium, antimony, and a transition metal described in JP-A-2001-199175 A hydrophilic layer formed by coating a coating solution containing a colloid of oxide or hydroxide, or organic hydrophilicity obtained by crosslinking or pseudo-crosslinking an organic hydrophilic polymer described in JP-A-2002-79772 A hydrophilic layer having a hydrophilic matrix, a hydrophilic layer having an inorganic hydrophilic matrix obtained by sol-gel conversion comprising hydrolysis, condensation reaction of polyalkoxysilane, titanate, zirconate or aluminate, or a metal oxide A hydrophilic layer made of an inorganic thin film having a surface is preferred. Arbitrariness. Among these, a hydrophilic layer formed by applying a coating solution containing a silicon oxide or a hydroxide colloid is preferable.

  Moreover, when using a polyester film etc. as a support body of this invention, it is preferable to provide an antistatic layer in the hydrophilic layer side of a support body, the opposite side, or both sides. In the case where the antistatic layer is provided between the support and the hydrophilic layer, it also contributes to improving the adhesion with the hydrophilic layer. As the antistatic layer, a polymer layer in which metal oxide fine particles or a matting agent are dispersed as described in JP-A-2002-79772 can be used.

The support preferably has a center line average roughness of 0.10 to 1.2 μm. Within this range, good adhesion to the photosensitive layer, good printing durability and good stain resistance can be obtained.
The color density of the support is preferably 0.15 to 0.65 as the reflection density value. Within this range, good image formability by preventing halation during image exposure and good plate inspection after development can be obtained.

(Undercoat layer)
In the lithographic printing plate precursor according to the invention, it is preferable to provide an undercoat layer of a compound containing a polymerizable group on a support. When an undercoat layer is used, the photosensitive layer is provided on the undercoat layer. The undercoat layer reinforces the adhesion between the support and the photosensitive layer in the exposed area, and easily peels the photosensitive layer from the support in the unexposed area, thereby improving the developability.
As the undercoat layer, specifically, a silane coupling agent having an addition-polymerizable ethylenic double bond reactive group described in JP-A-10-282679, JP-A-2-304441. The phosphorus compound etc. which have the ethylenic double bond reactive group of description are mentioned suitably. Particularly preferred compounds include compounds having a polymerizable group such as a methacryl group and an allyl group and a support-adsorbing group such as a sulfonic acid group, a phosphoric acid group, and a phosphoric acid ester group. A compound having a hydrophilicity-imparting group such as an ethylene oxide group in addition to the polymerizable group and the support-adsorbing group can also be exemplified as a suitable compound.
The coating amount (solid content) of the undercoat layer is preferably from 0.1-100 mg / m ^2, and more preferably 1 to 30 mg / m ^2.

[Back coat layer]
After the surface treatment is performed on the support or after the undercoat layer is formed, a back coat can be provided on the back surface of the support, if necessary.
Examples of the back coat include hydrolysis and polycondensation of organic polymer compounds described in JP-A-5-45885, organometallic compounds or inorganic metal compounds described in JP-A-6-35174. A coating layer made of a metal oxide obtained in this manner is preferred. Among them, it is inexpensive to use a silicon alkoxy compound such as Si (OCH ₃ ) ₄ , Si (OC ₂ H ₅ ) ₄ , Si (OC ₃ H ₇ ) ₄ , Si (OC ₄ H ₉ ) _4. It is preferable in terms of easy availability.

<Plate making method>
Hereinafter, the plate making method of the above-described planographic printing plate precursor (plate making method of the present invention) will be described.
The plate-making method of the lithographic printing plate precursor according to the present invention is an automatic processor equipped with a rubbing member after exposing the above-described lithographic printing plate precursor using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm. By rubbing the plate surface with a rubbing member in the presence of a developer having a pH of 2 to 10, the photosensitive layer in the non-exposed area is removed to obtain a lithographic printing plate.

  The exposure apparatus used in the present invention is equipped with a light source having a light emission maximum in the range of 360 nm to 450 nm, and in particular, a 405 nm laser commercially available from Nichia Corporation or the like is preferably used.

The exposure apparatus used in the present invention may be any of an internal drum system, an external drum system, a flat bed system, and the like. Further, by simultaneously recording an image by the multi-beam exposure method, a highly accurate image can be recorded at a high speed.
Further, at the time of exposure of the planographic printing plate precursor of the present invention, image recording can be performed on an FM screen.

  In the present invention, the entire exposed lithographic printing plate precursor may be heated between exposure and development, if necessary. By such heating, an image forming reaction in the photosensitive layer is promoted, and advantages such as improvement in sensitivity and printing durability and stabilization of sensitivity may occur. Moreover, when it has a protective layer on a photosensitive layer, it is also preferable to perform a water washing process before image development processing.

〔developing〕
After the lithographic printing plate precursor in the present invention is image-exposed, the plate surface is rubbed with a rubbing member in the presence of a developer having a pH of 2 to 10 or an aqueous solution containing a water-soluble polymer to thereby remove the unexposed portion. The photosensitive layer can be removed (and, if a protective layer is present, the protective layer is also removed), and an image can be formed on the surface of the aluminum plate support.
Hereinafter, the developer used in the present invention, the developer having a pH of 2 to 10 and an aqueous solution containing a water-soluble polymer will be described.

  As the developer having a pH of 2 to 10 used in the present invention, water alone or an aqueous solution containing water as a main component (containing 60% by mass or more of water) is preferable, and in particular, the same as generally known dampening water. An aqueous solution containing a composition, an aqueous solution containing a surfactant (anionic, nonionic, cationic, etc.) or an aqueous solution containing a water-soluble polymer compound is preferred. In particular, an aqueous solution containing both a surfactant and a water-soluble polymer compound is preferable. The pH of the developer is more preferably from 3 to 10, and particularly preferably from 4 to 8, from the viewpoint of removing the unexposed portion of the photosensitive layer.

