CN104227881A - Manufacturing method for artificial crystal product mould - Google Patents
Manufacturing method for artificial crystal product mould Download PDFInfo
- Publication number
- CN104227881A CN104227881A CN201310245677.7A CN201310245677A CN104227881A CN 104227881 A CN104227881 A CN 104227881A CN 201310245677 A CN201310245677 A CN 201310245677A CN 104227881 A CN104227881 A CN 104227881A
- Authority
- CN
- China
- Prior art keywords
- mould
- resin
- layers
- felt
- brush
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method for an artificial crystal product mould and belongs to the technical field of manufacturing of handiworks. The manufacturing method is realized by virtue of the technical scheme as follows: a product needing to be manufactured is modeled and polished to be smooth; a molded surface is coated with high-temperature-resisting wax for being brightened and is coated with one layer of polyvinyl alcohol de-molding agent; after the de-molding agent is completely dried, three layers of high-temperature-resisting gel coat resin are brushed to prepare a wear-resisting layer; after the wear-resisting layer is dried, high-temperature-resisting resin is brushed; three layers of surface felts are brushed in a spreading manner, and then are compacted by a brush; one layer of chopped felt is brushed on the upper surface of the outer surface felt and is stuck with resin to be compacted; five to six layers of medium-alkali glass fiber cloth are brushed on the chopped felt in the spreading manner and are stuck with the resin to be compacted; a product is put into a mould framework prepared in advance and the resin is stuck by the medium-alkali glass fiber cloth; a mould bracket is tightly packaged, compacted and pressurized; after the mould bracket is completely cured and molded, the mould is removed from a raw blank; and the de-molding agent is washed off and the mould is polished to be smooth by using waterproof abrasive paper with the type of more than 800# and sticking water, and the surface polishing treatment is carried out to obtain the artificial crystal product mould.
Description
Technical field
The invention belongs to technical field of artware manufacture, particularly relate to a kind of preparation method of artificial crystal production's mould.
Background technology
Synthetic quartz is a kind of polymer composite mixed by raw materials such as crystal resin, MEK, colour killing promoter, the product of the similar crystal formed after chemical reaction.
In modern house life, dazzling crystal glass decoration, expresses special passion and artistic grade with its exclusive fashion and elegance, all enjoys from ancient times to the present and be deeply in love.Brilliant, glittering and translucent is describe the gorgeous of it.An exquisite crystal glass product, the technique person several days even elaborate result of some months often, also Just because of this, crystal glass product rely on wherein the fantasy that contains and complicated artisan craftsmanship, dote on by the personage of numerous hobby art.
Summary of the invention
The invention provides a kind of preparation method of artificial crystal production's mould, adopt this mould making method to make Mold Making convenient, simple and direct.
The preparation method of artificial crystal production's mould of the present invention, is realized by following technical proposals:
(1) product-forming of required making is polished smooth;
(2) brushing high temperature resistant wax on the surface in moulding beats bright, and coats layer of polyethylene alcohol releasing agent;
(3) after releasing agent finish-drying, brush three layers of high-temperature plastic coating resin, make wearing layer;
(4) after wearing layer drying, brush high temperature resistant type resin again, then paving brushes three layers of surperficial felt brush and beats reality, repaves to brush the short felt of cutting of one deck and be stained with resin and beat reality on surperficial felt, cut on felt short, paving brushes 5-6 layers of medium-alkali glass fiber cloth and is stained with resin and beats reality;
(5) put into preprepared mold frame, with medium-alkali glass fiber cloth viscosity resin, mould rack bag is attacked severely real, pressurization;
(6) after thorough curing molding, mould can be taken off from former tire, wash away releasing agent, getting wet with the waterproof abrasive paper of more than 800# polishes smooth, and carries out surface finish process.
Detailed description of the invention
Below by specific embodiment, the present invention is further illustrated.
