AU2014317854B2

AU2014317854B2 - Two-part set-delayed cement compositions

Info

Publication number: AU2014317854B2
Application number: AU2014317854A
Authority: AU
Inventors: Kyriacos Agapiou; Peter James Boul; Lance Everett Brothers; Pauline Akinyi Otieno; Thomas Jason Pisklak
Original assignee: Halliburton Energy Services Inc
Current assignee: Halliburton Energy Services Inc
Priority date: 2013-09-09
Filing date: 2014-09-09
Publication date: 2016-07-21
Anticipated expiration: 2034-09-09
Also published as: RU2632086C1; GB2535880B; AU2014317854A1; NO20160246A1; GB201602526D0; WO2015035388A1; MX2016002867A; GB2535880A; CA2921230A1; CA2921230C

Abstract

A variety of methods and compositions are disclosed, including, in one embodiment a method of cementing comprising: providing a pozzolan slurry comprising a pozzolan and water; providing a lime slurry comprising hydrated lime and water; allowing the pozzolan slurry and the lime slurry to remain separate for about one day or longer; mixing the pozzolan slurry and the lime slurry to form a cement composition: and allowing the cement composition to set.

Description

TWO-PART SET-BELAYED CEMENT COMPOSITIONS

BACKGROUND

[0001] The present embodiments relate to subterranean cementing operations and, in certain embodiments, to set-delayed cemen compositions and methods of using set-delayed cement compositions in subterranean formations.

[0002] Cement compositions may be used in a variety of subterranean operations. For example, in subterranean well construction, a pipe string (e.g., casing, liners, expandable tiibiiiars, etc.) may be run into a we!lbore and cemented in place. The process of cementing the pipe string in place is commonl referred to as "primary cementing." In a typical primary cementing method, a cement composition may be pumped into an annulus between the walls of the we 11 bore and the exterior surface of the pipe string disposed therein. The cement composition may set in the annular space, thereby forming an annular sheath of hardened, substantially impermeable cement (i.e., a cement: sheath) that may support and position the pipe string in. the weJIbore and may bond the exterior surface of the pipe string to the subterranean formation. Among other things, the cement sheath surrounding the pipe string prevents the migration of fluids in the annulus and protects the pipe string from corrosion. Cement compositions may also be used in remedial cementing methods to seal cracks or holes in pipe strings or cement sheaths, to seal highly permeable formation zones or fractures, or to place a cement plug and the like.

[0003] A broad variety of cement compositions have been used in subterranean cementing operations, in some instances, set-delayed cement compositions have been used. Set-delayed cement compositions are characterized by remaining in a pumpable fluid state for at least about one day (e.g., about 7 days, about 2 weeks, about 2 years or more) at room temperature (e.g., about 80° F) in quiescent storage. When desired for use. the set-delayed cement compositions should be capable of activation and consequently develop reasonable compressive strengths. For example, a cement set activator may be added to a set-delayed cement composition to induce the composition to set into a hardened mass. Among other things, set-delayed cement compositions may be suitable for use in we! Shore application such as applications where it is desirable to prepare the cement composition in advance. This may allow the cement composition to be stored prior to use. hi addition, this may allow the cement composition to be prepared at a convenient location before transportation to the job site. Accordingly, capital expenditures may be reduced due to a reduction in the need for on- site bulk storage and mixin equipment. This may be particularly useful tor offshore cementing operations where space onboard the vessels may be limited. [0004] While set-delayed cement compositions have been developed heretofore, challenges exist with their successful use in subterranean cementing operations. For example, set-delayed cement compositions prepared with Portland cement may have uodesired gelation issues which can limit their use and effectiveness in cementing operations. Other set-delayed compositions that have been developed, for example, those comprising hydrated iinie and quartz, may he effective in some operations but may have limited use at lower temperatures as they may not develop sufficient compressive strength when used in subterranean formations having Sower bottom hole static temperatures, in addition, i may be problematic to activate some set-delayed cement compositions while maintaining acceptable thickening times and compressive strength development.

BRIEF DESCRIPTION OF TOE DRAWINGS

[0001] These drawings illustrate certain aspects of some of the embodiments of the present method_* and should not be used to limit or define the method,

[0002] FIG. I illustrates a system for preparation and delivery of a set-delayed Scement composition to a wellbore in accordance with certain embodiments.

[0003] FIG. 2 A illustrates surface equipment that may be used in placement of a set- delayed cement composition in a wellbore in accordance with certain embodiments.

[0004] FIG. 2B illustrates placement of a set-delayed cement composition into a wellbore annulus in accordance with certain embodiments.

0

DESCRIPTION OF PREFERRED EMBODIMENTS

[0005] The example embodiments relate to subterranean cementing operations and, more particularly_* in certain embodiments, to set-delayed cement compositions and methods of using set-delayed cement compositions- in subterranean formations.

[0006] Embodiments of the set-delayed cement compositions may generally comprise water, a pozzolan, and hydrated lime. Optionally,, the cement compositions may further comprise a dispersant and/or a. cement set retarder. Alternatively, embodiments of the set-delayed cement, composition may comprise two-part set-delayed cement composition comprising separate component -slurries with one component slurry comprising a pozzolan and the other component slurry comprising lime. Embodiments of the two-pan set-delayed cement compositions are discussed in detail below. Advantageously, embodiments of the set- delayed cement compositions may be capable of remaining in a pumpable fluid state for an extended period of time. For example, the set-delayed cement compositions may remain in a pumpable fluid state for at least about 1 day or longer. Advantageously, the set-delayed cement compositions may develop reasonable compressive strengths after activation at relatively low temperatures. While the set-delayed cement compositions may be suitable for a numbe of subterranean cementing operations, the may be particularly suitable for use in subterranean formations having relatively low bottom hole static temperatures, e.g., temperatures less than about 200° F or ranging from about Η⁾0^ώ F to about 200* F. In alternative embodiments, the set-delayed cement compositions may be used in subterranean formations having bottom bole static temperatures up to 450° F or higher.

[0007] The water used in embodiments may be from any source provided that it does not contain an excess of compounds that, may undesirably affect, other components in the set-delayed cement compositions. For example, a cement composition may comprise fresh water or salt water. Salt wate generally may include one or more dissolved salts therein and may be saturated or unsaturated as desired for a particular application. Seawater or brines may be suitable for use in embodiments. Further, the water may be present in an amount sufficient to form a pumpable slurry, in certain embodiments, the water may be present in the set-delayed cement compositions in an amount in the range of from about 33% to about 200% by weight of the pozzolan. in certain embodiments, the water may be present in the set-delayed cement compositions in. an amount in the range of from about 35% to about 70% by weight of the pozzolan. With the benefit of this disclosure one of ordinary skill in the art will recognize the appropriate amount of water for a chosen application.

[0008] Embodiments of the set-delayed cement compositions may comprise a pozzolan. Any pozzolan is suitable for use in embodiments. Example embodiments comprising a pozzolan may comprise fly ash, silica fume, metakao!in, a natural pozzolan (e.g., pumice), or combinations thereof.

[0009] Embodiments of the pozzolan may comprise fly ash. A. variety of fly ashes may be suitable, including fly ash. classified as Class C and Class P fly ash according to American Petroleum Institute, API Specification for Materials and ^'Testing for Well Cements, API. Specification 10. Fifth Ed., Jul I . 1 90. Class C fly ash comprises both silica and lime, so it may set to form a hardened mass upon mixing with water. Class F fl ash generally does not contain a sufficient amount of time to induce a ecmentitiou reaction., therefore, an additional source of calcium Ions i necessary for a set-delayed cement composition comprising Class F fly ash. In some embodiments, lime may be mixed with Class F fly ash in an amount hi the range of about 0, 1% to about 100% by weight of the fly ash. h some instances, the lime may be hydrated lime. Suitable examples of fly ash. include, but are not limited to, POZ IX* A cement additive, commercially available from Halliburton Energy Services, Inc., Houston, Texas,

10010 Embodiments of the pozzolan may comprise metakaoli . Generally, metakaolin is a white pozzolan that may be prepared by heating kaolin clay, for example, to temperatures in the range of about 600" C to about 800° C.

[00.1 1 ] Embodiments of the pozzolan m comprise a natural pozzolan. Natural pozzoians are generally present on the Earth's surface and set and harden in the presence of hydrated lime and water. Embodiments comprising a natural pozzolan may comprise pumi.ee, diatomaceous earth, volcanic ash, opaline shale, tuff, and combinations thereof The natural pozzoians may be ground, or unground. Generally, the natural pozzoians may have an particle size distribution as desired for a particular application. In certain embodiments, the natural pozzoians may have a mean particle size in a range of from about 1. micron to about 200 microns. The mean particle size corresponds to d50 values as measured by particle size analyzers such as those manufactured by Malvern instruments, Worcestershire, United Kingdom, In specific embodiments, the natural pozzoians may have a mean particle size in a range of from about 1 micron to about 200 micron, from about 5 microns to about 100 microns, or from about 10 micron to about 50 microns. In one particular embodiment, the natural pozzoians may have a mean particle size of less, than about 15 microns.. An example of a suitable commercial natural pozzolan Is pumice available from Hess Pumice Products, Inc., Ma!ad, Idaho, as DS-325 lightweight aggregate, which has a particle size of less than about 15 microns. It should be appreciated that particle sizes too small may have mixability problems while particle sizes too large may not be effectively suspended, in the compositions and may be less reactive due to their decreased surface area. One of ordinary skill in the art. with the benefit of this disclosure, should be able to select a particle size for the natural pozzolans suitable for use for a chosen application.