  Examples of the anionic surfactant used in the present invention include fatty acid salts, abietic acid salts, hydroxyalkane sulfonic acid salts, alkane sulfonic acid salts, dialkyl sulfosuccinic acid salts, linear alkyl benzene sulfonic acid salts, branched alkyl benzene sulfonic acid salts, Alkylnaphthalene sulfonates, alkylphenoxy polyoxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium, N-alkyl sulfosuccinic acid monoamide disodium salts, petroleum sulfonates , Sulfated castor oil, sulfated beef tallow oil, fatty acid alkyl ester sulfates, alkyl sulfates, polyoxyethylene alkyl ether sulfates, fatty acid compounds Glyceryl sulfate ester salt, polyoxyethylene alkylphenyl ether sulfate ester salt, polyoxyethylene styryl phenyl ether sulfate ester salt, alkyl phosphate ester salt, polyoxyethylene alkyl ether phosphate ester salt, polyoxyethylene alkylphenyl ether phosphate ester salt, styrene -Partial saponifications of maleic anhydride copolymer, partial saponifications of olefin-maleic anhydride copolymer, naphthalene sulfonate formalin condensate and the like. Among these, dialkyl sulfosuccinates, alkyl sulfate esters and alkyl naphthalene sulfonates are particularly preferably used.

  It does not specifically limit as a cationic surfactant used for this invention, A conventionally well-known thing can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.

Nonionic surfactants used in the present invention include polyethylene glycol type higher alcohol ethylene oxide adduct, alkylphenol ethylene oxide adduct, fatty acid ethylene oxide adduct, polyhydric alcohol fatty acid ester ethylene oxide adduct, higher alkylamine ethylene. Oxide adduct, fatty acid amide ethylene oxide adduct, fat and oil ethylene oxide adduct, polypropylene glycol ethylene oxide adduct, dimethylsiloxane-ethylene oxide block copolymer, dimethylsiloxane- (propylene oxide-ethylene oxide) block copolymer, etc. Fatty acid ester of alcohol type glycerol, fatty acid ester of pentaerythritol, sorbitol and sorbita Fatty acid esters of fatty acid esters of sucrose, alkyl ethers of polyhydric alcohols, fatty acid amides of alkanolamines.
These nonionic surfactants may be used alone or in combination of two or more. In the present invention, ethylene oxide adduct of sorbitol and / or sorbitan fatty acid ester, polypropylene glycol ethylene oxide adduct, dimethylsiloxane-ethylene oxide block copolymer, dimethylsiloxane- (propylene oxide-ethylene oxide) block copolymer, polyhydric alcohol Fatty acid esters are more preferred.

Further, from the viewpoint of stable solubility or turbidity in water, the nonionic surfactant used in the developer of the present invention is HLB (Hydrophile-Lipophile).
The (Balance) value is preferably 6 or more, and more preferably 8 or more. Furthermore, the ratio of the nonionic surfactant contained in the developer is preferably 0.01 to 10% by mass, and more preferably 0.01 to 5% by mass.
Also, acetylene glycol-based and acetylene alcohol-based oxyethylene adducts, fluorine-based and silicone-based surfactants can be used in the same manner.
As the surfactant used in the developer of the present invention, a nonionic surfactant is particularly suitable from the viewpoint of foam suppression.

Examples of the water-soluble polymer compound used in the developer of the present invention include soybean polysaccharide, modified starch, gum arabic, dextrin, fibrin derivatives (eg, carboxymethylcellulose, carboxyethylcellulose, methylcellulose, etc.) and modified products thereof, pullulan. , Polyvinyl alcohol and its derivatives, polyvinyl pyrrolidone, polyacrylamide and acrylamide copolymer, vinyl methyl ether / maleic anhydride copolymer, vinyl acetate / maleic anhydride copolymer, styrene / maleic anhydride copolymer, etc. It is done.

  A well-known thing can be used for the said soybean polysaccharide, for example, there exists a brand name Soya Five (made by Fuji Oil Co., Ltd.) as a commercial item, and the thing of various grades can be used. What can be preferably used is one in which the viscosity of a 10 mass% aqueous solution is in the range of 10 to 100 mPa / sec.

  As the modified starch, known ones can be used, and starch such as corn, potato, tapioca, rice and wheat is decomposed with acid or enzyme in the range of 5 to 30 glucose residues per molecule, and further in an alkali. It can be made by a method of adding oxypropylene or the like.

  Two or more water-soluble polymer compounds can be used in combination. The content of the water-soluble polymer compound in the developer is preferably from 0.1 to 20% by mass, and more preferably from 0.5 to 10% by mass.

  Further, the developer of the present invention may contain an organic solvent. Examples of the organic solvent that can be contained include aliphatic hydrocarbons (hexane, heptane, “Isopar E, H, G” (produced by Esso Chemical Co., Ltd.) or gasoline, kerosene, etc.), aromatic hydrocarbons (toluene). , Xylene, etc.), halogenated hydrocarbons (methylene dichloride, ethylene dichloride, tricrene, monochlorobenzene, etc.) and polar solvents.

