Background: A variety of veneering options to zirconia frameworks are now available. The purpose ... more Background: A variety of veneering options to zirconia frameworks are now available. The purpose of this study is to evaluate the effect of veneer materials, veneering methods, cement materials, and aging on the failure load of bilayered veneer zirconia. Material and methods: Zirconia bars (20 × 4 × 1 mm) were veneered to 2 mm total thickness (n = 10/group). Veneering method groups included: 1. Hand-layered feldsparthic porcelain (VM = Vita VM9, Vident) and fluorapatite glass–ceramic (CR = IPS e.max Ceram, IvoclarVivadent); 2. Pressed feldspathic porcelain (PM = Vita PM9, Vident) and fluorapatite glass–ceramic (ZP = IPS e.max ZirPress, IvoclarVivadent); 3. CAD-/CAM-milled feldspathic ceramic (TF = Vitablocs Triluxe Forte, Vident) and lithium-disilicate glass–ceramic (CAD = IPS e.max CAD, IvoclarVivadent). CAD/CAM veneers were either cemented with resin cements (P = Panavia21, KurarayDental), (R = RelyX Ultimate, 3M ESPE), (M = Multilink Automix, Ivoclar Vivadent) or fused with fusio...
Statement of problem: Current techniques for repairing porcelain-chipped restorations have severa... more Statement of problem: Current techniques for repairing porcelain-chipped restorations have several limitations. With advances in CAD/CAM technology, the combination of resin cements and high-strength ceramic materials might offer new options for repairing the chipping of veneering ceramic. Purpose: The purpose of this study is to compare the load-to-failure of veneered zirconia crowns repaired by different materials. Material and Methods: Veneered zirconia crowns were made on aluminum dies (n = 10/group). Feldspathic porcelain (Vita VM9, Vident) was applied to the zirconia coping (Vita In-Ceram YZ, Vident) in a cylindrical shape (Ø 10.5 mm, height 7.5 mm). A bevel cut on the porcelain veneer (45 degree, 3 mm width) was made at one side of each crown to simulate porcelain chipping. The crowns were then divided into four different groups according to the repair materials: 1. Conventional resin composite (A; Tetric EvoCeram, Ivoclar Vivadent); 2. Flowable resin composite (B; G-aenial U...
Objective. The purpose of this study was to evaluate the effect of glazing on flexural strength o... more Objective. The purpose of this study was to evaluate the effect of glazing on flexural strength of highly translucent zirconia materials. Materials and Methods. Specimens of three brands of zirconia bars (Prettau Zirconia, Zirkonzahn; inCoris TZI, Sirona; and Zirlux FC, Pentron Ceramics) were prepared and polished according to manufacturers’ instructions. Final specimen dimensions were 20 × 4 × 2 mm. The specimens from each brand were divided into 3 groups (N = 10): control, heat-treated, and glazed. Heat-treated specimens were fired without the application of the glaze material. The glaze material was applied to the glazed specimens before being fired. A three-point bending test (15 mm span) was performed in an Instron universal testing machine (ISO 6872). Data were analyzed by ANOVA and Tukey’s HSD post hoc test (α = 0.05). Results. Two-way ANOVA showed a significant influence of surface treatments on flexural strength of zirconia materials (P≤0.05). There was no significant diffe...
Background: A variety of veneering options to zirconia frameworks are now available. The purpose ... more Background: A variety of veneering options to zirconia frameworks are now available. The purpose of this study is to evaluate the effect of veneer materials, veneering methods, cement materials, and aging on the failure load of bilayered veneer zirconia. Material and methods: Zirconia bars (20 × 4 × 1 mm) were veneered to 2 mm total thickness (n = 10/group). Veneering method groups included: 1. Hand-layered feldsparthic porcelain (VM = Vita VM9, Vident) and fluorapatite glass–ceramic (CR = IPS e.max Ceram, IvoclarVivadent); 2. Pressed feldspathic porcelain (PM = Vita PM9, Vident) and fluorapatite glass–ceramic (ZP = IPS e.max ZirPress, IvoclarVivadent); 3. CAD-/CAM-milled feldspathic ceramic (TF = Vitablocs Triluxe Forte, Vident) and lithium-disilicate glass–ceramic (CAD = IPS e.max CAD, IvoclarVivadent). CAD/CAM veneers were either cemented with resin cements (P = Panavia21, KurarayDental), (R = RelyX Ultimate, 3M ESPE), (M = Multilink Automix, Ivoclar Vivadent) or fused with fusio...
Statement of problem: Current techniques for repairing porcelain-chipped restorations have severa... more Statement of problem: Current techniques for repairing porcelain-chipped restorations have several limitations. With advances in CAD/CAM technology, the combination of resin cements and high-strength ceramic materials might offer new options for repairing the chipping of veneering ceramic. Purpose: The purpose of this study is to compare the load-to-failure of veneered zirconia crowns repaired by different materials. Material and Methods: Veneered zirconia crowns were made on aluminum dies (n = 10/group). Feldspathic porcelain (Vita VM9, Vident) was applied to the zirconia coping (Vita In-Ceram YZ, Vident) in a cylindrical shape (Ø 10.5 mm, height 7.5 mm). A bevel cut on the porcelain veneer (45 degree, 3 mm width) was made at one side of each crown to simulate porcelain chipping. The crowns were then divided into four different groups according to the repair materials: 1. Conventional resin composite (A; Tetric EvoCeram, Ivoclar Vivadent); 2. Flowable resin composite (B; G-aenial U...
Objective. The purpose of this study was to evaluate the effect of glazing on flexural strength o... more Objective. The purpose of this study was to evaluate the effect of glazing on flexural strength of highly translucent zirconia materials. Materials and Methods. Specimens of three brands of zirconia bars (Prettau Zirconia, Zirkonzahn; inCoris TZI, Sirona; and Zirlux FC, Pentron Ceramics) were prepared and polished according to manufacturers’ instructions. Final specimen dimensions were 20 × 4 × 2 mm. The specimens from each brand were divided into 3 groups (N = 10): control, heat-treated, and glazed. Heat-treated specimens were fired without the application of the glaze material. The glaze material was applied to the glazed specimens before being fired. A three-point bending test (15 mm span) was performed in an Instron universal testing machine (ISO 6872). Data were analyzed by ANOVA and Tukey’s HSD post hoc test (α = 0.05). Results. Two-way ANOVA showed a significant influence of surface treatments on flexural strength of zirconia materials (P≤0.05). There was no significant diffe...
Uploads
Papers by Arthur Sun