CN108468713A - A kind of self-lubricating bearing and its manufacturing method for heavy-duty truck balance axle - Google Patents
A kind of self-lubricating bearing and its manufacturing method for heavy-duty truck balance axle Download PDFInfo
- Publication number
- CN108468713A CN108468713A CN201810387599.7A CN201810387599A CN108468713A CN 108468713 A CN108468713 A CN 108468713A CN 201810387599 A CN201810387599 A CN 201810387599A CN 108468713 A CN108468713 A CN 108468713A
- Authority
- CN
- China
- Prior art keywords
- bearing
- self
- outer ring
- lubricating
- inner race
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of self-lubricating bearing and its manufacturing method for heavy-duty truck balance axle, for solving existing heavy-duty truck balance axle bearing without the low disadvantage of self-lubricating property, service life.Self-lubricating bearing includes bearing inner race and bearing outer ring, and the inside and outside circle of bearing is made using unlike material.The manufacturing method of self-lubricating bearing, includes the following steps：Core model is installed on Wiring apparatus, the long fibre after epoxy resin presoaks is wound in by pretightning force by tubulose；Stop winding after being wound into predetermined outer ring size, core model is put into together with Wrapping formed long fibre in curing oven and carries out hot setting；Core model is detached with the long fibre after solidification, obtains fiber-reinforced resin matrix compound material pipe；Fiber-reinforced resin matrix compound material pipe is processed into bearing inner race or bearing outer ring；Steel bearings inner ring and composite material outer ring or steel bearings inner ring are assembled together with composite material outer ring.Self-lubricating bearing quality that the present invention obtains is small, lubricity is good.
Description
Technical field
The present invention relates to self-lubricating bearing technical fields, specifically a kind of self-lubricating for heavy-duty truck balance axle
Bearing and its manufacturing method.
Background technology
Active service heavy-duty truck balance axle bearing is made of inner ring and outer ring, and inside and outside circle generally use bearing steel material makes
It forms, is lubricated in the course of work of bearing by adding lubricating grease.The surface of the inner ring and outer ring sliding contact of bearing
It is a kind of spherical bearing for hemisphere face, is suitable for reciprocally swinging, banking motion and rotary motion.
Chinese patent (application number 2011201267967) mentions a kind of sliding bearing of axle balance shaft, skill to be solved
The sliding bearing that art problem is to provide should have the characteristics that not easy to wear, with long service life.It includes the ontology of circular ring shape, at this
One side end face of body is formed with the oil groove of several equally distributed sectors, the inner circle of the symmetrical center line and circular ring shape ontology of oil groove
Circumferential surface is tangent.The inside and outside circle of self-lubricating bearing in above-mentioned patent is still metal material, and service life is low and quality is big.In
State's patent (application number 2008101507732) refer to a kind of engineering plastic spherical plain bearing sheathing material, interior ball material and its at
Type method, the bearing use resin injection molding, and fibre reinforced plastics are made with glass fibre, polyamide and other materials
Oscillating bearing, but its glass fibre used is staple fiber so that and the compressive strength of bearing is relatively low, and then the application range of bearing
It is relatively narrow.
Invention content
The purpose of the present invention is to provide a kind of self-lubricating bearings and its manufacturing method for heavy-duty truck balance axle, use
In the existing heavy-duty truck balance axle bearing of solution without the low disadvantage of self-lubricating property, service life, and realize self-lubricating bearing
Lightweight.
The technical scheme adopted by the invention to solve the technical problem is that：A kind of self-lubricating for heavy-duty truck balance axle
Bearing, it includes bearing inner race and bearing outer ring, characterized in that two kinds of differences are respectively adopted in the bearing outer ring and bearing inner race
Material is made, and two kinds of unlike materials are bearing steel and fiber-reinforced resin matrix compound material.
Further, the fiber in the fiber-reinforced resin matrix compound material is that carbon fiber, glass fibre or aramid fiber are fine
Dimension.
Further, the contact surface between bearing inner race and bearing outer ring is spherical.
The manufacturing method of a kind of self-lubricating bearing for heavy-duty truck balance axle, characterized in that it includes the following steps：
(1), core model is installed on Wiring apparatus, the long fibre after epoxy resin presoaks is wound in by pretightning force
Tubulose；
(2), stop winding after being wound into predetermined outer ring size, core model is put into curing oven together with Wrapping formed long fibre
Middle carry out hot setting；
(3), core model is detached with the long fibre after solidification, obtains fiber-reinforced resin matrix compound material pipe；
(4), fiber-reinforced resin matrix compound material pipe is processed by bearing inner race or bearing outer ring by machining mode；
(5), the bearing outer ring or bearing inner race of On The Quality of Bearing Steels are obtained by machining mode；
(6), obtained bearing outer ring dress is handled by the bearing inner race obtained by step (4) processing and by step (5)
With together, or bearing outer ring and handle the assembly of obtained bearing inner race by step (5) that step (4) processing obtains will be passed through
Self-lubricating bearing is obtained together.
Further, winding angle is 35-90 degree when winding.