  Polar solvents include alcohols (methanol, ethanol, propanol, isopropanol, benzyl alcohol, ethylene glycol monomethyl ether, 2-ethoxyethanol, diethylene glycol monoethyl ether, diethylene glycol monohexyl ether, triethylene glycol monomethyl ether, propylene glycol monoethyl ether , Propylene glycol monomethyl ether, polyethylene glycol monomethyl ether, polypropylene glycol, tetraethylene glycol, ethylene glycol monobutyl ether, ethylene glycol monobenzyl ether, ethylene glycol monophenyl ether, methylphenyl carbinol, n-amyl alcohol, methyl amyl alcohol, etc.) , (Acetone, methyl ethyl ketone, ethyl butyl ketone, methyl isobutyl ketone, cyclohexanone, etc.), esters (ethyl acetate, propyl acetate, butyl acetate, amyl acetate, benzyl acetate, methyl lactate, butyl lactate, ethylene glycol monobutyl acetate, propylene Glycol monomethyl ether acetate, diethylene glycol acetate, diethyl phthalate, butyl levulinate, etc.) and others (triethyl phosphate, tricresyl phosphate, N-phenylethanolamine, N-phenyldiethanolamine, etc.).

  If the organic solvent is insoluble in water, it can be used after being solubilized in water using a surfactant or the like. If the developer contains an organic solvent, safety, ignition, From the viewpoint of property, the concentration of the solvent is preferably less than 40% by mass.

  In addition to the above, the developer of the present invention may contain a preservative, a chelate compound, an antifoaming agent, an organic acid, an inorganic acid, an inorganic salt, and the like.

Preservatives include phenol or derivatives thereof, formalin, imidazole derivatives, sodium dehydroacetate, 4-isothiazolin-3-one derivatives, benzisothiazolin-3-one, benztriazole derivatives, amiding anidine derivatives, quaternary ammonium salts, pyridine, Derivatives such as quinoline and guanidine, diazine, triazole derivatives, oxazole, oxazine derivatives, nitrobromoalcohol-based 2-bromo-2-nitropropane-1,3diol, 1,1-dibromo-1-nitro-2-ethanol, 1,1-dibromo-1-nitro-2-propanol and the like can be preferably used.

  Examples of the chelate compound include ethylenediaminetetraacetic acid, potassium salt thereof, sodium salt thereof; diethylenetriaminepentaacetic acid, potassium salt thereof, sodium salt thereof; triethylenetetraminehexaacetic acid, potassium salt thereof, sodium salt thereof, hydroxyethylethylenediaminetriacetic acid Nitrilotriacetic acid, sodium salt; 1-hydroxyethane-1,1-diphosphonic acid, potassium salt, sodium salt; aminotri (methylenephosphonic acid), potassium salt, sodium salt And organic phosphonic acids and phosphonoalkanetricarboxylic acids. Organic amine salts are also effective in place of the sodium and potassium salts of the chelating agents.

As the antifoaming agent, a general silicone-based self-emulsifying type, emulsifying type, or nonionic surfactant having a HLB of 5 or less can be used. Silicone defoamers are preferred.
Among them, emulsification dispersion type and solubilization can be used.

  Examples of organic acids include citric acid, acetic acid, succinic acid, malonic acid, salicylic acid, caprylic acid, tartaric acid, malic acid, lactic acid, levulinic acid, p-toluenesulfonic acid, xylenesulfonic acid, phytic acid, and organic phosphonic acid. . The organic acid can also be used in the form of its alkali metal salt or ammonium salt.

  Examples of inorganic acids and inorganic salts include phosphoric acid, metaphosphoric acid, primary ammonium phosphate, secondary ammonium phosphate, primary sodium phosphate, secondary sodium phosphate, primary potassium phosphate, secondary potassium phosphate, Examples include sodium tripolyphosphate, potassium pyrophosphate, sodium hexametaphosphate, magnesium nitrate, sodium nitrate, potassium nitrate, ammonium nitrate, sodium sulfate, potassium sulfate, ammonium sulfate, sodium sulfite, ammonium sulfite, sodium hydrogen sulfate, nickel sulfate and the like.

Examples of the water-soluble polymer used in another developer of the present invention, an aqueous solution containing a water-soluble polymer, include the above-mentioned water-soluble polymers, but the photosensitive layer components are more dissolved or dispersed in the developer. From the viewpoint of facilitating, the polymer preferably has a hydroxyl group, more preferably two or more hydroxyl groups in the constituent units constituting the polymer, gum arabic or carboxymethylcellulose Particularly preferred are polysaccharides such as The pH of the aqueous solution containing the water-soluble polymer is more preferably from 2 to 8, and particularly preferably from 3 to 7, from the viewpoint of stability of the water-soluble polymer in the aqueous solution.
In addition, in the aqueous solution containing a water-soluble polymer, a surfactant, an organic solvent, an antiseptic, a chelate compound, an antifoaming agent, an organic acid, an inorganic acid, as described in the case of a developer having a pH of 2 to 10. In addition, inorganic salts and the like can be contained in a range.

  The developer described above can be used as a developer and developer replenisher for the exposed negative lithographic printing plate precursor, and is preferably applied to an automatic processor described later. When developing using an automatic processor, the developing solution becomes fatigued according to the amount of processing, so the processing capability may be restored using a replenisher or a fresh developer. This replenishing method is also preferably applied to the lithographic printing plate making method of the present invention.

The development treatment with an aqueous solution having a pH of 2 to 10 in the present invention can be preferably carried out by an automatic processor equipped with a developer supply means and a rubbing member. As an automatic processor, for example, an automatic processor described in JP-A-2-220061 and JP-A-60-59351, which performs a rubbing process while transporting a lithographic printing plate precursor after image recording, or a cylinder Examples thereof include an automatic processor described in US Pat. Nos. 5,148,746, 5,568,768 and British Patent 2,297,719, which rub the lithographic printing plate precursor after image recording set thereon while rotating a cylinder. Among these, an automatic processor using a rotating brush roll as the rubbing member is particularly preferable.