[0012] Embodiments of the set-delayed cement compositions may comprise hydrated lime. As used herein, the term "hydrated lime" will be understood to .mean calcium hydroxide. \n some embodiments, the hydrated lime may be provided as quicklime (calcium oxide) which hydrates when mixed with water to form the hydrated lime. The hydrated lime- may be included in embodiments, for example, to form a hydraulic composiiion with the pozzolan. Far example, the hydrated lime may be included in a pozzolan-to-hydrated-lime weight ratio of about 10:1 to about 1 : 1 or a ratio of about 3: 1 to about 5: 1. Where present, the hydrated lime may be included in the set-delayed cement compositions in an amount in the range of from about 10% to about 100% by weight of the pozzolan, for example, in some embodiments, the hydrated lime may be present in an amount ranging between any of and/or including any of about 10%, about 20%, about 40%, about 60%, about 80%, or about 100% by weight of the pozzolan. In some embodiments, the cementitious components present in the set-delayed cement composition may consist essentially of the pozxolan and the hydrated lime. For example, the cementitious components may primarily comprise the pozzolan and the hydraied lime without, any additional cementitious components (e.g., Portland cement) that hydraulieall set in the presence of water. One of ordinary skill i the art, with the benefit of this disclosure, wi ll recognize the appropriate amount of hydrated lime to include for a chosen, application.

[0013] Embodiments of the set-delayed cement compositions may comprise a cement set retarder. A broad variety of cement set retarders may be suitable for use in the set-delayed cement compositions. For example, the cement, set. retarder may comprise phosphonic acids, such as ethylenediamine tetra(roethylene phosphonic acid), diethylenetriarame penta(^'methyk«.e phosphonic acid), etc.; ligriosulfenaies, such as sodium lignosulfonate, calcium lignosulfonate, etc.: salts such as stannous sulfate, lead acetate, monobasic calcium phosphate, organic acids, such as citric acid, tartaric acid, etc.; cellulose derivatives such as hydroxy! ethyl cellulose (HEC) and carboxymethyl hydroxyethyl cellulose (C HBC); synthetic co- or ter-polymers comprising sulfonate and carboxylic acid groups such as sulfonate-fiuietioiiaSized acrylamide-acrylic acid co-polymers: borate compounds such as alkali borates, sodium inelaborate, sodium tetraborate, potassium pentahorate: derivatives thereof, or mixtures thereof. Examples of suitable cement set retarders include, among others, phosphonic acid derivatives. One example of a suitable cement set retarder is Micro Matrix⁸' cement retarder, available from Halliburton Energy Services, Inc. Generally, the cement set retarder may be present in the set-deiayed cement compositions in an amount sufficient to delay the setting for a desired time, !n some embodiments, the cement set retarder ma be present in the set -delayed cement compositions in an amount in the range of from about 0.01% to about 10% by weight of the pozzolan. In specific embodiments, the ceme t act retarder may be present in an amount ranging between any of and/or including any of about 0,01%. about 0.1%, about 1%, about 2%, about 4%. about 6%, about 8%, or about 10% by weight of the pozzolan. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the cement set retarder to include for a chosen application.

[0014] As previously mentioned, embodiments of the set-delayed cement compositions may optionally comprise a dispersant. Examples of suitable dispersants include, without limitation, sulfooaied-formaldehyde-based dispersants (e.g., sulfonated acetone formaldehyde condensate}, examples of which may include Daxad*^' 19 dispersant available from Geo Specialty Chemicals, Ambler, Pennsylvania. Other suitable dispersants may be polycarboxylated ether dispersaiits such as Liquiment*'^' 558 I F and Ltquimenf* 5141, dispersants available from BASF Corporation Houston, Texas; or Ethacryf " G dispersant available from Coatex, Genay, France. An additional example of a suitable commercially available dispersant is CFR^{' U}~3 dispersant, available from Halliburton Energy Services, ine, Houston, Texas. The Liquiment* 514L dispersant may comprise 36% by weight of the polycarboxylated ether in water. While a variety of dispersants may be used in accordance with embodiments, polycarboxylated ether dispersants may be particularly suitable for use in some embodiments. Without being limited by theory, it is believed that polycarboxylated ether dispersants may synergistieally interact with other components of the set-delayed cement composition. For example, it is believed that the polycarboxylated ether dispersants may react with certain cement set retarders (e.g., phosphonic acid derivatives) resulting in formation of a gel that suspends the pozzolan and hydrated lime in the composition for an extended period of time.

[0015] in some embodiments, the dispersant may be included in the set-delayed cement compositions in an amount in the range of from about 0,01% to about 5% by weight of the pozzolan. In specific embodiments, the dispersant may be present in an amount ranging between an of and/or including any of about 0.01%, about 0.1 %, about 0.5%, about 1%, about 2%, about 3%, about 4%, or about S% by weight of the pozzolan. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the dispersant to include for a chosen application.

[00.16] Some embodiments of the set-delayed cement compositions may comprise silica sources in addition to the pozzolan; for example, crystalline silica and/or amorphous silica. Crystalline silica is a powder that may be included in embodiments of the set-delayed cement compositions, for example, t prevent cement compressive strength retrogression. Amorphous silica is a powder that may be included in embodiments of the set-deiayed cement compositions as a. lightweight filler and/or to increase cement compressive strength, Amorphous silica is generally a byproduct of a ferrostliooii production process, wherein the amorphous silica may be formed by oxidation and condensation of gaseous silicon suboxide, SiO, which is formed -as an intermediate during die process. An example of a suitable source of amorphous silica is Siliealite'*^" cement additive available from Halliburton Energy Services, inc., Houston. Texas, Embodiments comprising additional silica sources may utilize the additional silica source as needed to enhance compressive strength or set times.

[0 17] Other additives suitable for use in subterranean cementing operations also may be Included in embodiments of the set-delayed cement compositions. Examples of such additives include, but are not limited to: weighting agents, lightweight additives, gas- generating additives, mecbanical-propetty-enhaneing additives_* lost-circulation materials, filtration-control additives, fluid-loss-control additives, defoaming agents, foaming agents, thixoiropic additives, and combinations thereof In embodiments, one or more of these additives may be added to the set-delayed cement compositions after storing but prior to the placement of a set-delayed cement composition into ^'a subterranean formation. A person having ordinary skill in the art with the benefit of this disclosure, should readily be able to determine the type and amount of additive useful for a particular application and desired result.

[0018] Those of ordinary skill in the art will appreciate that embodiments of the set- deiayed cement compositions generally should have a density suitable for a particular application. By way of example, the cement compositions may have a density in the range of from about 4 pounds per gallon ("lb/gal") to about 20 lb/gal. in certain embodiments, the cement compositions may have a density in the range of from about S lb/gal to about 17 lb/gal. Embodiments of the set-delayed cement compositions may be foamed or unfoamed or may comprise other means to reduce their densities, such as hollow microspheres, low- density elastic beads, or other density-reducing additives known in the art. In embodiments, the density may be reduced after storage, but prior to placement in a subterranean formation. In embodiments, weighting additives may be used to increase the density of the set-delayed cement compositions. Examples of suitable weighting additives may include barite, hematite, hausmannite, calcium carbonate, siderite, ilmenite, or combinations thereof. In particular embodiments, the weighting additives ma have a specific gravity of 3 or greater. Those of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate density for a particular application.

[0019] As previously mentioned, the set-delayed cement compositions may have a delayed set in that they remain in a pumpabie fluid state for at least one day (e.g., about 1 day, about 2 weeks, about. 2 years or more) at room temperature (e.g., about 80° F) in quiescent storage. For example, the set-delayed cement compositions may remain in a pumpabie fluid state for a period of time from about I day to about 7 days or more, in some embodiments, the set-de!ayed cement .compositions may remain in a pumpabie fluid state for at .least about 1 day, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about 60 days, or longer, A fluid is considered to be in a pumpabie fluid state where the fluid has a consistency of less than 70 Bearden units of consistency ("Be"), as measured on pressurized consistometer in accordance with the procedure for determining cement thickening times set forth in API RP Practice 10B-2, Recommended Practice for ^'Testing Weil Cements, First Edition, July 2005,

10020 When, desired for use, embodiments of the set-delayed cement compositions may be activated (e.g., by combination with a cement set activator) to set into a hardened mass. The term "cement set activator" or "activator'', as used herein, refers to an additive that activates a set-delayed or heavily retarded cement, composition and may also accelerate the setting of the set-delayed, heavily retarded, or other cement composition. By way of example, embodiments, of the set-delayed cement compositions may be activated to form a hardened mass in a time period in the range of from about 1 hour to about 12 hours. For example, embodiments of the set-delayed cement compositions may set to form a hardened mass in a time period ranging between any of and/or including any of. about I day, about 2 days, about 4 days, about.6 days, about. 8 days, about 10 days, or about 12 days.

