CN103788861A - Novel matte UV (Ultraviolet) coating - Google Patents
Novel matte UV (Ultraviolet) coating Download PDFInfo
- Publication number
- CN103788861A CN103788861A CN201410021479.7A CN201410021479A CN103788861A CN 103788861 A CN103788861 A CN 103788861A CN 201410021479 A CN201410021479 A CN 201410021479A CN 103788861 A CN103788861 A CN 103788861A
- Authority
- CN
- China
- Prior art keywords
- coating
- weight
- acrylate
- lower melting
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a UV (Ultraviolet) matte coating without other inorganic fillers such as silicon dioxide, wax powder, titanium dioxide and the like. A preparation method of the UV coating comprises the steps of taking acrylic ester with a melting point at a temperature of higher than 30 DEG C to mix with one or some of common epoxy acrylate, urethane acrylate and polyester acrylate, and preparing the UV coating with matte effect on the surface by using the characteristic that the acrylic ester has a crystal at normal temperature and low melting point and forming uneven structures on the surface of the crystal. The method is easy to operate and construct, easy to control, simple in control and low in cost.
Description
Technical field
The present invention relates to a kind of dumb light UV coating that does not contain the fillers such as dumb light powder.
Background technology
Most dumb light UV coating is all in UV regular convention formula, to add other mineral fillers such as silicon-dioxide, wax powder, titanium dioxide with dumb light effect, so no doubt can all reduce glossiness and reach required dumb light effect.But, in actual application, find the viscosity that adds membership and greatly increase formula of other mineral fillers such as silicon-dioxide, wax powder, titanium dioxide, make in construction process very inconvenient, also reduce in addition the avidity between film layer and bottom, in storage process, easily precipitate, greatly reduce the uniformity coefficient of coating, thereby hindered its result of use.Certainly will need so a kind of novel method that does not contain the fillers such as silicon-dioxide to reach same dumb light effect.Patent CN103031050A the inside has been introduced and has been prepared dumb light feel oil with dumb light resin and dumb light hand feeling agent etc., but the inside also has the wax of 2-8 part to starch.The low luster coatings such as patent CN1436824, CN1778852, CN101210144, CN101643624 all contain other mineral fillers such as silicon-dioxide, wax powder, titanium dioxide.
What the present invention relates to does not also report in document and patent containing the dumb light UV coating of the fillers such as dumb light powder.
Summary of the invention
For the viscosity that adds membership and greatly increase formula of other mineral fillers such as silicon-dioxide, wax powder, titanium dioxide, bring very large inconvenience to construction process.The present invention selects fusing point higher than the acrylate of 30 degrees Celsius, arrange in pairs or groups with one or more of conventional epoxy acrylate, urethane acrylate, polyester acrylate, utilize the characteristic at normal temperature lower melting propylene acid esters with crystallization, by form the surface whole structure that is uneven at surface crystallization, carrying out preparation table mask has the UV coating of dumb light effect.The method operating process construction easily, be easy to control, step is simple, with low cost.
Coating provided by the invention contains matrix resin, thinner, lower melting propylene acid esters and light trigger, contains or do not contain auxiliary agent.
Embodiment
According to coating provided by the invention, the content of described lower melting propylene acid esters, matrix resin, thinner, light trigger and auxiliary agent is the conventional content of these components in UV coating.Take the total amount of coating as benchmark, the content of lower melting propylene acid esters is 5-50 % by weight, is preferably 10-30 % by weight, matrix resin content is 30-70 % by weight, preferably 40-60 % by weight, thinner 5-50 % by weight, preferably 10-25 % by weight, auxiliary agent content is 0-10 % by weight, preferably 0-5%.
Described matrix resin is a kind of or several in epoxy acrylate, urethane acrylate and the polyester acrylate in the matrix resin that existing UV coating is conventional.Wherein preferred epoxy acrylate, polyester acrylate or both mixtures.
Described thinner is the acrylate monomer that UV coating is conventional, for conventionally known to one of skill in the art.For example, single functionality acrylate can be selected the one in Hydroxyethyl acrylate (HEA), hydroxyethyl methylacrylate (HEMA), isobornyl methacrylate, isobornyl acrylate, glycidyl methacrylate, vinylformic acid caprolactone, decyl acrylate, 2-phenoxyethyl acrylate.Difunctionality acrylate can select 1,6-hexanediyl ester, polyoxyethylene glycol (400) dimethacrylate, HDDMA, 2 (2-ethoxy ethoxy) ethyl propylene acid esters, polyoxyethylene glycol (200) diacrylate, propylene glycol diacrylate, Triethylene glycol dimethacrylate, tetraethylene-glycol dimethacrylate.Three-functionality-degree acrylate can select the third oxidation Viscoat 295,3-third to be oxidized glycerol triacrylate, Viscoat 295, pentaerythritol triacrylate or 3-ethoxyquin Viscoat 295.High functionality can be selected Dipentaerythritol five/six acrylate.