The rotating brush roll that can be preferably used in the present invention can be appropriately selected in consideration of the difficulty of scratching the image area and the stiffness of the lithographic printing plate precursor support. As the rotating brush roll, a known one formed by planting a brush material on a plastic or metal roll can be used. For example, as described in Japanese Patent Application Laid-Open No. 58-159533, Japanese Patent Application Laid-Open No. 3-100554, or Japanese Utility Model Publication No. 62-167253, metal or plastic in which brush materials are implanted in rows. A brush roll can be used in which the groove mold material is radially wound around a plastic or metal roll as a core without a gap.
The brush material includes plastic fibers (for example, polyesters such as polyethylene terephthalate and polybutylene terephthalate, polyamides such as nylon 6.6 and nylon 6.10, polyacrylonitrile, poly (meth) acrylate, Acrylic and polyolefin synthetic fibers such as polypropylene and polystyrene) can be used. For example, the fiber has a hair diameter of 20 to 400 μm and a hair length of 5 to 30 mm. Can be used.
Furthermore, the outer diameter of the rotating brush roll is preferably 30 to 200 mm, and the peripheral speed at the tip of the brush rubbing the plate surface is preferably 0.1 to 5 m / sec.
Moreover, it is preferable to use two or more rotating brush rolls.

  The rotation direction of the rotating brush roll used in the present invention may be the same direction or the reverse direction with respect to the transport direction of the planographic printing plate precursor of the present invention. Thus, when two or more rotating brush rolls are used, it is preferable that at least one rotating brush roll rotates in the same direction and at least one rotating brush roll rotates in the opposite direction. This further ensures the removal of the heat sensitive layer in the non-image area. Furthermore, it is also effective to swing the rotating brush roll in the direction of the rotation axis of the brush roll.

  Although the temperature of the developer can be used at any temperature, it is preferably 10 ° C to 50 ° C.

  In the present invention, the lithographic printing plate after the rubbing treatment can be optionally washed with water, dried and desensitized. In the desensitizing treatment, a known desensitizing solution can be used.

  In addition, as the plate-making process of the lithographic printing plate from the lithographic printing plate precursor according to the present invention, the entire surface may be heated before exposure, during exposure, and between exposure and development, if necessary. By such heating, the image forming reaction in the photosensitive layer is promoted, and advantages such as improvement in sensitivity and printing durability and stabilization of sensitivity may occur. Further, for the purpose of improving the image strength and printing durability, it is also effective to subject the developed image to full post heating or full exposure. Usually, heating before development is preferably performed under mild conditions of 150 ° C. or less. If the temperature is too high, problems such as covering up to the non-image area occur. Very strong conditions are used for heating after development. Usually, it is the range of 200-500 degreeC. If the temperature is low, sufficient image strengthening action cannot be obtained. If the temperature is too high, problems such as deterioration of the support and thermal decomposition of the image area occur.

The planographic printing plate obtained by the above processing is loaded on an offset printing machine and used for printing a large number of sheets.
As plate cleaners used for removing stains on printing plates, conventionally known plate cleaners for PS plates are used. For example, CL-1, CL-2, CP, CN-4, CN, CG -1, PC-1, SR, IC (manufactured by Fuji Photo Film Co., Ltd.) and the like.

EXAMPLES Hereinafter, although an Example demonstrates this invention, this invention is not limited to these. In addition, Example 13-15 shall be read as "reference example."

Synthesis example of specific polyurethane resin (Synthesis example 1; specific polyurethane resin P-1)
In a 500 ml three-necked round bottom flask equipped with a condenser and a stirrer, 8.2 g (0.05 mol) of 2,2-bis (hydroxymethyl) butanoic acid, 13.0 g of the following diol compound (1) (0 .05 mol) was dissolved in 100 ml of N, N-dimethylacetamide. To this, 25.5 g (0.102 mol) of 4,4-diphenylmethane diisocyanate and 0.1 g of dibutyltin dilaurate were added, and the mixture was heated and stirred at 100 ° C. for 8 hours. Thereafter, the mixture was diluted with 100 ml of N, N-dimethylformamide and 200 ml of methyl alcohol and stirred for 30 minutes. The reaction solution was poured into 3 liters of water with stirring to precipitate a white polymer. The polymer was filtered off, washed with water, and dried under vacuum to obtain 37 g of polymer. The synthesized specific polyurethane resin is represented by (P-1) in the following table.
When the molecular weight was measured by gel permeation chromatography (GPC), the weight average molecular weight (polystyrene standard) was 95,000.

(Synthesis Example 2; specific polyurethane resin P-5)
In a 500 ml three-necked round bottom flask equipped with a condenser and a stirrer, 5.9 g (0.04 mol) of 2,2-bis (hydroxymethyl) butanoic acid and 15.9 G (0.06) of the following diol compound (0.06) Mol) was dissolved in 100 ml of N, N-dimethylacetamide. To this, 20.4 g (0.082 mol) of 4,4-diphenylmethane diisocyanate, 3.4 g (0.02 mol) of 1,6-hexamethylene diisocyanate, and 0.1 g of dibutyltin dilaurate were added at 100 ° C. And stirred for 8 hours. Thereafter, the mixture was diluted with 100 ml of N, N-dimethylformamide and 200 ml of methyl alcohol and stirred for 30 minutes. The reaction solution was poured into 3 liters of water with stirring to precipitate a white polymer. The polymer was filtered off, washed with water, and dried under vacuum to obtain 34 g of polymer. The synthesized specific polyurethane resin is represented by (P-5) in the following table.
When the molecular weight was measured by gel permeation chromatography (GPC), the weight average molecular weight (polystyrene standard) was 99,000.