[0021] in some embodiments, the set-delayed cement compositions may set to have a desirable compressive strength after activation. Compressive strength is generally the capacity of a materia! or structure to withstand axially directed pushing forces.. The compressive strength may be measured at a. specified time after the set-delayed cement composition, has been activated and the resultant composition is maintained under specified temperature and pressure conditions. Compressive strength can be measured by either destructive or non-destructive methods. The destructive method physically tests the strength of treatment fluid samples at various points in time by crushing the samples in a compression-testing machine. he compressive strength is calculated from the failure load divided by the cross-sectional area resisting the load and is reported in uni ts of pound-force per square inch (psi). Non-destructive methods, may employ a UCA^"" Ultrasonic Cement Analyser, available from farm instrument Company, Houston, IX Compressive strength values may be determined in accordance with A PI P 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005.

[0022] By way of example, the set-delayed cement compositions may develop a 24- hour compressi ve strength in the range of from about 50 psi to about 5000 psi, alternatively, from about 100 psi to about 4500 psi, or alternatively from about 500 psi to about 4000 psi. In some embodiments, the set-delayed cement compositions may develop a compressive strength in 24 hours of at least about 50 psi, at least about 100 psi, at least about 500 psi, or more. In some embodiments, the compressive strength values may he determined using destructive or non-destructive methods at a temperature ranging from 100° F to 200° F,

[0023] ^'In some embodiments, the set-delayed cement compositions may have desirable thickening times after activation. Thickening time typically refers to the time a fluid, such as a set-delayed cement composition, remains in a fluid state capable of being pumped. A number of different laboratory techniques may be used to measure thickening time. A pressurized consistonie er, operated in .accordance with the procedure set forth in the aforementioned API IIP Practice l B-2, may be used to measure whether a fluid is in a pumpabie fluid state. The thickening time may be the time for the treatment fluid to reach 70 Be and may be reported as the time to reach 70 Be. in some embodiments, the cement compositions may have a thickening time of greater than about 1 hour, alternatively, greater than about 2 hours, alternatively greater than about 5 hours at 3,000 psi and temperatures in a range of from about 50^s" F to about 400° F, alternatively, in a range of from about. 80° F to about 250° F, and alternatively at a temperature of about 140° F.

[0024] Embodiments ma include the addition of a cement set activator to the set- delayed cement compositions. Examples of suitable cement set activators include, but are not limited to: zeolites, amines such as triethano!amine, diethanolamine; silicates such as sodium silicate; zinc formate; calcium acetate; Groups IA and OA hydroxides such, as soclium hydroxide, magnesium hydroxide, and calcium hydroxide; monovalent salts such as sodium chloride; divalent salts such a calcium chloride; nanosilica {^'i.e., silica having a particle size of less than or equal to about 100 nanometers); polyphosphates; and combinations thereof, in some embodiments, a combination of the polyphosphate and a monovalent salt may be used for activation. The monovalent salt may be any salt that dissociates to ^"form a monovalent cation, such as sodium and potassium salts. Specific examples of suitable monovalent salts include potassium sulfate, and sodium sulfate. A variety of different polyphosphates may be used in combination with the monovalent salt for activation of the set-delayed cement compositions, including polymeric metaphosphate salts. phosphate salts, and combinations thereof. Specific examples of polymeric etaphosphate salts that may be used include sodium hesametaphosphate, sodium trimetaphosphaie, sodium tetrametaphosphate, sodium pentametaphosphate, sodi um heptametaphosphate, sodium octametaphosphate, and combinations thereof. A. specific example of a suitable cement set activator comprises a combination, of sodium, sulfate and sodium hexametaphosphate. In particular embodiments, the cement set activator may be provided and added t the set- delayed cement composition as a liquid additive, for example, a liquid additive comprising a monovalent salt, a polyphosphate, and optionally a dispersani.

[0025] The cement set activator should be added to embodiments of the set-delayed cement composition in an amount sufficient to induce the set-delayed composition to set into a hardened mass. In certain embodiments, the cement set activator may be added to the cement composition in an amount in the range of about 0. i.% to about 20% b weight of the pozzoian, in specific embodiments, the cement set activator may be present in an amount ranging between any of and/or including any of about 0< 1%, about 1%, about 5%, about 10%, about 15%, or about 20% by weight of the pozxolan. One of ordinary skill in the art, with the benefit of this disclosure_* will recognize the appropriate amount of the cement set activator to include for a chosen application.

[0026] Embodiments of the set-delayed cement compositions may comprise the use of two separate component slurries that are combined to .form a two-part set-delayed cement composition. Embodiments of the two-part set-delayed cement may comprise providing a pozzolan slurry and a lime slurry which are kept separate in lieu of adding cement set retarders. The two-part set-delayed cement composition may utilize two individual slurries in a manner such that neither slurry is able to hydrate and therefore set independently. Therefore, each individual slurry of the two-part set-delayed cement composition should remain in a set-delayed state (i.e. .remaining in -a pumpable fluid state for at least about one day [e.g., at least about 1 clay, about 2 weeks, about 2 years or more] at room temperature in quiescen storage). Embodiments of the two-part set-delayed cement composition may comprise two component slurries. One component slurry comprises a pozzolan and water. The other component slurry comprises lime and water. In embodiments, each slurry may be stored at a well site or other storage site until needed. When needed, the two component slurries may be mixed together prior to or while pumping downhote. The combined slurry may then thicken and set within a desired period of time.

[0027] Advantageously, the use of a two-part set-delayed, cement composition may allow for quicker setting at lower temperatures (e.g. temperatures less than 140° F). Furthermore, because the reactive components of the two-part set-delayed cement composition are kept separate* additional additives or higher concentrations of additives (e.g. additional silica sources, see above) may be added to the two-part set-delayed cement composition without risk of premature setting or gelation.,

[0028] Embodiments of the two-part set-delayed cement compositions may generally comprise two component slurries, a pozzolan slurry and a lime slurry. Both component slurries comprise water. Optionally, either component slurry may further comprise a dispersatit and/or a cement set retarder. Advantageously, embodiments of the two-part set-delayed cement compositions may be capable of remaining in a pumpabie fluid state for an extended period of time. For example, the two-part set-delayed cement compositions may remain in a pumpabie fluid state for at least about 1 day or longer. Advantageously, the two-part set-delayed cement compositions may develop reasonable compressive strengths after activating (e.g. by mixing the two component slurries) at relatively low temperatures. While the two-part set-delayed cement compositions may be suitable for a number of subterranean cementing operations, they may be particularly suitable for use in subterranean formations having relatively low bottom hole static temperatures, e.g., temperatures less than about 200° F or ranging from about 100° F to about 200° F, In alternative embodiments, the set-delayed cement compositions may be used in subterranean formations ha ving bottom hole static temperatures up to 450* F or higher.

[0029] Embodiments of the pozzolan slurry comprise a pozzolan. Any pozxolan is suitable for use in embodiments. Example embodiments comprising a poxzolan may comprise fly ash, silica fume, metakaolin, diaiomaceous earth, a natural pozzolao. (e.g., pumice), or combinations thereof, in a two-part set-delayed cement composition embodiment, the pozzolan may be a non-hydraulic pozzolan, i.e. a pozzolan that will not react when mixed with water in the absence of hydrated lime to form a cementitious material. By way of example, some types of Class€ fly ash may not be suitable for use in a two-part set-delayed cement composition embodiment, because Class € fly ash may comprise lime and will therefore react when, mixed with water to become cementitious.