Further, when carrying out hot setting, solidification temperature is 150-200 degrees Celsius, and hardening time is 4-5 hours.
The beneficial effects of the invention are as follows：Patent of the present invention has the following advantages：
(1), the molding mode wound using fiber obtains inner ring or the outer ring of bearing so that and bearing own wt reduces,
And there is good self-lubricating property.
(2), the radial compression intensity and modulus of fiber-reinforced resin matrix compound material is above bearing steel, therefore, bearing
Bearing capacity is strong, and non-deformability is strong.
Description of the drawings
Fig. 1 is one of the sectional view of self-lubricating bearing of the present invention；
Fig. 2 is the two of the sectional view of the self-lubricating bearing of the present invention；
In figure：1 bearing outer ring, 2 bearing inner races.
Specific implementation mode
The self-lubricating bearing and its manufacturing method of the present invention are described in detail below in conjunction with the accompanying drawings.
As shown in Figure 1, the self-lubricating bearing of the present invention includes bearing outer ring 1 and bearing inner race 2, wherein bearing outer ring uses
Fiber-reinforced resin matrix compound material makes, and bearing inner race is made of bearing steel material.Between bearing inner race and bearing outer ring
Contact surface be spherical.
As shown in Fig. 2, the self-lubricating bearing of the present invention includes bearing outer ring 1 and bearing inner race 2, wherein bearing outer ring uses
Bearing steel material makes, and bearing inner race is made of fiber-reinforced resin matrix compound material.Between bearing inner race and bearing outer ring
Contact surface be spherical.The self-lubricating bearing of above structure, has the following advantages：(1), the molding mode wound using fiber
Obtain inner ring or the outer ring of bearing so that bearing own wt reduces, and has good self-lubricating property.(2), fiber reinforcement
The radial compression intensity and modulus of polymer matrix composites is above bearing steel, and therefore, bearing load carrying capacity is strong, non-deformability
By force.
The production method of self-lubricating bearing of the present invention is described in detail below：
(1), core model is installed on Wiring apparatus, the long fibre after epoxy resin presoaks is wound in by pretightning force
Tubulose, winding angle is 35-90 degree when winding；
(2), stop winding after being wound into predetermined outer ring size, core model is put into curing oven together with Wrapping formed long fibre
In hot setting 4-5 hours is carried out under 150-200 degrees Celsius；
(3), core model is detached with the long fibre after solidification, obtains fiber-reinforced resin matrix compound material pipe；
(4), fiber-reinforced resin matrix compound material pipe is processed by bearing inner race or bearing outer ring by machining mode；
(5), the bearing outer ring or bearing inner race of On The Quality of Bearing Steels are obtained by machining mode；
(6), obtained bearing outer ring dress is handled by the bearing inner race obtained by step (4) processing and by step (5)
With together, or bearing outer ring and handle the assembly of obtained bearing inner race by step (5) that step (4) processing obtains will be passed through
Self-lubricating bearing is obtained together.
Claims (6)
1. a kind of self-lubricating bearing for heavy-duty truck balance axle, it includes bearing inner race and bearing outer ring, characterized in that institute
It states bearing outer ring and bearing inner race is respectively adopted two kinds of unlike materials and is made, and two kinds of unlike materials are bearing steel
And fiber-reinforced resin matrix compound material.
2. a kind of self-lubricating bearing for heavy-duty truck balance axle according to claim 1, characterized in that the fiber
Fiber in reinforced resin based composites is carbon fiber, glass fibre or aramid fiber.
3. a kind of self-lubricating bearing for heavy-duty truck balance axle according to claim 1, characterized in that bearing inner race
Contact surface between bearing outer ring is spherical.
4. a kind of manufacturing method of self-lubricating bearing for heavy-duty truck balance axle, characterized in that it includes the following steps：
(1), core model is installed on Wiring apparatus, the long fibre after epoxy resin presoaks is wound in by pretightning force by pipe
Shape；
(2), be wound into after predetermined outer ring size and stop winding, by core model together with Wrapping formed long fibre be put into curing oven into
Row hot setting；
(3), core model is detached with the long fibre after solidification, obtains fiber-reinforced resin matrix compound material pipe；
(4), fiber-reinforced resin matrix compound material pipe is processed by bearing inner race or bearing outer ring by machining mode；
(5), the bearing outer ring or bearing inner race of On The Quality of Bearing Steels are obtained by machining mode；
(6), the bearing inner race obtained by step (4) processing and the bearing outer ring obtained by step (5) processing are assemblied in
Together, or by the bearing outer ring obtained by step (4) processing and the bearing inner race obtained by step (5) processing it is assemblied in one
It rises and obtains self-lubricating bearing.
5. a kind of manufacturing method of self-lubricating bearing for heavy-duty truck balance axle according to claim 4, feature
It is that winding angle is 35-90 degree when winding.
6. a kind of manufacturing method of self-lubricating bearing for heavy-duty truck balance axle according to claim 4, feature
It is that when carrying out hot setting, solidification temperature is 150-200 degrees Celsius, and hardening time is 4-5 hours.