(Synthesis Example 3; specific polyurethane resin P-6)
In a 500 ml three-necked round bottom flask equipped with a condenser and a stirrer, 5.4 g (0.04 mol) of 2,2-bis (hydroxymethyl) propionic acid, 15.6 g (0) of the following diol compound (3) .06 mol) was dissolved in 100 ml of N, N-dimethylacetamide. To this, 21.4 g (0.102 mol) of naphthalene diisocyanate and 0.1 g of dibutyltin dilaurate were added, and the mixture was heated and stirred at 100 ° C. for 8 hours. Thereafter, the mixture was diluted with 100 ml of N, N-dimethylformamide and 200 ml of methyl alcohol and stirred for 30 minutes. The reaction solution was poured into 3 liters of water with stirring to precipitate a white polymer. The polymer was filtered off, washed with water, and dried under vacuum to obtain 34 g of polymer. The synthesized specific polyurethane resin is represented by (P-6) in the table below.
When the molecular weight was measured by gel permeation chromatography (GPC), the weight average molecular weight (polystyrene standard) was 96,000.

(Synthesis Example 4; specific polyurethane resin P-27)
Diol compound (4) (17.8 g), hexamethylene diisocyanate (16.8 g, manufactured by Wako Pure Chemical Industries, Ltd.), diphenylmethane diisocyanate (100.1 g, Wako Pure Chemicals) Co., Ltd.), polypropylene glycol having an average molecular weight of 1000 (200.0 g, manufactured by Wako Pure Chemical Industries, Ltd.), Blenmer GLM (40.0 g, manufactured by NOF Corporation), N, N-dimethylacetamide (400 g, Wako Pure) Yakutan Co., Ltd.) and Neostan U-600 (0.5 g, Nitto Kasei Co., Ltd.) were added and stirred at 100 ° C. for 8 hours. Thereafter, the mixture was allowed to cool to 40 ° C. and diluted with 1-methoxy-2-propanol (800 g). The reaction solution was poured into water (4 L) with stirring to precipitate a white polymer. The polymer was filtered off, washed with water, and then vacuum-dried to obtain a urethane polymer (P-27) (312 g).
The weight average molecular weight of this polymer obtained by measurement by gel permeation chromatography (GPC) was 60,000 in terms of polystyrene.
Furthermore, the structure (composition) in the polymer was identified by 1H-NMR and FT-IR spectra.

  Similarly to the synthesis examples 1 to 4, the polyurethane resins shown in Tables 1 to 9 exemplified as the specific polyurethane resin can also be synthesized.

Preparation of support body To remove rolling oil on the surface of an aluminum plate (material 1050) having a thickness of 0.3 mm, after performing a degreasing treatment at 50 ° C. for 30 seconds using a 10 mass% sodium aluminate aqueous solution, the bristle diameter The aluminum surface was grained using ^three 0.3 mm bundle-planted nylon brushes and a pumice-water suspension (specific gravity 1.1 g / cm ³ ) having a median diameter of 25 μm and washed well with water. This plate was etched by being immersed in a 25 mass% sodium hydroxide aqueous solution at 45 ° C for 9 seconds, washed with water, further immersed in 20 mass% nitric acid at 60 ° C for 20 seconds, and washed with water. At this time, the etching amount of the grained surface was about 3 g / m ² .

Next, an electrochemical roughening treatment was performed continuously using an alternating voltage of 60 Hz. The electrolytic solution at this time was a 1% by mass nitric acid aqueous solution (containing 0.5% by mass of aluminum ions) and a liquid temperature of 50 ° C. The AC power source waveform is electrochemical roughening treatment using a trapezoidal rectangular wave alternating current with a time ratio TP of 0.8 msec until the current value reaches a peak from zero, a duty ratio of 1: 1, and a trapezoidal rectangular wave alternating current. Went. Ferrite was used for the auxiliary anode. The current density was 30 A / dm ² at the peak current value, and 5% of the current flowing from the power source was shunted to the auxiliary anode. The amount of electricity in nitric acid electrolysis was 175 C / dm ² when the aluminum plate was the anode. Then, water washing by spraying was performed.

Next, a 0.5% by mass hydrochloric acid aqueous solution (containing 0.5% by mass of aluminum ions) and an electrolytic solution having a liquid temperature of 50 ° C. and nitric acid electrolysis under the condition of an electric quantity of 50 C / dm ² when the aluminum plate is an anode In the same manner as above, an electrochemical surface roughening treatment was performed, followed by washing with water by spraying. The plate was provided with a direct current anodized film of 2.5 g / m ² at a current density of 15 A / dm ² using 15% by mass sulfuric acid (containing 0.5% by mass of aluminum ions) as an electrolytic solution, then washed with water and dried.
The center line average roughness (Ra) of the support thus obtained was measured using a needle having a diameter of 2 μm and found to be 0.51 μm.

Furthermore, after applying the following undercoat liquid (1) to a bar, it was oven-dried at 80 ° C. for 10 seconds, applied to a dry coating amount of 10 mg / m ² , and a support 1 having an undercoat layer used in the following experiments. Was made.

<Undercoat liquid (1)>
・ Undercoat compound (1) 0.017 g
・ Methanol 9.00 g
・ Water 1.00g

[Example 1]
A photosensitive layer coating solution (1) having the following composition was bar coated on the support provided with the undercoat layer, followed by oven drying at 70 ° C. for 60 seconds, and a photosensitive layer having a dry coating amount of 1.1 g / m ² . A protective layer coating solution (1) having the following composition is applied on the substrate using a bar so that the dry coating amount is 0.75 g / m ^2, and then dried at 125 ° C. for 70 seconds. Thus, a lithographic printing plate precursor (1) was obtained.