[0030] Embodiments of the poz¾olan slurry may comprise fly ash. A variety of S y ashes mav be suitable, meludirut II y ash classified as Class F flv ash according to American Petroleum Institute, API Specification for Material and Testing for Well Cements, API Specification 1 , Fifth Ed., July ! , 1990. Class C fly ash comprises both silica and lime, so it may set to form a hardened mass upon .mixing with water and may thus be unsuitable for use in the ozzolan slurry as it may undesirably set when mixed with the water. Class F fly ash generally does not contain a sufficient, amount of lime to induce a cementitious reaction, therefore, should remain in a pumpabie fluid state when mixed with water. Suitable examples of fly ash include, but are not limited to, POZMIX*^' A cement additive, commercially available from Halliburton Energy Services, inc., Houston, Texas,

[0031] Embodiments of the pozzolan slurry may comprise metakaolm. Generally, metakao!in is a white pozzolan that. may be prepared by heating kaoiin clay, for example, to temperatures In the range of about 600° C to abo ut 800° C,

[0032] Embodiments of the pozzolan slurry may comprise a natural pozzolan. Natural pozxolans are generally present on. the Earth's surface and set and harden in the presence of hydraled lime and water. Embodiments comprising a natural pozzolan may comprise pumice, diatomaeeoos earth, volcanic ash, opaline shale, tuff, and combinations thereof. The natural pozzola.ns may be ground or unground. Generally, the natural pozzoians may have any particle size distribution as desired for a particular application, in certain embodiments, the atural pozzoians may have a mean particle size in a range of from about I micron to about 200 microns. The mean particle size corresponds to dSO values as measured by particle size analyzers such as those manufactured by Malvern Instruments, Worcestershire, United Kingdom, In specific embodiments, the natural pozzoians may have mean particle size in range of from about 1 micron to about 200 micron, from about 5 microns to about 100 microns, or from about 10 micron to about 50 microns. In one particular embodiment, the natural pozzolans may have a mean particle size of less than about 15 microns. An example of a suitable commercial natural pozzolan is pumice available from Hess Pumice Products, inc., Malad, Idaho, as DS-325 lightweight aggregate, which has a particle size of less than about 15 microns, it should be appreciated that particle sizes too small may have mixability problems while particle sizes too large may not be effectively suspended in the compositions and may be less reactive due to their decreased surface area. One of ordinary skill in the art, with the benefit of this disclosure, should be able to select a particle size for the natural pozzolans suitable for use for a chosen application.

[0033] Embodiments of the pozzolan slurry comprise water. The water used in embodiments of the pozzolan slurry ma be from any source provided that it does not contain an excess of compound that may undesirably affect other components in the pozzolan slurry. For example, the pozzo!an slurry may comprise fresh water or salt water. Salt water generall may include one or more dissolved salts therein and may be saturated or unsaturated as desired for a particular application. Seawater or brines may be suitable for use in embodiments. Further, the water may be present in an amount sufficient to form a pumpable slurry. In certain embodiments, the water may be individually present in the pozzolan slurry in an amount in the range of from about 33% to about 200% by weight of the pozzolan. In certain embodiments, the water may be present in the pozzolan slurry in an amount in the range of from about 35% to about 85% by weight of the pozzolan. With the benefit of this disclosure one of ordinary skill in the art will recognize the appropriate amount of water for a chosen application. Embodiments of the pozzoian slurry may comprise additives suitable for use in subterranean cementing operations. Any additive, including additional silica sou ces, may be added to the pozzoian slurry. Examples of additives include, but are not limited to: weighting additives, lightweight additives, gas-generating additives, mechanical-property-enhancjng additives, lost-circulation materials, filtration- control additives, iluid-loss-conirol additives, defoaming agents, foaming agents, ihixottopic adcHtives, dispersants, cement set activators/accelerators, cement set retarders, and combinations thereof. In embodiments of the pozzoian slurry, one or more of these additives may be added to the pozzoian slurry before or after storing. Additionally one or more of these additives may be added to the poz¾olan slurry before or after mixing the pozzoian slurry with the lime slurry. A person having ordinary skill in the art, with the benefit, of this disclosure, should readily be able to determine the type and amount of additive useful for a particular application and desired result.

[0034] Embodiments of the lime slurry comprise hydrated lime. As used herein, the term "hydrated time" wti.l be understood to mean, calcium hydroxide, in some embodiments, the h drated lime may be provided as quicklime (calcium oxide) which hydrates when mixed with water to form the hydrated lime. The hydrated lime may be included in embodiments of the lime slurry to form a hydraulic composition with the pozzoian. For example, the hydrated lime may be included in a po zolan-to-hy rated-linie weight ratio of about 1.0: 1 to about I ; I or a ratio of about 3: 1 to about 5; 1 , based on the combined mix of both component slurries. Where present, the lime slurry may comprise an amount of hydrated lime between about 10% to about 100% by weight of the pozzoian present in the pozzoian slurry. In some embodiments, the hydrated lime may be present in the lime slurry in an amount ranging between any of and/or including any of about 10%, about 20%, about 40%, about 60%, about 80%, or about 100% by weight of the pozzoian in the pozzoian slurry. In some embodiments, the cementhious components present in the two-part set-delayed cement composition may consist essentially of the pozzoian and the hydrated lime. For example, the cementhious components may primarily comprise the pozzoian (e.g., pumice) and the hydrated lime without any additional cementitious components (e.g., Portland cement) that hydrauliealiy set in the presence of water. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of hydrated lime to include for a chosen appl ication. [0035] Embodiments of the lime slurry comprise water. The water used in embodiments of the lime slurry may ^'be from any source provided that it does not contain an excess of compounds that may undesirably affect other components in the lime slurry. For example, the lime slurry may comprise fresh water or salt water. Salt water generally may include one or more dissolved sails therein and may be saturated or unsaturated as desired for a particular application. Sea ater or brines may be suitable tor use in embodiments. Further, the water may be present in an amount sufficient to form a pumpable slurry. In certain embodiments, the water may be individually present in the lime slurry in an amount in the range of from about 33% to about 200% b weight of the lime, hi certain embodiments, the water may be present in the lime slurry in an amount -in the range of from about 35% to about 70% by weight of the lime. With the benefit of this disclosure one of ordinary skill in the art will recognize the appropriate amount of water for a chosen application.

[0036] Embodiments of the lime sl urry may comprise additives suitable for use in subterranean cementing operations. Any additive, including additional silica, sources, may be added to the lime slurry. Examples of such additives include, but are not limited to: weighting additives, lightweight additives, gas-generating additives, mechanical-property- enhancing additives, lost-circulation materials, filtration-control additives, fluid-loss-control additives, defbaming agents, foaming agents, ihixotropk additives, dispersants, cement set activators/accelerators, cement set retarders, and combinations thereof, in embodiments of the lime slurry, one or more of these additives may be added to the lime slurry before or after storing. Additionally one or more of these additives may be added to the lime slurry before or after mixing the lime slurry with the pozzokn slurry. A person having ordinary skill in the art, with the benefit of this disclosure, should readily be able to detenu ine the type and amount of additive useful for a particular application and desired result

[0037] Embodiments of the two-part set-delayed cement compositions may comprise a cement set retarder as described above. Any cement set retarder described in embodiments of the set-delayed cement compositions above may also be -suitable, for embodiments of the two-part set-delayed cement compositions. Cement set retarders may be added to one or both component slurries or may be added to the combined slurry. Amongst other reasons, cement set retarders may be added to increase thickening time, i some embodiments, the cement set retarder may be present In the component slurries (either individually or in both) or in the combined slurry of the two-part set-delayed cement compositions in an amount in the range of from about 0.01% to about 10% by weight of the pozzolan. In specific embodiments, the cement set retarder may be present in an amount

I S ranging between any of and/or including any of about 0.01%, about 0.1%, about 1%, about

2%, about 4%, about 6%, about 8%, or about 10% by weight of the pozzolan for the pozzolan slurry or by weight of the lime for the lime slurry. One of ordinary skill in the art, with the benefit of this disclosure, will, recognize the appropriate amount of the cement set retarder to include for a chosen application,

[0038] As previously mentioned, embodiments of the two-part set-delayed cement compositions .may optionally comprise a dispersani as described above. Any dispersant described in embodiments of the set-delayed cement compositions may also be suitable for embodiments of the two-part set-delayed cement, compositions. .In some embodiments, the dispersani may be included in one or both of the component slurries, or in the combined slurry of the two-part set-delayed cement compositions in an amount in the range of from about 0,01% to about 5% by weight of the pozzolan or the hydrated lime. In specific embodiments, the dispersant may be present in an amount ranging between any of and/or including any of about 0.0!%, about 0.1%, about 0.5%, about 1 %, about 2%, about 3%, about 4%, or about 5% by weight of the pozzolan o the hydrated lime. One of ordinary, skill in the art, with the benefit of this disciosure, will recognize the appropriate amount of the dispersant to Include for a chosen application.

[0030] Embodiments may include the addition of a cement set activator to the two- part set-delayed cement compositions as described above. The cement set activator may be included to accelerate setting times, amongst other reasons. Any cement set activator described in embodiments of the set-delayed cement compositions may also be suitable for embodiments of the two-part set-delayed cement compositions. Any cement set activator may be added to either one or both of the component slurries as well as to the combined slurry in an amount sufficient to accelerate the setting of the combined two-part set-delayed composition (if added to only a component slurry, the acceleration of the set time should happen when the component slurries are mixed), in embodiments, the cement set activator may be added to the component slurries (either individually or both) or to the combined slurry of the two-part set-delayed cement composition in an amount in the range of about 0.5 % to about 20% by weight of the pozzolan. In specific embodiments, the cement set activator may be present in the component slurries (either individually or in both) or in the combined slurry of the two-part set-delayed cement composition in an amount ranging between any of and/or including any of about. 0, 1%, about ! %, about 5%, about 10%, about 15%, or about 20% by weight of the pozzolan. One of ordinary skill in the art_.,, with the benefit of this disciosure, will recognize the appropriate amount of the cement set activator to include for a chosen application. [0040] Those of ordinar skill in th art will appreciate that embodiments of the two-part set-delayed cement compositions generally should have a density suitable for a particular application. By way of example, the combined two-part set-delayed cement compositions may have a density in the range of from about 4 pounds per gallon ("^'lb/gal") to about 20 ib/gal in certain, embodiments, tbe combined two-part set-delayed cement compositions may have a density in the range of from about 8 lb/gal to about 1.7 lb gal. Embodiments of the two-part set-delayed cement compositions may be foamed or unfbamed or may comprise other means to reduce their densities, such as hollow microspheres, low- density elastic beads, or other density-reducing additives known in the art. in embodiments, the density may be reduced after storage, but prior to placement in a subterranean formation, in embodiments, weighting additives may be used to increase the density of the two-part set- delayed cement compositions. Examples of suitable weighting additives may include barite, hematite, hausmannite, calcium carbonate, siderite, iimenite, or combinations thereof, in particular embodiments, the weighting additives may have a specific gravit of 3 or greater. Those of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate density for a particular application.

