CN1657245A - Bamboo reinforced plywood - Google Patents
Bamboo reinforced plywood Download PDFInfo
- Publication number
- CN1657245A CN1657245A CN 200510038523 CN200510038523A CN1657245A CN 1657245 A CN1657245 A CN 1657245A CN 200510038523 CN200510038523 CN 200510038523 CN 200510038523 A CN200510038523 A CN 200510038523A CN 1657245 A CN1657245 A CN 1657245A
- Authority
- CN
- China
- Prior art keywords
- surf green
- bamboo
- bamboo strip
- veneer
- wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A bamboo reinforced ply-wood is made up of bamboo and wood through making bamboo strips, and preparing single wood plys, applying isocyanate adhesive to bamboo strips and phenolic resin to single wood plys, overlaying them in fibre direction to form a unit, combining more unit together, and hot pressing.
Description
One, technical field
The invention belongs to the glued board manufacturing technology field in the timber industry.
Two, background technology
Along with continuing of building of China and world fast-growing, high-yield woods carried out, quick growth poplar wood (as eastern cottonwood etc.) becomes a kind of relative rich in natural resources gradually and is adopted in a large number by the glued board manufacturing industry.Because the wood property characteristics of quick growth poplar wood, with the glued board of quick growth poplar wood manufacturing, its physical and mechanical property is relatively low purely.
Bamboo is the peculiar resource in China and Southeast Asia, and not only accumulation is big, physical and mechanical property is apparently higher than timber, and has fast, the normal operation of growth and advantage such as can upgrade naturally.Through research for many years, the application and development of China backroom boys and relevant enterprise, bamboo wood also is used in the wood-based plate manufacturing industry in a large number.
The poplar of having developed at present and the composite product of artificial bamboo board mainly contain:
03152841.4 1 kinds of container bottom boards of CN and manufacture method thereof
03112794.0 1 kinds of bamboo woods of CN strengthen laminated veneer lumber and manufacture method thereof
CN 92107278.3 bamboo weaving lagers stacked material making methods
CN 87100368.6 bamboo plywood manufacture methods
CN 91108203.4 improved technology for making ply-bamboo
CN 02258059.X poplar base composite plate
CN 98227629.X improved laminated bamboo-wood composite lumber or the like.
Because the surf green thin bamboo strip of bamboo and the chemical composition of the tabasheer thin bamboo strip have very big difference, therefore, the glue performance of the surf green thin bamboo strip and the tabasheer thin bamboo strip differs greatly, and general adhesive is generally very low for the bonding strength of the surf green thin bamboo strip.In the wood-based plate manufacturing industry as adhesive, the bonding strength of the surf green thin bamboo strip often can't satisfy basic performance requirement for main use Lauxite or phenolic resins.Therefore, bamboo wood in order to guarantee the bonding strength of finished product, generally all will be removed the surf green thin bamboo strip in the raw material preparatory stage in Wood-based Panel Production.This has just influenced the processing and utilization rate of bamboo wood greatly.
On the other hand, though the too late tabasheer thin bamboo strip of the glue performance of the surf green thin bamboo strip, its physical and mechanical property is much higher than the tabasheer thin bamboo strip again.Through experimental determination, its elastic modelling quantity (MOE) can reach 15000～20000MPa, and MOR (MOR) can reach 180～200MPa, is about the twice of tabasheer.If can adopt high performance isocyanates, and overcome the high problem of cost as adhesive, the surf green thin bamboo strip utilize prospect very desirable.
Isocyanate adhesive is as toluene di-isocyanate(TDI) (being called for short TDI); 4,4 '-methyl diphenylene diisocyanate (being called for short MDI); 1,6-hexamethylene diisocyanate (be called for short HDI) and triphenylmethane triisocyanate etc., directly use synthesis of polyurethane raw material---polyisocyanates uses as adhesive.Because characteristics such as its molecular weight is little, easy infiltration are suitable for gluing together the processing of farm products residue, especially as materials such as bark, bagasse, cocoanut fiber, straw, peanut shell, rice husks.Experiment showed, isocyanate adhesive is used to glue together the surf green thin bamboo strip that its glue performance is also very desirable.
