CN104262935A - Polyurethane mixed foaming agent - Google Patents
Polyurethane mixed foaming agent Download PDFInfo
- Publication number
- CN104262935A CN104262935A CN201410478895.XA CN201410478895A CN104262935A CN 104262935 A CN104262935 A CN 104262935A CN 201410478895 A CN201410478895 A CN 201410478895A CN 104262935 A CN104262935 A CN 104262935A
- Authority
- CN
- China
- Prior art keywords
- foaming agent
- hexafluoro
- mixed foaming
- butylene
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyurethane mixed foaming agent. The polyurethane mixed foaming agent is characterized by comprising hexafluoro-2-butene and at least one of pentane, 245fa and 65mfc; excellent characteristics of hexafluoro-2-butene that ODP (ozone depleting potential) is 0 and GWP (greenhouse-warming potential) is 2 are fully utilized; and pentane, 245fa and 65mfc are mixed with hexafluoro-2-butene to obtain the mixed foaming agent which has a low GWP value and low combustibility and explosibility, thus meeting the global requirement for environment protection and safe production.
Description
Technical field
The present invention relates to whipping agent.
Background technology
The whipping agent of current employing comprises 141b, pentane, 245fa, 365mfc etc., but above-mentioned whipping agent is progressively eliminated due to the OPD of 141b, reason that GWP value is high, 245fa, 365mfc due to GWP value height Countries started reduce use, and pentane due to its inflammable and explosive property to factory safety require very high.
Summary of the invention
The object of the invention is: provide a kind of urethane mixed foaming agent, it has OPD, GWP value is low, nonflammable and explosive feature.
The present invention is achieved in that a kind of urethane mixed foaming agent, it is characterized in that: it is made up of at least one in hexafluoro-2-butylene and pentane, 245fa and 65mfc three;
(1) its weight part ratio is:
Or (two) its weight part ratio is:
Or (three) its weight part ratio is:
Hexafluoro-2-butylene 1 ~ 60 part, pentamethylene 0.5 ~ 20 part,
245fa 0.5 ~ 20 part, 365mfc 0.5 ~ 15 part.
A kind of urethane mixed foaming agent of the present invention, the ODP (ODP) making full use of hexafluoro-2-butylene is 0, GWP (greenhouse latent energy value) is the good characteristic of 2, be aided with pentane, 245fa, 65mfc mixture becomes mixed foaming agent to obtain low GWP value, low inflammable and explosive property, meets global Environmental Safety production requirement.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
A kind of urethane mixed foaming agent, it is made up of the one in hexafluoro-2-butylene and pentane, 245fa and 65mfc three; Its weight part ratio is:
Hexafluoro-2-butylene, 60 parts, pentamethylene 25 parts;
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use on demand.
Embodiment 2
A kind of urethane mixed foaming agent, is characterized in that: it is made up of the one in hexafluoro-2-butylene and pentane, 245fa and 65mfc three; Its weight part ratio is:
Hexafluoro-2-butylene, 99.5 parts, pentamethylene 50 parts;
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use " " on demand.
Embodiment 3
A kind of urethane mixed foaming agent, is characterized in that: it is made up of the one in hexafluoro-2-butylene and pentane, 245fa and 65mfc three; Its weight part ratio is:
Hexafluoro-2-butylene, 1 part, pentamethylene 0.5 part;
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use on demand.
A kind of urethane mixed foaming agent, its heavy part ratio: hexafluoro-2-butylene, 1 ~ 99.5,245fa0.5 ~ 50 parts; The value indifference of its effect and embodiment 1, embodiment 2 and embodiment 3.
A kind of urethane mixed foaming agent, its heavy part ratio: hexafluoro-2-butylene, 1 ~ 99.5,365mfc0.5 ~ 50 parts; The value indifference of its effect and embodiment 1, embodiment 2 and embodiment 3.
Embodiment 4
A kind of urethane mixed foaming agent, its weight part ratio is:
Hexafluoro-2-butylene 85 parts, pentamethylene 15 parts, 245fa 20 parts;
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene, 245fa being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use on demand.
Technique effect; This mixed foaming agent has low GWP value, low inflammable and explosive property, and thermal conductivity is lower simultaneously.
Embodiment 5
A kind of urethane mixed foaming agent, its weight part ratio is:
Hexafluoro-2-butylene 45 parts, pentamethylene 7 parts,
245fa 10 parts.
Embodiment 6
A kind of urethane mixed foaming agent, its weight part ratio is:
Hexafluoro-2-butylene 1 part, pentamethylene 0.5 part,
245fa 0.5 part.
A kind of urethane mixed foaming agent, its weight part ratio is: hexafluoro-2-butylene 1 ~ 30 part, pentamethylene 0.5 ~ 15 part, 365mfc 0.5 ~ 15 part; Value and embodiment 4, embodiment 5 are identical with embodiment 6, its technique effect and embodiment 4, embodiment 5 and embodiment 6 indifference.
A kind of urethane mixed foaming agent, its weight part ratio is: hexafluoro-2-butylene 1 ~ 30 part, 245fa 0.5 ~ 20 part; 365mfc 0.5 ~ 15 part; Value and embodiment 4, embodiment 5 are identical with embodiment 6, its technique effect and embodiment 4, embodiment 5 and embodiment 6 indifference.
Embodiment 7
A kind of urethane mixed foaming agent, its weight part ratio is:
Hexafluoro-2-butylene 1 part, pentamethylene 20 parts,
245fa 30 parts, 365mfc 20 parts.
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene, 245fa, 365mfc being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use on demand.
Technique effect; This mixed foaming agent has low inflammable and explosive property, and thermal conductivity is lower.
Embodiment 8
A kind of urethane mixed foaming agent, its weight part ratio is:
Hexafluoro-2-butylene 40 parts, pentamethylene 10 parts,
245fa 20 parts, 365mfc 30 parts.
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene, 245fa, 365mfc being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use " " on demand.
Technique effect; This mixed foaming agent has low inflammable and explosive property, and thermal conductivity is lower.
Embodiment 9
A kind of urethane mixed foaming agent, its weight part ratio is:
Hexafluoro-2-butylene 60 parts, pentamethylene 20 parts,
245fa 10 parts, 365mfc 10 parts.
Preparation method is as follows: add storage tank after hexafluoro-2-butylene and pentamethylene, 245fa, 365mfc being weighed in proportion and carry out physical mixed.
Using method: the mixed foaming agent mixed is weighed direct use on demand.
Technique effect; This mixed foaming agent has low GWP value, low inflammable and explosive property, and thermal conductivity is lower simultaneously.
Above-described is only preferred embodiments of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the principles of the present invention, can also make some improvement and modification, this is also considered as protection scope of the present invention.
Claims (1)
1. a urethane mixed foaming agent, is characterized in that: it is made up of at least one in hexafluoro-2-butylene and pentane, 245fa and 65mfc three;
(1) its weight part ratio is:
Or (two) its weight part ratio is:
Or (three) its weight part ratio is:
Hexafluoro-2-butylene 1 ~ 60 part, pentamethylene 0.5 ~ 20 part,
245fa 0.5 ~ 30 part, 365mfc 0.5 ~ 30 part.