[0041] As previously mentioned, the component slurries of the two-part set-delayed cement compositions may have a delayed set in that, they remain In a pumpabie fluid state for at least one day (e.g., about I day. about 2 weeks, about 2 years or more) at room temperature (e.g., about 80* F) in quiescent storage. For example, the component slurries of the two-part set-deiayed cement compositions may remain in a pumpabie fluid state for a period of time from about 1 day to about 7 days or more, in some embodiments, the component slurries of the two-part set-delayed cement compositions may remain in a pumpabie fluid state for at least about i day, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about 60 days, or longer. A fluid is considered to be in a pumpabie fluid state where the fluid has a consistency of less than 70 Bearden units of consistency ("Be"), as measured on a pressurized consistometer in accordance with, the procedure for determining cement thickening times set forth in API RP Practice .10B-2, Recommended Pmetiee for Testing Well Cem is, First Edition, July 2005.

[0042] When desired for use. embodiments of the two-part set-delayed cement compositions may be activated (e.g., by combining the pozzo!an and lime slurries) to set into a hardened mass. B way of example, embodiments of the two-part set-delayed cement compositions may be activated to form a hardened mass in a time period in the range of from about 1 hour to about 12 hours. For example, embodiments of the two-part, set-delayed cement compositions may set to form a hardened mass in a time period ranging between any of and/or including any of about 1 day. about 2 days, about 4 days, about 6 days, about 8 days, about 10 days, or about 12 days.

[0043] In some embodiments, the two-part set-delayed cement compositions may set to have a desirable compressive strength after activation. Compressive strength is generally the capacity of a material or structure to withstand axiaily directed pushing forces. The compressive strength may be measured at a specified time after the two-part set-delayed cement composition has been activated and the resultant composition is maintained under specified temperature and pressure conditions. Compressive strength can be measured by either destructive or non-destructive .methods. The destructive method physically tests the strength of treatment fluid samples at various points in time by crushing the samples in a compression-testing machine. The compressive strength is calculated from the failure load divided by the cross-sectional area resisting the load and is reported in units of pound-force per square inch (psi ), ^'Non-destructive methods may employ a UCA^'" Ultrasonic Cement Analyzer, available from Fann Instrument Company, Houston, TX. Compressive strength values may be determined in accordance w ith API R.P 10B-2, Recommended Practice ar Testing Weil Cements, First Edition, July 2005.

[0044] By way of example, the two-part set-delayed cement compositions may develop a 24-hour compressive strength in the range of from about 50 psi to about 5000 psi, alternatively, from -about 100 psi to about 4500 psi, or alternatively from about 500 psi to about 4000 psi. In some embodiments, the two-part, set-delayed cement compositions may de velop a compressive strength in 24 hours of at least about 50 psi, at least about 1.00 psi, at least about 500 psi, or more, in some embodiments, the compressive strength values may be determined using destructive or non-destructive methods at a temperature ranging from 100° F to 200° I .

[0045] In some embodiments, the two-part set-delayed cement compositions may have desirable thickening times after activation. Thickening time typically refers to the time a fluid, such as a set-delayed cement composition, remains in a fluid state capable of being pumped. A number of different laboratory techniques may be used to measure thickening time, A pressurized consistometer. operated in accordance with the procedure set forth in the aforementioned API RP Practice 10B-2, may be used to measure whether a fluid is in a pumpable fluid state. The thickening time may be the time for the treatment fluid to reach 70 Be and may be reported as the time to reach 70 Be, In some embodiments, the two-part set- delayed cement compositions may have a thickening time of greater than about i hour, alternatively, greater than about 2 hours, alternatively greater than about 5 hours at between about 1 ,000 psi to about 20,000 psi and temperatures in a range of .from about 50° F to about 400° F, alternatively, in a range of from about 80° F to about 250° F, and alternatively at a temperature of about 1 0* F.

[0046] Embodiments of the two-part set-delayed cement composition may be used to displace a prior placed fluid (i.e. embodiments of the two-part set-delayed cement composition may be used as a spacer fluid). The pozxolan slurry of the two-part set-delayed cement composition_., comprising a posszolan and water, may be similar in composition to conventional spacer fluids. Because of this similarity, the pozzoSan slurry may be used as a spacer fluid in embodiments. The pozzoian slurry may be used to displace a drilling mud, separate cement from a drilling mud, displace another treatment fluid, separate the drilling mud from a treatment fluid, and/or separate cement from a treatment fluid. Advantageously, the use of the pozzolaa slurry as a spacer fluid may condition the subterranean formation with pari of the same composition that ultimately may be used as the annular sealant. Therefore, the risk of incompatibilities between sealant and spacer fluid may be reduced.

0047] in embodiments wherein the pozzolan component slurry of the two-part sei- delayed cement composition may be used as a spacer fluid, the density of the pozzolan slurry may be adjusted by the addition of water and/or a vlscosificr. The water and viseosificrs may be added in any amount to achieve the appropriate density to provide a suitable rheo!ogieaS hierarchy for a given application. An example of a suitable viscosiiler Is SA-1015™ suspending agent available from Halliburton Energy Services, Houston, TX. Additionally, weighting agents may be added to adjust the density as may be appropriate to maintain a suitable theological hierarchy. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate density and method of density adjustment necessary for a chosen application.

0048] Moreover, in embodiments wherein the pozzolan slurry may be used as a spacer fluid, the spacer fluid may be foamed with a foaming additive and/or a gas. The space fluid may be foamed, for example, to provide a spacer fluid with a reduced density. The gas used for foaming the composition ma be any suitable gas for foaming, including, but not limited to; air, nitrogen, or combinations thereof. Generally, the gas should be present in an amount sufficient to form the desired amount or quality of foam. Foaming additives ma be included in embodiments to, for example, facilitate foaming and/or stabilize the resultant foam formed therewith, Examples of suitable foaming additives include, but are not limited to; mixtures of an ammonium salt of an alkyl ether sulfate, a cocoamidopropyl betaine surfactant, a cocoamldopropyl dimethviamine oxide surfactant, sodium chloride, and wafer; mixtures of an ammonium salt of an alkyl ether sulfate surfactant, a cocoamidopropyl hydroxysuitaioe surfactant, a cocoamidopropyl dsniethyiamine oxide surfactant, sodium, chloride, and water; hydrolyzed keratin; mixtures of an ethoxylated alcohol ether sulfate surfactant, an alky! or alkeue amidapropyl betaine surfactant, and an a!kyi or alkene dimethylamlne oxide surfactant; aqueous solutions of an alpha-olefmic sulfonate surfactant and a betaine surfactant; and combinations thereof. An example of a suitable foaming additive is ZO ESEALANT™ 2000 agent, available from: Halliburton Energy Services, Houston, TX.

[0049] It is to be understood, that any additive, component, or embodiment disclosed herein may additionally be used or combined with embodiments of the two-part set-delayed cement composition. For example, previously described additives such as weighting agents, lightweight additives, gas-generating additives, meehamcai-property-enhancing additives, lost-circulation materials, filtration-control additives, fluid-loss-control additives, defoaming agents, foaming agents, thixotropie additives, dispersatits, cement set retarders, cement set activators accelerators, additional silica sources, and the like, and combinations thereof may all be used with embodiments of the pozzolan slurry, lime slurry, and the combined slurry of the two-part set-delayed cement compositions in the same manner as previously described. The two-part set-delayed cement composition embodiment is therefore inclusive of every additive, component, or other embodiment^" that may be used in combination; including the use of cement set activators and cement set retarders. For example, the two-part set-delayed cement composition may comprise a cement set activator to accelerate setting time and enhance earl strength, additionally or alternatively, the two-part set-delayed cement composition may comprise a cement set retarder to delay thickening time. Any additive, component_* or embodiment disclosed herein may be added to one or both of the component slurries or to the combined slurry of the two-part set-delayed cement compositions. Moreover, an additive, component, or embodiment disclosed herei that is used with the pozzolan slurry, the lime slurry, or the combined slurry may also be used with embodiments of the two-part set-delayed cement composition that comprise a spacer fluid.