Described light trigger kind and consumption are conventionally known to one of skill in the art, for example BP, 651,907, ITX, 1173,184,2959,369, TPO, 819, CQ, 784.Domestic corporation is as Beijing English power, Hua Tai etc., and abroad, as Switzerland's vapour bar, its trade mark is conventionally known to one of skill in the art.
Described lower melting propylene acid esters is octadecyl acrylate, vinylformic acid 18 methyl esters, Process Conditions of Cetane Acrylate, vinylformic acid ten pregnancy esters.
Described auxiliary agent is flow agent, defoamer, the dispersion agent that UV coating is conventional.Wherein flow agent is BYK333, BYK366, the BYK307 of BYK known in those skilled in the art company, DEGO410, DEGO432, the DEGO435 of German Di Gao company.Defoamer is BYK357, BYK354, the BYK352 of BYK known in those skilled in the art company.Dispersion agent is the Kerper-602 of Kerper company of the U.S. known in those skilled in the art, Kerper-605, Kerper-630.
The preparation method of UV coating provided by the invention be by matrix resin, thinner, lower melting propylene acid esters and light trigger 40 degrees Celsius of heating for dissolving, add or adding assistant not, mix.Wherein, take the total amount of coating as benchmark, the content of lower melting propylene acid esters is 5-50 % by weight, is preferably 10-30 % by weight, matrix resin content is 30-70 % by weight, preferably 40-60 % by weight, thinner 5-50 % by weight, preferably 10-25 % by weight, auxiliary agent content is 0-10 % by weight, preferably 0-5%.
UV low luster coating provided by the invention is suitable as the finish paint of PVC hectograph, paper.Coating thickness is 15-25 micron, and coating fast, through UV-irradiation 15-30 second, can obtain the rete that glossiness is 10-60.
Examples of implementation further illustrate
Give an example 1
Epoxy acrylate 40g, Viscoat 295 40g, octadecyl acrylate 10g, BYK352 is 5g, and Kerper605 is 4g, and initiator 184 is 1g, 20 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 20 seconds, it is 60 that glossometer records glossiness under 60 ° of angles.
Give an example 2
Polyester acrylate 60g, 1,6 hexanediol diacrylate 10g, Process Conditions of Cetane Acrylate 25g, BYK357 is 2g, and Kerper602 is 2g, and initiator TPO is 1g, 25 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 25 seconds, it is 45 that glossometer records glossiness under 60 ° of angles.
Give an example 3
Urethane acrylate 30g, Triethylene glycol dimethacrylate 40g, vinylformic acid 18 methyl esters 30g, initiator B P is 1g, 15 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 30 seconds, it is 30 that glossometer records glossiness under 60 ° of angles.
Give an example 4
Epoxy acrylate 20g, polyester acrylate 30g, Hydroxyethyl acrylate 40g, vinylformic acid ten pregnancy ester 5g, BYK354 is 2g, and Kerper630 is 2g, and initiator 1173 is 1g, 20 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 20 seconds, it is 25 that glossometer records glossiness under 60 ° of angles.
Give an example 5
Urethane acrylate 20g, polyester acrylate 50g, polyoxyethylene glycol (200) diacrylate 24g, octadecyl acrylate 5g, initiator 651 is 1g, 20 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 25 seconds, it is 15 that glossometer records glossiness under 60 ° of angles.
Give an example 6
Epoxy acrylate 70g, polyoxyethylene glycol (200) diacrylate 24g, octadecyl acrylate 5g, initiator 907 is 1g, 20 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 25 seconds, it is 15 that glossometer records glossiness under 60 ° of angles.
Give an example 7
Epoxy acrylate 19g, urethane acrylate 20g, Dipentaerythritol five/six acrylate 5g, vinylformic acid 18 methyl esters 50g, initiator 2959 is 1g, 15 microns of films after 40 degrees Celsius of dissolvings, ultra violet lamp 25 seconds, it is 10 that glossometer records glossiness under 60 ° of angles.
Claims (3)
1. coating provided by the invention, this coating comprises lower melting propylene acid esters, matrix resin, thinner, light trigger and auxiliary agent, it is characterized in that this coating contains lower melting propylene acid esters, take coating total amount as benchmark, content is 5-50 % by weight, is preferably 10-30 % by weight.
2. coating according to claim 1, it is characterized in that total amount take coating is as benchmark, the content of lower melting propylene acid esters is 5-50 % by weight, be preferably 10-30 % by weight, matrix resin content is 30-70 % by weight, preferably 40-60 % by weight, thinner 5-50 % by weight, preferably 10-25 % by weight, auxiliary agent content is 0-10 % by weight, preferably 0-5%.
3. coating according to claim 1, its lower melting propylene acid esters is fusing point higher than octadecyl acrylate, vinylformic acid 18 methyl esters, Process Conditions of Cetane Acrylate, the vinylformic acid ten pregnancy esters of 30 degrees Celsius.