<Photosensitive layer coating solution (1)>
-Binder polymer P-9 listed in Table 2 0.54 g
・ Polymerizable compound 0.40g
Isocyanuric acid EO-modified triacrylate (manufactured by Toa Gosei Co., Ltd., Aronix M-315)
・ Polymerizable compound Ethoxylated trimethylolpropane triacrylate 0.08 g
(Nippon Kayaku Co., Ltd., SR9035, EO addition mole number 15, molecular weight 1000)
・ The following sensitizing dye (1) 0.06 g
・ The following polymerization initiator (1) 0.18 g
・ The following co-sensitizer (1) 0.07 g
・ 0.40 g of ε-phthalocyanine pigment dispersion
(Pigment: 15 parts by mass, binder polymer (1) as a dispersant: 10 parts by mass,
Cyclohexanone / methoxypropyl acetate / 1-methoxy-2 as solvent
-Propanol = 15 parts by mass / 20 parts by mass / 40 parts by mass)
・ Thermal polymerization inhibitor 0.01g
N-nitrosophenylhydroxylamine aluminum salt ・ The following water-soluble fluorosurfactant (1) 0.001 g
・ Polyoxyethylene-polyoxypropylene condensate 0.04g
(Asahi Denka Kogyo Co., Ltd., Pluronic L44)
・ Tetraethylamine hydrochloride 0.01g
・ 3.5 g of 1-methoxy-2-propanol
・ Methyl ethyl ketone 8.0g

Protective layer coating solution (1)
Polyvinyl alcohol (saponification degree 98 mol%, polymerization degree 500) 40 g
Polyvinylpyrrolidone (molecular weight 50,000) 5g
Poly (vinyl pyrrolidone / vinyl acetate (1/1)) molecular weight 70,000 0.5g
Surfactant (Emalex 710, manufactured by Nippon Emulsion Co., Ltd.) 0.5g
950g of water

[Example 2]
The binder polymer P-9, the sensitizing dye (1), the polymerization initiator (1), and the co-sensitizer (1) in the photosensitive layer coating solution (1) are respectively P-11 shown in Table 3, and the following sensitization. A lithographic printing plate precursor (2) was obtained in the same manner as in Example 1 except that the dye (2), the polymerization initiator (2), and the cosensitizer (2) were changed.

Example 3
A lithographic printing plate precursor (3) was obtained in the same manner as in Example 1 except that the photosensitive layer coating solution (1) was changed to a photosensitive layer coating solution (2) having the following composition.

<Photosensitive layer coating solution (2)>
・ 0.2 g of the above polymerization initiator (1)
-0.1 g of the above sensitizing dye (1)
-3.0 g of binder polymer P-15 listed in Table 4
-Polymerizable compound 6.2g
Isocyanuric acid EO-modified diacrylate (Aronix M-215 manufactured by Toa Gosei Co., Ltd.)
・ Royco Crystal Violet 0.2g
・ 0.1 g of the above-mentioned fluorosurfactant (1)
・ The following microcapsule (1) dispersion 25.0 g
・ Methyl ethyl ketone 35.0g
・ 3-methoxy-2-propanol 35.0 g

(Synthesis of microcapsule (1))
As an oil phase component, trimethylolpropane and xylene diisocyanate adduct (Mitsui Takeda Chemical Co., Ltd., Takenate D-110N) 10 g, isocyanuric acid EO-modified diacrylate (Toa Gosei Co., Ltd. Aronix M-215) 4.15 g and 0.1 g of Pionein A-41C (manufactured by Takemoto Yushi Co., Ltd.) were dissolved in 17 g of ethyl acetate. As an aqueous phase component, 40 g of a 4% by mass aqueous solution of PVA-205 was prepared. The oil phase component and the aqueous phase component were mixed and emulsified for 10 minutes at 12000 rpm using a homogenizer. The obtained emulsion was added to 25 g of distilled water, stirred at room temperature for 30 minutes, and then stirred at 40 ° C. for 3 hours. The microcapsule liquid (1) thus obtained was diluted with distilled water so that the solid content concentration became 20% by mass. The average particle size was 0.25 μm.

Example 4
The binder polymer P-9 and the polymerizable compound Aronics M-315 in the photosensitive layer coating solution (1) were respectively converted into P-16 and polymerizable compound PLEX6661-O (produced by Rohm GmbH & KG, 7,7,9-trimethyl) listed in Table 4. The lithographic printing plate precursor (4) was prepared in the same manner as in Example 1 except that it was replaced with -4,13-dioxo-3,14-dioxa-5,12-diazahexadecane-1,16-diyldimethacrylate). Obtained.

[Examples 5 to 7]
Lithographic printing plate precursors (5) to (7) were obtained in the same manner as in Example 1 except that the binder polymer P-9 of the photosensitive layer coating solution (1) was changed as shown in Table 12.

Example 8
The binder polymer P-9 of the photosensitive layer coating solution (1) was changed as shown in Table 12, the protective layer coating solution (1) was changed to the protective layer coating solution (2) having the following composition, and the dry coating amount was A lithographic printing plate precursor (8) was obtained in the same manner as in Example 1 except that coating was performed using a bar so as to be 0.2 g / m ² .

