CN105729980B - A kind of flocking method of sauna house heating steel sheet - Google Patents
A kind of flocking method of sauna house heating steel sheet Download PDFInfo
- Publication number
- CN105729980B CN105729980B CN201610110652.XA CN201610110652A CN105729980B CN 105729980 B CN105729980 B CN 105729980B CN 201610110652 A CN201610110652 A CN 201610110652A CN 105729980 B CN105729980 B CN 105729980B
- Authority
- CN
- China
- Prior art keywords
- flocking
- parts
- steel plate
- water soluble
- galvanized steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of flocking method of sauna house heating steel sheet, from the galvanized steel plain sheet that Zinc Coating Thickness is 0.5mm, galvanized steel plain sheet is pre-processed successively, electrostatic spinning and drying；Water soluble flocking gluing agent is selected in glue spraying water, it is by following raw materials and its mass fraction：20 30 parts of cycloaliphatic epoxy resin；20 30 parts of watersoluble neoprene latex；8 10 parts of polyamide；57 parts of methyl tin；10 15 parts of nano aluminium oxide；10 20 parts of nano silicon；0.03 0.05 parts of sterilization antiseptic；90 100 parts of water；Prepared flocking steel plate has the adhesion of fine hair and steel plate greatly, and good heat conduction effect, long-term use will not decomposite toxic gas, the advantages of being difficult mouldy and breed bacteria.
Description
Technical field
The present invention relates to a kind of flocking method of sauna house heating steel sheet, belong to steel plate flocking technical field.
Background technology
At present, heating steel sheet used in sauna house, its outer surface is by the way of flocking, to prevent user of service from scalding
Wound, is general way；But under the conditions of long term high temperature, easily there is villus shedding, and because flocking in the heating steel sheet of flocking
Heating steel sheet surface wrap up one layer of glue can hinder the transmission of heat, cause heat-transfer effect undesirable, in addition, glue is absorbed
Substantial amounts of heat, accelerates the aging and decomposition of itself, adhesion strength decline occurs, if using the glue of benzene or formaldehyde for solvent
Glutinous agent, can decomposite harmful material, and damage is caused to the human body for steaming Saunas.
The content of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the invention provides a kind of flocking method of sauna house heating steel sheet,
Prepare as follows：
Step 1）Pretreatment：The galvanized steel plain sheet of selection is Zinc Coating Thickness 0.5mm steel plate, by galvanized steel plain sheet immersion quality point
Number is in 5% hydrochloric acid solution, after immersion 8-10min, taking-up galvanized steel plain sheet utilizes air-dry machine, carries out Quick-air-drying；
Step 2）Glue spraying water：Water soluble flocking gluing agent is preheating to 15-20 DEG C, and is uniformly applied to through step 1）Processing
On galvanized steel plain sheet, the smearing thickness of water soluble flocking gluing agent is controlled in 0.05-0.07mm, after having smeared, at room temperature, parks 10
min；
Step 3）Electrostatic spinning：Nylon fine hair is placed in flocking box body, switched on power, is formed in flocking box body
One high voltage electric field, then will be through step 2）Smear in the galvanized steel plain sheet feeding flocking box body of water soluble flocking gluing agent, carry out
Electrostatic spinning, after flocking is finished, removes from flocking box body, both obtains flocking steel plate；
Step 4）Drying：Will be through step 3）Obtained flocking steel plate, using two sections of drying, first in 45 DEG C of drying rooms, heating
After baking and curing 30min, remove, then carry out spontaneous curing.
Described step 2）In water soluble flocking gluing agent, be by following raw materials and its mass fraction：
20-30 parts of cycloaliphatic epoxy resin
20-30 parts of watersoluble neoprene latex
8-10 parts of polyamide
5-7 parts of methyl tin
10-15 parts of nano aluminium oxide
10-20 parts of nano silicon
0.03-0.05 parts of sterilization antiseptic
90-100 parts of water
Described sterilization antiseptic is 2- methyl -4,5- propylidene -4- isothiazoline -3- ketone.
The viscosity of described water soluble flocking gluing agent is 9000-11000mPa.s.