[0050] As will be appreciated by those of ordinary skill in the art, embodiments of the set-delayed cement compositions including the two-part set-delayed cement compositions may be used in a variety of subterranean operations, including primar and remedial cementing, in some embodiments, a set-delayed cement composition (i the two- part set-delayed cement composition embodiments, this may be a combined two-part set- delayed cement composition) may be provided that comprises water, a pozzolan. hydrated lime, a cement set retarder, and optionally a dispersant The set-delayed cement composition may be introduced into a subterranean formation and allowed to set therein. As used herein, introducing the set-delayed cement composition into a subterranean formation includes introduction into any portion of the subterranean formation, including, without limitation, into a wellbore drilled into the subterranean formation, into a near wellbore region surrounding the wellbore, or into both. Embodiments may further include activation, of the set-delayed cement composition. The activation of the set-delayed cement composition may comprise, for example, addition of a cement set accelerator to the set-delayed cement composit ion or the mixing of the two component slurries of the two-part set-delayed cement composition.

[0051] In some embodiments, a set -delayed cement composition may be provided that comprises water, a pozxokm, hydrated lime, a cement set retarder, and optionally a dispersani. The set-delayed cement composition: may be stored, for example, in a vessel or other suitable container. In alternative embodiments a two-part set-delayed cement composition, may be provided that comprises a .first part comprising a pozzolan and water component slurry and a second part comprising a hydrated lime and water component slurry. The first and second parts may individually stored and combined prior to or while pumping downhole. The- set-delayed cement compositions may be permitted to remain in storage for a desired time period, for example, the set-delayed cement compositions may remain in storage for a time period of about ί day, about 2 weeks, about 2 years, or longer. For example, the set-delayed cement compositions may remain in. storage for a time period of about I day, about 2 days, about 5 days, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about 60 days, or up to about 2 years, in some embodiments, the set-delayed cement composition may remain in storage tor a time period in a range of from about 1 day to about 2 years or longer, Thereafler, the set-delayed cement composition may be activated, for example, by mixing the two-component slurries together, introduced into a subterranean, formation, and allowed to set therein,

[0052] In primary cementing embodiments, for example, embodiments of the set- delayed cement composition may be introduced into an annular space between a conduit located in a wellbore and the walls of a wellbore (and or a larger conduit in the wellbore), wherein the wellbore penetrates the subterranean, formation. The set-delayed cement composition may be allowed to set in the annular space to form an annular sheath of hardened cement. The set-delayed cement composition may form a barrier that prevents the migration of fluids in the wellbore. The set-delayed cement composition may also, for example, support the conduit in the wellbore,

[0053] In remedial cementing embodiments, a set-delayed cement composition may be used, for example, in squeeze-cementing operations or in the placement of cement plugs. By way of example, the set-delayed composition may be placed in a wellbore to plug an. opening (e.g., a void or crack) in the formation, in a gravel pack, in the conduit, in the cement sheath., and/or between the cement sheath and the conduit (e.g., a microammlus).

[0054] An embodiment comprises a method of cementing comprising: providing a pozzolan slurry comprising a pozzolan and water: providing a lime slurry comprising hydrated lime and water; allowing the pozzolan slurry and the lime slurry to remain separate for aboui one day or longer; mixing the pozzolan slurr and the lime slurr to form a cement composition; and allowing the cement composition to set.

[0055] An embodiment comprises a method of displacing a fluid in a subterranean formation comprising: providing a pozzolan slurry comprising a pozzolan and water; providing a lime slurry comprising hydrated lime and water; introducing at least a portion, of the pozzolan slurry into a wellbore that penetrates a subterranean formation such mat the pozzolan slurry displaces at least one fluid from the wellbore; activating the set-delayed cement composition by mixing at least a portion of the pozzolan slurr and at least a portion of the lime slurry to form a cement composition; introducing the cement composition into a subterranean, formation; and allowing the cement composition to set in the subterranean, formation,

[0056] An embodiment comprises a system for cementing comprising: a pozzolan slurry comprising a pozzolan and water; a lime slurry for combination with the pozzolan slurry to form a cement composition comprising hydrated lime and water,

[0057] Referring now to FIG. I , preparation of a set-delayed cement composition in accordance with example embodiments will now be described. FIG. 1 illustrates a system 2 for preparation of a set-delayed cement composition and delivery to a wellbore in accordance with certain embodiments. As shown, the set-delayed cement composition may be mixed in mixing equipment 4, such as a jet mixer, re-circulating mixer, or a batch mixer, for example, and then pumped via pumping equipment 6 to the wellbore. hi some embodiments, the mixing equipment 4 and the pumping equipment 6 may be disposed on one or more cement trucks as will be apparent to those of ordinary skill in the art. in some embodiments, a jet mixer may be used, for example, to continuousl .mix the lime/settable material with the water as it is being pumped to the wellbore. In two-part set-delayed embodiments, mixing equipment (e.g., a jet mixer, re -circul ting mixer, and/or a batch mixer) may be used to mix the combined two-part set-delayed cement composition slurry.

0058] An example technique for placing a set-delayed cement composition into a subterranean formation will now be described with reference to FIGS. 2A and 2B. FIG. 2A illustrates surface equipment 10 that may be used i placement of a set-delayed cement composition in accordance with certain embodiments, it should be noted that while FIG. 2A generally depicts a land-based operation,, those skilled in the art will readily recognize that the principles described herein are equally applicable to subsea operations that employ ^•floating or sea-based platforms and rigs, without departing from the scope of the disclosure. As illustrated by FIG. 2A, the surface equipment S O may include a cementing unit 12, which ma include one or more cement trucks. The cementing unit 12 may include mixing equipment 4 and pumping equipment 6 (e.g., FIG. I) as will be apparent to those of ordinary skill in. the art. The cementing unit 12 may pump a set-delayed cement composition 14 through a feed pipe 16 and to a cementing head .18 which conveys the set-delayed cement composition 14 downhoie.

[00591 Turning now to FIG. 2B, the set-delayed cement composition 14 may be placed into a subterranean formation 20 in accordance with example embodiments. As illustrated, a wellbore 22 may be drilled into the subterranean formation 20, While wellbore 22 is shown extending generally vertically into the subterranean formation 20, the principles described herein are also applicable to vellbores that extend at an angle through the subterranean, formation 20, such as horizontal and slanted weilbores. As illustrated, the wellbore 2,2 comprises walls 24. In the illustrated embodiment, a surface casing 26 has been Inserted into the wellbore 22. The surface casing 26 may be cemented to the wails 24 of the wellbore 22 b cement sheath 28. In the illustrated embodiment, one or more additional conduits (e.g., intermediate casing, production casing, liners,, etc.), shown here as casing 30 may also be disposed in the wellbore 22. As illustrated, there is a wellbore atmulus 32 formed between the casing 30 and the walls 24 of the wellbore 22 and/or the surface casing 26. One or more centralizers 34 may be attached to the casing 30. for example, to centralize the easing 30 in the wellbore 22 prior to and during the cementing operation.

[0060] With continued reference to FIG. 2,8, the set-delayed cement composition 14 may he pumped dow the interior of the casing 30, The set-delayed cement composition 1.4 may be allowed to flow down the interior of the casing 30 through the casing shoe 42 at the bottom of the easing 30 and u around the easing 30 into the wellbore. an.nu.lus 32. The set- delayed cement composition 14 may he allowed to set in the wellbore annulus 32, for example, to form a cement sheath that supports and positions the casin 30 in the wellbore 22. While not illustrated, other techniques may also be utilized for introduction of the set- delayed cement composition 14. By way of example, reverse circulation techniques may he used that include introducing the set-delayed cement composition 14 into the subterranean formation.20 by wa of the wellbore annulus 32 instead of through the easing 30.

[0061 ] As it is introduced, the set-delayed cement composition 14 may displace other fluids 36, such as drilling fluids and/or spacer fluids tha may be present in the interior of the casing 30 and/or the wellbore annulus 32, At least a portion of the displaced fluids 36 may exit the wellbore annulus 32 via a flow line 38 and be deposited, for example, in one or more retention pits 40 (e.g., a mud pit), as shown on FIG. 2 A. Referring again to FIG. 2B, a bottom plug 44 may be introduced into the wellbore 22 ahead of the set-delayed cement composition 14, for example, to separate the set-delayed cement composition .14 from the fluids 36 that may he inside the easing 30 prior to cementing. After the bottom plug 44 reaches- the landing collar 46, a diaphragm or other suitable device should rupture to allow the set-delayed cement composition 14 through the bottom ping 44. hi FIG. 2B, the bottom plug 44 is shown on the landing collar 46. In the illustrated embodiment, a top plug 48 may be introduced into the wellbore 22 behind the set-delayed cement composition 14, The top plug 48 may separate the set-delayed cement composition 14 from a displacement fluid 50 and also push the set-delayed cement composition Ϊ4 through the bottom plug 44.