Protective layer coating solution (2)
・ The following mica dispersion (1) 13.0 g
Polyvinyl alcohol (saponification degree 98 mol%, polymerization degree 500) 1.3 g
-Sodium 2-ethylhexyl sulfosuccinate 0.2g
・ Poly (vinyl pyrrolidone / vinyl acetate (1/1)) molecular weight 70,000 g
・ Surfactant (Emalex 710, manufactured by Nippon Emulsion Co., Ltd.) 0.05g
・ 133g of water

(Preparation of mica dispersion (1))
To 368 g of water, 32 g of synthetic mica (“Somasif ME-100”: manufactured by Co-op Chemical Co., Ltd., aspect ratio: 1000 or more) is added and dispersed using an homogenizer until the average particle size (laser scattering method) becomes 0.5 μm. A mica dispersion (1) was obtained.

[Comparative Examples 1 and 2]
The same as Example 1 except that the binder polymer P-9 of the photosensitive layer coating solution (1) was changed to the comparative binder polymers CP-1 (Comparative Example 1) and CP-2 (Comparative Example 2) shown in Table 12. Thus, lithographic printing plate precursors (C1) and (C2) for comparison were obtained.

[Evaluation of planographic printing plate precursor]
(1) Exposure For each of the lithographic printing plate precursors (1) to (8) and the comparative lithographic printing plate precursors (1) and (2), Fuji Photo Film has an exposure amount of 90 μJ / cm ² and a resolution of 2438 dpi. An image including halftone dots and solids was drawn with an FM screen manufactured by TAFFETA 20.
The exposure apparatus includes a violet semiconductor laser setter Vx9600 (InGaN-based semiconductor laser 405) manufactured by FUJIFILM Electronic Imaging Ltd.
nm ± 10 nm emission / output 30 mW).

(2) Development The exposed lithographic printing plate precursor was subjected to development processing with an automatic developing processor having a structure shown in FIG. The pH of the developer was 4.5. The automatic processor is an automatic processor having two rotating brush rolls. As the rotating brush roll, the first brush roll and the polybutylene terephthalate fiber (hair diameter 200 μm, hair length 17 mm). Using a brush roll with an outer diameter of 90 mm implanted with 200 mm / min in the same direction as the conveying direction (peripheral speed 0.94 m / sec at the tip of the brush), the second brush roll is made of polybutylene terephthalate Using a brush roll having an outer diameter of 60 mm in which fibers (hair diameter: 200 μm, hair length: 17 mm) were planted, it was rotated 200 times per minute in the direction opposite to the conveying direction (peripheral speed of the brush tip: 0.63 m / sec). . The planographic printing plate precursor was transported at a transport speed of 100 cm / min.
The developer was showered from the spray pipe with a circulation pump and supplied to the plate surface. The tank capacity of the developer was 10 liters.

Developer 1
・ Water 100g
・ Sodium alkylnaphthalenesulfonate 5g
(Perox NB-L manufactured by Kao Corporation)
・ 1g gum arabic
・ Primary ammonium phosphate 0.05g
・ Citric acid 0.05g
・ Ethylenediaminetetraacetate tetrasodium salt 0.05g

(3) Evaluation of printing durability and stain resistance Each obtained lithographic printing plate was printed using a printing press Lislon manufactured by Komori Corporation. At this time, the number of sheets that can be printed while maintaining a sufficient ink density was measured visually to evaluate the printing durability and the stain resistance of the non-image area. The results are shown in Table 12.

(4) Evaluation of raw storability An unexposed lithographic printing plate precursor was allowed to stand for 3 days at 60 ° C./humidity of 50% (aged), then exposed and developed to obtain a lithographic printing plate. Using this planographic printing plate, printing was performed in the same manner as described above, and printing durability and stain resistance were evaluated. This evaluation of soiling properties is shown in Table 12 as an evaluation of raw storage stability. The printing durability did not change substantially before and after aging.

Example 9
A lithographic printing plate precursor (9) was obtained in the same manner as in Example 1 except that the binder polymer P-9 in the photosensitive layer coating solution (1) was changed to P-26. Using this lithographic printing plate precursor, image exposure, development treatment and evaluation were carried out in the same manner as in the evaluation of the lithographic printing plate precursor (1). The results are shown in Table 12.

[Examples 10 to 15, Comparative Example 3]
The lithographic printing plate precursors (10) to (15) and the lithographic printing for comparison were the same as in Example 1 except that the binder polymer P-9 of the photosensitive layer coating solution (1) was changed as shown in Table 12. An original plate (C3) was obtained. Image exposure and development were carried out in the same manner as in the evaluation of the lithographic printing plate precursor (1) except that these lithographic printing plate precursors were changed to Developer 1 or Developers 2 to 4 shown in Table 12 below. Processing and evaluation were performed. The results are shown in Table 12.

Developer 2
Solution obtained by removing only gum arabic from Developer 1 (pH = 4.5)
Developer 3
Liquid obtained by mixing potassium hydroxide (0.0177 g), water (1000 g) and gum arabic (10 g) (pH = 10.5)
Developer 4
Liquid obtained by mixing potassium hydroxide (0.0177 g) and water (1000 g) (pH = 10.5)

  From Table 12, the comparative example, which is a conventional lithographic printing plate precursor under mild development processing conditions, cannot achieve both printing durability and raw storage, whereas the lithographic printing plate precursor of the present invention is good It is clear that it has excellent raw shelf life while maintaining excellent printing durability.

It is explanatory drawing which shows the structure of an automatic developing processor.