Beneficial effects of the present invention：
1st, the adhesion of fine hair and steel plate is big, is pre-processed using galvanized steel plain sheet, and to galvanized steel sheet surface.So as to add
The big adhesive force of adhesive and steel plate；
2nd, good heat conduction effect, adds nano aluminium oxide in water soluble flocking gluing agent, improves the heat-transfer effect of steel plate；
3rd, toxic gas will not be decomposited by being used for a long time, water soluble flocking gluing agent used, and each raw material has good heat steady
It is qualitative, it is not easily decomposed using process；
4th, mouldy and breed bacteria is difficult, sterilization antiseptic 2- methyl -4,5- is added in water soluble flocking gluing agent sub-
Propyl group -4- isothiazoline -3- ketone, disclosure satisfy that under the high temperature conditions using the requirement do not decomposed with broad-spectrum sterilization.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
A kind of flocking method of sauna house heating steel sheet, is prepared as follows：
Step 1）Pretreatment：The galvanized steel plain sheet of selection is Zinc Coating Thickness 0.5mm steel plate, by galvanized steel plain sheet immersion quality point
Number is in 5% hydrochloric acid solution, after immersion 8-10min, taking-up galvanized steel plain sheet utilizes air-dry machine, carries out Quick-air-drying；
Step 2）Glue spraying water：Water soluble flocking gluing agent is preheating to 15-20 DEG C, and is uniformly applied to through step 1）Processing
On galvanized steel plain sheet, the smearing thickness of water soluble flocking gluing agent is controlled in 0.06mm, after having smeared, at room temperature, parks 10 min；
Step 3）Electrostatic spinning：Nylon fine hair is placed in flocking box body, switched on power, is formed in flocking box body
One high voltage electric field, then will be through step 2）Smear in the galvanized steel plain sheet feeding flocking box body of water soluble flocking gluing agent, carry out
Electrostatic spinning, after flocking is finished, removes from flocking box body, both obtains flocking steel plate；
Step 4）Drying：Will be through step 3）Obtained flocking steel plate, using two sections of drying, first in 45 DEG C of drying rooms, heating
After baking and curing 30min, remove, then carry out spontaneous curing.
Described step 2）In water soluble flocking gluing agent, be by following raw materials and its mass fraction：
25 parts of cycloaliphatic epoxy resin
20 parts of watersoluble neoprene latex
8 parts of polyamide
5 parts of methyl tin
12 parts of nano aluminium oxide
16 parts of nano silicon
0.05 part of sterilization antiseptic
100 parts of water
Described sterilization antiseptic is 2- methyl -4,5- propylidene -4- isothiazoline -3- ketone.
The viscosity of described water soluble flocking gluing agent is 10800mPa.s.
The experimental performance of prepared flocking steel plate, is shown in Table 1.
Table 1
| Assessment item | Experiment condition | Test result |
| Outward appearance | Range estimation | It is smooth, it is not show-through |
| Fine hair adhesive force | It is exposed for terminal with glue-line with inking knife scratch, record scratch number of times | 60 not holiday layers are scraped, 80 glue-lines is scraped and is completely exposed |
| Wash-resistant property | Washability test instrument, dry friction | Washability test instrument：Experiment 2000 times, nothing substantially comes off；Washability test instrument：Experiment 3000 times, villus shedding 1/10； |
| Ultraviolet ageing is tested | Ultraviolet aging test chamber, condition：60 DEG C, humidity is more than 95%, time：400h | Without significant change |
Claims (3)
1. a kind of flocking method of sauna house heating steel sheet, it is characterised in that：Prepare as follows：
Step 1）Pretreatment：The galvanized steel plain sheet of selection is Zinc Coating Thickness 0.5mm steel plate, is by galvanized steel plain sheet immersion mass fraction
In 5% hydrochloric acid solution, after immersion 8-10min, take out galvanized steel plain sheet and utilize air-dry machine, carry out Quick-air-drying；
Step 2）Glue spraying water：Water soluble flocking gluing agent is preheating to 15-20 DEG C, and is uniformly applied to through step 1）What is handled is zinc-plated
On steel plate, the smearing thickness of water soluble flocking gluing agent is controlled in 0.05-0.07mm, after having smeared, at room temperature, parks 10
min；
Step 3）Electrostatic spinning：Nylon fine hair is placed in flocking box body, switched on power, one is formd in flocking box body
Individual high voltage electric field, then will be through step 2）Smear in the galvanized steel plain sheet feeding flocking box body of water soluble flocking gluing agent, carry out electrostatic
Flocking, after flocking is finished, removes from flocking box body, produces flocking steel plate；
Step 4）Drying：Will be through step 3）Obtained flocking steel plate, first in 45 DEG C of drying rooms, after heating, drying solidification 30min, is moved
Go out, then carry out spontaneous curing；
Described step 2）In water soluble flocking gluing agent, be by following raw materials and its mass fraction：
20-30 parts of cycloaliphatic epoxy resin
20-30 parts of watersoluble neoprene latex
8-10 parts of polyamide
5-7 parts of methyl tin
10-15 parts of nano aluminium oxide
10-20 parts of nano silicon
0.03-0.05 parts of sterilization antiseptic
90-100 parts of water.
2. a kind of flocking method of sauna house heating steel sheet according to claim 1, it is characterised in that：Described sterilization is prevented
Rotten agent is 2- methyl -4,5- propylidene -4- isothiazoline -3- ketone.
3. a kind of flocking method of sauna house heating steel sheet according to claim 1, it is characterised in that：Described aqueous plant
The viscosity of suede adhesive is 9000-11000mPa.s.