CN100577345C - 一种焊接铝及铝合金的钎剂 - Google Patents
一种焊接铝及铝合金的钎剂 Download PDFInfo
- Publication number
- CN100577345C CN100577345C CN200710029683A CN200710029683A CN100577345C CN 100577345 C CN100577345 C CN 100577345C CN 200710029683 A CN200710029683 A CN 200710029683A CN 200710029683 A CN200710029683 A CN 200710029683A CN 100577345 C CN100577345 C CN 100577345C
- Authority
- CN
- China
- Prior art keywords
- aluminium
- aluminum
- brazing flux
- aluminium alloy
- aluminum alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种焊接铝及铝合金的钎剂,涉及一种钎焊材料。本发明所述的铝合金-铝合金、铝-铝合金钎焊用钎剂,以质量百分比计,含有共晶AlF3-CsF系钎剂97.0~99.9、氟化锌0.1~3.0、氟化锡0~0.5。是一种抗拉强度高的铝合金-铝合金、铝-铝合金钎焊用钎剂。
Description
技术领域
本发明涉及一种钎焊材料,特别涉及一种铝合金-铝合金、铝-铝合金钎焊用的钎焊材料。
背景技术
铝及铝合金与其它金属相比钎焊比较困难,主要是铝表面容易生成一层致密且化学稳定的Al2O3膜,难以去除。国内外对铝合金钎焊的钎剂有很多研究成果。北京大学张启运教授在[《Thermochimica Acta》,303(1997)]发表论文:“A study on the phase diagram of AlF3-CsF system”,公开了AlF3-CsF系相图,指出共晶组成为AlF3∶CsF=42.0∶58.0(摩尔比),熔化温度是471℃。该类钎剂具有较高的钎焊性能,对含镁量高的铝合金具有特殊的活性,对火焰的稳定性高。可用于火焰钎焊、保护气氛炉中钎焊、高频感应压力钎焊铝合金-铝合金、铝-铝合金等。共晶AlF3-CsF系钎剂配合80∶20锌铝钎料,在高频感应压力下,钎焊铝合金4047-铝合金6063,测得抗拉强度108~126MPa,钎焊铝(Al 99.70)-铝合金4047,测得抗拉强度115~130MPa,抗拉强度较低,应用范围受到限制。
发明内容
本发明的目的是提供一种抗拉强度高的铝合金-铝合金、铝-铝合金钎焊用钎剂。
本发明所述的铝合金-铝合金、铝-铝合金钎焊用钎剂,以质量百分比计,含有共晶AlF3-CsF系钎剂97.0~99.9、氟化锌0.1~3.0、氟化锡0~0.5。优选组分为共晶AlF3-CsF系钎剂97.8~99.7、氟化锌0.2~1.8、氟化锡0.1~0.4。
试验表明,在共晶AlF3-CsF系钎剂中加入氟化锌、氟化锡,焊接过程中,锌、锡元素可以被铝置换出来并形成合金。这一置换、合金化的过程,增强了钎剂的去膜能力,“液化”了焊接工件的表面,提高了钎料的润湿性能,从而增加了钎料与工件的结合强度。
试验结果表明,加入氟化锌、氟化锡的总量不宜超过3%,否则钎剂的熔化温度会提高,难与锌铝钎料相配合。
具体实施方式
将共晶(摩尔比为42.0∶58.0)AlF3-CsF系钎剂和氟化锌、氟化锡按配比混合,球磨至200目,即可制成本发明所述的钎剂。配合80∶20锌铝钎料,高频感应压力钎焊铝合金4047-铝合金6063、铝(Al 99.70)-铝合金4047,按GB/T228-2002测试方法,测试抗拉强度,结果见下表:
从上表可以看出,抗拉强度比未加入氟化锌、氟化锡的共晶AlF3-CsF系钎剂提高10%左右。
Claims (1)
1.一种焊接铝及铝合金的钎剂,其特征是以质量百分比计,含有共晶AlF3-CsF系钎剂97.8~99.7、氟化锌0.2~1.8、氟化锡0.1~0.4。