Explanation of symbols

61 Rotating brush roll 62 Receiving roll 63 Conveying roll 64 Conveying guide plate 65 Spray pipe 66 Pipe line 67 Filter 68 Feeding plate 69 Discharging plate 70 Developer tank 71 Circulating pump 72 Plate

Claims (12)

The lithographic printing plate precursor having at least a photosensitive layer on the support is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then the pH is adjusted by an automatic processor equipped with a rubbing member. In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of 2 to 10 developer, the photosensitive layer is (A) a light of 360 nm to 450 nm. It is formed by a photosensitive composition containing a sensitizing dye to be absorbed, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer, and (D) has an ethylenically unsaturated bond. Polyurethane resin having units and units having hydrophilic groups (excluding carboxyl groups) (however, the following diisocyanate compounds (i) -1 and (i) -4) and A lithographic printing plate precursor characterized by being a diol compound (ii) -1, (iii) -5 and (iv) -5, excluding a polyurethane resin synthesized) .
  A lithographic printing plate precursor having at least a photosensitive layer on a support is exposed using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, and then water-soluble by an automatic processor equipped with a rubbing member. In the planographic printing plate precursor in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface with a rubbing member in the presence of an aqueous solution containing a polymer, the photosensitive layer (A) absorbs light of 360 nm to 450 nm. Sensitizing dye, (B) a polymerization initiator, (C) a polymerizable compound and (D) a photosensitive composition containing a binder polymer, wherein (D) has an ethylenically unsaturated bond A lithographic printing plate precursor characterized by being a polyurethane resin having a hydrophilic group (excluding a carboxyl group) and a unit having a hydrophilic group. 3. The unit according to claim 1, wherein the unit having an ethylenically unsaturated bond is a unit having at least one of functional groups represented by the following general formulas (1) to (3). A lithographic printing plate precursor.
In general formula (1), R ^{1 to} R ³ each independently represents a hydrogen atom or a monovalent organic group, X represents an oxygen atom, a sulfur atom or —N (R ¹² ) —, and R ¹² represents hydrogen. Represents an atom or a monovalent organic group.
In the general formula (2), R ^{4 to} R ⁸ each independently represents a hydrogen atom or a monovalent organic group, Y represents an oxygen atom, a sulfur atom or —N (R ¹² ) —, and R ¹² represents a general formula. It is synonymous with R < ¹² > of Formula (1).
In the general formula (3), R ⁹ represents a hydrogen atom or an alkyl group which may have a substituent, and R ¹⁰ and R ¹¹ are each independently a hydrogen atom, a halogen atom, an amino group, or a dialkylamino group. A carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an alkyl group which may have a substituent, an aryl group which may have a substituent, an alkoxy group which may have a substituent, Aryloxy group which may have a substituent, alkylamino group which may have a substituent, arylamino group which may have a substituent, alkylsulfonyl group which may have a substituent, substituent Z represents an oxygen atom, a sulfur atom, —N (R ¹³ ) — or a phenylene group which may have a substituent, and R ¹³ has a substituent. Represents a good alkyl group. The lithographic printing plate precursor as claimed in any one of claims 1 to 3, wherein the binder polymer is a polyurethane resin having a (meth) acryloyl group. The binder polymer is a reaction product of a diisocyanate compound and a diol compound, and at least one of the diol compounds is a compound represented by the following general formula (G). The lithographic printing plate precursor as described in item 1.
In general formula (G), R ^{1 to} R ³ each independently represent a hydrogen atom or a monovalent organic group, A represents a divalent organic residue, X represents an oxygen atom, a sulfur atom or N (R ¹² )-And R ¹² represents a hydrogen atom or a monovalent organic group. Claims unit having a hydrophilic group, scan sulfone group, a sulfonic acid salt, characterized by a unit and / or polyether diol unit having at least one group selected from phosphate and phosphoric acid bases The lithographic printing plate precursor as described in any one of 1 to 5.   The lithographic printing plate precursor as claimed in any one of claims 1 to 6, wherein the lithographic printing plate precursor has a protective layer on a photosensitive layer.   The lithographic printing plate precursor as claimed in any one of claims 1 to 7, wherein a part or all of the photosensitive layer component is encapsulated in a microcapsule.   The lithographic printing plate precursor as claimed in any one of claims 1 to 8, wherein the rubbing member is at least two rotating brush rolls.   The lithographic printing plate precursor as claimed in any one of claims 1 to 9, wherein an image is recorded on an FM screen during the exposure. The support has at least a photosensitive layer, and the photosensitive layer is (A) a sensitizing dye that absorbs light of 360 nm to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer. A polyurethane resin having a unit having a hydrophilic group (excluding a carboxyl group) and a unit having an ethylenically unsaturated bond (provided below) A lithographic printing plate precursor which is a diisocyanate compound (i) -1 and (i) -4 and a polyurethane resin synthesized from the following diol compounds (ii) -1, (iii) -5 and (iv) -5) After exposure using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, the pH is 2 to 10 by an automatic processor equipped with a rubbing member. The presence of liquid, rubbing by rubbing the plate surface with a member, the planographic printing plate creation method of removing the photosensitive layer in the unexposed portion.
  The support has at least a photosensitive layer, and the photosensitive layer is (A) a sensitizing dye that absorbs light of 360 nm to 450 nm, (B) a polymerization initiator, (C) a polymerizable compound, and (D) a binder polymer. A lithographic printing which is a polyurethane resin having a unit having a hydrophilic group (excluding a carboxyl group) and a unit having an ethylenically unsaturated bond After exposing the plate precursor using an exposure apparatus equipped with a light source having an oscillation wavelength in the range of 360 nm to 450 nm, the rubbing member is subjected to an automatic processing machine equipped with a rubbing member in the presence of an aqueous solution containing a water-soluble polymer. A method for preparing a lithographic printing plate in which the photosensitive layer in the non-exposed area is removed by rubbing the plate surface.