[0062] ^'The exemplary set-delayed cement compositions disclosed herein may directly or indirectly affect one or more components or pieces of equipment associated with the preparation, delivery, recapture, recycling, reuse, and/or disposal of the disclosed set- delayed cement compositions. For example, the disclosed set-delayed cement compositions may directly or indirectly affect one or more mixers, related mixing equipment, mud pits, storage facilities or units, composition separators, heat exchangers, sensors, gauges, pumps, compressors, and the like used generate, store, monitor, regulate, and/or reconditio the exemplary set-delayed cement compositions. The disclosed set-delayed cement compositions may also directly or indirectly affect any transport or delivery equipment used to convey the set-delayed cement compositions to a well site or -downhole such as, for example, any transport vessels, conduits, pipelines, trucks, tubuSars, and or pipes used to compositi n all move the set-delayed cement compositions from one location to another, any pumps, compressors, or motors (e.g., topside or downhole) used to drive the set-delayed cement compositions into motion, any valves or related joints used to regulate the pressure or flow rate of the set-delayed cement compositions, and any sensors (i.e., pressure and temperature), gauges, and/or combinations thereof, and the like. The disclosed set-delayed cement compositions may also directly or indirectly affect the various downhole eqiiipraent and tools that may come into contact with the set-delayed cement compositions such as, but not limited to, wellbore casing, wellbore liner, completion string, insert, strings, drill string, coiled tubing, slickiine, wireline, drill pipe, drill collars, mud motors, downhole motors and/or pumps, cement pumps, surface-mounted motors and/or pumps, ceniralizers, turbo! teers. sc-ra.tc-he.rs, floats (e.g.. shoes, collars, valves, etc), logging tools and related telemetr equipment, actuators (e.g., electromechanical devices, hydromeehameal devices. etc.), sliding sleeves, production sleeves, plugs, screens, filters, flow control devices (e.g., inflow control devices, autonomous inflow control devices, outflow control devices, etc.), couplings (e.g., electro-hydraulic wet connect, dry connect, inductive coupler, etc.), control lines (e.g., electrical, fiber optic, hydraulic, etc.), surveillance lines, drill bits and reamers, sensors or distributed sensors, downhole heat exchangers, valves and corresponding actuation devices, too! seals, packers, cement plugs, bridge plugs, and other wellbore isolation devices, or components, and the like.

EXAMPLES

[0063] To facilitate a better understanding of the present embodiments, the following examples of certain aspects of some embodiments are gi ven.. In no way should the following examples be read to limit, or define, the entire scope of the embodiments.

Example 1

[0064] A two part set-delayed cement composition was prepared which comprised the following component slurries:

Table I

Slurry A Compositional Makeup Slurry B Com ositional Makeup

[0065] Slurry A was prepared in a Waring* blender by first adding water to the blender followed by a dispersant, Liquimeni*¹ 558 I F dispersant. The dispersant was allowed to fully disperse, then the pumice, silica (Silica! tie^'4' cement, additive), and a weight additive (MicroMax* FF weight additive) were added. After all of the components were added, Slurry A was blended at a speed of 6000 rpra for 40 seconds to fully homogenize the sample. Slurry B was prepared in the same manner as Slurry A. The calculated density of Slurry A was 13.33 pounds per gallon (ppg) and Slurry B was 12.75 ppg.

0066] Immediately after preparation (designated Day 0) and periodically thereafter, the rheological properties of the samples were determined using a Model 35A Fann Viscometer and a No. 2 spring with a Fann Yield Stress Adapter (FYSA), in accordance with the procedure set forth in API IIP Practice 108-2, Recommended Practice for Testing Well Cements. Dispersant was added as needed io maintain adequat viscosity values. % bwoP refers to "percent by weight of the pumice," and % hwoHL refers to "percent by weight of hydrated lime,"

Fable 2

Slurry A heulogkal Profile

Fable 3

Slurry B Rheoiogical Profile

[0067] To form the sellabl combined slurry, 129,4 grams of Slurry B was added to 500.0 grams of Slurry A, This was performed by adding Slurry A to a Waring"' blender set to 4000 rpm and slowly pouring in Slurry B to form Slurry A8 with a final slurry composition of: Table 4

AB Compositional Makeup

[0068] The calculated density of Slurry AB was 13,23 ppg. A portion of Slurry AB was accelerated with 10% bwoP Ca(¾ by mixing 200.0 grams of Slurry AB with 21.92 grams of 43% CaC!j. solution. This sample is shown in table 5 as accelerated, immediately after preparation, the rheology of the sample was measured using a Model 35A Pann Viscometer and a No. 2 spring with a Fann Yield Stress Adapter (FYSA), in accordance with the procedure set forth in API RP Practice ! OB-2 , Recommended Practice for Testing Weil Cement*.

Table 5

Slurry AB Rlieoioaical Profile

Accelerated j 1 2 j 12 j 28 j 50 j i 1

[0069] After mixing the two component slurries to activate the .set-delayed cement composition, the combined slurry was cured in a 2" by 4" plastic cylinder that was placed in a water bath at between about 0° F to about 150° P to form set cylinders. Then the destructive compressive strength (C.S.) was measured using a mechanical press in accordance with API RP Practice lOB-2, Recommended Practice for Testing Well Cements, The results of this test are set forth in Table 6 below. The reported compressive strengths are an average for two cylinders of each sample. Compressive strength measurements were taken at 24 hours,

[0070] For comparison, a non-two part set-delayed slurry was prepared by combining 350 grams water, 500 grams pumice, 100 grams hydrated lime, 20 grams Mier max^'*^' weight additive, 6.25 grams Micro Matrix^'"' cement reiarder, and 3.5 grams Liquiment* 5581 dispersant. This slurry (NCI ) was aged 35 days prior to use, activated with 10% bwoP CaC solution, and cured in the water baths at the same time as Slurry AB.

Table 6

Compressive Strength Tests

[0071] As Example i shows, slurry AB is more active at lower temperatures than NCL Without being limited by theory, this effect ma be due to the lack of cement retarders in slurry AB and/or the inclusion of a -silica -additive.

1 0 Example 2

[0072] in the previous examples the poxzo!an and lime slurries were mixed to give a hydrated lime content of 20.0% hwoP, The next example illustrates how it may he advantageous to mix the two parts in different ratios to produce slurries with varying lime content. In this example. 258_*8 grams of Slurry B was mixed with 500.0 grams of Slurry A. to give a iime ί Sconterst of 40% bwoP:

Table ?

Slurry AB Compositional Makeup

Component % hwoP I

Water 1 15.0 Pumice i .o 1

Silica Additive 20.0

H drated .Lime 40.0

Weighting Agent 14.0

Dispersant 0.93

[0073] After mixing, this sample was cured in a water bath at 90° F for 24 hours then crushed to obtain a compressive strength of 150 psi. The strength of this sample was about 33% greater than the sample with only 20% lime content (105 psi).

Example 3.

[0074] A two part set-delayed cement composition was prepared which comprised the following component slurries:

Table 8

Slurry€ Compositional Makeup Slurry D Compositional Makeup

0075] Slurry C was prepared in a Waring* blender by first adding water to the blender followed by a dispersant, Liquimeni* 558 I F dispersant. The dispersant was allowed to fully disperse, then the pumice and a weight additive (Miero ax*^' FF weight additive) were added. After all of the components were added. Slurr C was blended at a speed of 6000 rpm for 40 seconds to fully homogenize the sample. Slurry D was prepared in the same maimer as Slurry C. The calculated density of Slurry C was 13.24 pounds per gallon (ppg) and Slurry B was 12,75 ppg.

[0076] immediately after preparation (designated Day 0) and periodically thereafter, the theological properties of the samples were determined using a Mode! 35A Fann Viscometer and a No. 2 spring with a Fann Yield Stress Adapter (FYS A), in accordance with the procedure set forth in API F Practice 10B-2, Recommended Practice for Testing Wei! Cements. Dispersant was added as needed to maintain adequate viscosity values.

Table 9

C beological Profile FYSA Readings Additional

Dispersant

3 6 100 200 300 3D 6D f% bwoP)

Day 0 3 4 83.5 1 ? 251 0.5 0.5 —

Day 3 14.5 16,5 46 75 104 7 S —

Da 7 5 8 81 154.5 224 1 0.01

Day 40 4 6.5 56.5 106 154 1.5 1.5 0.02

Table 10

Slurry D Rheotogi al Profile

[0077] To form the sellable combined slurry. .129.4 grams of Slurr D was added to 500.0 grains of Slurry C. ^'i is was performed by adding Slurry C to a Waring* blender set to 4000 rpm and slowly pouring in Slurry D to form Slurry CD with a final slurry composition

Table 11

Slurry CD Compositional Makeup

Hydrated Lime 20.0 I

Weighting Agent Ϊ6.5

Dispersant 0.80

[0078] The calculated density of Slurry CD was 13.13 ppg. A portion of Slurry CD was accelerated with 10% bwoP CaC¾ by mixing 200.0 grams of Slurry CD with 21.51 grams of 43% CaCla solution. This sample is shown in table I I as accelerated, immediately after preparation, the rheology of the sample was measured using a Mode! 35A Fann Viscometer and a No. 2 spring with a Fann Yield Stress Adapter (FYS A), in accordance with the procedure set forth in API RP Practice I B-2, Recommended Practice for Testing Wei! Cements.

