FR2916371B1 - PROCESS FOR PREPARING FORGED PARTS HAVING EXCELLENT TRACTION RESISTANCE AND ELONGATION FROM STEEL MAMINERY WIRES - Google Patents

PROCESS FOR PREPARING FORGED PARTS HAVING EXCELLENT TRACTION RESISTANCE AND ELONGATION FROM STEEL MAMINERY WIRES

Info

Publication number
FR2916371B1
FR2916371B1 FR0755247A FR0755247A FR2916371B1 FR 2916371 B1 FR2916371 B1 FR 2916371B1 FR 0755247 A FR0755247 A FR 0755247A FR 0755247 A FR0755247 A FR 0755247A FR 2916371 B1 FR2916371 B1 FR 2916371B1
Authority
FR
France
Prior art keywords
maminery
elongation
wires
steel
forged parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
FR0755247A
Other languages
French (fr)
Other versions
FR2916371A1 (en
Inventor
Yun Te Chang
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FWU Kuang Enterprises Co Ltd
Original Assignee
FWU Kuang Enterprises Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FWU Kuang Enterprises Co Ltd filed Critical FWU Kuang Enterprises Co Ltd
Priority to FR0755247A priority Critical patent/FR2916371B1/en
Publication of FR2916371A1 publication Critical patent/FR2916371A1/en
Application granted granted Critical
Publication of FR2916371B1 publication Critical patent/FR2916371B1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/0093—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for screws; for bolts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21K—MAKING FORGED OR PRESSED METAL PRODUCTS, e.g. HORSE-SHOES, RIVETS, BOLTS OR WHEELS
    • B21K1/00—Making machine elements
    • B21K1/44—Making machine elements bolts, studs, or the like
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
    • C21D1/20—Isothermal quenching, e.g. bainitic hardening
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/25—Hardening, combined with annealing between 300 degrees Celsius and 600 degrees Celsius, i.e. heat refining ("Vergüten")
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C21D1/30—Stress-relieving
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
    • C21D9/525—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length for wire, for rods
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Child & Adolescent Psychology (AREA)
  • Heat Treatment Of Steel (AREA)
FR0755247A 2007-05-24 2007-05-24 PROCESS FOR PREPARING FORGED PARTS HAVING EXCELLENT TRACTION RESISTANCE AND ELONGATION FROM STEEL MAMINERY WIRES Active FR2916371B1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
FR0755247A FR2916371B1 (en) 2007-05-24 2007-05-24 PROCESS FOR PREPARING FORGED PARTS HAVING EXCELLENT TRACTION RESISTANCE AND ELONGATION FROM STEEL MAMINERY WIRES

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
FR0755247A FR2916371B1 (en) 2007-05-24 2007-05-24 PROCESS FOR PREPARING FORGED PARTS HAVING EXCELLENT TRACTION RESISTANCE AND ELONGATION FROM STEEL MAMINERY WIRES

Publications (2)

Publication Number Publication Date
FR2916371A1 FR2916371A1 (en) 2008-11-28
FR2916371B1 true FR2916371B1 (en) 2010-02-26

Family

ID=38926344

Family Applications (1)

Application Number Title Priority Date Filing Date
FR0755247A Active FR2916371B1 (en) 2007-05-24 2007-05-24 PROCESS FOR PREPARING FORGED PARTS HAVING EXCELLENT TRACTION RESISTANCE AND ELONGATION FROM STEEL MAMINERY WIRES

Country Status (1)

Country Link
FR (1) FR2916371B1 (en)

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5021153B1 (en) * 1970-12-28 1975-07-21
DE2817628C2 (en) * 1978-04-21 1985-08-14 Hilti Ag, Schaan Tough, high-strength steel alloys and processes for making such workpieces
DE3918700A1 (en) * 1989-06-08 1990-12-13 Diehl Gmbh & Co PROCESS FOR INCREASING THE STRENGTH OF PAYMENT STEEL AND USE OF SUCH A PAYMENT STEEL THUS BEING TREATED
JP3160329B2 (en) * 1991-10-18 2001-04-25 川崎製鉄株式会社 Manufacturing method of heat resistant high strength bolt
FR2744733B1 (en) * 1996-02-08 1998-04-24 Ascometal Sa STEEL FOR MANUFACTURING FORGED PART AND METHOD FOR MANUFACTURING FORGED PART
RU2256705C1 (en) * 2004-01-26 2005-07-20 Открытое акционерное общество "ТРУБОДЕТАЛЬ" Method of thermal treatment of items

Also Published As

Publication number Publication date
FR2916371A1 (en) 2008-11-28

Similar Documents

Publication Publication Date Title
FR2948712B1 (en) METHOD FOR STRENGTHENING A CONSTRUCTION STRUCTURE AND STRENGTHENING THE STRENGTH
ZA201000290B (en) Process for manufacturing steel sheet having high tensile strength and ductility characteristics, and sheet thus produced
EP2634281A4 (en) High-strength hot-dip galvanized steel sheet having excellent uniform elongation and plating properties, and method for manufacturing same
ZA200905998B (en) Steel for tool-less hot forming or quenching with improved ductility
EP2233597A4 (en) High-strength hot-dip-galvanized steel sheet having excellent moldability, and method for production thereof
EP2799567A4 (en) High strength steel pipe having excellent ductility and low temperature toughness, high strength steel sheet, and method for producing steel sheet
SI2414581T1 (en) High elongation steel cord with preformed strands
EP2484791A4 (en) Steel plate having low yield ratio, high strength and high uniform elongation and method for producing same
EP2423344A4 (en) High strength, high toughness steel wire rod, and method for manufacturing same
ZA200901450B (en) Steel plate with yield strength of 800 MPa grade and low weld cracking sensitivity, and manufacture method thereof
EP2371979A4 (en) High-strength cold-rolled steel sheet having excellent workability, molten galvanized high-strength steel sheet, and method for producing the same
BRPI0903902A2 (en) Steel rod and high strength steel wire having superior ductility and production method thereof.
EP2258882A4 (en) High-strength and high-electroconductivity copper alloy pipe, bar, and wire rod
EP2377965A4 (en) Aluminum-plated steel sheet having superior corrosion resistance, hot press formed product using the same, and method for production thereof
EP2554699A4 (en) Steel sheet with high tensile strength and superior ductility and method for producing same
EP2554706A4 (en) Hot-rolled steel sheet with high tensile strength and superior processability and method for producing same
IL201000A0 (en) Process for producing polyamide
EP2238271A4 (en) Wire rods having superior strength and ductility for drawing and method for manufacturing the same
BRPI0918857A2 (en) polyamide production method
EP2322680A4 (en) Environmentally-friendly, pb-free free-machining steel, and manufacturing method for same
PL2447383T3 (en) Pearlite based high-carbon steel rail having excellent ductility and process for production thereof
BRPI1008134A2 (en) "Reinforcement cage making machine, reinforcement cage welding machine and related production method"
EP2169057A4 (en) Double-stranded rna originating in lactic acid bacterium
EP2503014A4 (en) High strength hot-rolled steel plate exhibiting excellent acid pickling property, chemical conversion processability, fatigue property, stretch flangeability, and resistance to surface deterioration during molding, and having isotropic strength and ductility, and method for producing said high strength hot-rolled steel plate
IL210783A0 (en) High strength, high toughness steel alloy

Legal Events

Date Code Title Description
PLFP Fee payment

Year of fee payment: 10

PLFP Fee payment

Year of fee payment: 11