But isocyanate adhesive is big except toxicity, the operation requirement of shelter higher, its price also wants high more than adhesive such as phenolic resins, Lauxites.Adopt common laminated structure and manufacture method, because consumption glue amount is bigger, the manufacturing cost of glued board is high, has become to hinder the biggest problem that it is promoted the use of.
Three, summary of the invention
The objective of the invention is to explore a kind of high-intensity wood, bamboo composite plywood manufacturing technology of effectively utilizing surf green thin bamboo strip resource, and seek to reduce the approach of manufacturing cost.
Technical solution of the present invention is: surf green is processed into bamboo strip, timber is processed into behind the veneer dryly, it is characterized in that:
A. the surf green bamboo strip adopts the isocyanate adhesive applying glue, and veneer adopts the synvaren applying glue;
B. the machine direction of veneer and surf green bamboo strip is arranged in the same way, and every two-layer veneer and one deck surf green bamboo strip constitute an assembly unit;
C. each assembly unit is strengthened glued board according to making surf green after the symmetry principle assembly of glued board manufacturing, the hot pressing again.
For making things convenient for assembly, also can adopt and execute isocyanate adhesive after the surf green bamboo strip is woven into bamboo curtain with cotton thread, and copy said structure to carry out assembly.
Adopt manufacturing process provided by the invention and assembly structure, can effectively utilize the surf green resource of a large amount of preciousnesses that extensive artificial bamboo board processing enterprise discarded, improve the utilization rate of bamboo wood greatly.Because just use isocyanate adhesive at surf green, the consumption of isocyanate adhesive is little, the increase of production cost is not remarkable, and the physical and mechanical property of finished product can reach very high index.
Four, description of drawings
Fig. 1 strengthens the assembly cellular construction schematic diagram of glued board for surf green.(1) is veneer among the figure, and (2) are the surf green bamboo strip; The machine direction of veneer and surf green bamboo strip must be arranged in the same way.
Fig. 2 has used 3 assembly unit altogether for the finished product structural representation of surf green enhancing glued board among the figure.
Five, the specific embodiment
Embodiment 1:
A. be raw material with mao bamboon, the surf green of mao bamboon is made the surf green bamboo strip that thickness is 0.8～1.5mm, dry back is flooded with the toluene di-isocyanate(TDI) adhesive; Quick growth poplar wood is peeled into the veneer of 0.7～1.5mm, drying; Board using poplar board all adopts common synvaren when the needs applying glue.
B. adopt the assembly structure shown in the accompanying drawing 1, between the two-layer board using poplar board of arranging in the same way, the coverage rate with 30～50% is put into the surf green bamboo strip that imposes the toluene di-isocyanate(TDI) adhesive in the same way, and it is standby to constitute an assembly unit;
C. as shown in Figure 2, using 3 assembly unit once more behind the assembly, is that 135～145 ℃, pressure are hot pressing under 2.5～3.0MPa condition in temperature, can make surf green and strengthen glued board.
Embodiment 2:
For making things convenient for assembly, the surf green bamboo strip can be woven into bamboo curtain with cotton thread, impose toluene di-isocyanate(TDI) or other isocyanate adhesives after the drying.
All the other are with embodiment 1.
Adopt method and structure provided by the invention, the Main physical mechanical property that the surf green of making strengthens glued board is as follows:
Density---0.6～1.1g/cm
3
Elastic feel quantity---5500～12000MPa
MOR---50～100MPa
Impact flexibility---60～100J/m
2
Realize effectively utilizing surf green thin bamboo strip resource, reduced the goal of the invention of manufacturing cost.
Claims (2)
1. a surf green strengthens glued board, surf green is processed into bamboo strip, timber is processed into behind the veneer dryly, it is characterized in that:
A. the surf green bamboo strip adopts the isocyanate adhesive applying glue, and veneer adopts the synvaren applying glue;
B. the machine direction of veneer and surf green bamboo strip is arranged in the same way, and every two-layer veneer and one deck surf green bamboo strip constitute an assembly unit;
C. with each assembly unit assembly once more, after hot pressing, make surf green and strengthen glued board.
2. surf green as claimed in claim 1 strengthens glued board, carries out assembly after it is characterized in that the surf green bamboo strip is woven into bamboo curtain with cotton thread.