Table 12

Slurry CD Rheological Profile

0079] After mixing the two component slurries to activate the set-delayed cement composition, the combined slurry was cured in a 2" by 4" plastic cylinder that was placed in a water bath at I 0^c F to form set cylinders. Then the destructive compressive strength (C.S.) was measured using a mechanical press in accordance with API RP Practice I0B-2, Recommended Practice for Testing Weil Cements, The results of this test are set forth in Table 12 below. The reported compressive strengths are an average for two cylinders of each sample. The samples and controls- were cured at 1 atmosphere, between about 90° F to about 150* F; compressive strength measurements were taken at 24 or 48 hours.

[0080] For comparison, a non-two part set-delayed slurry was prepared by combining 350 grams water, 500 grams pumice, 100 grams hydraied lime, 20 grams Mieromax*^' weight additive, 6.25 grams Micro Matrix*^' cement reiarder, and 3,5 grams Liquirnent* 558 IF dispersant. This slurry (NC I ) was aged 35 days prior to use, activated with 10% bwoP CaCii solution, and cured in the water baths at the same time as Slurry AB. Table Ϊ3

Compressive Strength Tests

* Slurry remained unset and fio afale

** Slurry was gelled and not flowahle

Example 4

10081 j A two part set-delayed cement composition was prepared which comprised the following component slurries:

Table 14

Slurry E Compositional Makeup Slurry F Compositional Makeup

Component Weight (g)

Water 150.0

Hydrated Lime 200.0

Dispersant 0.7

[0082] Slurry E was prepared in a Waring*^' blender by first adding water to the blender followed by a dispersant, Liquiment*^' 558 I F dispersant, The dispersant was allowed to fully disperse, then the pumice was added. After all of the components were added. Slurry B was blended at a speed o 000 rpm for 40 seconds to fully homogenize the sample. Slurry F was prepared In the same manner as Slurry E. The calculated density of Slurry E was 13,4 pounds per gallon (ppg) and Slurry F was 12,4 ppg. Slurr E and Slurry F were then stored for 48 hours. After 48 hours neither siurry contained free water. However, Siurry F was slightly gelled and required mixing to make, it fiowable.

[0083] At 48 hours, 778.7 grams of Slurry E was added to 1 5.4 grams of Slurry F, This was performed by adding Slurry E to a Waring*^" blender set to 4000 rpro and slowly pouring in Slurry F to form Slurry EF. When they were mixed a gel formed and 1 ,0 gram of dispersant (Liquiment* 558 I F dispersant) was added to make the mixture flowable.

Table 15

Compositional Mix of Slurry .EF

100841 The calculated density of the final slurry was 13.2 ppg. 15.0 grams of CaCb powder (2,5% bwoP+HL) was added to the final slurry before placing it in a consistometer. The thickening time was measured as 5:38 hours at 140° F and 3000 psi. The thickening tim was measured using a high-temperature high-pressure consistometer in accordance with the procedure for determining cement thickening times set forth in API. RP Practice 108-2, Recommended Practice for Testing Well Cements, First Edition, July 2005.

[0085] it should be understood that the compositions and methods are described in terms of "comprising," "containing," or "including^"" various components or steps, the compositions and methods can also "consist essentially of or "consist of the various components and steps. Moreover, the indefinite articles " " or "an," as used in the claims, are defined herein to mean one or more than one of the element that it introduces.

[0086] For the sake of brevity, only certain ranges are explicitly disclosed herein.

However, ranges from any lower limit ma be combined with any upper limit to recite a range not explicitly recited, as well as, ranges from any lower limit may be combined with any other lower limit to recite a range not explicitl recited, in the same way, ranges from any upper limit may be combined with any other upper limit to recite a range not explicitly recited. Additionally, whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range are specifically disclosed. In particular, every range of values (of the form, "from about a to about bf or, equivalenily, "from approximately a to b," or, equivalentiy, "from, approximately a-b") disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values even if not explicitly recited. Thus, every point or indi vidual value may serve as sis own lower or upper limit combined with any other point or individual value or any other lower or upper limit, to recite a range not explicitly recited.

[0087] Therefore, the present embodiments are. well adapted to attain the ends and advantages mentioned as. well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, and ma be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Although individual embodiments are discussed, the disclosure covers all combinations of ail of the embodiments, Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. Also, the terms in the claims have their plain, ordinar meaning unless otherwise explicitly and clearly defined by the patentee. It is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit, of those embodiments. If there is any conflict in the usages of a word or term in this specification and one or more patent(s) or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted.

Claims

What is claimed is:

1. A method of cementing comprising:

providing a pozzolan slurry comprising a pozzolan and water;

providing a lime slurry comprising hydrated lime and water;

allowing the pozzolan slurry and the lime slurry to remain separate for about one day or longer;

mixing the pozzolan. slurry and the lime slurry to form a cement composition; and

allowing the cement composition to set.

2. A method according to claim I wherein the cement composition is introduced into a weSl ore penetrating a subterranean formation and allowed to set within,

3. A method according to claim I or 2 wherein the pozzolan is selected from the group consisting of fly ash, silica, fume, metakaoHn, pumice, and any combination thereof,

4. A method according to any of claims I to 3 wherein at least one of the pozzolan slurry, the lime slurry, or the cement composition further comprises a dispersant

5. A method according to claim 4 wherein the dispersant comprises at least one dispersant selected from the group consisting of a sulfonated-fonnaldehyde-based dispersant a polyearboxylated ether dispersant, and any combination thereof;

6. A method according t any of claims 1 to 5 wherein at least one of the poxzolan slurry, the lime slurry, or the cement composition further comprises a cement set retarder,

7. A method according to claim 6 wherein the cement set retarder is selected from the group consisting of a phosphonic acid, a phosphonic acid derivative, a Hgnosui.fbna.te, a. salt, an organic acid, a carboxymethylated hydroxyethyiated cellulose, a synthetic co~ or ter-polymer comprising sulfonate and carboxylic acid groups, a borate compound, and any combination thereof.

S, A method according to any of claims I to 7 wherein at least one of the pozzolan slurry, the lime slurry, or the cement composition further comprises a cement set activator; wherein the cement set activator comprises at least one cement set activator selected from the group consisting of an amine, a silicate, zinc formate, calcium acetate, a Group ΪΑ hydroxide; a Group II A hydroxide, a monovalent salt, a divalent salt, nanosilica, a polyphosphate, and any combination thereof.

9, A method accordin to any of claim 1 to 8 further comprising storing at least one of the pozzolan slurry or the lime slurry fo a time period of about 7 days or longer prior to the step of mixing.

10. A method accord ing to any of claims 1 to 9 further comprising pumping the cement composition through a feed pipe and into a wellbore annulus that is penetrating the subterranean, formation.

1 1. A method of displacing a fluid in a subterranean formation comprisi n g:

providing a pozzolan slurry comprising a pozzolan and water;

providing a lime slurry comprising hydrated lime and water;

introducing at least a portion of the pozzolan slum' into a well bore that penetrates a subterranean formation such thai the pozzo^'lan slurry displaces at least one fluid from the wellbore;

activating the set-delayed cement composition by mixing at least a portion of the pozzolan slurry and at least a portion of th lime slurry to form a cement ^•composition;

introducing the cement composition into a subterranean formation; and

allowing the cement composition to set in. the subterranean fonnasion.

12. A method according to claim 1 1 wherein the pozzolan is selected from the group consisting of fly ash, silica fume, metakaolm, pumice, and any combination thereof.

13. A method according to claim 1 1 or 12 wherein the portion of the pozzolan slurry that displaces at least one fluid from the wellbore is foamed prior to displacing at least one fluid from the wellbore.

14. A method accordin to any of claims 11 to 13 wherein at least one of^" the pozzolan slurry, the lime slurry, or the cement composition further comprises a dispersant.

15. A method according to any of claims I I to 14 wherein a least one of the pozzolan. slurry, the lime slurry, or the cement composition further comprises a cement set retarder,

16. A method according to any of claims 1 1 to 15 wherein at least one of the pozzolan. slurry, the lime slurry, or the cement composition, comprises a cement set activator.

17. A method according to any of claims 1 1 to 16 further co prising storing at least one of the pozzolan slurry or the .time slurry for a time period of about 7 days or longer prior to the step of mixing.

18. A. method according to any of claims I I to 17 further comprising pumping the cement composition through a feed pipe and into a wellbore aonuius that is penetrating the subterranean formation.

19. A system for cementing comprising;

a poxzolan slurry comprising a pozzoian and water;

a lime slurry for combination with the po∞>Ian slurry to form a cement composition, wherein the lime slurry comprises hydrated lime and water,

20, The system of claim 19 further comprising mixing equipment for mixing the poxzolan slurry and the lime slurry to form the cement composition, and pumping equipment for delivering the cement composition into a we!ibore.