The preparation method of artificial crystal production's mould,---former tire is waxed, and---releasing agent brushed by former tire, and------------brush fire resistant resin---spread three layers of surperficial felt and---spreads the short felt of cutting of one deck and---spread 3-6 layers of glass-fiber-fabric and---put into the timbering of well in advance and---with glass-fiber-fabric adhesive high-temperature resistant resin, support bag is attacked severely real pressurization and---from former tire, mould is taken off------smooth with more than 800# liquid honing---surface finish---mould molding that washes away die surface releasing agent after solidification brush the 3rd time mould gel coat resin brush second time mould gel coat resin brush first pass mould gel coat resin in technological process: former tire polishing.
Mold Making operation sequence and points for attention:
The product-forming of required making polishes smooth by 1, glossiness and the former tire degree of polishing of mould have direct relation, and polish more smooth, after mould molding, products made thereby gets over gloss, must make an effort in former tire polishing finishing, just can produce high-quality product;
2brushing high temperature resistant wax (U.S. produces Brazil wax, ship board, three Star's waxes or 99 wax polishs are produced in Taiwan) on the surface in moulding beats bright as mirror with soft cloth;
3coat layer of polyethylene alcohol releasing agent (releasing agent configuration proportion is that polyvinyl alcohol 17-99 type 9 parts of+100 parts of water boil, and as allowing its quick-drying, can add the alcohol of 10-20%).Notice that the molecular weight of polyvinyl alcohol that uses should higher than 80%, otherwise stripping result declines;
4after releasing agent finish-drying, brush three layers of high-temperature plastic coating resin, make wearing layer (superficial layer);
5after wearing layer drying, then brush high temperature resistant type resin, then paving brushes three layers of surperficial felt brush and beats reality (the neutral Chopped Strand Mat 30 grams/square of alkali-free);
6repave on surperficial felt and brush the short felt of cutting of one deck and be stained with resin and beat reality (300-400 grams/squares, medium-alkali glass fiber felt);
7cut on felt short, paving brushes 5-6 layers of 04# medium-alkali glass fiber cloth and is stained with resin and beats reality;
8put into preprepared mold frame (mould rack can use timber well in advance);
9with 04# medium-alkali glass fiber cloth viscosity resin, mould rack bag is attacked severely real, pressurization;
10after thorough curing molding, mould can be taken off from former tire, wash away releasing agent, getting wet with the waterproof abrasive paper of more than 800# polishes smooth, and carries out surface finish process, has just made a complete mould.
Attention: in Mold Making, required resin must add curing agent and promoter, and its formula rate is: resin 100 parts of curing agent 4 parts of-8 parts of promoter 3-6 parts (determine according to temperature, temperature Gao Shaojia, temperature is low to be added).
Claims (2)
1. a preparation method for artificial crystal production's mould, is characterized in that comprising the following steps:
(1) product-forming of required making is polished smooth;
(2) brushing high temperature resistant wax on the surface in moulding beats bright, and coats layer of polyethylene alcohol releasing agent;
(3) after releasing agent finish-drying, brush three layers of high-temperature plastic coating resin, make wearing layer;
(4) after wearing layer drying, brush high temperature resistant type resin again, then paving brushes three layers of surperficial felt brush and beats reality, repaves to brush the short felt of cutting of one deck and be stained with resin and beat reality on surperficial felt, cut on felt short, paving brushes 5-6 layers of medium-alkali glass fiber cloth and is stained with resin and beats reality;
(5) put into preprepared mold frame, with medium-alkali glass fiber cloth viscosity resin, mould rack bag is attacked severely real, pressurization;
(6) after thorough curing molding, mould can be taken off from former tire, wash away releasing agent, getting wet with the waterproof abrasive paper of more than 800# polishes smooth, and carries out surface finish process.
2. the preparation method of artificial crystal production's mould according to claim 1, it is characterized in that: described resin must add curing agent and promoter, its formula rate (weight ratio) is 100:(4-8): (3-6).